CN103133851A - 一种添加茶叶末和茶多酚的人造板及其制造方法 - Google Patents

一种添加茶叶末和茶多酚的人造板及其制造方法 Download PDF

Info

Publication number
CN103133851A
CN103133851A CN2013100876586A CN201310087658A CN103133851A CN 103133851 A CN103133851 A CN 103133851A CN 2013100876586 A CN2013100876586 A CN 2013100876586A CN 201310087658 A CN201310087658 A CN 201310087658A CN 103133851 A CN103133851 A CN 103133851A
Authority
CN
China
Prior art keywords
board
man
tea
wood raw
dust
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100876586A
Other languages
English (en)
Inventor
郭漫笳
裴艳丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
PARADISE FOR LOVER OF CHINESE CULTURE & HANDCRAFTBNQJ HANDICRAFTS (HEBEI) INC
Original Assignee
郭漫笳
裴艳丽
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 郭漫笳, 裴艳丽 filed Critical 郭漫笳
Priority to CN2013100876586A priority Critical patent/CN103133851A/zh
Publication of CN103133851A publication Critical patent/CN103133851A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种添加茶叶末和茶多酚的人造板,该人造板由木材原料、茶叶末、茶多酚、粘合剂、阻燃剂和防腐剂组成,其优选的组成为木材原料1m3、茶叶末0.05~0.3m3、茶多酚0.5~3Kg、粘合剂5~20Kg、阻燃剂0~3Kg和防腐剂0~3Kg。本发明的添加茶叶末和人造板的制造方法包括以下步骤:木材原料处理、预蒸、干燥、材料混合和人造板成型。采用本法制造的人造板不仅能杀灭人造板本身以及制造过程中的细菌,在人造板应用于室内装修和家具中时,抑制和杀灭室内的细菌;而且还能去除木材和室内的甲醛,起到净化空气的作用。

