CN102964758B - 一种复合调湿材料的制备方法 - Google Patents

一种复合调湿材料的制备方法 Download PDF

Info

Publication number
CN102964758B
CN102964758B CN201210469998.0A CN201210469998A CN102964758B CN 102964758 B CN102964758 B CN 102964758B CN 201210469998 A CN201210469998 A CN 201210469998A CN 102964758 B CN102964758 B CN 102964758B
Authority
CN
China
Prior art keywords
parts
mass
stir
mixing solutions
adjusting material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210469998.0A
Other languages
English (en)
Other versions
CN102964758A (zh
Inventor
胡婷婷
梁世良
曹丽芬
彭志勤
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang University of Technology ZJUT
Original Assignee
Zhejiang University of Technology ZJUT
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang University of Technology ZJUT filed Critical Zhejiang University of Technology ZJUT
Priority to CN201210469998.0A priority Critical patent/CN102964758B/zh
Publication of CN102964758A publication Critical patent/CN102964758A/zh
Application granted granted Critical
Publication of CN102964758B publication Critical patent/CN102964758B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种复合调湿材料的制备方法,其步骤如下:a、按质量份数取5份氯化钠和10份碳酸钾加入到35份水中,搅拌均匀得到混合溶液,然后往该混合溶液中加入15份聚丙烯酸钠树脂,备用;b、按质量份数取5份经过250~300℃、2~2.5小时焙烧的海泡石,6份聚乙烯醇和2份尿素配制成溶液加入到步骤a所得混合物中,混合、搅拌;c、按质量份数取3份氯化钠和66.7份碳酸钾加入到200份水中搅拌配成混合溶液;d、将步骤b所得的混合物加入到步骤c所得的混合溶液中,混合、搅拌均匀,然后放入140-150℃烘箱中进行烘制,制得调湿材料;它具有本发明得到的产品成本低,响应速度快,效果好;工艺简单,使用方便;无毒无害。

