CN103030288A - 一种以煤矸石为主料的微晶玻璃及其制备方法 - Google Patents

一种以煤矸石为主料的微晶玻璃及其制备方法 Download PDF

Info

Publication number
CN103030288A
CN103030288A CN2012105153767A CN201210515376A CN103030288A CN 103030288 A CN103030288 A CN 103030288A CN 2012105153767 A CN2012105153767 A CN 2012105153767A CN 201210515376 A CN201210515376 A CN 201210515376A CN 103030288 A CN103030288 A CN 103030288A
Authority
CN
China
Prior art keywords
parts
oxide
glass
plant ash
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012105153767A
Other languages
English (en)
Other versions
CN103030288B (zh
Inventor
毛庆云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Boao Zongheng Network Technology Co ltd
Zhangjiakou Sheng Ming Venus glass Limited by Share Ltd.
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210515376.7A priority Critical patent/CN103030288B/zh
Publication of CN103030288A publication Critical patent/CN103030288A/zh
Application granted granted Critical
Publication of CN103030288B publication Critical patent/CN103030288B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种以煤矸石为主料的微晶玻璃，它是由下述重量份的原料组成：煤矸石58-65、二氧化硅19-25、方解石16-21、氧化钙8-10、食盐7-10、氧化钾7-9、氧化铝4.5-6、碳酸钡2.5-4、氧化镁3-5、氧化锌3-4、木炭2.8-4、石膏3-4、滑石粉2-3、氧化硼2.2-3、碳酸钠2.5-3、硼砂2-4、氧化锂2-4、氟化钙2-3、改性草木灰2.3-3、氧化镍0.1-0.2、五氧化二钒0.3-0.5、二氧化钛0.6-0.8、三氧化二锑0.8-1.3；本发明生产的微晶玻璃平面度好、机械强度高、硬度大、具有良好的抗热性、抗弯曲强度、耐腐蚀性和耐磨性，产品可制成各类管材、板材，可广泛应用于建筑上的耐磨耐腐蚀材料、建筑装饰材料。

