CN103044792A - 一种耐水性能优异的无铅硫化csm - Google Patents
一种耐水性能优异的无铅硫化csm Download PDFInfo
- Publication number
- CN103044792A CN103044792A CN2012105875301A CN201210587530A CN103044792A CN 103044792 A CN103044792 A CN 103044792A CN 2012105875301 A CN2012105875301 A CN 2012105875301A CN 201210587530 A CN201210587530 A CN 201210587530A CN 103044792 A CN103044792 A CN 103044792A
- Authority
- CN
- China
- Prior art keywords
- parts
- csm
- water resistance
- carbon black
- hydrotalcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐水性能优异的无铅硫化CSM,由以下质量份组份制成:CSM40 100份;助剂L-24 1~3份;防老剂 1~3份;炭黑N550 30~60份;炭黑N774 20~50份;轻质碳酸钙 5~20份;增塑剂 5~25份;水滑石 10~30份;促进剂TRA 1~3份;促进剂DM 0.5~1.5份。采用水滑石(DHT-4A)促进剂硫化体系,膨胀率在10%以内;工艺性能好、硫化速度快、胶料的贮存稳定性好。
Description
技术领域
本发明涉及一种无铅硫化CSM。
背景技术
随着橡胶工业的高速发展,对橡胶制品的耐热、耐油、耐臭氧和耐天候等综合性能的要求也越来越高,氯磺化聚乙烯橡胶(CSM)由于具有优良的综合性能,已经在汽车零部件领域得到了广泛的应用。传统的氧化铅硫化体系能够赋予氯磺化聚乙烯橡胶优异的耐油、耐水以及耐热的综合平衡性能,但是限于环保法规的要求,该硫化体系已经不再使用。取而代之的是以氧化镁或者氢氧化钙为吸酸剂的无铅硫化体系,该硫化体系能够赋予胶料良好的耐热以及耐油性能,但是所得硫化胶的耐水性能较差,相关文献报道,含氧化镁的CSM胶料经耐热水试验100℃×70h,体积变化率可达90%,正是这一缺点使得氯磺化聚乙烯的应用具有一定的局限性。
发明内容
本发明所要解决的技术问题是提供一种胶料的耐热水体积膨胀率在10%以内,工艺性能好、硫化速度快、胶料的贮存稳定性好的耐水性能优异的无铅硫化CSM。
为解决上述技术问题,本发明的技术方案是:一种耐水性能优异的无铅硫化CSM,由以下质量份组份制成:
CSM40 100份;
助剂L-24 1~3份;
防老剂 1~3份;
炭黑N550 30~60份;
炭黑N774 20~50份;
轻质碳酸钙 5~20份;
增塑剂 5~25份;
水滑石 10~30份;
促进剂TRA 1~3份;
促进剂DM 0.5~1.5份。
作为优选的技术方案,所述增塑剂为增塑剂DOS;所述防老剂为防老剂NBC;所述水滑石为水滑石DHT-4A。
由于采用了上述技术方案,采用水滑石(DHT-4A)促进剂硫化体系,使得胶料的耐热水体积膨胀率在10%以内;工艺性能好、硫化速度快、胶料的贮存稳定性好。
具体实施方式
采用氯磺化聚乙烯牌号为CSM40,江西虹润化工生产,门尼粘度ML(1+4)100℃为55,水滑石采用日本协和生产的DHT-4A,具体实施例如下:
实施例一:
序号 | 组分 | 用量(质量份) |
1 | CSM40 | 100 |
2 | 加工助剂L-24 | 3 |
3 | 防老剂NBC | 2 |
4 | 炭黑N550 | 60 |
5 | 炭黑N774 | 20 |
6 | 轻质碳酸钙 | 5 |
7 | 增塑剂DOS | 10 |
8 | 硫化剂DHT-4A | 10 |
9 | 促进剂TRA | 3 |
10 | 促进剂DM | 0.5 |
实施例二:
序号 | 组分 | 用量(质量份) |
1 | CSM40 | 100 |
2 | 加工助剂L-24 | 1 |
3 | 防老剂NBC | 1 |
4 | 炭黑N550 | 50 |
5 | 炭黑N774 | 30 |
6 | 轻质碳酸钙 | 5 |
7 | 增塑剂DOS | 8 |
8 | 硫化剂DHT-4A | 15 |
9 | 促进剂TRA | 2.5 |
10 | 促进剂DM | 0.5 |
实施例三:
序号 | 组分 | 用量(质量份) |
1 | CSM40 | 100 |
2 | 加工助剂L-24 | 2 |
3 | 防老剂NBC | 1.5 |
4 | 炭黑N550 | 40 |
5 | 炭黑N774 | 40 |
6 | 轻质碳酸钙 | 10 |
7 | 增塑剂DOS | 12 |
8 | 硫化剂DHT-4A | 20 |
9 | 促进剂TRA | 2 |
10 | 促进剂DM | 1 |
实施例四:
序号 | 组分 | 用量(质量份) |
1 | CSM40 | 100 |
2 | 加工助剂L-24 | 1.5 |
3 | 防老剂NBC | 1.5 |
4 | 炭黑N550 | 30 |
5 | 炭黑N774 | 50 |
6 | 轻质碳酸钙 | 15 |
7 | 增塑剂DOS | 12 |
8 | 硫化剂DHT-4A | 25 |
9 | 促进剂TRA | 1.5 |
10 | 促进剂DM | 1.5 |
实施例五:
序号 | 组分 | 用量(质量份) |
1 | CSM40 | 100 |
2 | 加工助剂L-24 | 1.5 |
3 | 防老剂NBC | 2 |
4 | 炭黑N550 | 40 |
5 | 炭黑N774 | 40 |
6 | 轻质碳酸钙 | 20 |
7 | 增塑剂DOS | 10 |
8 | 硫化剂DHT-4A | 30 |
9 | 促进剂TRA | 1 |
10 | 促进剂DM | 1.5 |
进行100℃×70h耐热水试验,测定试样的体积变化率,从而测定其耐热水性能,结果如下:
序号 | 体积变化率(%) |
实施例一 | +9.5 |
实施例二 | +8.7 |
实施例三 | +8.1 |
实施例四 | +7.5 |
实施例五 | +7.8 |
可以得出,水滑石是一种具有特殊晶体结构的离子化合物,由于其特有的晶体结构,水滑石在与氯化氢反应时,氯离子进入晶体结构中,形成的晶体结构是稳定的,基本上不溶于水和油,因此水滑石可以作为氯磺化聚乙烯硫化时的吸酸剂和硫化剂。采用水滑石(DHT-4A)促进剂硫化体系,使得胶料的耐热水体积膨胀率在10%以内;而且工艺性能好、硫化速度快、胶料的贮存稳定性较好。
Claims (4)
1. 一种耐水性能优异的无铅硫化CSM,其特征是由以下质量份组份制成:
CSM40 100份;
助剂L-24 1~3份;
防老剂 1~3份;
炭黑N550 30~60份;
炭黑N774 20~50份;
轻质碳酸钙 5~20份;
增塑剂 5~25份;
水滑石 10~30份;
促进剂TRA 1~3份;
促进剂DM 0.5~1.5份。
2. 如权利要求1所述的一种耐水性能优异的无铅硫化CSM,其特征是:所述增塑剂为增塑剂DOS。
3. 如权利要求1所述的一种耐水性能优异的无铅硫化CSM,其特征是:所述防老剂为防老剂NBC。
4. 如权利要求1至3任一权利要求所述的一种耐水性能优异的无铅硫化CSM,其特征是:所述水滑石为水滑石DHT-4A。