CN103146267B - 废聚苯乙烯制备能释放微量元素负离子的多功能涂料 - Google Patents
废聚苯乙烯制备能释放微量元素负离子的多功能涂料 Download PDFInfo
- Publication number
- CN103146267B CN103146267B CN201310102490.1A CN201310102490A CN103146267B CN 103146267 B CN103146267 B CN 103146267B CN 201310102490 A CN201310102490 A CN 201310102490A CN 103146267 B CN103146267 B CN 103146267B
- Authority
- CN
- China
- Prior art keywords
- negative ion
- trace elements
- coating
- energy release
- deposed polystyrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
废聚苯乙烯制备能释放微量元素负离子的多功能涂料是属于废物利用、节约能源、变废为宝的废聚苯乙烯制备各种涂料配制生产技术领域。废聚苯乙烯是农业生产中最广泛应用的塑料之一，本身带有各种有毒化学物质，废物体积大，耐腐蚀，不易降解老化腐烂，严重破坏土壤、农田、地下水源污染。本发明将废聚苯乙烯塑料PS、松香、氧化锌溶于溶剂中制得PS改性树脂，加入能释放微量元素，拮抗有毒有害物质和气体的麦饭石、奇冰石及自发不断地产生负离子的电气石、方英石和各种填料、颜料，经研磨、过滤制得能释放微量元素负离子，有益人体健康的各种功能性涂料。
Description
技术领域：
本发明废聚苯乙烯制备能释放微量元素负离子的各种涂料，是属于废物利用节约能源变废为宝的废聚苯乙烯制备各种涂料配制生产技术领域。
背景技术：
聚苯乙烯塑料PS或称聚苯乙烯泡沫塑料PSF是属于热塑性塑料应用范围仅次于聚氯乙烯PVC和聚乙烯PE，占世界上第三位，最广泛应用的塑料之一，因为聚苯乙烯PS制品透明度高、刚性大、耐腐蚀，所以广泛用于仪表外壳、光学零件、透明窗镜、模型、瓶盖、容器、日用品、托盘、绝缘材料、电视机、收音机、电冰箱、洗衣机、各种仪表、办公设备、电器外壳等零配件，由于因聚苯乙烯泡沫塑料密度小，仅0.02-0.04g/cm3，质量轻，废弃物所占的体积大，又不容易降解，埋在地下的废聚苯乙烯本身所带有的各种有毒化学物质，又会污染地下水源，破坏地下水源质量和破坏土壤农田环境结构，造成严重的环境污染，成为全球性环境白色污染公害，因此，回收和利用废聚苯乙烯塑料PS变废为宝，节约资源，造福人类是本发明的宗旨。
发明内容：
本发明的目的在于提供一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料。
本发明的技术解决方案：
一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征是：
1、用废聚苯乙烯泡沫塑料制备功能性地面涂料，按质量百分比由下列成分组成分两步：首先制备基料
A、配方：
(1)基料配方
B、涂料配方
2、废聚苯乙烯泡沫塑料制备功效性乳液涂料，按质量百分比由下列成分组成
A、配方：
3、废聚苯乙烯制备除甲醛抗菌抗电磁波远红外，释放微量元素，净化空气的内墙多功能涂料，按质量百分比由下列成分组成
A、配方：
4、废聚苯乙烯制备厨房、卫生间墙面涂料，按质量百分比由下列成分组成
A、配方：
B、配方面料：
5、废聚苯乙烯立体功能性多彩涂料，按质量百分比由下列成分组成
(一)涂料配方与生产
A、立体多彩涂料配方：
