CN103102831B - A kind of corrugated board composite caking agent - Google Patents

Abstract

The invention discloses a kind of corrugated board composite caking agent, it is made up of following raw material: smoke sheet rubber, nano-sized carbon, styrene, polyisobutene, acrylate, acrylic acid, sodium peroxydisulfate, allyloxy hydroxypropyl azochlorosulfonate acid sodium; Starch, NaOH, borax, modification trees ash, water; Zinc dialkyl dithiophosphate, cumyl peroxide DCP, Silane coupling agent KH550, aluminium hydroxide, sodium carbonate, ammonium persulfate, diatomite, lauryl sodium sulfate; Constant product quality of the present invention, cohesive force is strong, very power is good, quick-drying is non-foaming, comprehensively improve the various performances of corrugated case, add modification trees ash, effectively reduce the destruction of hydrone to binding agent, the water-resistance of binding agent is improved a lot, because the hydrophilicity of glue declines, make its characteristic with good quick-drying, thereby be conducive on watt line, using at a high speed.

Description

A kind of corrugated board composite caking agent

Technical field

The present invention relates generally to a kind of composite caking agent, relates in particular to a kind of corrugated board composite caking agent.

Background technology

At present, watt line produce in the adhesive of corrugated board mainly use amylan adhesive, we know, the peel strength standard of existing amylum adhesive is 5.88n/m2, its production technology is one-step method glue and two step method glue, glue is divided into again cold glue and two kinds of methods of hot glue, facts have proved, adopts the hot adhesive-preparing technology binder performance more made than cold adhesive-preparing technology good. But, existing adhesive can not be stablized, glue kinematic viscosity declines very fast, shorter general about 24 hours of resting period just started to go bad, body paper is to be made up of multiple fiber molecule, starch adhesive is penetrated into fiber and forms the glue nail of root top shape from the surperficial pore of paper, between lining paper and stupefied peak, is followed closely effectively and is bonded together by glue. High-strength corrugated board papery is better, and tightness is high, and top sizing pore is blocked, and general glue permeability is poor, easily occurs false stickyly, bubbles, the quality problems such as come unstuck. Address this problem, must ensure glue stability, by accurate starch thickener poor the viscosity high fluidity through overcuring, in right amount, spread upon equably on corrugation crest line, meet this technological requirement of high-strength corrugated board bonding mechanism, must manufacture glue performance aspect and be resolved. Dry slow, come unstuck distortion, moisture absorption.

Summary of the invention

The object of the invention is exactly for a kind of corrugated board composite caking agent is provided.

The present invention is achieved by the following technical solutions:

A kind of corrugated board composite caking agent, it is made up of A, B, tri-kinds of material of C:

Described A material is made up of the raw material of following weight parts: smoke sheet rubber 1-2, nano-sized carbon 0.5-1, styrene 5-8, polyisobutene 2-3, acrylate 2-3, acrylic acid 3-5, sodium peroxydisulfate 1-2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 2-3;

Described B material is made up of the raw material of following weight parts: starch 15-20, NaOH 1-2, borax 0.5-1, modification trees ash 1-2, water 20-30;

The preparation method of described modification trees ashes is:

(1) 10-15% hydrogen peroxide dipping 3-4 hour for trees ashes, deionized water washing, then soak 3-4 hour with 10-12% sodium hydroxide solution, then with deionized water washing to neutral, oven dry;

(2) in trees ashes, add the sldium lauryl sulfate, the nano-sized carbon of 1-2%, the polyisobutene of 2-3%, the 3-5% alum powder that are equivalent to its weight 2-3%, high speed 1200-1500 rev/min of stirring, ovendry power is broken into superfines;

Described C material is made up of the raw material of following weight parts: zinc dialkyl dithiophosphate 1-2, cumyl peroxide DCP1-2, Silane coupling agent KH550 1-2, aluminium hydroxide 1-2, sodium carbonate 1-2, ammonium persulfate 1-2, diatomite 3-5, lauryl sodium sulfate 1-2, water 120-130;

Described corrugated board by the preparation method of composite caking agent is:

(1) take A material, first styrene is put into reactor, be heated to 70-75 DEG C, then add other material, stir, then be warming up to 110-125 DEG C, reaction 2-3 hour, discharging;

(2) take B material, heat water to 80-90 DEG C, NaOH, borax is soluble in water, mix, then add starch, stir reaction 30-45 minute;

(3) take C material, heat water to 90-100 DEG C, other material and A, B reacting rear material are added to the water successively, limit edged stirs, insulated and stirred reaction 1-2 hour at 90-100 DEG C, and before reaction finishes, tune PH is 6.8-7.2, discharging and get final product.

Advantage of the present invention is:

Formula Design of the present invention is reasonable, and raw material is easy to get, and production technology is simple, coordinative composition of equipments is easy, constant product quality, cohesive force is strong, very power is good, quick-drying is non-foaming, comprehensively improves the various performances of corrugated case, add modification trees ash, effectively reduce the destruction of hydrone to binding agent, the water-resistance of binding agent is improved a lot, because the hydrophilicity of glue declines, make its characteristic with good quick-drying, thereby be conducive on watt line, using at a high speed.