Description

一种添加茶叶末和茶多酚的人造板及其制造方法
技术领域
[0001] 本发明涉及人造板制造领域,尤其涉及ー种添加茶叶末和茶多酚的人造板及其制
造方法。
背景技术
[0002] 人造板是以木材或其他非木材植物为原料,经一定机械加工分离成各种单元材料后,施加或不施加胶粘剂和其他添加剂胶合而成的板材或模压制品。主要包括胶合板、刨花(碎料)板和纤维板等三大类产品,其延伸产品和深加工产品达上百种。人造板的诞生,标志着木材加工现代化时期的开始,使过程从单纯改变木材形状发展到改善木材性质。这ー发展,不但涉及全部木材加工エ艺,需要吸收纺织、造纸等领域的技木,从而形成独立的加工エ艺。此外,人造板还可提高木材的综合利用率,I立方米人造板可代替3〜5立方米原木使用,所以大力发展人造板制造业能在一定程度上解决我国林业资源匮乏的问题。目前人造板已经广泛应用于室内装修、家具制造等领域中。
[0003] 茶多酚是茶叶中多酚类物质的总称,包括黄烷醇类、花色苷类、黄酮类、黄酮醇类和酚酸类等。其中以黄烷醇类物质(儿茶素)最为重要。茶多酚又称茶鞣或茶单宁,是形成茶叶色香味的主要成份之一,也是茶叶中有保健功能的主要成份之一。研究表明,茶多酚等活性物质具解毒和抗辐射作用,能有效地阻止放射性物质侵入骨髄,并可使锶90和钴60迅速排出体外,被健康及医学界誉为“辐射克星”。
[0004] 研究发现茶多酚具有很好的抗菌作用,它能杀灭肉毒杆菌及其孢子,抑制细菌外毒素的活性。对引起腹泻、呼吸道和皮肤感染的各种病原菌有抗菌作用。茶多酚对引起化脓性感染、烧伤、外伤的金黄色葡萄球菌、变形杆菌、绿脓杆菌有很明显的抑制作用,而这三种菌株对药物又易产生耐药性,由此引起的败血症死亡率高达80%。唐裕芳,张妙玲等,茶多酚的抑菌活性研究,2005,22 (5)研究发现茶多酚对细菌有较强的抑菌活性。
[0005] 茶多酌■还具有很好的去甲醒作用,Herrick F.ff., Bock L.H.Thermosetting,exterior-plywood type adhesives from barkextracts.1958,8,中研究发现甲醒能与茶多酚类化合物在C-6和C-8上发生亲核反应。之后研究人员还利用茶多酚作为甲醛捕获剂进行了初步应用试验。励建荣,俞其林等,茶多酚与甲醛的反应特性研究,2008,8 (2)研究发现茶多酚是ー种良好的甲醛捕获剂,能很好的去除甲醛。
[0006] 我们研究发现将茶叶末和茶多酚添加到人造板中,不仅能杀灭人造板本身以及制造过程中的细菌,在人造板应用于室内装修和家具中时,抑制和杀灭室内的细菌;而且还能去除木材和室内的甲醛,起到浄化空气的作用。
发明内容
[0007] 本发明的技术方案如下:
本发明所公开的人造板由木材原料、茶叶末、茶多酚、粘合剂、阻燃剂和防腐剂组成。
[0008] 本发明所公开的人造板的组成为:木材原料Im3 茶叶末 0.05〜Im3 茶多酚 0.5〜IOKg 粘合剂 3〜50Kg 阻燃剂 (TlOKg 防腐剂 0〜10Kg。
[0009]优选:
木材原料Im3
茶叶末 0.05〜0.5m3 茶多酚 0.5〜5Kg 粘合剂 5〜30Kg 阻燃剂 0〜5Kg 防腐剂 (T5Kg。
[0010] 更优选:
木材原料Im3
茶叶末 0.05〜0.3m3 茶多酚 0.5〜3Kg 粘合剂 5〜20Kg 阻燃剂 OlKg 防腐剂 (T3Kg。
[0011] 本发明所公开的人造板,木材原料选自农作物秸杆、甘蔗渣、芦苇或高大乔木茎干中的ー种或几种。
[0012] 本发明所公开的人造板,粘合剂选自酚醛树脂、酚醛树脂改性的树脂、间苯ニ酚甲醛树脂、间苯ニ酚甲醛树脂改性的树脂、脲醛树脂、脲醛树脂改性的树脂、三聚氰胺甲醛树脂或其改性后的树脂中的ー种或几种。
[0013] 本发明所公开的人造板,阻燃剂选自氯化脂环烃、四氯邻苯ニ甲酸酐、磷酸酷、含卤磷酸酯、齒化磷、氧化锑、氢氧化铝、氢氧化镁、硼酸锌、聚磷酸铵或氯丁胶乳中的ー种或几种。
[0014] 本发明所公开的人造板,防腐剂选自丁基乳胶、氯丁胶乳、双こ酸钠、丙酸钙、乳酸钠、乳酸链球菌素、纳他霉素、聚赖氨酸、苯甲酸钠、山梨酸钾、脱氢こ酸钠或过氧化氢中的ー种或几种。
[0015] 本发明所公开的人造板的制造方法包括以下步骤:
(1)将木材原料切断、削片或研磨制成料片或颗粒,
(2)再将木材原料放入蒸熟池中预蒸,在蒸汽压カ为0.6^0.9Mpa下,蒸煮4〜15分钟,
(3)在130°C 〜180°C下进行气流干燥,干燥后的纤维含水率为29^12%,
(4)将茶叶末进行超微粉碎 ,再将粉碎后的茶叶末、木材原料、茶多酚、粘合剂、防腐剂和阻燃剂充分搅拌混合,
(5)将混合后的原料均匀布在模具中,然后再热压成型或冷压成型即得。
[0016] 在步骤(2)进行预蒸之前,在将木材原料在45°C〜99°C的碱性水中浸泡6(Tl80分钟。
[0017] 本发明所公开的茶多酚人造板包括胶合板、纤维板或刨花板。
[0018] 本发明将茶叶末和茶多酚添加到人造板中,一方面能将废弃不用的茶叶末再利用,另ー方面还能防止环境污染,所制造的人造板不仅能杀灭人造板本身以及制造过程中的细菌,在人造板应用于室内装修和家具中时,抑制和杀灭室内的细菌;而且还能去除木材和室内的甲醛,起到浄化空气的作用。
具体实施方式
[0019] 下面的实施例是对本发明的进ー步详细描述。
[0020] 实施例1
