CN102965998A - 一种韧性调湿材料的制备方法 - Google Patents

一种韧性调湿材料的制备方法 Download PDF

Info

Publication number
CN102965998A
CN102965998A CN2012104739121A CN201210473912A CN102965998A CN 102965998 A CN102965998 A CN 102965998A CN 2012104739121 A CN2012104739121 A CN 2012104739121A CN 201210473912 A CN201210473912 A CN 201210473912A CN 102965998 A CN102965998 A CN 102965998A
Authority
CN
China
Prior art keywords
parts
humidity
preparation
sodium
tough
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012104739121A
Other languages
English (en)
Other versions
CN102965998B (zh
Inventor
曹丽芬
王秉
胡智文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Sci Tech University ZSTU
Zhejiang University of Science and Technology ZUST
Original Assignee
Zhejiang Sci Tech University ZSTU
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Sci Tech University ZSTU filed Critical Zhejiang Sci Tech University ZSTU
Priority to CN201210473912.1A priority Critical patent/CN102965998B/zh
Publication of CN102965998A publication Critical patent/CN102965998A/zh
Application granted granted Critical
Publication of CN102965998B publication Critical patent/CN102965998B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种韧性调湿材料的制备方法，其步骤如下：a、按质量份数取0.1份羧甲基纤维素钠加入到5份水中配制成凝胶状，放置备用；b、按质量份数取0.3份氯化钠，2.7份碳酸钾，1.25份吡咯烷酮羧酸钠和0.4份硅藻土加入到100份水中配制成溶液；再加入4-4.5份生活用纸和0.25份聚丙烯酸钠粉末；搅拌、打浆；c、将步骤a和步骤b得到的产物混合后，再打浆4-5次，然后加入0.5~1.5份粘胶纤维并搅拌均匀；d、对步骤c得到的原料进行抄纸，并在80-90℃下烘干，即可得到韧性调湿材料；本发明制备工艺简单、成本低，其得到的调湿材料调湿效果好、响应快、使用方便；不易断裂，吸放湿速率快，并且可重复利用。

