CN103114441A - 奈米灭虫聚酯纤维的制程 - Google Patents
奈米灭虫聚酯纤维的制程 Download PDFInfo
- Publication number
- CN103114441A CN103114441A CN2013100395054A CN201310039505A CN103114441A CN 103114441 A CN103114441 A CN 103114441A CN 2013100395054 A CN2013100395054 A CN 2013100395054A CN 201310039505 A CN201310039505 A CN 201310039505A CN 103114441 A CN103114441 A CN 103114441A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- deinsectization
- processing procedure
- rice
- degree
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明为奈米灭虫聚酯纤维的制程,指一种将具灭虫性的奈米等级粒子与聚酯纤维结合的制程,其制程如下:将7%~13%的醚菊酯、1%~3%的抗氧化剂、16%~22%的抗UV剂、1%~7%的流动改质剂及55%~75%的低密度聚酯纤维比例组合以140度~230度的温度下均匀混合炼制成一奈米等级粒子;将该奈米等级粒子与聚酯纤维分别以10%:90%的比例以140度~230度的温度下均匀混合,将其制作成丝线状,通过上述的步骤,将灭虫谱域广、残存期长及药性影响小的奈米等级粒子与聚酯纤维制作成丝线状,再将其广泛运用于各种场合,已达成长期使用、灭虫效果良好及无毒性影响的实用进步性。
Description
技术领域
本发明为提供一种奈米灭虫聚酯纤维的制程,尤其是指一种长期使用、灭虫效果良好及无毒性影响的奈米灭虫聚酯纤维的制程。
背景技术
当今社会人们对生活质量的重视下,对原有的织物有着更高的要求,除了舒适美观及保暖抗寒外,更要求各种于不同的防护效果。
对此,市面上即有针对防虫而生的织物产生,将丝线与灭虫药剂作结合,再将其制作成各种不同形式的物品,如帐篷、蚊帐等,藉此达成防止虫害的问题。
早期的作法是将丝线制作成布料后,将其浸泡于防虫药剂中,让布料吸附防虫药剂,但此种作法会导致布料的质感变硬、防水性不佳等问题,且经过洗涤后更会导致防虫效果逐渐劣化等问题。
而近期的作法,是将防虫药剂直接与丝线混和炼制成,直接制成具有防虫特性的纺织品,藉此减少了上述早期作法的部分问题。
然而上述的将防虫药剂直接与丝线混和炼制的作法,存在以下问题:
一、此种作法是将溴氰菊酯及氯菊酯作为防虫的药物,其防虫效果有限,且对人体及生态环境影响较大。
二、将溴氰菊酯及氯菊酯搭配其它混合物作成粒状,再将其配合其它物品制作成丝线,其结合度有限,导致使用期降低。
发明内容
本发明的目的在于提供一种奈米灭虫聚酯纤维的制程,将醚菊酯作为灭虫药物,并搭配其它助剂混合炼制,解决原有作法的溴氰菊酯及氯菊酯所存在的防虫效果有限及对人体、生态环境影响较大的问题,达到灭虫效果良好及无毒性影响的实用进步性;
将醚菊酯作为灭虫药物,并搭配其它助剂混合炼制,并制作成奈米等级,解决原有防虫粒子所存在的结合度不足的问题点加以突破,达到长期使用的实用进步性。
为达上述的目的,本发明的奈米灭虫聚酯纤维的制程,指一种将具灭虫性的奈米等级粒子与聚酯纤维结合的制程,其制程包含有:将7%~13%的醚菊酯、1%~3%的抗氧化剂、16%~22%的抗UV剂、1%~7%的流动改质剂及55%~75%的低密度聚酯纤维比例组合以140度~230度的温度下均匀混合炼制成一奈米等级粒子;将该奈米等级粒子与聚酯纤维分别以10%:90%的比例以140度~230度的温度下均匀混合,将其制作成丝线状。
藉由上述的步骤,将充分将醚菊酯、抗氧化剂、抗UV剂、流动改质剂及低密度聚酯纤维均匀混合,再与聚酯纤维结合制作成丝线装,其中因灭虫粒子为奈米等级,使结合上效果更佳,达成长期使用的目的,更因醚菊酯的特性(灭虫谱域广、残存期长及药性影响小),达成灭虫效果良好及无毒性影响的实用进步性。
本发明具体包括:本发明指一种将具灭虫性的奈米等级粒子与聚酯纤维结合的制程,其制程包括:
(a)将7%~13%的醚菊酯、1%~3%的抗氧化剂、16%~22%的抗UV剂、1%~7%的流动改质剂及55%~75%的低密度聚酯纤维比例组合以140度~230度的温度下均匀混合炼制成一奈米等级粒子;
