CN102912578A - Production method of high-elasticity anti-wrinkle anti-oil worsted fabric - Google Patents
Production method of high-elasticity anti-wrinkle anti-oil worsted fabric Download PDFInfo
- Publication number
- CN102912578A CN102912578A CN201210403206XA CN201210403206A CN102912578A CN 102912578 A CN102912578 A CN 102912578A CN 201210403206X A CN201210403206X A CN 201210403206XA CN 201210403206 A CN201210403206 A CN 201210403206A CN 102912578 A CN102912578 A CN 102912578A
- Authority
- CN
- China
- Prior art keywords
- finishing
- fabric
- worsted fabric
- controlled
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a production method of high-elasticity anti-wrinkle anti-oil worsted fabric. The method comprises spinning, weaving of the worsted fabric and dyeing and finishing of the worsted fabric, wherein 1) the spinning comprises the following steps of: selecting the wool with fineness of 17.0-18.5 microns, controlling the single yarn twist multiplier to 80-90 in the spinning process, and controlling the plied yarn twist multiplier to 150-190; 2) the weaving of the worsted fabric comprises the following steps of: controlling the total tightness of textile in the weaving process to 100-120, and controlling the warp-weft ratio between 0.85 and 0.95; and 3) the dyeing and finishing of the worsted fabric comprises the following steps of: in the dyeing and finishing process, selecting the overfeeding-drying-setting technology, wherein 1.2-1.3 times of overfeeding is adopted, the breadth is controlled to 150-160cm, the drying temperature is 80 DEG C, and the setting temperature is controlled to 180 DEG C. Through the dyeing and finishing technology, the textile retracts in the warp and weft directions, the warp-direction and weft-direction densities of the textile are increased, and the textile obtains better elasticity and anti-wrinkle property; and the finishing technology can realize very ideal waterproof, anti-oil, anti-dirt and anti-wrinkle effects.
Description
Technical field
The present invention relates to textile technology field or elastic finishing technology, nanometer three anti-processing technology and the application of crease-resistant technology in wool worsted fabric, specifically a kind of production methods of high-elastic crease-resistant oil-stain-preventing wool worsted fabric.
Background technology
Development along with the epoch, scientific and technological progress improves day by day to the influence power of people's quality of life and cultural taste, larger transformation has occured in people's dressing theory thereupon, the time that people go out is more and more, toss about in bed in different places, therefore the wool worsted fabric of the function of suitable travelling more and more becomes a kind of consumption demand of business people or travelling personage.
Summary of the invention
Technical assignment of the present invention is to solve the deficiencies in the prior art, and a kind of production method of high-elastic crease-resistant oil-stain-preventing wool worsted fabric is provided.
Technical scheme of the present invention realizes in the following manner, and technique comprises: the weaving and the wool worsted fabric dyeing and finishing of spinning, wool worsted fabric, wherein;
1) spinning: selecting fineness is the wool of 17.0 μ m-18.5 μ m, and single twist multiplier is controlled at 80-90 in spinning process, and a strand yarn twist factor is controlled at 150-190;
2) weaving of wool worsted fabric: be controlled at 100-120 at the Cloth Forces in Weaving Machines total tightness degree, the longitude and latitude ratio is controlled between the 0.85-0.95; (whether total tightness degree has unit)
3) wool worsted fabric dyeing and finishing: comprise preparation and the wool worsted fabric arrangement of multifunctional composite finishing agent, the concrete technology step is as follows:
A) preparation of multifunctional composite finishing agent:
TexCOTE nanometer finishing agent BE04:3-5 part
Bleeding agent: 2-3 part
Softener: 3-5 part
Wool shrinkproof agent DM-3501 agent: 5-8 part
Demineralized water 70-85 part
Above-mentioned auxiliary agent is mixed with 40 ℃ soft water in proportion, be mixed with the multifunctional composite finishing agent for subsequent use;
B) finishing technique
In dyeing and finishing process, select " overfeeding-oven dry-typing " technique, overfeeding 1.2-1.3 doubly, fabric width is controlled at the 150-160 centimetre, and 80 ℃ of bake out temperatures, setting temperature are controlled at 180 ℃, by " overfeeding-oven dry-typing " PROCESS FOR TREATMENT, fabric is at longitude and latitude both direction retraction, the increasing through broadwise density of fabric, and fabric obtains preferably elasticity and wrinkle resistance; This finishing technique can reach ideal waterproof, grease proofing, antifouling, anti-wrinkle effect, and concrete technology is as follows:
1) wool worsted fabric is put into multifunction finishing agent and pad 20-40min;
2) pad rear wool worsted fabric and enter drying machine drying 3-6min, temperature is controlled at 80 ℃;
3) the dryer temperature is risen to 140-180 ℃, bake qualitative 3-6min and be finished product.
