CN103811971A - 一种耐高温电刷的生产工艺 - Google Patents

一种耐高温电刷的生产工艺 Download PDF

Info

Publication number
CN103811971A
CN103811971A CN201210450030.3A CN201210450030A CN103811971A CN 103811971 A CN103811971 A CN 103811971A CN 201210450030 A CN201210450030 A CN 201210450030A CN 103811971 A CN103811971 A CN 103811971A
Authority
CN
China
Prior art keywords
high temperature
temperature resistant
polyarylate
copper
graphite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210450030.3A
Other languages
English (en)
Inventor
钱俊勇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210450030.3A priority Critical patent/CN103811971A/zh
Publication of CN103811971A publication Critical patent/CN103811971A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种耐高温电刷的生产工艺，该生产工艺依次包括：步骤一：选取原材料，分别为陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料；步骤二：将所述石墨经过石墨化提纯；步骤三：将所述陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料按照重量比为2：3：3：1：2：1的比例混合；步骤四:压制，将所述混合物制成混合坯料，再放入模具中进行压制成型，制成半成品；步骤五：烧结，将所述半成品放在锅炉中高温烧结而成，所述温度为800℃-1000℃；步骤六：检测，进行磨损检测、耐高温检测，选取合格品。因此本发明工艺简单、易操作比较的耐高温。

Description

一种耐高温电刷的生产工艺
技术领域
本发明涉及一种电刷的生产工艺，尤其涉及一种耐高温电刷的生产工艺。
背景技术
电刷是与运动件作滑动接触而形成电连接的一种导电部件。电刷是用于换向器或滑环上，作为导入导出电流的滑动接触体。它的导电，导热以及润滑性能良好， 并具有一定的机械强度和换向性火花的本能。几乎所有的直流电机以及换向式电机都使用电刷，它是电机的重要组成部件，电刷在日常生活中的应用越来越广泛，很多家用电器都需要用到电刷，比如吸尘器，家用粉碎机等。电刷一般都是在高速运转中工作，因此在工作中电刷的温度会升高。
发明内容
本发明所要解决的技术问题是提供一种工艺简单耐高温电刷的生产工艺。
为解决上述技术问题，本发明所采用的技术方案是：一种耐高温电刷的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料；
步骤二：将所述石墨经过石墨化提纯；
步骤三：将所述陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料按照重量比为2：3：3：1：2：1的比例混合；
步骤四:压制，将所述混合物制成混合坯料，再放入模具中进行压制成型，制成半成品；
步骤五：烧结，将所述半成品放在锅炉中高温烧结而成，所述温度为800℃
-1000℃；
步骤六：检测，进行磨损检测、耐高温检测，选取合格品。
所述温度为900℃。
与现有技术相比，本发明的有益效果为：
由于本发明的电刷的生产工艺采用了合理的结构及科学的工艺步骤及条件，所以能够制作出耐高温性能较好的电刷，且制作工序少、易操作，因此本发明工艺简单、易操作比较的耐高温。
具体实施方式
    以下结合具体实施方式详细说明本发明
一种耐高温电刷的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料；
步骤二：将所述石墨经过石墨化提纯；
步骤三：将所述陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料按照重量比为2：3：3：1：2：1的比例混合；
步骤四:压制，将所述混合物制成混合坯料，再放入模具中进行压制成型，制成半成品；
步骤五：烧结，将所述半成品放在锅炉中高温烧结而成，所述温度为800℃
-1000℃；
步骤六：检测，进行磨损检测、耐高温检测，选取合格品。
上述生产工艺采用了合理的结构及科学的工艺步骤及条件，所以能够制作出性能比较好的耐高温电刷，且制作工序少、易操作。
实施例1
    一种耐高温电刷的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料；
步骤二：将所述石墨经过石墨化提纯；
步骤三：将所述陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料按照重量比为2：3：3：1：2：1的比例混合；
步骤四:压制，将所述混合物制成混合坯料，再放入模具中进行压制成型，制成半成品；
步骤五：烧结，将所述半成品放在锅炉中高温烧结而成，所述温度为900℃；
步骤六：检测，进行磨损检测、耐高温检测，选取合格品。
综上所述，本发明工艺简单、易操作、且耐高温。
以上所述仅为本发明的较佳实施方式，本发明的保护范围并不以上述实施方式为限，但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化，皆应纳入权利要求书中记载的保护范围内。

Claims (2)

1.一种耐高温电刷的生产工艺，其特征在于：该生产工艺依次包括：
步骤一：选取原材料，分别为陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料；
步骤二：将所述石墨经过石墨化提纯；
步骤三：将所述陶瓷粉、聚醚铜、聚芳酯、石墨粉、二硫化铜、润滑材料按照重量比为2：3：3：1：2：1的比例混合；
步骤四:压制，将所述混合物制成混合坯料，再放入模具中进行压制成型，制成半成品；
步骤五：烧结，将所述半成品放在锅炉中高温烧结而成，所述温度为800℃
-1000℃；
步骤六：检测，进行磨损检测、耐高温检测，选取合格品。
2.根据权利要求1所述的一种耐高温电刷的生产工艺，其特征在于：所述温度为900℃。
CN201210450030.3A 2012-11-12 2012-11-12 一种耐高温电刷的生产工艺 Pending CN103811971A (zh)