CN102994833A - 金属锰块 - Google Patents
金属锰块 Download PDFInfo
- Publication number
- CN102994833A CN102994833A CN2012104195264A CN201210419526A CN102994833A CN 102994833 A CN102994833 A CN 102994833A CN 2012104195264 A CN2012104195264 A CN 2012104195264A CN 201210419526 A CN201210419526 A CN 201210419526A CN 102994833 A CN102994833 A CN 102994833A
- Authority
- CN
- China
- Prior art keywords
- percent
- manganese
- metal
- iron
- metal block
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了金属锰块,其特征在于:该金属锰块成分按重量百分比为:锰90-98%;碳0.01-0.1%;硅0.05-0.5%;硫0.01-0.1%;磷0.01-0.1%;铁1-5%;镍0.005-0.5%;铜0.005-0.6%;铝0.01-1%;镁0.01-1%;钙0.01-1%。本发明的优点是:锰块中含有掺有别的金属,使得锰块变得坚硬,抗氧化性能高。
Description
技术领域
本发明涉及一种金属锰块。
背景技术
锰是银灰色的金属,很像铁,但比铁要软一些。然而纯净的金属锰的用途并不太广,因为它比铁还易生锈,在潮湿的空气中,没一会儿便变得灰蒙蒙的,失去了光泽——表面生成了一层氧化锰。再者,锰的熔点又比铁低,机械强度不如钢铁,而价格又比钢铁贵得多,因此人们几乎不生产金属锰,而大量生产钢铁。
因此,急需一种改进的技术来解决现有技术中所存在的这一问题。
发明内容
本发明的目的是提供一种金属锰块。
本发明采用的技术方案是:
金属锰块,其特征在于:该金属锰块成分按重量百分比为:
锰 90-98%;
碳 0.01-0.1%;
硅 0.05-0.5%;
硫 0.01-0.1%;
磷 0.01-0.1%;
铁 1-5%;
镍 0.005-0.5%;
铜 0.005-0.6%;
铝 0.01-1%;
镁 0.01-1%;
钙 0.01-1%。
本发明的优点是:锰块中含有掺有别的金属,使得锰块变得坚硬,抗氧化性能高。
具体实施方式
实施例1
本发明的金属锰块,该金属锰块成分按重量百分比为:
锰 92%;
碳 0.5%;
硅 0.3%;
硫 0.05%;
磷 0.05%;
铁 5%;
镍 0.01%;
铜 0.05%;
铝 1%;
镁 0.2%;
钙 0.3%。
实施例2
本发明的金属锰块,该金属锰块成分按重量百分比为:
锰 95%;
碳 0.05%;
硅 0.2%;
硫 0.05%;
磷 0.05%;
铁 3.95%;
镍 0.02%;
铜 0.03%;
铝 0.15%;
镁 0.2%;
钙 0.3%。
实施例3
本发明的金属锰块,该金属锰块成分按重量百分比为:
锰 97%;
碳 0.03%;
硅 0.07%;
硫 0.05%;
磷 0.08%;
铁 2.55%;
镍 0.05%;
铜 0.02%;
铝 0.07%;
镁 0.08%;
钙 0.05%。
锰块中含有掺有别的金属,使得锰块变得坚硬,抗氧化性能高。
Claims (1)
1.金属锰块,其特征在于:该金属锰块成分按重量百分比为:
锰 90-98%;
碳 0.01-0.1%;
硅 0.05-0.5%;
硫 0.01-0.1%;
磷 0.01-0.1%;
铁 1-5%;
镍 0.005-0.5%;
铜 0.005-0.6%;
铝 0.01-1%;
镁 0.01-1%;
钙 0.01-1%。