CN1403520A - Starch adhesive reinforcer specially for paper pipe and its prepn process - Google Patents
Starch adhesive reinforcer specially for paper pipe and its prepn process Download PDFInfo
- Publication number
- CN1403520A CN1403520A CN 02139142 CN02139142A CN1403520A CN 1403520 A CN1403520 A CN 1403520A CN 02139142 CN02139142 CN 02139142 CN 02139142 A CN02139142 A CN 02139142A CN 1403520 A CN1403520 A CN 1403520A
- Authority
- CN
- China
- Prior art keywords
- component
- water
- aqueous solution
- paper tube
- starch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The starch adhesive resinforcer specially for paper pipe is prepared with raw material components, including the component A comprising calcium carbonate and potassium permanganate and the component B comprising sodium hydroxide and borax. Its preparation includes the steps of: mixing calcium carbonate powder and potassium permanganate to constitute the component A, dilute with water to form a water solution with 20-25% solid content, mixing sodium hydroxide and borax to consitute the component B, dilute with water to form a water solution with 12-16% solid content, mixing the water solution of component A and the water solution of component B and setting for 12 hr before adding starch at room temperature. The paper pipe with the starch adhesive reinforcer has high compression strength, less likelihood of being damped and deformed, and high wear resistance.
Description
(1) technical field:
The present invention relates to a kind of tackiness agent toughener, relate in particular to a kind of starch adhesive toughener and preparation technology thereof of be used to bond kinking paper tube, toiler roll pipe.
(2) background technology:
At present, the supporting tube that is used to support yardage roll, the coil of wire, toilet roll reel all is to utilize multi-layer packaging paper to form through rolling, airing through smearing tackiness agent again.The tackiness agent that this class paper tube adopted has bubble flower alkali, poly-ethanol tackiness agent, carboxymethyl cellulose gum stick, white glue with vinyl, starch adhesive etc.Because its raw material of starch adhesive is easy to get, preparation technology is simple, promptly normal temperature is made low cost of manufacture down, starch adhesive is liked using by the many paper tubes of event manufactory, and that the shortcoming of starch adhesive is an initial bonding strength is little, moisture-sensitive, and the paper tube wear resistance of making, anti-drawing property and crushing resistance are all poor.
(3) summary of the invention: be used for the existing problem of paper tube starch adhesive at present in order to solve, the invention provides and a kind of starch adhesive is played enhancement, makes it the starch specialized tackiness agent toughener of paper tube that adhesive property improves, the technical solution of the utility model realizes in the following manner:
The starch specialized tackiness agent toughener of a kind of paper tube, it is formed by following A, the two component preparation of raw material of B, i.e. the A component: lime carbonate 12.0-16.0 part, potassium permanganate 0.8-1.0 part; B component: sodium hydroxide 4.0-8.0 part, borax 0.5-3.0 part.
For reducing the production cost of this toughener, the lime carbonate that the present invention adopts is water-ground limestone.
Preparation technology of the present invention is: earlier Paris white, potassium permanganate in the A component are mixed by above-mentioned prescription, be diluted with water to the aqueous solution that solid content is 20%-25%; By above-mentioned prescription B component sodium hydroxide, borax are mixed, be diluted with water to the aqueous solution that solid content is 12%-16%, with after placing 12 hours after the A component aqueous solution, the B component aqueous solution, adding gets final product during the room temperature preparation starch adhesive at last.
Positively effect of the present utility model is: the paper tube ultimate compression strength height of 1, making, through pressure pump test, before adding this toughener diameter be 250 centimetres paper tube to bear pressure be every square of 6-7 normal atmosphere, adding after this toughener is 12-14 normal atmosphere; 2, moisture-sensitive not through test, was made paper tube and is placed the distortion of making moist in 10-20 days before adding this toughener, after adding this toughener, place do not make moist in 6 months, indeformable; 3, wear-resisting, before adding this toughener, make paper tube side cut, deburring, polishing fluffing, paper tube side cut, deburring, the polishing of making after adding this toughener are phozy.