Description

一种以煤矸石为主料的微晶玻璃及其制备方法
技术领域
    本发明主要涉及一种微晶玻璃及其制备方法，尤其涉及一种以煤矸石为主料的微晶玻璃及其制备方法。
背景技术
微晶玻璃，又称玻璃陶瓷，是综合玻璃和陶瓷技术发展起来的一种新型材料，是微晶体和玻璃相均匀分布的材料，其理化性能集中了玻璃、陶瓷及天然石材的三重优点，如机械强度高、耐腐蚀、耐热、耐磨、抗氧化性能好、电性能优良、膨胀系数可调、热稳定性好等，且优于天然石材和陶瓷，可用于建筑幕墙及室内高档装饰，还可做机械上的结构材料，电子、电工上的绝缘材料，大规模集成电路的底板材料，微波炉耐热系列器皿，化工与防腐材料和矿山耐磨材料等等，是具有发展前途的21 世纪的新型材料。因而广泛用于电子、化工、军事、航天、核工业和建筑等领域。因微晶玻璃可用矿石、工业尾矿、冶金矿渣、粉煤灰、煤矸石等作为主要生产原料，且生产过过程中无污染，产品本身无放射性污染，故又被称为环保产品或绿色材料，传统生产的微晶玻璃的表层及其内层经常存在大量工艺性气孔，而且抗折强度和耐水性等性能不强，限制了微晶玻璃的应用领域。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种表面光洁致密无气孔。
本发明是通过以下技术方案实现的：
一种以煤矸石为主料的微晶玻璃，它是由下述重量份的原料组成：
煤矸石58-65、二氧化硅19-25、方解石16-21、氧化钙8-10、食盐 7-10、氧化钾7-9、氧化铝4.5-6、碳酸钡2.5-4、氧化镁3-5、氧化锌3-4、木炭2.8-4、石膏3-4、滑石粉2-3、氧化硼2.2-3、碳酸钠2.5-3、硼砂2-4、氧化锂2-4、氟化钙2-3、改性草木灰2.3-3、氧化镍0.1-0.2、五氧化二钒0.3-0.5、二氧化钛0.6-0.8、三氧化二锑0.8-1.3；
所述的改性草木灰的制备方法为：将草木灰用12-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干，粉碎成超细粉末。
一种以煤矸石为主料的微晶玻璃的制备方法，包括以下步骤：
（1）将除了改性草木灰以外的原料组分混合加入到玻璃熔炉内，在1540-1600℃的高温下熔炼2-3小时，再降至1410-1450℃下澄清1.7-2小时，制得玻璃液；
（2）将上述表面澄清的玻璃液直接投入水中，冷淬成碎玻璃体，加入球磨机中，球磨成细度为0.05-0.07mm的玻璃粉末，烘干；
（3）将得到的玻璃粉末与上述重量份的改性草木灰混合，加入混合料重量20-25%的改性玻璃体粉末，混合均匀，在60-65MPa 压力下成型，得到生坯；
所述的改性玻璃体粉末的制备方法为：将重量份为15-20的草木灰、重量份为50-58的石英砂、重量份为8-11的凹凸棒土、重量份为20-25的方解石，混合加入玻璃熔炉中，加热到1500-1600℃的高温下，熔炼2-3小时，再降至1400-1450℃下澄清1.5-2小时，制得玻璃液，然后淬入冷水中得到碎璃体，再研磨成3-5μm改性玻璃体粉末；
（4）将生坯放入高温箱式电阻炉中，温度制度：在室温下以7-8℃ /min速率升温到300-320℃；再以3-5℃ /min速率升温到780-820℃，保温1-1.5h ；然后再以6-8℃ /min速率加热到1220-1260℃，保温3-3.5h；
（5）退火：将上述晶化后的玻璃以3-5℃/min的退火降温速度进行退火处理，当温度降至于580-600℃时，保持恒温35-40分钟，然后再6-8℃/min速率升温到820-850℃，然后再以5-7℃/min 速率继续降温，当温度降至于270-300℃时，再自然冷却到室温；
（6）出料，按照要求的尺寸切割成板块，研磨抛光、修边即可。
本发明的优点是：
本发明生产的微晶玻璃平面度好、机械强度高、硬度大、具有良好的抗热性、抗弯曲强度、耐腐蚀性和耐磨性，产品可制成各类管材、板材，可广泛应用于建筑上的耐磨耐腐蚀材料、建筑装饰材料、实验室用加热器具、高温热交换器、代石英玻璃、高温窗、雷达天线罩等。
具体实施方式
实施例1
一种以煤矸石为主料的微晶玻璃，它是由下述重量份（公斤）的原料组成：
煤矸石65、二氧化硅25、方解石21、氧化钙10、食盐10、氧化钾9、氧化铝4.5、碳酸钡2.5、氧化镁5、氧化锌4、木炭2.8、石膏4、滑石粉3、氧化硼2.2-3、碳酸钠2.5、硼砂4、氧化锂4、氟化钙3、改性草木灰2.3、氧化镍0.2、五氧化二钒0.5、二氧化钛0.8、三氧化二锑1.3；
所述的改性草木灰的制备方法为：将草木灰用15%盐酸浸泡4小时，去离子水洗涤，再用12%氢氧化钠溶液浸泡4小时，再用去离子水洗涤至中性，烘干，粉碎成超细粉末。
一种以煤矸石为主料的微晶玻璃的制备方法，包括以下步骤：
（1）将除了改性草木灰以外的原料组分混合加入到玻璃熔炉内，在1540℃的高温下熔炼3小时，再降至1450℃下澄清1.7小时，制得玻璃液；
（2）将上述表面澄清的玻璃液直接投入水中，冷淬成碎玻璃体，加入球磨机中，球磨成细度为0.07mm的玻璃粉末，烘干；
（3）将得到的玻璃粉末与上述重量份的改性草木灰混合，加入混合料重量25%的改性玻璃体粉末，混合均匀，在65MPa 压力下成型，得到生坯；
所述的改性玻璃体粉末的制备方法为：将重量份为20的草木灰、重量份为58的石英砂、重量份为11的凹凸棒土、重量份为25的方解石，混合加入玻璃熔炉中，加热到1600℃的高温下，熔炼3小时，再降至1450℃下澄清1.5小时，制得玻璃液，然后淬入冷水中得到碎璃体，再研磨成5μm改性玻璃体粉末；
（4）将生坯放入高温箱式电阻炉中，温度制度：在室温下以8℃ /min速率升温到320℃；再以5℃ /min速率升温到820℃，保温1.5h ；然后再以6-8℃ /min速率加热到1260℃，保温3.5h；
（5）退火：将上述晶化后的玻璃以5℃/min的退火降温速度进行退火处理，当温度降至于600℃时，保持恒温40分钟，然后再8℃/min速率升温到850℃，然后再以7℃/min 速率继续降温，当温度降至于300℃时，再自然冷却到室温；
（6）出料，按照要求的尺寸切割成板块，研磨抛光、修边即可。
性能测试：
抗折强度测试：采用MC009-wds10M 型电子万能材料性能试验机利用三点弯曲法测定样品的抗折强度，取6个条状样品(9mm×7mm×85mm) 进行测试，计算抗折强度，最后求平均值。
显微硬度测定：用HXD-1000数字显微硬度测试仪测定样品的硬度，每个样品测三个点，用平均值表示其显微硬度，共测三个样品，最后计算三个样品的显微硬度的平均值。
耐水性能测试：采用粉末浸泡失重法进行测定(DTN12116)，将样品粉碎，取40目下、60目上微晶玻璃粉2克，于50ml 容量瓶中，加水至刻度，在98±0.5℃温度下保温60分钟，测定其100cm2 的失重率(mg/100cm2)。
测试结果：
1、样品外观质量：表面致密，无气孔等缺陷，抛光后表面光亮。
2、机械性能：平均抗折强度89.8MPa，平均显微硬度893.8kgf/mm2。
3、耐水解等级：1 级，失重率为：0.281mg/100cm2。