将废聚苯乙烯塑料PS或聚苯乙烯泡沫塑料PSE、松香、甘油、氧化锌溶于溶剂中，制得聚苯乙烯改性树脂，然后再加入能释放微量元素拮抗有毒有害物质和气体的麦饭石、奇冰石，及自发不断地产生负离子的电气石、方英石、磷石英蛋白石。其中的一种或数种和各种填料和颜料，经研磨过滤，可制成各种废聚苯乙烯塑料PS各种功能性涂料。该制品干燥快、性能稳定、耐化学性能好，广泛用于各种设施的防腐，并能释放微量元素吸附和拮抗重金属元素和有毒有害气体，永久自发产生负离子改善空气质量、环保健康。
工艺的第一步，将废归塑料进行分类预选，用清水洗净，并晾干、晒干或烘干，然后用粉碎机粉碎成小粒。第二步，将干燥的塑料颗粒加入装有配制好的有机溶剂，溶剂质量份配比组成％：即二甲苯70％、乙酸乙酯20％、丁醇10％的容器中，加入催化剂A加热至PS全部溶解，制成“塑料胶浆”；第三步，在另一容器中加入配制好的改性树脂，然后与“塑料胶浆”按比例混合，制成清漆；第四步，在清漆中添加颜料、填料、麦饭石、电气石、甲壳素粘胶纤维及助剂，高速搅拌分散均匀研磨过800目筛粒径达5-20μm的纳米细粉，用200号溶剂汽油调节色漆粘度，过滤即得合格色漆成品。
下面结合实施例子对本发明进一步说明：
具体实施方式：
实施例1：一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征是：用废聚苯乙烯泡沫塑料制备功能性地面涂料，按质量百分比由下列成分组成
分两步：首先制备基料
A、配方：
(2)基料配方
B、涂料配方
C、制备工艺
①基料的配制过程。将净化处理的废聚苯乙烯泡沫塑料粉碎成发泡颗粒后加入工业用甲苯及由化学试剂店购得化学纯乙酸乙酯；由北京洁尔爽高科技有限公司开发的纳米远红外负离子粉900；阻燃剂900；天然高效抗菌壳聚糖SCJ-920，与聚苯乙烯泡沫塑料颗粒充分混匀溶解后再加入松香，继续搅拌后视为油相；在另外一反应器中将羧甲基纤维素CMC，及化学试剂级的十二烷基苯磺酸钠化学纯和水制成的水相，在油相和水相的温度同在80℃时，在不断搅拌的情况下，将水相慢慢地加油相中；在60-70℃下恒温搅拌2h，冷却后得白色粘稠液体用于苯乙烯型地面多功能涂料配方的基料。
②涂料的配制：按涂料配方质量份配比组成％的要求，将上述所得的基料、颜料、填料、助剂及少量的乳化剂共同置于高速搅拌机内分散，然后研磨过800目筛细度粒径达45μm以下。
D、性能
①利用废聚苯乙烯泡沫塑料制成的水乳型地面涂料具有对水泥地面良好的粘结性能和良好的耐水、耐碱性及耐磨性；
②麦饭石纳米粉具有强力吸附、净水、拮抗有毒有害重金属元素和气体，发射远红外，负离子，净化空气，杀菌，阻燃多功效涂料，能创造良好的空气质量有益人体健康。
实施例2：一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征是：废聚苯乙烯泡沫塑料制备功效性乳液涂料，按质量百分比由下列成分组成
A、配方：
B、制备方法：
(1)预处理：将收回的废归聚苯乙烯清洗后放在热碱水中浸泡一段时间，然后进行搅拌使之相互碰撞和摩擦，以除去污垢，然后将聚苯乙烯放入清水池中进行进一步搅拌清洗，过清水3-4次为佳，再将清洗好的聚苯乙烯烘干或晒干，最后用粉碎好的PS泡沫塑料放好备用。
(2)溶解与改性反应：按配方质量份配比将称取苯、二甲苯，配成混合溶液，在室温条件下，将称取一定量的预处理好的废聚苯乙烯泡沫塑料PS，加入到配制好的混合溶液中，边加边搅拌，使之充分溶解。待完全溶解后，加入适量的增塑剂邻苯二甲酸丁酯，用水浴加热并不断搅拌。在温度75-80℃的温度下滴加增塑剂，在1-1.5h内滴完配方质量配比要求后继续反0.5h，得出组分一。
