CN102920039A - 直立棉罩杯冷压成型方法 - Google Patents

直立棉罩杯冷压成型方法 Download PDF

Info

Publication number
CN102920039A
CN102920039A CN2011102266006A CN201110226600A CN102920039A CN 102920039 A CN102920039 A CN 102920039A CN 2011102266006 A CN2011102266006 A CN 2011102266006A CN 201110226600 A CN201110226600 A CN 201110226600A CN 102920039 A CN102920039 A CN 102920039A
Authority
CN
China
Prior art keywords
cup
upright cotton
seconds
vertical cotton
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2011102266006A
Other languages
English (en)
Inventor
叶文春
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2011102266006A priority Critical patent/CN102920039A/zh
Publication of CN102920039A publication Critical patent/CN102920039A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种直立棉罩杯冷压成型方法，它包括如下步骤：(1)将直立棉烘烤加热，炉膛温度为200℃～300℃，烘烤时间35～45秒；(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为25～35秒，压力值是3kg～5kg；(3)打开模具，取出完成定型的直立棉罩杯。该方法成型快，仅需要30秒左右，在模具里采用低温低温冷压成型，加温也只需少许的温度，比传统海棉大大节约成本。加工出来的直立棉模杯比带布经过传统方法加工出来的直立棉模杯手感好。

Description

直立棉罩杯冷压成型方法
技术领域
本发明涉及女性内衣文胸罩杯的成型方法，尤其是一种直立棉罩杯冷压成型方法。
背景技术
随着市场对文胸的要求越来越高，针对于要求罩杯透气性好和吸湿效果强这一需求，纤维棉罩杯被广泛应用。直立棉是由100％的聚脂纤维(中国商品名也叫做绦纶纤维)制作而成，它里面不含胶水，所以几乎没有挥发物，是最接近自然而且对人体无害对环境无污染的弹性材料，具有弹性好、透气性好，散热快，手感柔软，质感轻，是制作女性内衣文胸罩杯的最好材料。
现有技术中，女性内衣文胸罩杯一般都是通过模具高温模压成型，其缺点是破坏了纤维棉特有的物理性质，改变了其柔软的手感和最佳的透气性。
发明内容
本发明的目的在于克服现有技术存在的问题，提供一种工艺简单，不破坏直立棉物理性能，成型的罩杯弹性好、透气性好，手感柔软的直立棉罩杯冷压成型方法。
本发明的目的是这样实现的：一种直立棉罩杯冷压成型方法，它包括如下步骤：
(1)将直立棉烘烤加热，炉膛温度为200℃～300℃，烘烤时间35～45秒；
(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为25～35秒，压力值是3kg～5kg；
(3)打开模具，取出完成定型的直立棉罩杯。
本发明更优选的技术方案是：一种直立棉罩杯冷压成型方法，它包括如下步骤：
(1)将直立棉烘烤加热，炉膛温度为230℃～280℃，烘烤时间38～42秒；
(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为28～32秒，压力值是3.5kg～4.5kg；
(3)打开模具，取出完成定型的直立棉罩杯。
本发明的有益效果在于：成型快，仅30秒左右，而传统海棉需要两分钟左右。传统海棉定型机需要200℃左右的模具高温，而直立棉冷压成型不需要任何温度只需对直立棉进行烘烤到特定的软度，在模具里采用低温低温冷压成型，加温也只需少许的温度，比传统海棉大大节约成本。加工出来的直立棉模杯比带布经过传统方法加工出来的直立棉模杯手感好。
具体实施方式
实施例1：一种直立棉罩杯冷压成型方法，它包括如下步骤：(1)将直立棉烘烤加热，炉膛温度为230℃，烘烤时间40秒；(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为30秒，压力值是3.5kg；(3)打开模具，取出完成定型的直立棉罩杯。
实施例2：一种直立棉罩杯冷压成型方法，它包括如下步骤：(1)将直立棉烘烤加热，炉膛温度为280℃，烘烤时间38秒；(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为32秒，压力值是4.5kg；(3)打开模具，取出完成定型的直立棉罩杯。
实施例3：一种直立棉罩杯冷压成型方法，它包括如下步骤：(1)将直立棉烘烤加热，炉膛温度为250℃，烘烤时间42秒；(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为28秒，压力值是4.0kg；(3)打开模具，取出完成定型的直立棉罩杯。
实施例4：一种直立棉罩杯冷压成型方法，它包括如下步骤：(1)将直立棉烘烤加热，炉膛温度为300℃，烘烤时间36秒；(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为25秒，压力值是5.0kg；(3)打开模具，取出完成定型的直立棉罩杯。

Claims (2)

1.一种直立棉罩杯冷压成型方法，它包括如下步骤：
(1)将直立棉烘烤加热，炉膛温度为200℃～300℃，烘烤时间35～45秒；
(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为25～35秒，压力值是3kg～5kg；
(3)打开模具，取出完成定型的直立棉罩杯。
2.根据权利要求1所述的直立棉罩杯冷压成型方法，其特征在于：它包括如下步骤：
(1)将直立棉烘烤加热，炉膛温度为230℃～280℃，烘烤时间38～42秒；
(2)将经过烘烤的直立棉放在温度低于100℃的罩杯模具里压制，模压时间为28～32秒，压力值是3.5kg～4.5kg；
(3)打开模具，取出完成定型的直立棉罩杯。
CN2011102266006A 2011-08-09 2011-08-09 直立棉罩杯冷压成型方法 Pending CN102920039A (zh)