Claims (2)

1.一种以煤矸石为主料的微晶玻璃，其特征在于它是由下述重量份的原料组成：
煤矸石58-65、二氧化硅19-25、方解石16-21、氧化钙8-10、食盐 7-10、氧化钾7-9、氧化铝4.5-6、碳酸钡2.5-4、氧化镁3-5、氧化锌3-4、木炭2.8-4、石膏3-4、滑石粉2-3、氧化硼2.2-3、碳酸钠2.5-3、硼砂2-4、氧化锂2-4、氟化钙2-3、改性草木灰2.3-3、氧化镍0.1-0.2、五氧化二钒0.3-0.5、二氧化钛0.6-0.8、三氧化二锑0.8-1.3；
所述的改性草木灰的制备方法为：将草木灰用12-15%盐酸浸泡3-4小时，去离子水洗涤，再用10-12%氢氧化钠溶液浸泡3-4小时，再用去离子水洗涤至中性，烘干，粉碎成超细粉末。
2.一种如权利要求1所述的以煤矸石为主料的微晶玻璃的制备方法，其特征在于包括以下步骤：
（1）将除了改性草木灰以外的原料组分混合加入到玻璃熔炉内，在1540-1600℃的高温下熔炼2-3小时，再降至1410-1450℃下澄清1.7-2小时，制得玻璃液；
（2）将上述表面澄清的玻璃液直接投入水中，冷淬成碎玻璃体，加入球磨机中，球磨成细度为0.05-0.07mm的玻璃粉末，烘干；
（3）将得到的玻璃粉末与上述重量份的改性草木灰混合，加入混合料重量20-25%的改性玻璃体粉末，混合均匀，在60-65MPa 压力下成型，得到生坯；
所述的改性玻璃体粉末的制备方法为：将重量份为15-20的草木灰、重量份为50-58的石英砂、重量份为8-11的凹凸棒土、重量份为20-25的方解石，混合加入玻璃熔炉中，加热到1500-1600℃的高温下，熔炼2-3小时，再降至1400-1450℃下澄清1.5-2小时，制得玻璃液，然后淬入冷水中得到碎璃体，再研磨成3-5μm改性玻璃体粉末；
（4）将生坯放入高温箱式电阻炉中，温度制度：在室温下以7-8℃ /min速率升温到300-320℃；再以3-5℃ /min速率升温到780-820℃，保温1-1.5h ；然后再以6-8℃ /min速率加热到1220-1260℃，保温3-3.5h；
（5）退火：将上述晶化后的玻璃以3-5℃/min的退火降温速度进行退火处理，当温度降至于580-600℃时，保持恒温35-40分钟，然后再6-8℃/min速率升温到820-850℃，然后再以5-7℃/min 速率继续降温，当温度降至于270-300℃时，再自然冷却到室温；
（6）出料，按照要求的尺寸切割成板块，研磨抛光、修边即可。
CN201210515376.7A 2012-12-05 2012-12-05 一种以煤矸石为主料的微晶玻璃及其制备方法 Expired - Fee Related CN103030288B (zh)