Description

一种韧性调湿材料的制备方法
技术领域
本发明涉及一种环境材料的制备，特别是一种韧性调湿材料的制备方法，主要适用于环境的湿度调节。
背景技术
在现在强调可持续发展的大环境下，能源越来越短缺。主动调湿的调节范围小，能源消耗大。随着人们对于生活环境要求的提高，制备一种可循环利用，并且绿色环保的调湿材料成为目前的趋势。
调湿材料的数量决定调节的范围，对于大范围的湿度调节。调湿材料成为建筑材料的需求越来越大。研究表明人们最适宜生活的环境为湿度40%-60%，在这个湿度下各种病毒和细菌均是最少的。在这个湿度下，各种材料如木料、纸制品、服装等也可以更好的得到保护。本调湿材料可以大范围的调节湿度，可以用作墙纸，也可以用作木板砖的底层材料很好的调节湿度。
发明内容
本发明是要克服上述现有技术中存在的不足，提供一种工艺简单、制备成本低的韧性调湿材料的制备方法，以便得到柔韧性更好、可重复利用、能够自动调节周围环境湿度，且温湿度响应快的调湿材料。
本发明所采用的技术方案是：一种韧性调湿材料的制备方法，其特征在于步骤如下：
a、按质量份数取0.1份羧甲基纤维素钠加入到5份水中配制成凝胶状，放置备用；
b、按质量份数取0.3份氯化钠，2.7份碳酸钾，1.25份吡咯烷酮羧酸钠和0.4份硅藻土加入到100份水中配制成溶液；再加入4-4.5份生活用纸和0.25份聚丙烯酸钠粉末；搅拌、打浆；
c、将步骤a和步骤b得到的产物混合后，再打浆4-5次，然后加入0.5~1.5份粘胶纤维并搅拌均匀；
d、对步骤c得到的原料进行抄纸，并在80-90℃下烘干，即可得到韧性调湿材料。
本发明的有益效果是：1、本发明在原料中加入粘胶纤维，使得制备出的调湿材料具有更好的韧性，且不易断裂，可以用于制作墙体材料、包装材料或木板砖的底层材料等多种不同的材料中，扩大了其适用范围，提高了材料的韧性，保证了质量。2、与现有技术相比，本发明制备工艺简单、成本低，其得到的调湿材料调湿效果好、响应快、使用方便；不易断裂，吸放湿速率快，并且可重复利用。
与申请（专利）号（CN200810039074.0）纤维调湿板；与申请（专利）号：CN201110251155.9一种有机—无机复合调湿纸及其制备方法；申请（专利）号：CN200810039073.6纤维调湿板的制备方法及设备；申请（专利）号：CN200910101495.6一种博物馆微环境调湿纸的制备方法；申请（专利）号：CN201010268154.0一种高效复合调湿纸的制备方法相比，本专利使用了盐、PCA、粘胶纤维等，使用无机盐不仅提高了吸放湿速率、湿含量并且制备方法简单，产品性能稳定湿度调节范围为50%-60%，加入中空粘胶纤维这种长纤维和少量的树脂增加了纸质调湿板的韧性，相对于纸质调湿板韧性有显著的增加。
具体实施方式
下面结合实施例对本发明作进一步说明：
实施例1：一种韧性调湿材料的制备方法，其特征在于步骤如下：
a、按质量份数取0.1份羧甲基纤维素钠加入到5份水中配制成凝胶状，放置备用；
b、按质量份数取0.3份氯化钠，2.7份碳酸钾，1.25份吡咯烷酮羧酸钠和0.4份硅藻土加入到100份水中配制成溶液；再加入4份生活用纸和0.25份聚丙烯酸钠粉末；搅拌、打浆；
c、将步骤a和步骤b得到的产物混合后，再打浆4次，然后加入0.5份粘胶纤维并搅拌均匀；
d、对步骤c得到的原料进行抄纸，并在80℃下烘干，即可得到韧性调湿材料。
实施例2：一种韧性调湿材料的制备方法，其特征在于步骤如下：
a、按质量份数取0.1份羧甲基纤维素钠加入到5份水中配制成凝胶状，放置备用；
b、按质量份数取0.3份氯化钠，2.7份碳酸钾，1.25份吡咯烷酮羧酸钠和0.4份硅藻土加入到100份水中配制成溶液；再加入4.25份生活用纸和0.25份聚丙烯酸钠粉末；搅拌、打浆；
c、将步骤a和步骤b得到的产物混合后，再打浆5次，然后加入1份粘胶纤维并搅拌均匀；
d、对步骤c得到的原料进行抄纸，并在85℃下烘干，即可得到韧性调湿材料。
实施例3：一种韧性调湿材料的制备方法，其特征在于步骤如下：
a、按质量份数取0.1份羧甲基纤维素钠加入到5份水中配制成凝胶状，放置备用；
b、按质量份数取0.3份氯化钠，2.7份碳酸钾，1.25份吡咯烷酮羧酸钠和0.4份硅藻土加入到100份水中配制成溶液；再加入4.5份生活用纸和0.25份聚丙烯酸钠粉末；搅拌、打浆；
c、将步骤a和步骤b得到的产物混合后，再打浆5次，然后加入1.5份粘胶纤维并搅拌均匀；
d、对步骤c得到的原料进行抄纸，并在90℃下烘干，即可得到韧性调湿材料。
上述各实施例中原料均按质量份数称取。

Claims (1)

1.一种韧性调湿材料的制备方法，其特征在于步骤如下：
a、按质量份数取0.1份羧甲基纤维素钠加入到5份水中配制成凝胶状，放置备用；
b、按质量份数取0.3份氯化钠，2.7份碳酸钾，1.25份吡咯烷酮羧酸钠和0.4份硅藻土加入到100份水中配制成溶液；再加入4-4.5份生活用纸和0.25份聚丙烯酸钠粉末；搅拌、打浆；
c、将步骤a和步骤b得到的产物混合后，再打浆4-5次，然后加入0.5~1.5份粘胶纤维并搅拌均匀；
d、对步骤c得到的原料进行抄纸，并在80-90℃下烘干，即可得到韧性调湿材料。
CN201210473912.1A 2012-11-19 2012-11-19 一种韧性调湿材料的制备方法 Expired - Fee Related CN102965998B (zh)