1.1人造板组成 木材原料 Im3
茶叶末 0.5m3
茶多酹 5Kg
酚醛树脂粘合剂 30Kg 磷酸酯阻燃剂 5Kg 丁基乳胶防腐剂 5Kg
1.2制造方法
(1)将木材原料切断、削片或研磨制成料片或颗粒,
(2)将木材原料在45°C的碱性水中浸泡180分钟。再将木材原料放入蒸熟池中预蒸,在蒸汽压カ为0.6Mpa下,蒸煮15分钟,
(3)在130°C下进行气流干燥,直至干燥后的纤维含水率为29^12%,
(4)将茶叶末进行超微粉碎,再将粉碎后的茶叶末、木材原料、茶多酚、粘合剂、防腐剂和阻燃剂充分搅拌混合,
(5)将混合后的原料均匀布在模具中,然后再热压成型或冷压成型即得。
[0021] 1.3人造板抑菌杀菌效果
将制备的人造板放置于ー个10平方米的密封室内。采用GB/T18883-2002的撞击法测定人造板放置前和放置48小时后室内空气的菌落总数。
[0022] 结果表明在放置人造板前室内的菌落总数为2581cfu/m3,而放置人造板48小时之后室内菌落总数为2413 cfu/m3,所以结果表明本发明的人造板具有很好的抑菌和杀菌作用。
[0023] 1.4人造板去甲醛效果
以GB18580-2001的干燥器法检测中密度纤维板的甲醛释放量0.26mg/L,而以美国加州空气管理署(CARB)气候箱法检测,甲醛释放量仅为0.04PPM。结果表明本发明的人造板具有很好的去甲醛作用。
[0024] 实施例2
2.1人造板组成
木材原料 Im3
茶叶末 0.05m3茶多酹 0.5Kg
酚醛树脂粘合剂 5Kg 磷酸酯阻燃剂 3Kg 丁基乳胶防腐剂 3Kg
2.2制造方法
(1)将木材原料切断、削片或研磨制成料片或颗粒,
(2)将木材原料在99°C的碱性水中浸泡60分钟。再将木材原料放入蒸熟池中预蒸,在蒸汽压カ为0.9Mpa下,蒸煮4分钟,
(3)在180°C下进行气流干燥,直至干燥后的纤维含水率为29^12%,
(4)将茶叶末进行超微粉碎,再将粉碎后的茶叶末、木材原料、茶多酚、粘合剂、防腐剂和阻燃剂充分搅拌混合,
(5)将混合后的原料均匀布在模具中,然后再热压成型或冷压成型即得。
[0025] 2.3人造板抑菌杀菌效果
将制备的人造板放置于ー个10平方米的密封室内。采用GB/T18883-2002的撞击法测定人造板放置前和放置48小时后室内空气的菌落总数。
[0026] 结果表明在放置人造板前室内的菌落总数为2590cfu/m3,而放置人造板48小时之后室内菌落总数为2510 cfu/m3,所以结果表明本发明的人造板具有很好的抑菌和杀菌作用。
[0027] 2.4人造板去甲醛效果
以GB18580-2001的干燥器法检测中密度纤维板的甲醛释放量0.27mg/L,而以美国加州空气管理署(CARB)气候箱法检测,甲醛释放量仅为0.05PPM。结果表明本发明的人造板具有很好的去甲醛作用。
[0028] 实施例3
3.1人造板组成
木材原料 Im3
茶叶末 0.3m3
茶多酹 3Kg
酚醛树脂粘合剂 20Kg 磷酸酯阻燃剂 3Kg 丁基乳胶防腐剂 3Kg
3.2制造方法
(1)将木材原料切断、削片或研磨制成料片或颗粒,
(2)将木材原料在70°C的碱性水中浸泡120分钟。再将木材原料放入蒸熟池中预蒸,在蒸汽压カ为0.8Mpa下,蒸煮10分钟,
(3)在150°C下进行气流干燥,直至干燥后的纤维含水率为29^12%,
(4)将茶叶末进行超微粉碎,再将粉碎后的茶叶末、木材原料、茶多酚、粘合剂、防腐剂和阻燃剂充分搅拌混合,
(5)将混合后的原料均匀布在模具中,然后再热压成型或冷压成型即得。
[0029] 3.3人造板抑菌杀菌效果 将制备的人造板放置于ー个10平方米的密封室内。采用GB/T18883-2002的撞击法测定人造板放置前和放置48小时后室内空气的菌落总数。
[0030] 结果表明在放置人造板前室内的菌落总数为2595cfu/m3,而放置人造板48小时之后室内菌落总数为2450 cfu/m3,所以结果表明本发明的人造板具有很好的抑菌和杀菌作用。
[0031] 3.4人造板去甲醛效果
以GB18580-2001的干燥器法检测中密度纤维板的甲醛释放量0.25mg/L,而以美国加州空气管理署(CARB)气候箱法检测,甲醛释放量仅为0.03PPM。结果表明本发明的人造板具有很好的去甲醛作用。
[0032] 实施例4
4.1人造板组成 木材原料 Im3
茶叶末 0.2m3
茶多酚 2Kg
酚醛树脂粘合剂 15Kg 磷酸酯阻燃剂 2Kg 丁基乳胶防腐剂 2Kg
4.2制造方法 制造方法同实施例3.4.3人造板抑菌杀菌效果
将制备的人造板放置于ー个10平方米的密封室内。采用GB/T18883-2002的撞击法测定人造板放置前和放置48小时后室内空气的菌落总数。
[0033] 结果表明在放置人造板前室内的菌落总数为2605cfu/m3,而放置人造板48小时之后室内菌落总数为2480 cfu/m3,所以结果表明本发明的人造板具有很好的抑菌和杀菌作用。
[0034] 4.4人造板去甲醛效果
以GB18580-2001的干燥器法检测中密度纤维板的甲醛释放量0.25mg/L,而以美国加州空气管理署(CARB)气候箱法检测,甲醛释放量仅为0.04PPM。结果表明本发明的人造板具有很好的去甲醛作用。
[0035] 尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。

