CN103087652A - Speed glue and preparation method thereof - Google Patents
Speed glue and preparation method thereof Download PDFInfo
- Publication number
- CN103087652A CN103087652A CN 201210450974 CN201210450974A CN103087652A CN 103087652 A CN103087652 A CN 103087652A CN 201210450974 CN201210450974 CN 201210450974 CN 201210450974 A CN201210450974 A CN 201210450974A CN 103087652 A CN103087652 A CN 103087652A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixed solution
- starch
- glue
- quick setting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses speed glue and a preparation method thereof, and in particular relates to speed glue for bonding paper products such as paper boxes, paper cylinders and cement bags and a preparation method thereof. The speed glue is formed by mixing and reacting starch, cleaned water, silicone oil, carbolic acid, sodium hydroxide, oxidant, a quick desiccant and a complexing stopping agent and the like. The glue is slow in drying speed, poor in humidity resistance, and low in adhesive fastness. The paper products such as paper boxes, paper cylinders and cement bags produced by using the glue are poorer in quality.
Description
Technical field
The present invention relates to a kind of glue and preparation method thereof.Specifically, be the quick setting cement and preparation method thereof of the paper products such as bonding carton, paper web, bag of cement.
Background technology
All know at paper products production industries such as carton, paper web, bag of cements, being used for the glue of the paper products such as bonding carton, paper web, bag of cement is traditional glue.This glue, rate of drying is slow, and humidity resistance is poor, viscosity fastness is low, therefore, and the paper products such as the carton of this glue production of employing, paper web, bag of cement, second-rate.
Summary of the invention
The problem to be solved in the present invention is to provide a kind of quick setting cement.This quick setting cement, rate of drying is fast, and humidity resistance is good, viscosity fastness is high, therefore, and the paper products such as the carton of this glue production of employing, paper web, bag of cement, quality is good.
Another problem that the present invention will solve is to provide a kind of method for preparing quick setting cement.
For addressing the above problem, take following technical scheme:
Quick setting cement characteristics of the present invention are the raw materials that contain following parts by weight:
90 ~ 110 parts of starch;
250 ~ 300 parts, clear water;
0.02 ~ 0.04 part of silicone oil;
0.5 ~ 0.7 part of PHENOL 99.8 MIN ((CARBOLIC ACID));
13 ~ 15 parts, sodium hydroxide;
6 ~ 8 parts, oxygenant;
5 ~ 7 parts of Rapid dry drying prescription;
7 ~ 9 parts of agent are ended in complexing.
The method characteristic for preparing described quick setting cement is to comprise the following steps successively:
First starch, 50% clear water and oxygenant are dropped in reactor together, mix, obtain mixed solution;
Then, sodium hydroxide is added in mixed solution react, along with the first retrogradation, rear thinning of mixed solution, when making the viscosity of mixed solution reach 50 ~ 70s;
Afterwards, add complexing to end agent, make the viscosity of mixed solution reach 30 ~ 40s;
Afterwards, in uniform stirring, add remaining 50% clear water and silicone oil;
At last, when continuing stirring, add Rapid dry drying prescription and PHENOL 99.8 MIN ((CARBOLIC ACID)), and mix, obtain quick setting cement of the present invention.
Take following scheme, have the following advantages:
Can be found out by such scheme, owing to containing the Rapid dry drying prescription in raw material of the present invention, in use procedure, rate of drying is fast, and humidity resistance is good, viscosity fastness is high, therefore, the paper products such as the carton of this glue production of employing, paper web, bag of cement, quality is good.
Embodiment
Embodiment one
First choose raw material according to following part by weight:
90 parts of starch;
250 parts, clear water;
0.02 part of silicone oil;
0.5 part of PHENOL 99.8 MIN ((CARBOLIC ACID));
13 parts, sodium hydroxide;
6 parts, oxygenant;
5 parts of Rapid dry drying prescription;
7 parts of agent are ended in complexing.
Described starch is wheat starch.