Outstanding beneficial effect of the present invention: the high-elastic crease-resistant oil-stain-preventing wool worsted fabric that the present invention produces, the suitable for making travel clothing, this wool worsted fabric has preferably elasticity, makes the wearer feel more comfortable in motion process; And have preferably waterproof, grease proofing, antifouling property, make the wearer needn't worry the living environmental pollution that happens suddenly; To have certain wrinkle resistance simultaneously, make fabric be difficult for wrinkle.Concrete function is summarized as follows:
(1) good elasticity;
(2) preferably waterproof, grease proofing, stain resistance energy, and have preferably wrinkle resistance;
The specific embodiment
The below does to describe in detail into-step to method of the present invention.
It is the wool of 17.0 μ m-18.5 μ m that spinning material uses fineness, and the wool of this fineness had both had preferably natural crimp and elastic performance, and enough fibre lengths are arranged again, can be the final excellent resilient properties of fabric and laid the first stone.
Single twist multiplier is controlled at 80-90 in spinning process, and a strand yarn twist factor is controlled at 150-190, is controlled at 100-120 at the Cloth Forces in Weaving Machines total tightness degree, and the longitude and latitude ratio is controlled between the 0.85-0.95.
In dyeing and finishing process, most critical be " overfeeding-oven dry-typing " technique, overfeeding 1.2-1.3 doubly, fabric width is controlled at the 150-160 centimetre, 80 ℃ of bake out temperatures, setting temperature are controlled at 180 ℃.Fabric longitude and latitude both direction retraction after " overfeeding-oven dry-typing " technique makes increasing through broadwise density of fabric, namely can realize fabric in the situation that do not make used additives produce preferably elastic performance.
(2) obtain preferably NBC protective performance and wrinkle resistance, technical process is as follows:
A) preparation of many finishing agents:
TexCOTE nanometer finishing agent BE04, bleeding agent, softener, hair anti-piping compound DM-3501 agent, these several finishing agents at home auxiliary agent manufacturer are all available.Four kinds of auxiliary agents mix according to a certain percentage, form multifunctional finishing auxiliary; The multifunctional finishing auxiliary prescription is as follows:
TexCOTE nanometer finishing agent BE04:4.5 part
Bleeding agent: 2.5 parts
Softener: 3.5 parts
Wool shrinkproof agent DM-3501 agent: 6.5 parts
Be that 40 ℃ soft water mixes with the auxiliary agent of aforementioned proportion and 83 parts of temperature, be made into multifunction finishing agent.
B) finishing technique
Adopt " padding → place → pad → dry → bake " technological process: pad, put into multifunction finishing agent and pad 80 ℃ of 20-40min → oven dry, 3-6min → bake 140-180 ℃, 3-6min.
Overfeeding 1.2-1.3 times, fabric width is controlled at the 150-160 centimetre, and 80 ℃ of bake out temperatures, setting temperature are controlled at 180 ℃, and this finishing technique can reach ideal waterproof, grease proofing, antifouling, anti-wrinkle effect by wool worsted fabric.
Embodiment 1
Adopting with fineness is the raw wool of 17.5 μ m, produces fineness of yarn and is 90 and publicly prop up bifilarly, and twist factor 180 is weaved total tightness degree and be 110 travelling wool worsted fabric.
The multifunctional finishing auxiliary prescription is as follows:
TexCOTE nanometer finishing agent BE04:3 part
Bleeding agent: 2 parts
Softener: 3 parts
Wool shrinkproof agent DM-3501 agent: 5 parts
The auxiliary agent of aforementioned proportion 70 parts of soft water with 40 ℃ are mixed, be made into multifunction finishing agent.
Its arrangement production technology is:
Pad → place → pad → overfeeding-dry-bake → finalize the design.