(3)按配方质量份配比要求称取六偏磷酸钠、羟甲基纤维素CMC、甲壳素纤维、钛白粉、滑石粉、载银纳米二氧化钛(AT)抗菌剂、纳米ZnO光催化无机抗菌剂、轻质碳酸钙、十二烷基苯硫酸钠、麦饭石纳米粉、电气石纳米粉，然后混合均匀，加水至混合物料覆盖层面，再加丙二醇，然后继续搅拌，使物料充分分散均匀，即得组分二。
(4)混合得产品，在乳液釜中搅拌的情况下，及组分一与组分二在同样温度75-80℃的温度条件下，将组分一慢慢地加入组分二的乳液釜中，继续搅拌充分混合，待温度降至60-70℃时，用25％的氨水调pH值至7-9，乳化、搅拌、冷却后，即得本发明功能乳液涂料。
C、性能：
产品主要性能指标
| 项目 | 技术指标 | 性能结果 |
| 外观 | 无硬块，搅拌后均匀 | 合格 |
| 固含量/％ | 不少于45 | 51 |
| 粘度/s | 1.5 | |
| 表面干燥时间/s | 不大于7500 | 780 |
| 遮盖率(g/m2) | 不大于250 | 75.5 |
| 耐酸率(20h) | 不起泡、不掉粉 | 合格 |
| 耐碱率(48h) | 不起泡、不掉粉 | 合格 |
| 耐水率(96h) | 不起泡、不掉粉 | 合格 |
| 耐冷率(120h) | 不起泡、不掉粉 | 合格 |
| 耐热率(120h) | 不起泡、不掉粉 | 合格 |
| 耐紫外线率(120h) | 不起泡、不掉粉 | 合格 |
(1)该涂料具有良好的附着力、耐水性，经检测各种性能指标均达到技术指标要求；
(2)用水调节粘度，施工方便，人力、成本大大降低；
(3)达到环保、生物降解，废物利用，节约资源，经济实惠。
D、用途：
本涂料有较强的杀灭细菌，拮抗和吸附有毒有害铅、汞、砷等重金属和气体，释放微量元素负离子，有益人体健康。
实施例3：一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征是：废聚苯乙烯制备除甲醛抗菌抗电磁波远红外，释放微量元素，净化空气的内墙多功能涂料，按质量百分比由下列成分组成
A、配方：
B、制备方法：
按物料配方配比经粉碎研磨好的各种物料在容器内搅拌混合研磨调配成涂料。
C、原料配方来源
(1)二氧化钛、二氧化硅、氧化锌、Fe2O3、铁氧化、氧化镁、铁锰纳米粉均是麦饭石中的主要成分，并还有远红外辐射性能；
(2)奇冰石即电气石，是一种天然的负离子发生器；
(3)磷酸盐复合银系无机抗菌剂HN-300，由江苏泰兴纳米材料厂开发生产；
(4)成膜组分为纯丙乳液、苯丙乳液、乙丙乳液中的一种或几种混合液，其他增稠剂、流平剂、消泡剂，化工原料商店有供。
D、产品作用
本发明涂料用于内墙装璜涂料，可释放微量元素，补充调节、拮抗人体内元素平衡，发射远红外，抗电磁波污染，拮抗空气中铅、汞、砷、镉等重金属元素及消除甲醛有害气体，强效抗菌杀菌，自发不断地产生有益人体健康的负离子。
实施例4：一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征是：废聚苯乙烯制备厨房、卫生间墙面涂料，按质量百分比由下列成分组成
A、配方：
B、配方面料：
C、制备方法：
(1)配方底料的制作
首先将废聚苯乙烯泡沫塑料烘干或晒干，破碎与季戊四醇胶水按配方要求量加入含有60℃温度以上的热水反应釜内，并继续加热至溶解后停止加热，依次缓缓地加入脲醛树脂胶及聚醋酸乙烯乳液，搅拌下反应一定时间约10-15min后停止搅拌，得温度降至40℃以下，加入群青及消泡剂，继续搅拌3-5min后，将全部的固体原料麦饭石纳米粉、电气石纳米粉等边搅拌边缓缓地将所有物料依次加入继续搅拌30-40min后转入研磨机进行研磨，研磨后计量包装备用。
(2)配方面料的制作
将六偏磷酸钠加入水中溶解，将淀粉、二氧化硅、二氧化钛、硅酸钠、乙二醇依次加入搅拌成基料，再将余下的填料依次加入基料中搅拌均匀，最后加入纤维素溶液搅拌均匀后转入胶体研磨机中研磨2-3遍。
