CN102904144A - 一种无毒电刷的生产工艺 - Google Patents

一种无毒电刷的生产工艺 Download PDF

Info

Publication number
CN102904144A
CN102904144A CN201210415753XA CN201210415753A CN102904144A CN 102904144 A CN102904144 A CN 102904144A CN 201210415753X A CN201210415753X A CN 201210415753XA CN 201210415753 A CN201210415753 A CN 201210415753A CN 102904144 A CN102904144 A CN 102904144A
Authority
CN
China
Prior art keywords
mixture
powder
production technology
nontoxic
production process
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210415753XA
Other languages
English (en)
Inventor
岑志勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIMEN TONGDA CARBON INDUSTRY Co Ltd
Original Assignee
HAIMEN TONGDA CARBON INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIMEN TONGDA CARBON INDUSTRY Co Ltd filed Critical HAIMEN TONGDA CARBON INDUSTRY Co Ltd
Priority to CN201210415753XA priority Critical patent/CN102904144A/zh
Publication of CN102904144A publication Critical patent/CN102904144A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种无毒电刷的生产工艺，该生产工艺依次包括：步骤一：选取原材料，分别为石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料；步骤二：将所述石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料按照重量比为5：1：2：2：1：1的比例混合搅拌；步骤三:将上述合物放在搅拌机中粉碎成粉末状；步骤四：筛选一定大小的粉末混合物，所述粉末混合物个体的大小为0.02mm－0.04mm；步骤五：将筛选出来的混合物放进消毒液中浸泡5-7小时；步骤六：清洗混合物，晾干，放在模具中压制成半成品；步骤七：将所述半成品放在石墨化炉中，高温烧结，所述温度为：5000℃-6000℃。步骤八：冷却，精整成型。因此本发明工艺简单、无毒。

Description

一种无毒电刷的生产工艺
技术领域
本发明涉及一种生产工艺，尤其涉及一种无毒电刷的生产工艺。
背景技术
电刷是与运动件作滑动接触而形成电连接的一种导电部件。电刷是用于换向器或滑环上，作为导入导出电流的滑动接触体。它的导电，导热以及润滑性能良好， 并具有一定的机械强度和换向性火花的本能。几乎所有的直流电机以及换向式电机都使用电刷，它是电机的重要组成部件，电刷在日常生活中的应用越来越广泛，很多家用电器都需要用到电刷，比如吸尘器，家用粉碎机、家用饮水机等。但是一般常见的电刷具有使用寿命短、不耐磨、火花大等缺点。
发明内容
本发明所要解决的技术问题是提供一种工艺简单、无毒、适用于家用饮水机上电刷的生产工艺。
为解决上述技术问题，本发明所采用的技术方案是：一种无毒电刷的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料；
步骤二：将所述石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料按照重量比为5：1：2：2：1：1的比例混合搅拌；
步骤三: 将上述合物放在搅拌机中粉碎成粉末状；
步骤四：筛选一定大小的粉末混合物，所述粉末混合物个体的大小为0.02mm－0.04mm；
步骤五：将筛选出来的混合物放进消毒液中浸泡5-7小时；
步骤六：清洗混合物，晾干，放在模具中压制成半成品；
步骤七：将所述半成品放在石墨化炉中，高温烧结，所述温度为：5000℃-6000℃。
步骤八：冷却，精整成型。
所述大小为0.03mm。
所述时间为6小时。
所述温度为5500℃
与现有技术相比，本发明的有益效果为：
由于本发明的电刷的生产工艺采用了合理的结构及科学的工艺步骤及条件，所以能够制作出无毒的电刷，且制作工序少、易操作，因此本发明工艺简单、无毒。
具体实施方式
    以下结合具体实施方式详细说明本发明
一种无毒电刷的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料；
步骤二：将所述石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料按照重量比为5：1：2：2：1：1的比例混合搅拌；
步骤三: 将上述合物放在搅拌机中粉碎成粉末状；
步骤四：筛选一定大小的粉末混合物，所述粉末混合物个体的大小为0.02mm－0.04mm；
步骤五：将筛选出来的混合物放进消毒液中浸泡5-7小时；
步骤六：清洗混合物，晾干，放在模具中压制成半成品；
步骤七：将所述半成品放在石墨化炉中，高温烧结，所述温度为：5000℃-6000℃。
步骤八：冷却，精整成型。
上述生产工艺采用了合理的结构及科学的工艺步骤及条件，所以能够制作出无毒的电刷，且制作工序少、易操作。
实施例1：
一种无毒电刷的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料；
步骤二：将所述石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料按照重量比为5：1：2：2：1：1的比例混合搅拌；
步骤三: 将上述合物放在搅拌机中粉碎成粉末状；
步骤四：筛选一定大小的粉末混合物，所述粉末混合物个体的大小为0.03mm；
步骤五：将筛选出来的混合物放进消毒液中浸泡6小时；
步骤六：清洗混合物，晾干，放在模具中压制成半成品；
步骤七：将所述半成品放在石墨化炉中，高温烧结，所述温度为：5500℃。
步骤八：冷却，精整成型。
综上所述，本发明工艺简单、易操作。
以上所述仅为本发明的较佳实施方式，本发明的保护范围并不以上述实施方式为限，但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化，皆应纳入权利要求书中记载的保护范围内。

Claims (5)

1.一种无毒电刷的生产工艺，其特征在于：该生产工艺依次包括：
步骤一：选取原材料，分别为石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料；
步骤二：将所述石墨粉、钛粉、铝粉、酒精、粘结剂、润滑材料按照重量比为5：1：2：2：1：1的比例混合搅拌；
步骤三: 将上述合物放在搅拌机中粉碎成粉末状；
步骤四：筛选一定大小的粉末混合物，所述粉末混合物个体的大小为0.02mm－0.04mm；
步骤五：将筛选出来的混合物放进消毒液中浸泡5-7小时；
步骤六：清洗混合物，晾干，放在模具中压制成半成品；
步骤七：将所述半成品放在石墨化炉中，高温烧结，所述温度为：5000℃-6000℃。
2.步骤八：冷却，精整成型。
3.根据权利要求1所述的一种电刷的生产工艺，其特征在于：所述大小为0.03mm。
4. 根据权利要求1所述的一种电刷的生产工艺，其特征在于：所述时间为6小时。
5.根据权利要求1所述的一种电刷的生产工艺，其特征在于：所述温度为5500℃。
CN201210415753XA 2012-10-26 2012-10-26 一种无毒电刷的生产工艺 Pending CN102904144A (zh)