CN102965940A - 一种织物用不透气性防水剂及其制备方法 - Google Patents
一种织物用不透气性防水剂及其制备方法 Download PDFInfo
- Publication number
- CN102965940A CN102965940A CN 201210513287 CN201210513287A CN102965940A CN 102965940 A CN102965940 A CN 102965940A CN 201210513287 CN201210513287 CN 201210513287 CN 201210513287 A CN201210513287 A CN 201210513287A CN 102965940 A CN102965940 A CN 102965940A
- Authority
- CN
- China
- Prior art keywords
- parts
- fabric
- alcohol
- stearic acid
- waterproofing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明公开了一种织物用不透气性防水剂及其制备方法。以重量份计，本发明由以下组分组成：硝化纤维素：1～3，聚氯乙烯树脂：10～20，甲乙酮：30～50，聚醋酸乙烯：3～8，聚乙烯醇：20～40，硬脂酸：10～20，羟基硅油乳液：10～30，N-羟甲基十八酰胺：4～8，十八醇：40～60。与现有技术相比，本发明具有如下有益效果：（1）能在织物表面形成一层防水薄膜，具有良好的防水性；（2）皮膜坚韧，耐摩擦，耐酸碱，耐水洗和干洗，持久性良好。
Description
技术领域
本发明属于纺织助剂技术领域，更具体是涉及一种织物用不透气性防水剂及其制备方法。
背景技术
我国很早就开始使用桐油涂布在用品和织物上，形成油性皮膜以防水，除桐油外，还可使用亚麻仁油、苏子油等干油性与半干油、熟炼油、干燥促进剂等混配而制成防水剂。其防水性优良，手感柔软，颜色浅淡，曾广泛应用多年，缺点为缺乏韧性和耐久性。
发明内容
本发明的目的在于克服现有技术存在的不足，提供一种织物用不透气性防水剂。
本发明的另一目的在于提供该织物用不透气性防水剂的制备方法。
为达到上述目的，本发明采取了如下的技术方案：
一种织物用不透气性防水剂，以重量份计，由以下组分组成：
硝化纤维素：1～3，聚氯乙烯树脂：10～20，甲乙酮：30～50，
聚醋酸乙烯：3～8，聚乙烯醇：20～40，硬脂酸：10～20，
羟基硅油乳液：10～30，N-羟甲基十八酰胺：4～8，
十八醇：40～60。
所述的一种织物用不透气性防水剂的制备方法，包括如下步骤：
（1）将聚氯乙烯树脂放置于甲乙酮中，加热置40～60℃，混合，搅拌均匀；
（2）聚醋酸乙烯、聚乙烯醇、硬脂酸及十八醇混合，反应2～5小时；
（3）将步骤（1）和步骤（2）的产物混合，搅拌均匀；
（4）冷却至室温，加入其余组分，搅拌混合均匀后即可得成品。
与现有技术相比，本发明具有如下有益效果：
（1）能在织物表面形成一层防水薄膜，具有良好的防水性；
（2）皮膜坚韧，耐摩擦，耐酸碱，耐水洗和干洗，持久性良好。
具体实施方式
以下结合具体实施例来对本发明作进一步的描述。
实施例1
一种织物用不透气性防水剂，以重量份计，由以下组分组成：
硝化纤维素：1，聚氯乙烯树脂：10，甲乙酮：30，
聚醋酸乙烯：3，聚乙烯醇：20，硬脂酸：10，
羟基硅油乳液：10，N-羟甲基十八酰胺：4，十八醇：40。
实施例2
一种织物用不透气性防水剂，以重量份计，由以下组分组成：
硝化纤维素：3，聚氯乙烯树脂：20，甲乙酮：50，
聚醋酸乙烯：8，聚乙烯醇：40，硬脂酸：20，
羟基硅油乳液：30，N-羟甲基十八酰胺：8，十八醇：60。
实施例3
一种织物用不透气性防水剂，以重量份计，由以下组分组成：
硝化纤维素：2，聚氯乙烯树脂：16，甲乙酮：40，
聚醋酸乙烯：6，聚乙烯醇：30，硬脂酸：15，
羟基硅油乳液：20，N-羟甲基十八酰胺：6，十八醇：50。
上述实施例中，所述的一种织物用不透气性防水剂的制备方法，包括如下步骤：
（1）将聚氯乙烯树脂放置于甲乙酮中，加热置40～60℃，混合，搅拌均匀；
（2）聚醋酸乙烯、聚乙烯醇、硬脂酸及十八醇混合，反应2～5小时；
（3）将步骤（1）和步骤（2）的产物混合，搅拌均匀；
（4）冷却至室温，加入其余组分，搅拌混合均匀后即可得成品。
Claims (5)
1.一种织物用不透气性防水剂，其特征在于，以重量份计，由以下组分组成：
硝化纤维素：1～3，聚氯乙烯树脂：10～20，甲乙酮：30～50，
聚醋酸乙烯：3～8，聚乙烯醇：20～40，硬脂酸：10～20，
羟基硅油乳液：10～30，N-羟甲基十八酰胺：4～8，
十八醇：40～60。
2.根据权利要求1所述的一种织物用不透气性防水剂，其特征在于，以重量份计，由以下组分组成：
硝化纤维素：1，聚氯乙烯树脂：10，甲乙酮：30，
聚醋酸乙烯：3，聚乙烯醇：20，硬脂酸：10，
羟基硅油乳液：10，N-羟甲基十八酰胺：4，十八醇：40。
3.根据权利要求1所述的一种织物用不透气性防水剂，其特征在于，以重量份计，由以下组分组成：
硝化纤维素：3，聚氯乙烯树脂：20，甲乙酮：50，
聚醋酸乙烯：8，聚乙烯醇：40，硬脂酸：20，
羟基硅油乳液：30，N-羟甲基十八酰胺：8，十八醇：60。
4.根据权利要求1所述的一种织物用不透气性防水剂，其特征在于，以重量份计，由以下组分组成：
硝化纤维素：2，聚氯乙烯树脂：16，甲乙酮：40，
聚醋酸乙烯：6，聚乙烯醇：30，硬脂酸：15，
羟基硅油乳液：20，N-羟甲基十八酰胺：6，十八醇：50。
5.权利要求1所述的一种织物用不透气性防水剂的制备方法，其特征在于，包括如下步骤：
（1）将聚氯乙烯树脂放置于甲乙酮中，加热置40～60℃，混合，搅拌均匀；
（2）聚醋酸乙烯、聚乙烯醇、硬脂酸及十八醇混合，反应2～5小时；
（3）将步骤（1）和步骤（2）的产物混合，搅拌均匀；
（4）冷却至室温，加入其余组分，搅拌混合均匀后即可得成品。