CN102977699B - 一种超耐候氟碳自洁涂料及其制备方法 - Google Patents

一种超耐候氟碳自洁涂料及其制备方法 Download PDF

Info

Publication number
CN102977699B
CN102977699B CN201210506061.6A CN201210506061A CN102977699B CN 102977699 B CN102977699 B CN 102977699B CN 201210506061 A CN201210506061 A CN 201210506061A CN 102977699 B CN102977699 B CN 102977699B
Authority
CN
China
Prior art keywords
super
fluorocarbon
weather
self
super weather
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210506061.6A
Other languages
English (en)
Other versions
CN102977699A (zh
Inventor
黄介华
胡胜初
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Huhuang New Material Technology Group Co.,Ltd.
Original Assignee
WUXI HUHUANG PAINT CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI HUHUANG PAINT CO Ltd filed Critical WUXI HUHUANG PAINT CO Ltd
Priority to CN201210506061.6A priority Critical patent/CN102977699B/zh
Publication of CN102977699A publication Critical patent/CN102977699A/zh
Application granted granted Critical
Publication of CN102977699B publication Critical patent/CN102977699B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开一种超耐候氟碳自洁涂料及其制备方法,按重量百分含量计,包含如下组分:高沸点溶剂 6%~18%、耐候丙稀酸树脂25%~30%、导电溶剂15%~20%、氟碳树脂26%~35%、氨基树脂1%~5%、超耐候颜料10%~18%、自洁纳米剂1%~5%。本发明氟碳自洁涂料由于采用了超耐候丙稀酸树脂和氟碳树脂,采用了无机超耐候颜料,保证了在二十年以内色差的稳定性,方案里边采用了一款新型的自洁纳米剂助剂,使油漆在涂装完成后具有了荷叶的自洁效果。

Description

一种超耐候氟碳自洁涂料及其制备方法
技术领域
本发明属于油漆化工领域,具体涉及一种超耐候氟碳自洁涂料及其制备方法。
背景技术
在城市快速发展的今天,建筑(外墙)涂料得到飞速发展,每一栋大型建筑高楼,有娱乐场所,都离不开涂料的装饰,在五颜六色的外墙涂料点缀下,城市才变和格外的漂亮、时尚。但随着时间的流逝(2~5年内),外墙涂料在大气层的污染下,慢慢地失去光彩,随之而来的,就是后期清洁保养,有的甚至还需重涂,这些除了费用的增加外,在高楼施工还具有一定的风险性。
发明内容
本发明的目的在于提供一种超耐候氟碳自洁涂料。
本发明的另一目的在于提供一种超耐候氟碳自洁涂料的制备方法。
本发明的目的可以通过以下技术方案实现:
一种超耐候氟碳自洁涂料,按重量百分含量计,包含如下组分:
所述的高沸点溶剂为乙二醇丁醚。
所述的耐候丙稀酸树脂为热塑性丙稀酸树脂,优选为BM44。
所述的导电溶剂为二甲苯或甲苯。
所述的超耐候颜料为有色无机颜料,可根据客户需要选择,例如钛白粉、黑色粉CMC等。
所述的自洁纳米剂为BYK3700。
上述的超耐候氟碳自洁涂料的制备方法包括以下步骤:按比例将高沸点溶剂、耐候丙稀酸树脂、导电溶剂、氟碳树脂、氨基树脂、超耐候颜料和自洁纳米剂依次加入后混合均匀并研磨到细度≤15微米。
本发明的超耐候自洁氟碳涂料,在二十年以内,基本色差在5个单位以内,具有荷叶自洁效果,很难受大气层的污染,雨水一冲洗,干净如新。
本发明技术方案所使用的原料除特别说明外均可通过市场购买获得。
本发明的有益效果:
本发明氟碳自洁涂料由于采用了超耐候丙稀酸树脂和氟碳树脂,采用了无机超耐候颜料,保证了在二十年以内色差的稳定性,方案里边采用了一款新型的自洁纳米剂助剂,使油漆在涂装完成后具有了荷叶的自洁效果。
具体实施方式
使用原料:
高沸点溶剂:BCS(乙二醇丁醚),江苏三木化工股份有限公司
耐候丙稀酸树脂:B44,罗门哈斯
导电溶剂:二甲苯, 中石化
氟碳树脂:山东东岳集团
氨基树脂:巴斯夫L303
超耐候颜料:无机颜料杜邦960
自洁纳米剂:BYK3700
实施例1
一种超耐候氟碳自洁涂料,按重量百分含量计,包含如下组分:
按比例将高沸点溶剂、耐候丙稀酸树脂、导电溶剂、氟碳树脂、氨基树脂、超耐候颜料和自洁纳米剂依次加入后混合均匀并研磨到细度≤15微米。
实施例2
一种超耐候氟碳自洁涂料,按重量百分含量计,包含如下组分:
按比例将高沸点溶剂、耐候丙稀酸树脂、导电溶剂、氟碳树脂、氨基树脂、超耐候颜料和自洁纳米剂依次加入后混合均匀并研磨到细度≤15微米。
实施例3
一种超耐候氟碳自洁涂料,按重量百分含量计,包含如下组分:
按比例将高沸点溶剂、耐候丙稀酸树脂、导电溶剂、氟碳树脂、氨基树脂、超耐候颜料和自洁纳米剂依次加入后混合均匀并研磨到细度≤15微米。
实施例1~3制备的超耐候氟碳自洁涂料的性能检测结果
结果:本发明氟碳自洁涂料使用时二十年以内色差稳定,油漆在涂装完成后具有了荷叶的自洁效果,附着力高、耐沸水、耐冲击、耐硝酸、硬度高。

Claims (8)

1.一种超耐候氟碳自洁涂料,其特征在于按重量百分含量计,包含如下组分:
高沸点溶剂6%-18%
耐候丙烯酸树脂25%-30%
导电溶剂15%-20%
氟碳树脂26%-35%
氨基树脂1%-5%
超耐候颜料10-18%
自洁纳米剂1%-5% 。
2.根据权利要求1所述的超耐候氟碳自洁涂料,其特征在于所述的高沸点溶剂为乙二醇丁醚。
3.根据权利要求1所述的超耐候氟碳自洁涂料,其特征在于所述的耐候丙稀酸树脂为BM44。
4.根据权利要求1所述的超耐候氟碳自洁涂料,其特征在于所述的导电溶剂为二甲苯或甲苯。
5.根据权利要求1所述的超耐候氟碳自洁涂料,其特征在于所述的超耐候颜料为有色无机颜料。
6.根据权利要求1所述的超耐候氟碳自洁涂料,其特征在于所述的自洁纳米剂为BYK3700。
7.根据权利要求1所述的超耐候氟碳自洁涂料,其特征在于其制备方法包括以下步骤:按比例将高沸点溶剂、耐候丙烯酸树脂、导电溶剂、氟碳树脂、氨基树脂、超耐候颜料和自洁纳米剂依次加入后混合均匀并研磨到细度≤15微米。
8.权利要求1所述的超耐候氟碳自洁涂料的制备方法,其特征在于包括以下步骤:按比例将高沸点溶剂、耐候丙烯酸树脂、导电溶剂、氟碳树脂、氨基树脂、超耐候颜料和自洁纳米剂依次加入后混合均匀并研磨到细度≤15微米。
CN201210506061.6A 2012-11-30 2012-11-30 一种超耐候氟碳自洁涂料及其制备方法 Active CN102977699B (zh)