CN102977241A - 一种采用硬脂酸金属盐提高pvc抗冲击力的方法 - Google Patents
一种采用硬脂酸金属盐提高pvc抗冲击力的方法 Download PDFInfo
- Publication number
- CN102977241A CN102977241A CN 201210519793 CN201210519793A CN102977241A CN 102977241 A CN102977241 A CN 102977241A CN 201210519793 CN201210519793 CN 201210519793 CN 201210519793 A CN201210519793 A CN 201210519793A CN 102977241 A CN102977241 A CN 102977241A
- Authority
- CN
- China
- Prior art keywords
- pvc
- impact resistance
- initiator
- metallic stearates
- pure water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种采用硬脂酸金属盐提高PVC抗冲击力的方法。在反应釜中加入氯乙烯单体、纯水、分散剂、引发剂、抗冲击改性剂及常规量的脂肪酸锌热稳定剂和KZ终止剂，其中在反应釜中同时加入硬脂酸金属盐，加入的单体、纯水、分散剂、引发剂与硬脂酸金属盐的质量比例为150-250∶300-350∶10-20∶1.5-3.0∶1-5，聚合反应温度为54-58℃。本发明具有操作方便、节约成本、提高生产效率、节能环保的优点，且生产的PVC管材具有高强度和高韧性并重的特点，抗冲击能力强，市场竞争力大。
Description
技术领域
本发明涉及一种提高PVC抗冲击力的方法，尤其涉及一种采用硬脂酸金属盐提高PVC抗冲击力的方法。
背景技术
目前市场上的PVC材料同时具有刚性与韧性两种特性，但抗冲击性能不是很理想，很难达到人们的要求，起不到传递冲击能的作用，不耐老化，耐候性不好，对生产过程造成一定的影响，如何来改变塑料的抗冲击性能已成为化工届一个重要的问题。
发明内容
本发明的目的在于提供一种采用硬脂酸金属盐提高PVC抗冲击力的方法，可以克服目前PVC抗冲击性差，不耐老化，耐候性不好的缺陷。
本发明采用的技术方案如下：
在反应釜中加入氯乙烯单体、纯水、分散剂、引发剂、抗冲击改性剂及常规量的脂肪酸锌热稳定剂和KZ终止剂，其中在反应釜中同时加入硬脂酸金属盐，加入的单体、纯水、分散剂、引发剂与硬脂酸金属盐的的质量比例为150-250∶300-350∶10-20∶1.5-3.0∶1-5，聚合反应温度为54-58℃。
所述的硬脂酸金属盐为硬脂酸铅、硬脂酸钙和硬脂酸锌，质量比为1-3∶4-6∶2-5。
本发明在不改变现有主要生产装置的条件下，通过调整聚合反应的配方和工艺控制条件，即通过加入合适量的硬脂酸金属盐，使PVC的抗冲击力提高3倍以上。
本发明具有以下优点：本发明在不改变现有主要生产装置的条件下，提高PVC的抗冲击力3倍以上，节约了动力、能源消耗，提高了装置生产能力，生产系统运行安全稳定，具有较好的经济效益。
具体实施方式
以下以具体实施例来说明本发明的技术方案，但本发明的保护范围不限于此：
实施例1
在反应釜中加入氯乙烯单体、纯水、分散剂、引发剂、抗冲击改性剂及常规量的脂肪酸锌热稳定剂和KZ终止剂，其中在反应釜中同时加入硬脂酸铅、硬脂酸钙和硬脂酸锌，质量比为1∶4∶5。加入的单体、纯水、分散剂、引发剂与硬脂酸金属盐的质量比例为170∶350∶10∶1.5∶5，聚合反应温度为58℃，反应时间为7 小时，生产出的PVC产品的抗冲击力提高3.5倍。
实施例2
在反应釜中加入氯乙烯单体、纯水、分散剂、引发剂、抗冲击改性剂及常规量的脂肪酸锌热稳定剂和KZ终止剂，其中在反应釜中同时加入硬脂酸铅、硬脂酸钙和硬脂酸锌，质量比为3∶6∶2。加入的单体、纯水、分散剂、引发剂与硬脂酸金属盐的质量比例为250∶300∶20∶3.0∶1，聚合反应温度为54℃，反应时间为7 小时，生产出的PVC产品的抗冲击力提高3.2倍。
Claims (2)
1.一种采用硬脂酸金属盐提高PVC抗冲击力的方法，在反应釜中加入氯乙烯单体、纯水、分散剂、引发剂、抗冲击改性剂及常规量的脂肪酸锌热稳定剂和KZ终止剂，其特征在于，在反应釜中同时加入硬脂酸金属盐，加入的单体、纯水、分散剂、引发剂与硬脂酸金属盐的的质量比例为150-250∶300-350∶10-20∶1.5-3.0∶1-5，聚合反应温度为54-58℃。
2.如权利要求1所述的采用硬脂酸金属盐提高PVC抗冲击力的方法，其特征在于，所述的硬脂酸金属盐为硬脂酸铅、硬脂酸钙和硬脂酸锌，质量比为1-3∶4-6∶2-5。