Then, starch, 50% clear water and oxygenant are dropped in reactor together, mix, obtain mixed solution.
Afterwards, sodium hydroxide is added in mixed solution react, along with the first retrogradation, rear thinning of mixed solution, when making the viscosity of mixed solution reach 50s.
Afterwards, add complexing to end agent, make the viscosity of mixed solution reach 30s.
Afterwards, in uniform stirring, add remaining 50% clear water and silicone oil.
At last, when continuing stirring, add Rapid dry drying prescription and PHENOL 99.8 MIN ((CARBOLIC ACID)), and mix, obtain quick setting cement of the present invention.
Embodiment two
First choose raw material in following ratio:
100 parts of starch;
280 parts, clear water;
0.03 part of silicone oil;
0.6 part of PHENOL 99.8 MIN ((CARBOLIC ACID));
14 parts, sodium hydroxide;
7 parts, oxygenant;
6 parts of Rapid dry drying prescription;
8 parts of agent are ended in complexing.
Described starch is wheat starch.
Afterwards, starch, 50% clear water and oxygenant are dropped in reactor together, mix, obtain mixed solution.
Then, sodium hydroxide is added in mixed solution react, along with the first retrogradation, rear thinning of mixed solution, when making the viscosity of mixed solution reach 60s.
Afterwards, add complexing to end agent, make the viscosity of mixed solution reach 35s.
Afterwards, in uniform stirring, add remaining 50% clear water and silicone oil.
At last, when continuing stirring, add Rapid dry drying prescription and PHENOL 99.8 MIN ((CARBOLIC ACID)), and mix, obtain quick setting cement of the present invention.
Embodiment three
First choose raw material according to following part by weight:
110 parts of starch;
300 parts, clear water;
0.04 part of silicone oil;
0.7 part of PHENOL 99.8 MIN ((CARBOLIC ACID));
15 parts, sodium hydroxide;
8 parts, oxygenant;
7 parts of Rapid dry drying prescription;
9 parts of agent are ended in complexing.
Described starch is wheat starch.
Then, starch, 50% clear water and oxygenant are dropped in reactor together, mix, obtain mixed solution;
Afterwards, sodium hydroxide is added in mixed solution react, along with the first retrogradation, rear thinning of mixed solution, when making the viscosity of mixed solution reach 50 ~ 70s.
Afterwards, add complexing to end agent, make the viscosity of mixed solution reach 30 ~ 40s.
Afterwards, in uniform stirring, add remaining 50% clear water and silicone oil.
At last, when continuing stirring, add Rapid dry drying prescription and PHENOL 99.8 MIN ((CARBOLIC ACID)), and mix, obtain quick setting cement of the present invention.
Claims (3)
1. quick setting cement is characterized in that containing the raw material of following parts by weight:
90 ~ 110 parts of starch;
250 ~ 300 parts, clear water;
0.02 ~ 0.04 part of silicone oil;
0.5 ~ 0.7 part of PHENOL 99.8 MIN ((CARBOLIC ACID));
13 ~ 15 parts, sodium hydroxide;
6 ~ 8 parts, oxygenant;
5 ~ 7 parts of Rapid dry drying prescription;
7 ~ 9 parts of agent are ended in complexing.
2. quick setting cement according to claim 1, is characterized in that described starch is wheat starch.
3. the method for preparing the described quick setting cement of claim 1 is characterized in that comprising the following steps successively:
First starch, 50% clear water and oxygenant are dropped in reactor together, mix, obtain mixed solution;
Then, sodium hydroxide is added in mixed solution react, along with the first retrogradation, rear thinning of mixed solution, when making the viscosity of mixed solution reach 50 ~ 70s;
Afterwards, add complexing to end agent, make the viscosity of mixed solution reach 30 ~ 40s;
Afterwards, in uniform stirring, add remaining 50% clear water and silicone oil;
At last, when continuing stirring, add Rapid dry drying prescription and PHENOL 99.8 MIN ((CARBOLIC ACID)), and mix, obtain quick setting cement of the present invention.