Claims (10)

1.ー种添加茶叶末和茶多酚的人造板,其特征在于:该人造板由木材原料、茶叶末、茶多酚、粘合剂、阻燃剂和防腐剂组成。
2.如权利要求1所述的ー种人造板,其特征在于:该人造板的组成为: 木材原料Im3 茶叶末 0.05〜Im3 茶多酚 0.5〜IOKg 粘合剂 3〜50Kg 阻燃剂 (TlOKg 防腐剂 0〜10Kg。
3.如权利要求1所述的ー种人造板,其特征在于:该人造板的组成为: 木材原料Im3 茶叶末 0.05〜0.5m3 茶多酚 0.5〜5Kg 粘合剂 5〜30Kg 阻燃剂 0〜5Kg 防腐剂 (T5Kg。
4.如权利要求1所述的ー种人造板,其特征在于:该人造板的组成为: 木材原料Im3 茶叶末 0.05〜0.3m3 茶多酚 0.5〜3Kg 粘合剂 5〜20Kg 阻燃剂 OlKg 防腐剂 (T3Kg。
5.如权利要求1-4任一项权利要求所述的ー种人造板,其特征在于:木材原料选自农作物秸杆、甘蔗渣、芦苇或高大乔木茎干中的ー种或几种。
6.如权利要求1-4任一项权利要求所述的ー种人造板,其特征在于:粘合剂选自酚醛树脂、酚醛树脂改性的树脂、间苯ニ酚甲醛树脂、间苯ニ酚甲醛树脂改性的树脂、脲醛树脂、脲醛树脂改性的树脂、三聚氰胺甲醛树脂或其改性后的树脂中的ー种或几种。
7.如权利要求1-4任一项权利要求所述的ー种人造板,其特征在于:阻燃剂选自氯化脂环烃、四氯邻苯ニ甲酸酐、磷酸酷、含卤磷酸酷、卤化磷、氧化锑、氢氧化铝、氢氧化镁、硼酸锌、聚磷酸铵或氯丁胶乳中的ー种或几种。
8.如权利要求1-4任一项权利要求所述的ー种人造板,其特征在于:防腐剂选自丁基乳胶、氯丁胶乳、双 こ酸钠、丙酸钙、乳酸钠、乳酸链球菌素、纳他霉素、聚赖氨酸、苯甲酸钠、山梨酸钾、脱氢こ酸钠或过氧化氢中的ー种或几种。
9.一种如权利要求1-4任一项权利要求所述的ー种人造板的制造方法,其特征在于:所述方法包括以下步骤: (1)将木材原料切断、削片或研磨制成料片或颗粒, (2)将木材原料在45°C〜99°C的碱性水中浸泡6(Tl80分钟,再将木材原料放入蒸熟池中预蒸,在蒸汽压カ为0.6^0.9Mpa下,蒸煮4〜15分钟,(3)在130°C 〜180°C下进行气流干燥,干燥后的纤维含水率为29^12%, (4)将茶叶末进行超微粉碎,至粒径小于2mm,再将粉碎后的茶叶末、木材原料、茶多酚、粘合剂、防腐剂和阻燃剂充分搅拌混合, (5)将混合后的原料均匀布在模具中,然后再热压成型或冷压成型即得。
10.一种如权利要求9所述的方法制造的人造板,其特征在于:所述的人造板为胶合板、纤维板或 刨花板。
CN2013100876586A 2013-03-19 2013-03-19 一种添加茶叶末和茶多酚的人造板及其制造方法 Pending CN103133851A (zh)