(b)将该奈米等级粒子与聚酯纤维分别以10%:90%的比例以140度~230度的温度下均匀混合,将其制作成丝线状。
其中该醚菊酯的最佳比例为10%;
其中该抗氧化剂的最佳比例为2%;
其中该抗UV剂的最佳比例为19%;
其中该流动改质剂的最佳比例为4%;
其中该低密度聚酯纤维的最佳比例为65%;
其中该聚酯纤维为一聚丙烯,且该制程最佳温度为210度;
其中该聚酯纤维为一聚乙烯,且该制程最佳温度为180度。
本发明的优点在于:
一、因使用具有灭虫谱域广、残存期长及药性影响小等特性的醚菊酯制作成奈米等级粒子,使灭虫效果大幅改善,且对人体及环境影响甚微,藉此达成灭虫效果良好及无毒性影响的实用进步性。
二、因将灭虫粒子以奈米等级的方式混合及相关制作,其成品的结合度相当优异,不易因外在因子导致效果减少,藉此达成长期使用的实用进步性。
附图说明
图1 为本发明较佳实施例的制作流程示意图。
图2 为本发明较佳实施例的局部示意图。
具体实施方式
如附图1所示,为本发明较佳实施例的制作流程示意图,由图中可清楚看出本发明奈米灭虫聚酯纤维的制程,其步骤包括有:
(a)将7%~13%的醚菊酯、1%~3%的抗氧化剂、16%~22%的抗UV剂、1%~7%的流动改质剂及55%~75%的低密度聚酯纤维比例组合以140度~230度的温度下均匀混合炼制成一奈米等级粒子;
(b)将该奈米等级粒子与聚酯纤维分别以10%:90%的比例以140度~230度的温度下均匀混合,将其制作成丝线状。
其中该醚菊酯的最佳比例为10%。
其中该抗氧化剂的最佳比例为2%。
其中该抗UV剂的最佳比例为19%。
其中该流动改质剂的最佳比例为4%。
其中该低密度聚酯纤维的最佳比例为65%。
其中该聚酯纤维为一聚丙烯,且该制程最佳温度为210度。
其中该聚酯纤维为一聚乙烯,且该制程最佳温度为180度。
更进一步对上述的步骤进行说明,如附图1及附图2所示,为本发明较佳实施例的制作流程示意图及局部示意图,在此次实施例的聚酯纤维以聚丙烯作为范例,并以最佳比例及温度作说明,由图中可清楚看出,将醚菊酯奈米尺度化后,加入抗氧化剂、抗UV剂、流动改质剂及低密度聚酯纤维以210度的温度下混合炼制,其比例分别为醚菊酯10%、抗氧化剂2%、抗UV剂19%、流动改质剂4%及低密度聚酯纤维65%,制作成奈米等级粒子,此后再将上述的奈米等级粒子与聚酯纤维均匀混合,并在210度的温度下进行制作成丝线1,其中该奈米等级粒子占总数的10%,而聚酯纤维占总数的90%,此后将丝线1制作成各种不同的成品(如蚊帐、帐篷、渔网等);而聚酯纤维如为聚乙烯时,其调配比例皆相同,但其制程的最佳温度改为180度,其步骤皆如上述,因丝线1上含醚菊酯成份的奈米微粒2,有效防止虫害,完成本发明的奈米灭虫聚酯纤维的制程。
Claims (8)
1.一种奈米灭虫聚酯纤维的制程,指一种将具灭虫性的奈米等级粒子与聚酯纤维结合的制程,其特征在于该制程包括:
(a)将7%~13%的醚菊酯、1%~3%的抗氧化剂、16%~22%的抗UV剂、1%~7%的流动改质剂及55%~75%的低密度聚酯纤维比例组合以140度~230度的温度下均匀混合炼制成一奈米等级粒子;
(b)将该奈米等级粒子与聚酯纤维分别以10%:90%的比例以140度~230度的温度下均匀混合,将其制作成丝线状。
2.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该醚菊酯的最佳比例为10%。
3.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该抗氧化剂的最佳比例为2%。
4.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该抗UV剂的最佳比例为19%。
5.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该流动改质剂的最佳比例为4%。
6.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该低密度聚酯纤维的最佳比例为65%。
7.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该聚酯纤维为一聚丙烯,且该制程最佳温度为210度。
8.根据权利要求1所述的奈米灭虫聚酯纤维的制程,其特征在于:其中该聚酯纤维为一聚乙烯,且该制程最佳温度为180度。