CN103088310A - 以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法 - Google Patents

以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法 Download PDF

Info

Publication number
CN103088310A
CN103088310A CN2013100081076A CN201310008107A CN103088310A CN 103088310 A CN103088310 A CN 103088310A CN 2013100081076 A CN2013100081076 A CN 2013100081076A CN 201310008107 A CN201310008107 A CN 201310008107A CN 103088310 A CN103088310 A CN 103088310A
Authority
CN
China
Prior art keywords
tantalum
vitreous carbon
graphite foam
template
reticular
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013100081076A
Other languages
English (en)
Inventor
郭建明
杨艳文
郭建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Qingdao Gao Tai New Material Co Ltd
Original Assignee
Qingdao Gao Tai New Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Qingdao Gao Tai New Material Co Ltd filed Critical Qingdao Gao Tai New Material Co Ltd
Priority to CN2013100081076A priority Critical patent/CN103088310A/zh
Publication of CN103088310A publication Critical patent/CN103088310A/zh
Pending legal-status Critical Current

Abstract

一种涂覆均匀、无颗粒残留、生物相容性好以及方便后期加工的以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法。技术方案是：其特征是包括下列步骤：(1)准备模板和钽源：其中，所述模板为三维网状石墨泡沫或网状玻璃碳，所述钽源为五氟化钽、五氯化钽或乙醇钽；(2)将所述三维网状石墨泡沫或网状玻璃碳模板置于气相沉积炉用气相沉积的方法进行反应，制成成品。

Description

以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法
技术领域
本发明属于医用多孔钽的制备方法领域，尤其是一种涂覆均匀、无颗粒残留、生物相容性好以及方便后期加工的以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法。 
背景技术
目前，多孔医用植入物的制备多采用多孔不锈钢、多孔钛等。存在的问题是生物相容性不好、重量大，不能很好地和生物体长在一起。也有场家采用粉末冶方法制造金多孔钽的方法，该方法既要达到钽的熔点，又要避免多孔钽的塌陷，存在烧结难以控制的问题，而且后期加工难度也很大，还容易产生粉末颗粒的残留。 
发明内容
本发明的目的是提供一种涂覆均匀、无颗粒残留、生物相容性好以及方便后期加工的以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法。 
本发明的技术方案是：以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法，其特征是包括下列步骤：(1)准备模板和钽源：其中，所述模板为三维网状石墨泡沫或网状玻璃碳，所述钽源为五氟化钽、五氯化钽或乙醇钽；(2)将所述三维网状石墨泡沫或网状玻璃碳模板置于气相沉积炉用气相沉积的方法进行反应，制成成品。 
所述气相沉积的方法包括下列步骤：对气相沉积炉进行真空加热，加热温度达到100-2000℃，保温1-3小时，然后往气相沉积炉通入氢气，再通入以氢气或氢气氩气混合气体以及钽源，钽源与模板进行反应，反应温度为300-1000℃，反应时间为？。 
所述作为模板的三维网状石墨泡沫或网状玻璃碳有相互连通的 开孔结构，材质含碳量在10％以上，泡的大小为8-2000PPI。 
优选的，钽源与模板反应温度为900℃。 
本发明的效果是：以三维网状石墨泡沫或网状玻璃碳为模板制作医用多孔钽的方法，钽的生物相容性更好，做成多孔不仅重量能减轻，而且其多孔形状和真正的人体组织相仿，相关的骨组织，肌肉组织，血管和神经等都能穿过空隙，以便更好地和生物体长在一起。 
下面结合实施例对本发明做进一步的说明。 
具体实施方式
以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法，包括下列步骤：(1)准备模板和钽源：其中，所述模板为三维网状石墨泡沫或网状玻璃碳，所述钽源为五氟化钽、五氯化钽或乙醇钽；(2)将所述三维网状石墨泡沫或网状玻璃碳模板置于气相沉积炉用气相沉积的方法进行反应，制成成品。 
气相沉积的方法包括下列步骤：对气相沉积炉进行真空加热，加热温度达到100-2000℃，保温1-3小时，然后往气相沉积炉通入氢气，再通入以氢气或氢气氩气混合气体以及钽源，钽源与模板进行反应，反应温度为300-1000℃，反应时间为？。 
作为模板的三维网状石墨泡沫或网状玻璃碳有相互连通的开孔结构，材质含碳量在10％以上，泡的大小为8-2000PPI。 
优选的，钽源与模板反应温度为900℃。 

Claims (4)

1.以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法，其特征是包括下列步骤：(1)准备模板和钽源：其中，所述模板为三维网状石墨泡沫或网状玻璃碳，所述钽源为五氟化钽、五氯化钽或乙醇钽；(2)将所述三维网状石墨泡沫或网状玻璃碳模板置于气相沉积炉用气相沉积的方法进行反应，制成成品。
2.根据权利要求1所述的以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法，其特征是所述气相沉积的方法包括下列步骤：对气相沉积炉进行真空加热，加热温度达到100-2000℃，保温1-3小时，然后往气相沉积炉通入氢气，再通入以氢气或氢气氩气混合气体以及钽源，钽源与模板进行反应，反应温度为300-1000℃，反应时间为？。
3.根据权利要求1或2所述的以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法，其特征是所述作为模板的三维网状石墨泡沫或网状玻璃碳有相互连通的开孔结构，材质含碳量在10％以上，泡的大小为8-2000PPI。
4.根据权利要求1或2所述的以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法，其特征是优选的，钽源与模板反应温度为900℃。
CN2013100081076A 2013-01-10 2013-01-10 以三维网状石墨泡沫或网状玻璃碳制作医用多孔钽的方法 Pending CN103088310A (zh)