Description

一种复合调湿材料的制备方法
技术领域
本发明涉及一种环境材料的制备,特别是一种复合调湿材料的制备方法,主要适用于环境的湿度调节。
背景技术
调湿材料已经成为现在追求生活质量的人的必需品。调湿材料一般以调湿颗粒,调湿纸,调湿球还有块状的调湿材料为主。调湿材料比较的致密,响应速度有所影响且一般摆放在比较不太显眼的地方,一种可塑性调湿材料将引起大家的关注。
研究表明,人类生活最适宜的湿度为40-60%之间,在这个湿度范围内细菌、真菌类繁殖比较的慢。对于我们生活物品,在这个湿度下也会得到更好的保护,不容易发生破损等。主动调湿器不仅耗能,而且损耗严重,不符合绿色能源。调湿材料能自动调节湿度在适宜的范围以内,并且可以快速的调节环境的湿
度,可重复使用。
发明内容
本发明是要克服上述现有技术中存在的不足,提供一种成本低、制备工艺简单方便的复合调湿材料的制备方法,以得到能自动调节周围环境湿度、湿度响应快,并且可以在形状上进行加工的调湿材料。
本发明所采用的技术方案是:一种复合调湿材料的制备方法,其特征在于步骤如下:
a、按质量份数取5份氯化钠和10份碳酸钾加入到35份水中,搅拌均匀得到混合溶液,然后往该混合溶液中加入15份聚丙烯酸钠树脂,备用;
b、按质量份数取5份经过250~300℃、2~2.5小时焙烧的海泡石,6份聚乙烯醇和2份尿素配制成溶液加入到步骤a所得混合物中,混合、搅拌;
c、按质量份数取3份氯化钠和66.7份碳酸钾加入到200份水中搅拌配成混合溶液;
d、将步骤b所得的混合物加入到步骤c所得的混合溶液中,混合、搅拌均匀,然后放入140-150℃烘箱中进行烘制,制得调湿材料。
聚乙烯醇聚合度为1750±50。
本发明的有益效果是:1、本发明以尿素为发泡剂,聚乙烯醇为制膜剂制复合调湿材料,一方面提高了产品的吸放湿性能,可以很好的调节微环境的湿度,保护物品免受湿度的影响,另一方面增强了产品的形状可塑性,即可以根据需要方便的在产品形状上进行加工改变。2、与现有技术相比,本发明得到的产品成本低,响应速度快,效果好;工艺简单,使用方便;无毒无害。
具体实施方式
本发明以尿素为发泡剂,聚乙烯醇为制膜剂制复合调湿材料,一方面提高了产品的吸放湿性能,另一方面增强了产品的形状可塑性,即可以根据需要方便的在产品形状上进行加工改变。
下面结合实施例对本发明作进一步说明:
实施例1:一种复合调湿材料的制备方法,其特征在于步骤如下:
a、按质量份数取5份氯化钠和10份碳酸钾加入到35份水中,搅拌均匀得到混合溶液,然后往该混合溶液中加入15份聚丙烯酸钠树脂,备用;
b、按质量份数取5份经过250℃、2小时焙烧的海泡石,6份聚乙烯醇和2份尿素配制成溶液加入到步骤a所得混合物中,混合、搅拌;
c、按质量份数取3份氯化钠和66.7份碳酸钾加入到200份水中搅拌配成混合溶液;
d、将步骤b所得的混合物加入到步骤c所得的混合溶液中,混合、搅拌均匀,然后放入140℃烘箱中进行烘制,制得调湿材料。
聚乙烯醇聚合度为1750±50。
实施例2:一种复合调湿材料的制备方法,其特征在于步骤如下:
a、按质量份数取5份氯化钠和10份碳酸钾加入到35份水中,搅拌均匀得到混合溶液,然后往该混合溶液中加入15份聚丙烯酸钠树脂,备用;
b、按质量份数取5份经过275℃、2.25小时焙烧的海泡石,6份聚乙烯醇和2份尿素配制成溶液加入到步骤a所得混合物中,混合、搅拌;
c、按质量份数取3份氯化钠和66.7份碳酸钾加入到200份水中搅拌配成混合溶液;
d、将步骤b所得的混合物加入到步骤c所得的混合溶液中,混合、搅拌均匀,然后放入145℃烘箱中进行烘制,制得调湿材料。
聚乙烯醇聚合度为1750±50。
实施例3:一种复合调湿材料的制备方法,其特征在于步骤如下:
a、按质量份数取5份氯化钠和10份碳酸钾加入到35份水中,搅拌均匀得到混合溶液,然后往该混合溶液中加入15份聚丙烯酸钠树脂,备用;
b、按质量份数取5份经过300℃、2.5小时焙烧的海泡石,6份聚乙烯醇和2份尿素配制成溶液加入到步骤a所得混合物中,混合、搅拌;
c、按质量份数取3份氯化钠和66.7份碳酸钾加入到200份水中搅拌配成混合溶液;
d、将步骤b所得的混合物加入到步骤c所得的混合溶液中,混合、搅拌均匀,然后放入150℃烘箱中进行烘制,制得调湿材料。
聚乙烯醇聚合度为1750±50。
上述各实施例中原料均按质量份数称取。

Claims (1)

1.一种复合调湿材料的制备方法,其特征在于步骤如下:
a、按质量份数取5份氯化钠和10份碳酸钾加入到35份水中,搅拌均匀得到混合溶液,然后往该混合溶液中加入15份聚丙烯酸钠树脂,备用;
b、按质量份数取5份经过250~300℃、2~2.5小时焙烧的海泡石,6份聚乙烯醇和2份尿素配制成溶液加入到步骤a所得混合物中,混合、搅拌;所述的聚乙烯醇聚合度为1750±50;
c、按质量份数取3份氯化钠和66.7份碳酸钾加入到200份水中搅拌配成混合溶液;
d、将步骤b所得的混合物加入到步骤c所得的混合溶液中,混合、搅拌均匀,然后放入140-150℃烘箱中进行烘制,制得调湿材料。
CN201210469998.0A 2012-11-19 2012-11-19 一种复合调湿材料的制备方法 Expired - Fee Related CN102964758B (zh)