CN103102834A - Binder containing modified tree ashes - Google Patents
Binder containing modified tree ashes Download PDFInfo
- Publication number
- CN103102834A CN103102834A CN2012105270718A CN201210527071A CN103102834A CN 103102834 A CN103102834 A CN 103102834A CN 2012105270718 A CN2012105270718 A CN 2012105270718A CN 201210527071 A CN201210527071 A CN 201210527071A CN 103102834 A CN103102834 A CN 103102834A
- Authority
- CN
- China
- Prior art keywords
- sodium
- water
- binder
- trees ash
- comprised
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a binder containing modified trees ashes. The binder comprises the following materials: lignosulfonate, nanometer carbon, styrene, hydroxyethyl methylacrylate, acrylic ester, acrylic acid, sodium persulfate, allyloxy hydroxypropyl sodium sulfonate, starch, sodium hydroxide, borax, modified tree ashes, sodium sulfate, ammonium persulfate, dicumyl peroxide DCP, urea, sodium benzoate, ammonium carbonate and water. The binder disclosed by the invention is stable in quality, strong in adhesion force, good in bearing capacity, quick-drying without bubbles and capable of comprehensively improving various performances of a corrugated case. The modified tree ashes are added for reducing the damages of water molecules to the binder, so that the water resistance of the binder is greatly improved; the hydrophilic performance of the glue is reduced, so that the binder has good quick-drying characteristic, thereby facilitating the application on a high-speed corrugated line.
Description
Technical field
The present invention relates generally to a kind of composite caking agent, relates in particular to a kind of binding agent that contains modification trees ash.
Background technology
At present, in watt line production, the tackiness agent of corrugated cardboard mainly uses the amylan tackiness agent, we know, the stripping strength standard of existing Starch Adhesive is 5.88n/m2, its production technique is single stage method glue and two step method glue, glue is divided into again cold glue and two kinds of methods of hot glue, facts have proved, adopts the hot adhesive-preparing technology binder performance more made than cold adhesive-preparing technology good.But, existing tackiness agent can not be stablized, glue kinematic viscosity descends very fast, shorter general about 24 hours of shelf-time just began to go bad, body paper is to be made of multiple fiber molecule, starch adhesive is penetrated into fiber and forms the glue nail of root top shape from the surperficial pore of paper, follows closely effectively by glue between lining paper and stupefied peak to be bonded together.The high-strength corrugated board papery is better, and tightness is high, and the top sizing pore is blocked, and general glue perviousness is relatively poor, easily occurs false stickingly, bubbles, the quality problems such as come unstuck.Address this problem, must guarantee glue stability, will be accurate through the poor starch thickener of the viscosity high workability of overcuring, in right amount, spread upon equably on the corrugation crest line, satisfy this processing requirement of high-strength corrugated board bonding mechanism, must manufacture the glue performance aspect and be resolved.Dry slow, come unstuck distortion, moisture absorption.
Summary of the invention
The object of the invention is exactly for a kind of binding agent that contains modification trees ash is provided.
The present invention is achieved by the following technical solutions:
A kind of binding agent that contains modification trees ash, it is comprised of A, B, three kinds of material of C:
Described A material is comprised of the raw material of following weight parts: sulfonated lignin 1-2, nano-sized carbon 1-2, vinylbenzene, hydroxyethyl methylacrylate 1-2, acrylate 1-2, vinylformic acid 6-8, Sodium Persulfate 1-2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 1-2;
Described B material is comprised of the raw material of following weight parts: starch 15-20, sodium hydroxide 1-2, borax 0.8-1, modification trees ash 1-2, water 25-30;
The preparation method of described modification trees ash is:
(1) the trees ash is used 10-15% hydrogen peroxide dipping 3-4 hour, deionized water wash, then soaked 3-4 hour with the 10-12% sodium hydroxide solution, more extremely neutral with deionized water wash, oven dry;
(2) in the trees ash, add the sodium laurylsulfate, the nano-sized carbon of 1-2%, the polyisobutene of 2-3%, the 3-5% alum powder that are equivalent to its weight 2-3%, high speed 1200-1500 rev/min of stirring, ovendry power is broken into ultrafine powder;
Described C material is comprised of the raw material of following weight parts: sodium sulfate 1-2, ammonium persulphate 1-2, dicumyl peroxide DCP1-2, urea 1-2, Sodium Benzoate 1-2, volatile salt 1-2, water 125-130;
The preparation method of described Starch pre-expandity is:
(1) take the A material, first vinylbenzene is put into reactor, be heated to 70-75 ℃, then add other material, stir, then be warming up to 110-125 ℃, reacted discharging 2-3 hour;
(2) take B material, heat water to 80-90 ℃, sodium hydroxide, borax is soluble in water, mixing, then add starch, and stir, reacted 30-45 minute;
(3) take C material, heat water to 90-100 ℃, other material and A, B reacting rear material are added to the water successively, the limit edged stirs, 90-100 ℃ of lower insulated and stirred reaction 1-2 hour, and before reaction finished, accent PH was 6.8-7.2, discharging and get final product.