Overfeeding 1.2-1.3 times, fabric width is controlled at the 150-160 centimetre, and 80 ℃ of bake out temperatures, setting temperature are controlled at 180 ℃,
Compregnate: the compregnate process adds the multifunction finishing agent for preparing
Place: at room temperature, placed 30 minutes
Overfeeding: 1.2 times of overfeedings, 150 centimeters of fabric widths
Oven dry: 80 ℃, 3 minutes
Bake: 150 ℃, 3 minutes
Typing: 180 ℃, 3 minutes
Embodiment 2
Adopting with fineness is the raw wool of 17.5 μ m, produces fineness of yarn and is 90 and publicly prop up bifilarly, and twist factor 180 is weaved total tightness degree and be 110 travelling wool worsted fabric.
The multifunctional finishing auxiliary prescription is as follows:
TexCOTE nanometer finishing agent BE04:5 part
Bleeding agent: 3 parts
Softener: 5 parts
Wool shrinkproof agent DM-3501 agent: 8 parts
The auxiliary agent of the aforementioned proportion 70-80 part soft water with 40 ℃ is mixed, be made into multifunction finishing agent.
Its arrangement production technology is identical with embodiment 1.
Embodiment 3
Adopting with fineness is the raw wool of 17.5 μ m, produces fineness of yarn and is 90 and publicly prop up bifilarly, and twist factor 180 is weaved total tightness degree and be 110 travelling wool worsted fabric.
The multifunctional finishing auxiliary prescription is as follows:
TexCOTE nanometer finishing agent BE04:4 part
Bleeding agent: 2.5 parts
Softener: 4 parts
Wool shrinkproof agent DM-3501 agent: 7 parts
The auxiliary agent of aforementioned proportion 75 parts of soft water with 40 ℃ are mixed, be made into multifunction finishing agent.
Its arrangement production technology is identical with embodiment 1.
Through the hair worsted fabric of this technique, the characteristics that product has that good springiness, wrinkle resistance are good, waterproof, grease proofing, stain resistance can be good are fit to the travelling dress.
Except the disclosed technical characterictic of specification of the present invention, be the public office technology of those skilled in the art.
Claims (1)
1. the production method of a high-elastic crease-resistant oil-stain-preventing wool worsted fabric is characterized in that, technique comprises: spinning, the weaving and the wool worsted fabric dyeing and finishing of wool worsted fabric, wherein;
1) spinning: selecting fineness is the wool of 17.0 μ m-18.5 μ m, and single twist multiplier is controlled at 80-90 in spinning process, and a strand yarn twist factor is controlled at 150-190;
2) weaving of wool worsted fabric: be controlled at 100-120 at the Cloth Forces in Weaving Machines total tightness degree, the longitude and latitude ratio is controlled between the 0.85-0.95; (whether total tightness degree has unit)
3) wool worsted fabric dyeing and finishing: comprise preparation and the wool worsted fabric arrangement of multifunctional composite finishing agent, the concrete technology step is as follows:
A) preparation of multifunctional composite finishing agent:
TexCOTE nanometer finishing agent BE04:3-5 part
Bleeding agent: 2-3 part
Softener: 3-5 part
Wool shrinkproof agent DM-3501 agent: 5-8 part
Demineralized water 70-85 part
Above-mentioned auxiliary agent is mixed with 40 ℃ soft water in proportion, be mixed with the multifunctional composite finishing agent for subsequent use;
B) finishing technique
In dyeing and finishing process, select " overfeeding-oven dry-typing " technique, overfeeding 1.2-1.3 doubly, fabric width is controlled at the 150-160 centimetre, and 80 ℃ of bake out temperatures, setting temperature are controlled at 180 ℃, by " overfeeding-oven dry-typing " PROCESS FOR TREATMENT, fabric is at longitude and latitude both direction retraction, the increasing through broadwise density of fabric, and fabric obtains preferably elasticity and wrinkle resistance; This finishing technique can reach ideal waterproof, grease proofing, antifouling, anti-wrinkle effect, and concrete technology is as follows:
1) wool worsted fabric is put into multifunction finishing agent and pad 20～40min;
2) pad rear wool worsted fabric and enter drying machine drying 3-6min, temperature is controlled at 80 ℃;
3) the dryer temperature is risen to 140-180 ℃, bake qualitative 3-6min and be finished product.