Detailed description of the invention

Embodiment 1

A kind of corrugated board composite caking agent, it is made up of A, B, tri-kinds of material of C:

Described A material is made up of the raw material of following weight parts: smoke sheet rubber 2, nano-sized carbon 1, styrene 8, polyisobutene 3, acrylate 3, acrylic acid 5, sodium peroxydisulfate 2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 3;

Described B material is made up of the raw material of following weight parts: starch 20, NaOH 2, borax 1, modification trees ash 2, water 30;

The preparation method of described modification trees ash is:

(1) 15% hydrogen peroxide dipping 4 hours for trees ashes, deionized water washing, then soak 4 hours with 12% sodium hydroxide solution, then with deionized water washing to neutrality, oven dry;

(2) in trees ash, add and be equivalent to the sldium lauryl sulfate of its weight 3%, 2% nano-sized carbon, 3% polyisobutene, 5% alum powder, 1500 revs/min of stirrings at a high speed, ovendry power is broken into superfines;

Described C material is made up of the raw material of following weight parts: zinc dialkyl dithiophosphate 2, cumyl peroxide DCP2, Silane coupling agent KH550 2, aluminium hydroxide 2, sodium carbonate 2, ammonium persulfate 2, diatomite 5, lauryl sodium sulfate 2, water 130;

Described corrugated board by the preparation method of composite caking agent is:

(1) take A material, first styrene is put into reactor, be heated to 75 DEG C, then add other material, stir, then be warming up to 125 DEG C, react discharging 3 hours;

(2) take B material, heat water to 90 DEG C, NaOH, borax is soluble in water, mix, then add starch, stir, react 45 minutes;

(3) take C material, heat water to 100 DEG C, other material and A, B reacting rear material are added to the water successively, limit edged stirs, insulated and stirred reaction 2 hours at 100 DEG C, and before reaction finishes, adjusting PH is 7.2, discharging and get final product.

Performance test:

The present invention fills a prescription through testing throughout the year, and its bonding strength reaches 7.61n/cm², the physical properties such as side pressure strength exceed common adhesive 20-30% left and right, can deposit summer and autumn and never degenerate for 7 days, can deposit winter in spring and never degenerate for 14 days. Glue consumption: every layer of starch is 3.5g/m². Can solve lightweight paper plate and reveal the chop line problem such as trace, and can solve cardboard and come unstuck, bubble, false sticky, the quality problems such as prying, because glue consumption reduces cost-saving 30% left and right.

Air humidity is greater than in 90% situation, guarantees the quality 60 days, and carton ducks in drink, within 48 hours, do not come unstuck, and after carton is dry, good bonding, mass conservation.

Claims (1)

1. a corrugated board composite caking agent, is characterized in that it is made up of A, B, tri-kinds of material of C:

Described A material is made up of the raw material of following weight parts: smoke sheet rubber 1-2, nano-sized carbon 0.5-1, styrene 5-8, polyisobutene 2-3, acrylate 2-3, acrylic acid 3-5, sodium peroxydisulfate 1-2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 2-3;

Described B material is made up of the raw material of following weight parts: starch 15-20, NaOH 1-2, borax 0.5-1, modification trees ash 1-2, water 20-30;

The preparation method of described modification trees ash is:

(1) 10-15% hydrogen peroxide dipping 3-4 hour for trees ashes, deionized water washing, then soak 3-4 hour with 10-12% sodium hydroxide solution, then with deionized water washing to neutral, oven dry;

(2) in trees ashes, add the sldium lauryl sulfate, the nano-sized carbon of 1-2%, the polyisobutene of 2-3%, the 3-5% alum powder that are equivalent to its weight 2-3%, high speed 1200-1500 rev/min of stirring, ovendry power is broken into superfines;

Described C material is made up of the raw material of following weight parts: zinc dialkyl dithiophosphate 1-2, cumyl peroxide DCP1-2, Silane coupling agent KH550 1-2, aluminium hydroxide 1-2, sodium carbonate 1-2, ammonium persulfate 1-2, diatomite 3-5, lauryl sodium sulfate 1-2, water 120-130;

Described corrugated board by the preparation method of composite caking agent is:

(1) take A material, first styrene is put into reactor, be heated to 70-75 DEG C, then add other material, stir, then be warming up to 110-125 DEG C, reaction 2-3 hour, discharging;

(2) take B material, heat water to 80-90 DEG C, NaOH, borax is soluble in water, mix, then add starch, stir reaction 30-45 minute;

(3) take C material, heat water to 90-100 DEG C, other material and A, B reacting rear material are added to the water successively, limit edged stirs, insulated and stirred reaction 1-2 hour at 90-100 DEG C, and before reaction finishes, tune pH is 6.8-7.2, discharging and get final product.