CN102952366A - 一种纤维浸渍酚醛树脂及其制备方法 - Google Patents

一种纤维浸渍酚醛树脂及其制备方法 Download PDF

Info

Publication number
CN102952366A
CN102952366A CN 201110260776 CN201110260776A CN102952366A CN 102952366 A CN102952366 A CN 102952366A CN 201110260776 CN201110260776 CN 201110260776 CN 201110260776 A CN201110260776 A CN 201110260776A CN 102952366 A CN102952366 A CN 102952366A
Authority
CN
China
Prior art keywords
toughener
phenol
add
basic catalyst
resol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN 201110260776
Other languages
English (en)
Inventor
姜丽
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN 201110260776 priority Critical patent/CN102952366A/zh
Publication of CN102952366A publication Critical patent/CN102952366A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种纤维树脂，具体涉及一种纤维浸渍酚醛树脂及其制备方法，属化工技术领域。该树脂配方包括：苯酚、碱性催化剂、甲醛、乙醇和增强剂；所述的碱性催化剂为氨水、二乙胺、三乙胺、二甲基乙醇胺或其组合；所述的增强剂为硅烷偶联剂；所述的增强剂为长链烷基三氧基硅烷、乙烯基三乙氧基硅烷或乙烯基三甲氧基硅烷。

Description

一种纤维浸渍酚醛树脂及其制备方法
技术领域
本发明涉及一种纤维树脂，具体涉及一种纤维浸渍酚醛树脂及其制备方法，属化工技术领域。 
背景技术
目前，纤维树脂应用范围很广，其配方及加工技术相对落后，对周边的环境影响很大，如何改进配方及加工工艺成为企业亟待解决的难题。 
发明内容
本发明的目的是为克服上述现有技术的不足之处，提供一种纤维浸渍酚醛树脂及其制备方法，该方法通过调整树脂配方及加工工艺，使纤维浸渍酚醛树脂产品符合市场需求。 
本发明是以如下技术方案实现的：一种纤维浸渍酚醛树脂，其特征在于：该树脂配方包括：苯酚、碱性催化剂、甲醛、乙醇和增强剂；所述的碱性催化剂为氨水、二乙胺、三乙胺、二甲基乙醇胺或其组合；所述的增强剂为硅烷偶联剂；所述的增强剂为长链烷基三氧基硅烷、乙烯基三乙氧基硅烷或乙烯基三甲氧基硅烷。 
一种制备如权利要求1所述的纤维浸渍酚醛树脂的方法，其特征在于：在搅拌过程中依次进行加料，先将预热熔融的苯酚以真空方式吸入反应釜内，接着加入1-5％的碱性催化剂(以苯酚的加入量计)，升温至80℃，在80℃下分批加入甲醛，进行缩聚反应，保温反应2小时，控制分子量在MV300-500，接着进行真空蒸馏脱水，直至粘度2000-5000CPS/25℃，冷却降温至40℃以下，加入乙醇和增强剂，混和均匀后放料。 
本发明的优点是：该酚醛树脂配方合理，加工工艺简单，所得产品为棕红色透明树脂，可以广泛应用于化工领域。 
具体实施方式
下面结合实施例对本发明作进一步详细说明： 
实施例1、 
一种纤维浸渍酚醛树脂，该树脂配方包括：苯酚、碱性催化剂、甲醛、乙醇 和增强剂；所述的碱性催化剂为氨水、二乙胺、三乙胺、二甲基乙醇胺或其组合；所述的增强剂为硅烷偶联剂；所述的增强剂为长链烷基三氧基硅烷、乙烯基三乙氧基硅烷或乙烯基三甲氧基硅烷。 
一种制备如权利要求1所述的纤维浸渍酚醛树脂的方法，其特征在于：在搅拌过程中依次进行加料，先将预热熔融的苯酚以真空方式吸入反应釜内，接着加入1-5％的碱性催化剂(以苯酚的加入量计)，升温至80℃，在80℃下分批加入甲醛，进行缩聚反应，保温反应2小时，控制分子量在MV300-500，接着进行真空蒸馏脱水，直至粘度2000-5000CPS/25℃，冷却降温至40℃以下，加入乙醇和增强剂，混和均匀后放料。 
实施例2、 
在搅拌过程中依次进行加料，先将预热熔融的苯酚200kg以真空方式吸入反应釜内，接着加入催化剂3kg，升温至80℃，在80℃下分批加入甲醛(37％)320kg，进行缩聚反应，保温反应2小时，控制分子量在MV390，然后在50℃、真空度为-0.092MPs，直至粘度2000cps/25，℃冷却降温至40℃以下，加入乙醇20kg，硅烷0.5kg，并调节树脂固含在75％，粘度在1500cps/25℃得棕红色透明树脂395kg。 

Claims (2)

1.一种纤维浸渍酚醛树脂，其特征在于：该树脂配方包括：苯酚、碱性催化剂、甲醛、乙醇和增强剂；所述的碱性催化剂为氨水、二乙胺、三乙胺、二甲基乙醇胺或其组合；所述的增强剂为硅烷偶联剂；所述的增强剂为长链烷基三氧基硅烷、乙烯基三乙氧基硅烷或乙烯基三甲氧基硅烷。
2.一种制备如权利要求1所述的纤维浸渍酚醛树脂的方法，其特征在于：在搅拌过程中依次进行加料，先将预热熔融的苯酚以真空方式吸入反应釜内，接着加入1-5％的碱性催化剂(以苯酚的加入量计)，升温至80℃，在80℃下分批加入甲醛，进行缩聚反应，保温反应2小时，控制分子量在MV300-500，接着进行真空蒸馏脱水，直至粘度2000-5000CPS/25℃，冷却降温至40℃以下，加入乙醇和增强剂，混和均匀后放料。
CN 201110260776 2011-08-27 2011-08-27 一种纤维浸渍酚醛树脂及其制备方法 Pending CN102952366A (zh)