CN103160092A - 一种无卤抗菌阻燃的不饱和聚酯模塑料 - Google Patents
一种无卤抗菌阻燃的不饱和聚酯模塑料 Download PDFInfo
- Publication number
- CN103160092A CN103160092A CN201110422189XA CN201110422189A CN103160092A CN 103160092 A CN103160092 A CN 103160092A CN 201110422189X A CN201110422189X A CN 201110422189XA CN 201110422189 A CN201110422189 A CN 201110422189A CN 103160092 A CN103160092 A CN 103160092A
- Authority
- CN
- China
- Prior art keywords
- parts
- unsaturated polyester
- fire
- antibiotic
- halogen
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种无卤抗菌的阻燃的不饱和聚酯模塑料，属于热固性模塑料技术领域。其是由以下重量份数的原料构成：不饱和聚酯树脂
36~41
份；低收缩添加剂
24~28.6
份；引发剂
0.6~1.1
份；阻聚剂
0.006~0.01
份；增稠剂
0.16~0.5
份；填料
100~140
份；阻燃剂
5~10
份；脱模剂
2.4~3.2
份；抗菌剂
0.1
～
0.3
份；增强纤维
26~34
份。本发明提供的无卤抗菌的阻燃的不饱和聚酯模塑料具有强度好、收缩低、电性能优异、抵抗细菌侵蚀、阻燃的特点。
Description
技术领域
本发明属于热固性模塑料技术领域，具体涉及一种无卤抗菌阻燃的不饱和聚酯模塑料。
背景技术
不饱和聚酯模塑料具有比强度高，电性能好，成型加工容易等优点，被人们广泛使用。随着不饱和聚酯模塑料不断的用于日用家电器，随着时间延长，电器会被细菌腐蚀，产生难闻的气味。近年火灾频繁发生，造成的人员死亡也是越来越多，据统计，大部分火灾致人死亡是由于浓烟窒息导致的，因此，开发抗菌、阻燃、少烟的材料是当务之急。
发明内容
本发明的任务是提供一种强度好、收缩低和环保抗菌的无卤抗菌阻燃的不饱和聚酯模塑料。
本发明的任务是这样来完成的，一种无卤抗菌的阻燃的不饱和聚酯模塑料，其是由以下重量份数的原料构成：
不饱和聚酯树脂36～41份；
低收缩添加剂24～28.6份；
引发剂0.6～1.1份；
阻聚剂0.006～0.01份；
增稠剂0.16～0.5份；
填料100～140份；
阻燃剂5～10份；
脱模剂2.4～3.2份；
抗菌剂0.1～0.3份；
增强纤维26～34份。
在本发明的一个实施例中，所述的不饱和聚酯树脂为邻苯型不饱和聚酯树脂，其树脂固含量为58～63％。
在本发明的另一个实施例中，所述的低收缩添加剂为聚甲基丙烯酸甲酯型低收缩剂，低收缩添加剂其固含量为40～42％。
在本发明的又一个实施例中，所述的引发剂为过氧化苯甲酸叔丁酯。
在本发明的再一个实施例中，所述的阻聚剂为对苯醌。
在本发明的还有一个实施例中，所述的增稠剂为轻质氧化镁。
在本发明的更而一个实施例中，所述的填料为氢氧化铝。
在本发明的进而一个实施例子中，所述的阻燃剂是三聚氰胺焦磷酸盐。
在本发明的又更而一个实施例中，所述的脱模剂是硬脂酸锌、硬脂酸钙中的任意一种。
在本发明的又进而一个实施例中，所述的抗菌剂为苯并咪唑基氨基甲酸酯，所述的增强纤维为无碱玻璃纤维。
本发明提供的无卤抗菌的阻燃的不饱和聚酯模塑料具有强度好、收缩低、电性能优异、抵抗细菌侵蚀、阻燃的特点。可应用于开关、日用电器外壳等制件。经过测试，弯曲强度90MPa，冲击强度(无缺口)30KJ/m2，收缩率小于0.15％，电阻1×1013Ω，电气强度12.0MV/m，介电损耗因数0.015，耐电弧180S，耐漏电起痕指数600V垂直燃烧(UL-94-V-01.6mm)V-0。
具体实施方式
实施例1
邻苯型不饱和聚酯树脂52份；
聚甲基丙烯酸甲酯型低收缩剂36.5份；
过氧化苯甲酸叔丁酯0.4份；
对苯醌0.006份；
轻质氧化镁0.12份；
氢氧化铝162份；
三聚氰胺焦磷酸盐21份；
硬脂酸钙2.2份；
苯并咪唑基氨基甲酸酯0.1份；
玻璃纤维35.2份。
具体实施时，首先把上述比例的邻苯型不饱和聚酯树脂、聚甲基丙烯酸甲酯型低收缩剂加入打浆机中，快速搅拌3分钟，然后加入上述比例的对苯醌、轻质氧化镁、过氧化苯甲酸叔丁酯、苯并咪唑基氨基甲酸酯等组份继续搅拌20分钟。接下来，将搅拌均匀的浆料移入捏合机中捏合6分钟，接着依次加入上述比例的三聚氰胺焦磷酸盐、硬脂酸钙和氢氧化铝等组分后捏合25分钟，最后加入玻璃纤维组份后继续捏合6分钟。即得到本色的无卤抗菌的阻燃的不饱和聚酯模塑料。