D、产品应用
本发明涂料适合厨房、卫生间、公共厕所及其他条件环境恶劣情况下使用。
E、产品特性
(1)所选用底面料材料无毒、无味、无污染天然环保；
(2)所有底料粘接力强，耐候性最佳，在环境条件差的情况下长期无脱落。面料附着力强，光洁度好，有绝佳的抗污染能力；
(3)抗菌、除毒吸附有毒有害重金属元素和气体，释放微量元素，自发不断地产生负离子，除臭，净化空气。
实施例5：一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征是：废聚苯乙烯立体功能性多彩涂料，按质量百分比由下列成分组成
(一)涂料配方与生产
A、立体多彩涂料配方：
B、制备方法：
(1)A浆的制备
第一部首先在常温下，将壳聚糖黏胶纤维、废聚苯乙烯泡沫塑料、羟甲基纤维素和硼砂及水加入反应釜中开动搅拌机，开始升温搅拌，将物料全部溶解，搅拌均匀后，缓慢降至常温即成A浆倒出备用。
(2)B浆的制备
第二部将适量的水加入反应釜中，开动搅拌机后加麦饭石纳米粉、电气石纳米粉、钛白粉进行搅拌均匀后再加入聚醋酸乙烯乳液继续搅拌均匀后，最后边搅拌边加入半量的乙二醇，还不停地搅拌均匀后即得B浆，倒出备用。
(3)C浆的制备
第三部是将羟丙基纤维素和硫酸钠、氯化钠溶液搅匀混合均匀即成C浆。
(4)D浆的制备
第四部是将云母粉、金属粉、颜料和余下半量的乙二醇搅拌均匀即得D浆。
(5)成品
第五部，成品就是将上述制备的A浆和B浆依次加入至反应釜内，搅拌均匀后，再加入C浆，此时再加入轻质碳酸钙再继续搅拌均匀，然后过滤，除去多余的水分，即成成品。(6)包装入库
第六部，即按上述配方的质量份配比要求加入相同质量份的水，并配上D浆搅拌均匀即可包装入库。
C、产品应用
本发明主要用于建筑上的装潢装饰涂料，在施工现场，配兑相同质量份的水，再加入包装随带的D浆，人工搅拌均匀后即可用压缩机和喷枪按喷油漆的施工方法一次喷上施工表面，如需花纹，可根据花纹色板设计所需要什么样的多彩花纹饰面来确定颜色。
D、产品特性
本功能多彩涂料粘接性强，附着力100％，耐水洗大于6000次，饰面反复水洗不掉粉，不褪色，涂饰面上的脏物可水洗如新，耐酸碱、耐寒冷，热夏气候变化，阻燃性能好。该涂料可储存在12个月以上，其饰面色彩鲜艳，有特强的立体感。格调高雅，饰面呈彩点状分布，花纹明显，花色繁多。该涂料不使用有机溶剂等有害物质，使用天然抗菌剂生物降除，释放微量元素，自发不断产生负离子、净化空气，有益人体健康，无毒、无害、无放射，长期使用能为人体营造优质的环境空间，适用各种室内装潢用的理想优选涂料。
Claims (5)
1.废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征：
功能性面涂料制备方法分二步：第一步，首先制备基料配方；第二步，制备涂料配方
A、第一步，制备基料配方，按质量百分比由下列成分组成
B、第二步，制备涂料配方按质量百分比由下列成分组成
2.一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征：
一种制备功能性乳液涂料，按质量百分比由下列成分组成
3.一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征：
内墙多功能涂料，按质量百分比由下列成分组成
4.一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征：
厨房、卫生间墙面涂料，按质量百分比由下列成分组成
A、配方底料
B、配方面料
5.一种废聚苯乙烯制备能释放微量元素负离子的多功能涂料，其特征：
立体功能性多彩涂料，按质量百分比由下列成分组成
立体多彩涂料配方