(5) embodiment:
Embodiment one: 12.0 parts in lime carbonate, 0.8 part in potassium permanganate; B component: 4.0 parts in sodium hydroxide, 0.5 part of borax.Preparation technology is: earlier Paris white, potassium permanganate in the A component are mixed by above-mentioned prescription, be diluted with water to solid content and be 20% the aqueous solution; By above-mentioned B component sodium hydroxide, borax are mixed again, be diluted with water to solid content and be 12% the aqueous solution,, add during the room temperature preparation starch adhesive and get final product at last with after placing 12 hours after the A component aqueous solution, the B component aqueous solution.
Embodiment two: the A component: 13.0 parts in lime carbonate, 0.9 part in potassium permanganate; B component: 5.0 parts in sodium hydroxide, 1.0 parts of boraxs.Preparation technology is: earlier Paris white, potassium permanganate in the A component are mixed by above-mentioned prescription, be diluted with water to solid content and be 22% the aqueous solution; By above-mentioned B component sodium hydroxide, borax are mixed again, be diluted with water to solid content and be 13% the aqueous solution,, add during the room temperature preparation starch adhesive and get final product at last with after placing 12 hours after the A component aqueous solution, the B component aqueous solution.
Embodiment three: the A component: 15.0 parts in lime carbonate, 0.9 part in potassium permanganate; B component: 6.0 parts in sodium hydroxide, 2.0 parts of boraxs.Preparation technology of the present invention is: earlier Paris white, potassium permanganate in the A component are mixed by above-mentioned prescription, be diluted with water to solid content and be 24% the aqueous solution; By above-mentioned we B component sodium hydroxide, borax are mixed again, be diluted with water to solid content and be 14% the aqueous solution,, add during the room temperature preparation starch adhesive and get final product at last with after placing 12 hours after the A component aqueous solution, the B component aqueous solution.
Embodiment four, A component: 16.0 parts in lime carbonate, 1.0 parts in potassium permanganate; B component: 8.0 parts in sodium hydroxide, 3.0 parts of boraxs.
Preparation technology of the present invention is: earlier Paris white, potassium permanganate in the A component are mixed by above-mentioned prescription, be diluted with water to solid content and be 25% the aqueous solution; By above-mentioned prescription B component sodium hydroxide, borax are mixed again, be diluted with water to solid content and be 16% the aqueous solution,, add during the room temperature preparation starch adhesive and get final product at last with after placing 12 hours after the A component aqueous solution, the B component aqueous solution.
Embodiment five: 14.0 parts of water-ground limestones, 1.0 parts in potassium permanganate; B component: 6.0 parts in sodium hydroxide, 2.0 parts of boraxs.Preparation technology is: earlier Paris white, potassium permanganate in the A component are mixed by above-mentioned prescription, be diluted with water to solid content and be 20% the aqueous solution; By above-mentioned B component sodium hydroxide, borax are mixed again, be diluted with water to solid content and be 12% the aqueous solution,, add during the room temperature preparation starch adhesive and get final product at last with after placing 12 hours after the A component aqueous solution, the B component aqueous solution.
This product pressure-bearing testing method is: made paper tube defines rows, placement force pump, progressively pressurization on paper tube in a row then, and until the paper tube distortion, then the apparent pressure data of pressure pump is that paper tube bears pressure.
Claims (4)
1, the starch specialized tackiness agent toughener of a kind of paper tube, it is formed by following A, the two component preparation of raw material of B: A component: lime carbonate 12.0-16.0 part, potassium permanganate 0.8-1.0 part; B component: sodium hydroxide 4.0-8.0 part, borax 0.5-3.0 part.
2, the starch specialized tackiness agent of paper tube according to claim 1 is characterized in that lime carbonate is water-ground limestone.
3, the starch specialized tackiness agent toughener of a kind of paper tube preparation technology is characterized in that with the A in the two component raw materials of A, B be that Paris white, potassium permanganate mix, and is diluted with water to the aqueous solution that solid content is 20-25%; Sodium hydroxide, borax in the B component are mixed again, be diluted with water to the aqueous solution that solid content is 12-16, with after placing 12 hours after the A component aqueous solution, the B component aqueous solution, adding gets final product during the room temperature preparation starch adhesive at last.
4, the starch specialized tackiness agent toughener of paper tube according to claim 3 preparation technology is characterized in that lime carbonate is water-ground limestone.