CN103102832B - A kind of high-strength waterproof corrugated cases adhesive - Google Patents
A kind of high-strength waterproof corrugated cases adhesive Download PDFInfo
- Publication number
- CN103102832B CN103102832B CN201210527069.0A CN201210527069A CN103102832B CN 103102832 B CN103102832 B CN 103102832B CN 201210527069 A CN201210527069 A CN 201210527069A CN 103102832 B CN103102832 B CN 103102832B
- Authority
- CN
- China
- Prior art keywords
- sodium
- water
- acid
- hour
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of high-strength waterproof corrugated cases adhesive, it is made up of following raw material: stearic acid, nanometer sepiolite powder, styrene, hydroxyethyl methacrylate, acrylate, acrylic acid, sodium peroxydisulfate, allyloxy hydroxypropyl azochlorosulfonate acid sodium, starch, NaOH, borax, modification trees ash; Chitosan-acetic acid solution, aluminium powder, sodium carbonate, hydrogen peroxide, sodium acid carbonate, water; Constant product quality of the present invention, cohesive force is strong, very power is good, quick-drying is non-foaming, comprehensively improve the various performances of corrugated case, add modification trees ash, effectively reduce the destruction of hydrone to binding agent, the water-resistance of binding agent is improved a lot, because the hydrophilicity of glue declines, make its characteristic with good quick-drying, thereby be conducive on watt line, using at a high speed.
Description
Technical field
The present invention relates generally to a kind of bonding agent, relates in particular to a kind of high-strength waterproof corrugated cases adhesive.
Background technology
At present, watt line produce in the adhesive of corrugated board mainly use amylan adhesive, we know, the peel strength standard of existing amylum adhesive is 5.88n/m2, its production technology is one-step method glue and two step method glue, glue is divided into again cold glue and two kinds of methods of hot glue, facts have proved, adopts the hot adhesive-preparing technology binder performance more made than cold adhesive-preparing technology good. But, existing adhesive can not be stablized, glue kinematic viscosity declines very fast, shorter general about 24 hours of resting period just started to go bad, body paper is to be made up of multiple fiber molecule, starch adhesive is penetrated into fiber and forms the glue nail of root top shape from the surperficial pore of paper, between lining paper and stupefied peak, is followed closely effectively and is bonded together by glue. High-strength corrugated board papery is better, and tightness is high, and top sizing pore is blocked, and general glue permeability is poor, easily occurs false stickyly, bubbles, the quality problems such as come unstuck. Address this problem, must ensure glue stability, by accurate starch thickener poor the viscosity high fluidity through overcuring, in right amount, spread upon equably on corrugation crest line, meet this technological requirement of high-strength corrugated board bonding mechanism, must manufacture glue performance aspect and be resolved. Dry slow, come unstuck distortion, moisture absorption.
Summary of the invention
The object of the invention is exactly for a kind of high-strength waterproof corrugated cases adhesive is provided.
The present invention is achieved by the following technical solutions:
A kind of high-strength waterproof corrugated cases adhesive, it is made up of A, B, tri-kinds of material of C:
Described A material is made up of the raw material of following weight parts: stearic acid 1-2, nanometer sepiolite powder 1-2, styrene, hydroxyethyl methacrylate 1-2, acrylate 2-3, acrylic acid 4-6, sodium peroxydisulfate 1-2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 1-2;
Described B material is made up of the raw material of following weight parts: starch 18-20, NaOH 1-2, borax 0.6-1, modification trees ash 1-2, water 25-30;
The preparation method of described modification trees ash is:
(1) 10-15% hydrogen peroxide dipping 3-4 hour for trees ashes, deionized water washing, then soak 3-4 hour with 10-12% sodium hydroxide solution, then with deionized water washing to neutral, oven dry;
(2) in trees ashes, add the sldium lauryl sulfate, the nano-sized carbon of 1-2%, the polyisobutene of 2-3%, the 3-5% alum powder that are equivalent to its weight 2-3%, high speed 1200-1500 rev/min of stirring, ovendry power is broken into superfines;
Described C material is made up of the raw material of following weight parts: chitosan-acetic acid solution 1-2, aluminium powder 1-2, sodium carbonate 1-2, hydrogen peroxide 2-4, sodium acid carbonate 1-2, water 120-125;
Described corrugated board by the preparation method of composite caking agent is:
(1) take A material, first styrene is put into reactor, be heated to 70-75 DEG C, then add other material, stir, then be warming up to 110-125 DEG C, reaction 2-3 hour, discharging;
(2) take B material, heat water to 80-90 DEG C, NaOH, borax is soluble in water, mix, then add starch, stir reaction 30-45 minute;
(3) take C material, heat water to 90-100 DEG C, other material and A, B reacting rear material are added to the water successively, limit edged stirs, insulated and stirred reaction 1-2 hour at 90-100 DEG C, and before reaction finishes, tune PH is 6.8-7.2, discharging and get final product.