实施例2
邻苯型不饱和聚酯树脂54份；
聚甲基丙烯酸甲酯型低收缩剂38.5份；
过氧化苯甲酸叔丁酯0.5份；
对苯醌0.007份；
轻质氧化镁0.18份；
氢氧化铝189份；
三聚氰胺焦磷酸盐23份；
硬脂酸锌2.4份；
苯并咪唑基氨基甲酸酯0.2份；
玻璃纤维38.2份；
黑糊3.2份。
具体实施时，首先把上述比例的邻苯型不饱和聚酯树脂、聚甲基丙烯酸甲酯型低收缩剂加入打浆机中，搅拌5分钟，然后加入上述比例的对苯醌、轻质氧化镁、过氧化苯甲酸叔丁酯、苯并咪唑基氨基甲酸酯和黑糊颜料等继续搅拌30分钟。接下来，将搅拌均匀的浆料移入捏合机中捏合6分钟，接着依次加入上述比例的三聚氰胺焦磷酸盐、硬脂酸锌和氢氧化铝等组份后捏合30分钟，最后加入玻璃纤维组份后继续捏合6分钟。即得到黑色的无卤抗菌的阻燃的不饱和聚酯模塑料。
实施例3
邻苯型不饱和聚酯树脂56份；
聚甲基丙烯酸甲酯型低收缩剂39份；
过氧化苯甲酸叔丁酯0.6份；
对苯酚0.008份；
轻质氧化镁0.26份；
氢氧化铝220份；
三聚氰胺焦磷酸盐24份；
硬脂酸锌2.6份；
苯并咪唑基氨基甲酸酯0.3份；
玻璃纤维40份；
蓝糊3.5份。
具体实施时，首先把上述比例的邻苯型不饱和聚酯树脂、聚甲基丙烯酸甲酯型低收缩剂加入打浆机中，搅拌5分钟，然后加入上述比例的对苯醌、轻质氧化镁、过氧化苯甲酸叔丁酯、苯并咪唑基氨基甲酸酯和蓝糊颜料等继续搅拌30分钟。接下来，将搅拌均匀的浆料移入捏合机中捏合6分钟，接着依次加入上述比例的三聚氰胺焦磷酸盐、硬脂酸锌和氢氧化铝等组份后捏合30分钟，最后加入玻璃纤维组份后继续捏合6分钟。即得到蓝色的无卤抗菌的阻燃的不饱和聚酯模塑料。
实施例4
邻苯型不饱和聚酯树脂57份；
聚甲基丙烯酸甲酯型低收缩剂40份；
过氧化苯甲酸叔丁酯0.7份；
对苯醌0.008份；
轻质氧化镁0.28份；
氢氧化铝238份；
三聚氰胺焦磷酸盐25份；
硬脂酸钙2.8份；
苯并咪唑基氨基甲酸酯0.3份；
玻璃纤维41份；
酞氰绿0.5份。
具体实施时，首先把上述比例的邻苯型不饱和聚酯树脂、聚甲基丙烯酸甲酯型低收缩剂加入打浆机中，快速搅拌5分钟，然后加入上述比例的对苯醌、轻质氧化镁、过氧化苯甲酸叔丁酯、苯并咪唑基氨基甲酸酯和酞氰绿等继续搅拌25分钟。接下来，将搅拌均匀的浆料移入捏合机中捏合6分钟，接着依次加入上述比例的三聚氰胺焦磷酸盐、硬脂酸钙和氢氧化铝等组分后捏合25分钟，最后加入玻璃纤维组份后继续捏合6分钟。即得到绿色的无卤抗菌的阻燃的不饱和聚酯模塑料。
由上面实施例所得到的无卤抗菌的阻燃的不饱和聚酯模塑料经测试具有下表所示的性能：
Claims (10)
1.一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于其是由以下重量份数的原料构成：
不饱和聚酯树脂 36~41份；
低收缩添加剂 24~28.6份；
引发剂 0.6~ 1.1份；
阻聚剂 0.006~0.01份；
增稠剂 0.16~0.5份；
填料 100~140份；
阻燃剂 5 ~10份；
脱模剂 2.4~3.2份；
抗菌剂 0.1～0.3份；
增强纤维 26~34份。
2.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的不饱和聚酯树脂为邻苯型不饱和聚酯树脂，其树脂固含量为58~63%。
3.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的低收缩添加剂为聚甲基丙烯酸甲酯型低收缩剂，低收缩添加剂其固含量为40~42%。
4.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的引发剂为过氧化苯甲酸叔丁酯。
5.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的阻聚剂为对苯醌。
6.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的增稠剂为轻质氧化镁。
7.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的填料为氢氧化铝。
8.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的阻燃剂是三聚氰胺焦磷酸盐。
9.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的脱模剂是硬脂酸锌、硬脂酸钙中的任意一种。
10.根据权利要求1所述的一种无卤抗菌的阻燃的不饱和聚酯模塑料，其特征在于所述的抗菌剂为苯并咪唑基氨基甲酸酯，所述的增强纤维为无碱玻璃纤维。