Advantage of the present invention is:
Formulating of recipe of the present invention is reasonable, and raw material is easy to get, and production technique is simple, coordinative composition of equipments is easy, constant product quality, cohesive force is strong, very power is good, quick-drying is non-foaming, comprehensively improves the various performances of Corrugated Box, add modification trees ash, effectively reduce water molecules to the destruction of binding agent, make the water resisting property of binding agent improve a lot, due to the hydrophilicity decline of glue, make its characteristic with good quick-drying, thereby be conducive to using on watt line at a high speed.
Embodiment
Embodiment 1
A kind of binding agent that contains modification trees ash, it is comprised of A, B, three kinds of material of C:
Described A material is comprised of the raw material of following weight parts: sulfonated lignin 2, nano-sized carbon 2, vinylbenzene, hydroxyethyl methylacrylate 2, acrylate 2, vinylformic acid 8, Sodium Persulfate 2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 2;
Described B material is comprised of the raw material of following weight parts: starch 20, sodium hydroxide 2, borax 0.8-1, modification trees ash 2, water 30;
The preparation method of described modification trees ash is:
(1) the trees ash is used 10-15% hydrogen peroxide dipping 4 hours, deionized water wash, then soaked 4 hours with 12% sodium hydroxide solution, more extremely neutral with deionized water wash, oven dry;
(2) in the trees ash, add the sodium laurylsulfate that is equivalent to its weight 3%, 2% nano-sized carbon, 3% polyisobutene, 5% alum powder, 1500 rev/mins of stirrings at a high speed, ovendry power is broken into ultrafine powder;
Described C material is comprised of the raw material of following weight parts: sodium sulfate 2, ammonium persulphate 2, dicumyl peroxide DCP2, urea 2, Sodium Benzoate 2, volatile salt 2, water 130;
The preparation method of described Starch pre-expandity is:
(1) take the A material, first vinylbenzene is put into reactor, be heated to 75 ℃, then add other material, stir, then be warming up to 125 ℃, reacted discharging 3 hours;
(2) take B material, heat water to 90 ℃, sodium hydroxide, borax is soluble in water, mixing, then add starch, and stir, reacted 45 minutes;
(3) take C material, heat water to 100 ℃, other material and A, B reacting rear material are added to the water successively, the limit edged stirs, 100 ℃ of lower insulated and stirred reactions 2 hours, and before reaction finished, transferring PH was 7.2, discharging and get final product.
Performance test:
The present invention's formula is through testing throughout the year, and its bond strength reaches 7.61n/cm
2, the physicalies such as side pressure strength surpass common adhesive 20-30% left and right, can deposit summer and autumn and never degenerate in 7 days, can deposit winter in spring and never degenerate in 14 days.The glue consumption: every layer of starch is 3.5g/m
2Can solve the lightweight paper plate and reveal the chop line problems such as trace, and can solve cardboard and come unstuck, bubble, false sticking, the quality problems such as prying are saved cost 30% left and right because the glue consumption reduces.
Atmospheric moisture was guaranteed the quality 60 days greater than in 90% situation, and carton ducks in drink, do not come unstuck in 48 hours, and after the carton drying, good bonding, mass conservation.
Claims (1)
1. binding agent that contains modification trees ash is characterized in that it is comprised of A, B, three kinds of material of C:
Described A material is comprised of the raw material of following weight parts: sulfonated lignin 1-2, nano-sized carbon 1-2, vinylbenzene, hydroxyethyl methylacrylate 1-2, acrylate 1-2, vinylformic acid 6-8, Sodium Persulfate 1-2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 1-2;
Described B material is comprised of the raw material of following weight parts: starch 15-20, sodium hydroxide 1-2, borax 0.8-1, modification trees ash 1-2, water 25-30;
The preparation method of described modification trees ash is:
(1) the trees ash is used 10-15% hydrogen peroxide dipping 3-4 hour, deionized water wash, then soaked 3-4 hour with the 10-12% sodium hydroxide solution, more extremely neutral with deionized water wash, oven dry;
(2) in the trees ash, add the sodium laurylsulfate, the nano-sized carbon of 1-2%, the polyisobutene of 2-3%, the 3-5% alum powder that are equivalent to its weight 2-3%, high speed 1200-1500 rev/min of stirring, ovendry power is broken into ultrafine powder;
Described C material is comprised of the raw material of following weight parts: sodium sulfate 1-2, ammonium persulphate 1-2, dicumyl peroxide DCP1-2, urea 1-2, Sodium Benzoate 1-2, volatile salt 1-2, water 125-130;
The described preparation method who contains the binding agent of modification trees ash is:
(1) take the A material, first vinylbenzene is put into reactor, be heated to 70-75 ℃, then add other material, stir, then be warming up to 110-125 ℃, reacted discharging 2-3 hour;
(2) take B material, heat water to 80-90 ℃, sodium hydroxide, borax is soluble in water, mixing, then add starch, and stir, reacted 30-45 minute;
(3) take C material, heat water to 90-100 ℃, other material and A, B reacting rear material are added to the water successively, the limit edged stirs, 90-100 ℃ of lower insulated and stirred reaction 1-2 hour, and before reaction finished, accent PH was 6.8-7.2, discharging and get final product.