CN102993799A - 一种皮革涂饰剂及其制备方法 - Google Patents
一种皮革涂饰剂及其制备方法 Download PDFInfo
- Publication number
- CN102993799A CN102993799A CN 201210484186 CN201210484186A CN102993799A CN 102993799 A CN102993799 A CN 102993799A CN 201210484186 CN201210484186 CN 201210484186 CN 201210484186 A CN201210484186 A CN 201210484186A CN 102993799 A CN102993799 A CN 102993799A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- finishing agent
- polyvinyl alcohol
- dibutyl phthalate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种皮革涂饰剂及其制备方法。以重量份计,本发明由以下组分组成:甲醛:3~5,改性改性聚氨酯乳液:20~40,聚乙烯醇:10~20,丙烯酸酯:3~5,甲酸:1~3,六亚甲基四胺:1~3,乙二铵:2~4,氨水:6~9,邻苯二甲酸二丁酯:3~5,水:80~100。与现有技术相比,本发明具有如下有益效果:(1)水溶性很好,性能稳定,长期存放不分层、无浮蜡。(2)能够适用于各种皮革的涂饰,涂饰后的皮革光泽柔和自然,手感丰满滋润,能提高皮革表面的耐摩擦能力。
Description
技术领域
本发明属于皮革助剂技术领域,更具体是涉及一种皮革涂饰剂及其制备方法。
背景技术
皮革涂饰添加剂做为涂饰高档皮革的主要助剂,能赋予皮革特别的光亮度和蜡感。因此,皮革涂饰剂的使用非常广泛。皮革涂饰添加剂可分别用于皮革的底层、中层和顶层涂饰,皮革涂饰添加剂还可与不同离子性能的涂饰剂配伍使用。
发明内容
本发明的目的在于克服现有技术存在的不足,提供一种皮革涂饰剂。
本发明的另一目的在于提供该皮革涂饰剂的制备方法。
为达到上述目的,本发明采取了如下的技术方案:
一种皮革涂饰剂,以重量份计,由以下组分组成:
甲醛:3~5,改性改性聚氨酯乳液:20~40,
聚乙烯醇:10~20,丙烯酸酯:3~5,甲酸:1~3,
六亚甲基四胺:1~3,乙二铵:2~4,氨水:6~9,
邻苯二甲酸二丁酯:3~5,水:80~100。
所述的一种皮革涂饰剂的制备方法,其特征在于,包括如下步骤:
(1)将改性改性聚氨酯乳液、聚乙烯醇及丙烯酸酯混合,升温至80~100℃,搅拌均匀;
(2)将邻苯二甲酸二丁酯加入水中,搅拌混合均匀;
(3)将步骤(1)的产物加入步骤(2)的产物中,搅拌混合均匀;
(4)冷却至室温,加入其余组分,搅拌混合均匀后即可得成品。
与现有技术相比,本发明具有如下有益效果:
(1)水溶性很好,性能稳定,长期存放不分层、无浮蜡。
(2)能够适用于各种皮革的涂饰,涂饰后的皮革光泽柔和自然,手感丰满滋润,能提高皮革表面的耐摩擦能力。
具体实施方式
以下结合具体实施例来对本发明作进一步的描述。
实施例1
一种皮革涂饰剂,以重量份计,由以下组分组成:
甲醛:3,改性改性聚氨酯乳液:20,
聚乙烯醇:10,丙烯酸酯:3,甲酸:1,
六亚甲基四胺:1,乙二铵:2,氨水:6,
邻苯二甲酸二丁酯:3,水:80。
实施例2
一种皮革涂饰剂,以重量份计,由以下组分组成:
甲醛:5,改性改性聚氨酯乳液:40,
聚乙烯醇:20,丙烯酸酯:5,甲酸:3,
六亚甲基四胺:3,乙二铵:4,氨水:9,
邻苯二甲酸二丁酯:5,水:100。
实施例3
一种皮革涂饰剂,以重量份计,由以下组分组成:
甲醛:4,改性改性聚氨酯乳液:30,
聚乙烯醇:16,丙烯酸酯:4,甲酸:2,
六亚甲基四胺:2,乙二铵:3,氨水:8,
邻苯二甲酸二丁酯:4,水:90。
上述实施例中,所述的一种皮革涂饰剂的制备方法,包括如下步骤:
(1)将改性改性聚氨酯乳液、聚乙烯醇及丙烯酸酯混合,升温至80~100℃,搅拌均匀;
(2)将邻苯二甲酸二丁酯加入水中,搅拌混合均匀;
(3)将步骤(1)的产物加入步骤(2)的产物中,搅拌混合均匀;
(4)冷却至室温,加入其余组分,搅拌混合均匀后即可得成品。
Claims (5)
1.一种皮革涂饰剂,其特征在于,以重量份计,由以下组分组成:
甲醛:3~5,改性改性聚氨酯乳液:20~40,
聚乙烯醇:10~20,丙烯酸酯:3~5,甲酸:1~3,
六亚甲基四胺:1~3,乙二铵:2~4,氨水:6~9,
邻苯二甲酸二丁酯:3~5,水:80~100。
2.根据权利要求1所述的一种皮革涂饰剂,其特征在于,以重量份计,由以下组分组成:
甲醛:3,改性改性聚氨酯乳液:20,
聚乙烯醇:10,丙烯酸酯:3,甲酸:1,
六亚甲基四胺:1,乙二铵:2,氨水:6,
邻苯二甲酸二丁酯:3,水:80。
3.根据权利要求1所述的一种皮革涂饰剂,其特征在于,以重量份计,由以下组分组成:
甲醛:5,改性改性聚氨酯乳液:40,
聚乙烯醇:20,丙烯酸酯:5,甲酸:3,
六亚甲基四胺:3,乙二铵:4,氨水:9,
邻苯二甲酸二丁酯:5,水:100。
4.根据权利要求1所述的一种皮革涂饰剂,其特征在于,以重量份计,由以下组分组成:
甲醛:4,改性改性聚氨酯乳液:30,
聚乙烯醇:16,丙烯酸酯:4,甲酸:2,
六亚甲基四胺:2,乙二铵:3,氨水:8,
邻苯二甲酸二丁酯:4,水:90。
5.权利要求1所述的一种皮革涂饰剂的制备方法,其特征在于,包括如下步骤:
(1)将改性改性聚氨酯乳液、聚乙烯醇及丙烯酸酯混合,升温至80~100℃,搅拌均匀;
(2)将邻苯二甲酸二丁酯加入水中,搅拌混合均匀;
(3)将步骤(1)的产物加入步骤(2)的产物中,搅拌混合均匀;
(4)冷却至室温,加入其余组分,搅拌混合均匀后即可得成品。