Advantage of the present invention is:
Formula Design of the present invention is reasonable, and raw material is easy to get, and production technology is simple, coordinative composition of equipments is easy, constant product quality, cohesive force is strong, very power is good, quick-drying is non-foaming, comprehensively improves the various performances of corrugated case, add modification trees ash, effectively reduce the destruction of hydrone to binding agent, the water-resistance of binding agent is improved a lot, because the hydrophilicity of glue declines, make its characteristic with good quick-drying, thereby be conducive on watt line, using at a high speed.
Detailed description of the invention
Embodiment 1
A kind of high-strength waterproof corrugated cases adhesive, it is made up of A, B, tri-kinds of material of C:
Described A material is made up of the raw material of following weight parts: stearic acid 2, nanometer sepiolite powder 2, styrene, hydroxyethyl methacrylate 1, acrylate 3, acrylic acid 6, sodium peroxydisulfate 2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 2;
Described B material is made up of the raw material of following weight parts: starch 20, NaOH 2, borax 1, modification trees ash 2, water 30;
The preparation method of described modification trees ash is:
(1) 15% hydrogen peroxide dipping 4 hours for trees ashes, deionized water washing, then soak 4 hours with 12% sodium hydroxide solution, then with deionized water washing to neutral, oven dry;
(2) in trees ashes, add and be equivalent to the sldium lauryl sulfate of its weight 3%, 2% nano-sized carbon, 3% polyisobutene, 5% alum powder, 1500 revs/min of stirrings at a high speed, ovendry power is broken into superfines;
Described C material is made up of the raw material of following weight parts: chitosan-acetic acid solution 2, aluminium powder 2, sodium carbonate 2, hydrogen peroxide 4, sodium acid carbonate 2, water 125;
Described corrugated board by the preparation method of composite caking agent is:
(1) take A material, first styrene is put into reactor, be heated to 75 DEG C, then add other material, stir, then be warming up to 125 DEG C, react discharging 3 hours;
(2) take B material, heat water to 90 DEG C, NaOH, borax is soluble in water, mix, then add starch, stir, react 45 minutes;
(3) take C material, heat water to 100 DEG C, other material and A, B reacting rear material are added to the water successively, limit edged stirs, insulated and stirred reaction 2 hours at 100 DEG C, and before reaction finishes, adjusting PH is 7.2, discharging and get final product.
Performance test:
The present invention fills a prescription through testing throughout the year, and its bonding strength reaches 7.61n/cm2, the physical properties such as side pressure strength exceed common adhesive 20-30% left and right, can deposit summer and autumn and never degenerate for 7 days, can deposit winter in spring and never degenerate for 14 days. Glue consumption: every layer of starch is 3.5g/m2. Can solve lightweight paper plate and reveal the chop line problem such as trace, and can solve cardboard and come unstuck, bubble, false sticky, the quality problems such as prying, because glue consumption reduces cost-saving 30% left and right.
Air humidity is greater than in 90% situation, guarantees the quality 60 days, and carton ducks in drink, within 48 hours, do not come unstuck, and after carton is dry, good bonding, mass conservation.
Claims (1)
1. a high-strength waterproof corrugated cases adhesive, is characterized in that it is made up of A, B, tri-kinds of material of C:
Described A material is made up of the raw material of following weight parts: stearic acid 1-2, nanometer sepiolite powder 1-2, styrene, hydroxyethyl methacrylate 1-2, acrylate 2-3, acrylic acid 4-6, sodium peroxydisulfate 1-2, allyloxy hydroxypropyl azochlorosulfonate acid sodium 1-2;
Described B material is made up of the raw material of following weight parts: starch 18-20, NaOH 1-2, borax 0.6-1, modification trees ash 1-2, water 25-30;
The preparation method of described modification trees ash is:
(1) 10-15% hydrogen peroxide dipping 3-4 hour for trees ashes, deionized water washing, then soak 3-4 hour with 10-12% sodium hydroxide solution, then with deionized water washing to neutral, oven dry;
(2) in trees ashes, add the sldium lauryl sulfate, the nano-sized carbon of 1-2%, the polyisobutene of 2-3%, the 3-5% alum powder that are equivalent to its weight 2-3%, high speed 1200-1500 rev/min of stirring, ovendry power is broken into superfines;
Described C material is made up of the raw material of following weight parts: chitosan-acetic acid solution 1-2, aluminium powder 1-2, sodium carbonate 1-2, hydrogen peroxide 2-4, sodium acid carbonate 1-2, water 120-125;
The preparation method of described high-strength waterproof corrugated cases adhesive is:
(1) take A material, first styrene is put into reactor, be heated to 70-75 DEG C, then add other material, stir, then be warming up to 110-125 DEG C, reaction 2-3 hour, discharging;
(2) take B material, heat water to 80-90 DEG C, NaOH, borax is soluble in water, mix, then add starch, stir reaction 30-45 minute;
(3) take C material, heat water to 90-100 DEG C, other material and A, B reacting rear material are added to the water successively, limit edged stirs, insulated and stirred reaction 1-2 hour at 90-100 DEG C, and before reaction finishes, tune pH is 6.8-7.2, discharging and get final product.