CN103158207A - 一种再生利用废弃环氧模塑料的生产工艺 - Google Patents
一种再生利用废弃环氧模塑料的生产工艺 Download PDFInfo
- Publication number
- CN103158207A CN103158207A CN2013101045217A CN201310104521A CN103158207A CN 103158207 A CN103158207 A CN 103158207A CN 2013101045217 A CN2013101045217 A CN 2013101045217A CN 201310104521 A CN201310104521 A CN 201310104521A CN 103158207 A CN103158207 A CN 103158207A
- Authority
- CN
- China
- Prior art keywords
- waste epoxy
- moulding compound
- epoxy moulding
- district
- density polyethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种再生利用废弃环氧模塑料的生产工艺，包括：①将条状的废弃环氧模塑料放入球磨机内球磨成粉状；②将颗粒状的高密度聚乙烯与球磨成粉状的废弃环氧模塑料按照一定的比例放入转矩流变仪中进行共混；③将共混得到的物料趁热剪切成细小的片状；④将剪切好的细小片状的共混料放入双螺杆挤出机中进行牵引挤出并切粒，即可得到以高密度聚乙烯为基材，废弃环氧模塑料为填料的热塑性加工原料。该工艺操作简单，生产周期短，所制得的热塑性加工原料应用广泛，并可循环利用，具有环保的特点。
Description
技术领域
本发明涉及一种再生利用废弃环氧模塑料的生产工艺，尤其涉及一种再生利用废旧电子元器件中的废弃环氧模塑料的生产工艺。
背景技术
环氧模塑料机械强度大，绝缘耐热性能好，成本低，生产工艺简单，因此被广泛用于制作电子元器件的封装材料。随着各种电子产品的报废，作为封装材料的环氧模塑料也成为电子废弃物的一部分流入环境，由于环氧模塑料已固化交联，具有不溶不熔的特性，因此处理困难，对环境造成了一定的威胁。目前国内外处理废弃环氧模塑料的主要方式还是以填埋和焚烧为主，不仅污染环境，而且浪费土地资源。回收利用的技术主要以热解法和溶液法为主，虽然在一定范围内可以处理掉一些废弃环氧模塑料，但各有缺点，热解法成本高、二次污染严重，而溶液法技术难度大，生产周期长，因此在应用上都受到了一定的限制。
发明内容
本发明的目的是提供一种生产成本低廉、操作简单、生产周期短、不产生二次污染的再生利用废弃环氧模塑料的生产工艺，将高密度聚乙烯与废弃环氧模塑料按照一定比例熔融共混，然后通过挤出造粒制得可循环利用的热塑性加工原料，以克服上述现有技术中的不足。
为了实现上述发明目的，本发明采用了如下技术方案：
一种再生利用废弃环氧模塑料的生产工艺，包括下列步骤：
①将条状的废弃环氧模塑料放入球磨机内球磨成粉状；
②将颗粒状的高密度聚乙烯与球磨成粉状的废弃环氧模塑料按照一定的比例放入转矩流变仪中进行共混；
③将共混得到的物料趁热剪切成细小的片状；
④将剪切好的细小片状的共混料放入双螺杆挤出机中进行牵引挤出并切粒，即可得到以高密度聚乙烯为基材，废弃环氧模塑料为填料的热塑性加工原料。
所述粉状的废弃环氧模塑料的规格为200目。
所述颗粒状的高密度聚乙烯与粉状的废弃环氧模塑料的投料比例为，每100份高密度聚乙烯中添加废弃环氧模塑料5～25份。
所述转矩流变仪的温度为180～220℃，转速为60～100rpm，共混时间为6min。
所述挤出机的挤出温度为，一区：155℃，二区：165℃，三区：175℃，四区：190℃，五区：205℃。
以上原料组分均以重量计。
本发明在采用上述技术方案后相对于现有技术具有如下优点：
本发明采用的再生利用废弃环氧模塑料的生产工艺操作简单，生产周期短，适用于大规模回收利用；整个生产过程只使用高密度聚乙烯一种材料，生产成本低廉；所制得的加工原料具备热塑性，加工方式多样，应用范围广泛，并可循环利用，且整个过程中无二次污染物产生，具有环保的特点。
具体实施方式
实施例一
将条状的废弃环氧模塑料放入球磨机内球磨成粉状；
将100份颗粒状的高密度聚乙烯与5份粉状的废弃环氧模塑料放入转矩流变仪中共混6min；
将共混得到的物料趁热剪切成细小的片状；
将剪切好的细小片状的共混料放入双螺杆挤出机中进行牵引挤出并切粒，即可得到以高密度聚乙烯为基材，废弃环氧模塑料为填料的热塑性加工原料。
其中，所述转矩流变仪的温度为180℃，转速为60rpm。
所述挤出机的挤出温度为，一区：155℃，二区：165℃，三区：175℃，四区：190℃，五区：205℃。
以上原料组分均以重量计。
实施例二
将条状的废弃环氧模塑料放入球磨机内球磨成粉状；
将100份颗粒状的高密度聚乙烯与25份粉状的废弃环氧模塑料放入转矩流变仪中共混6min；
将共混得到的物料趁热剪切成细小的片状；
将剪切好的细小片状的共混料放入双螺杆挤出机中进行牵引挤出并切粒，即可得到以高密度聚乙烯为基材，废弃环氧模塑料为填料的热塑性加工原料。
其中，所述转矩流变仪的温度为220℃，转速为100rpm。
所述挤出机的挤出温度为，一区：155℃，二区：165℃，三区：175℃，四区：190℃，五区：205℃。以上原料组分均以重量计。
Claims (5)
1.一种再生利用废弃环氧模塑料的生产工艺，其特征在于包括如下步骤：
①将条状的废弃环氧模塑料放入球磨机内球磨成粉状；
②将颗粒状的高密度聚乙烯与球磨成粉状的废弃环氧模塑料按照一定的比例放入转矩流变仪中进行共混；
③将共混得到的物料趁热剪切成细小的片状；
④将剪切好的细小片状的共混料放入双螺杆挤出机中进行牵引挤出并切粒，即可得到以高密度聚乙烯为基材，废弃环氧模塑料为填料的热塑性加工原料。
2.如权利要求1所述的一种再生利用废弃环氧模塑料的生产工艺，其特征在于：所述粉状的废弃环氧模塑料的规格为200目。
3.如权利要求1所述的一种再生利用废弃环氧模塑料的生产工艺，其特征在于：所述颗粒状的高密度聚乙烯与粉状的废弃环氧模塑料的投料比例为，每100份高密度聚乙烯中添加废弃环氧模塑料5～25份。
4.如权利要求1所述的一种再生利用废弃环氧模塑料的生产工艺，其特征在于：所述转矩流变仪的温度为180～220℃，转速为60～100rpm，共混时间为6min。
5.如权利要求1所述的一种再生利用废弃环氧模塑料的生产工艺，其特征在于：所述挤出机的挤出温度为，一区：155℃，二区：165℃，三区：175℃，四区：190℃，五区：205℃。