CN102898980A - 紫外光固化丙烯酸酯胶黏剂 - Google Patents
紫外光固化丙烯酸酯胶黏剂 Download PDFInfo
- Publication number
- CN102898980A CN102898980A CN2012103601082A CN201210360108A CN102898980A CN 102898980 A CN102898980 A CN 102898980A CN 2012103601082 A CN2012103601082 A CN 2012103601082A CN 201210360108 A CN201210360108 A CN 201210360108A CN 102898980 A CN102898980 A CN 102898980A
- Authority
- CN
- China
- Prior art keywords
- parts
- acrylic ester
- curing acrylic
- ester adhesive
- sizing agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
紫外光固化丙烯酸酯胶黏剂，按质量份计由以下成份组成：甲基丙烯酸甲酯40～50份，丙烯酸丁酯50～60份，醋酸乙烯酯5～10份，丙烯酸3～5份，邻苯二甲酸二辛酯5～20份，过氧化苯甲酰0.2～1份，甲苯60～70份，四氢呋喃甲醇5～10份，石英粉5～10份，过硫酸铵0.5～2份。本发明提供的紫外光固化丙烯酸酯胶黏剂，在双层玻璃检测中，40℃下，钢球227g从12m落下不穿透，背面剥落碎片重量小于20g，100℃水煮3小时不老化，剪切强度保持在6～7MPa。
Description
技术领域
本发明属于胶黏剂技术领域，尤其涉及一种紫外光固化丙烯酸酯胶黏剂。
背景技术
紫外光固化胶黏剂是近年来发展较快的一种胶黏剂，它是利用紫外光引发具有化学活性的液态材料快速聚合交联，数秒内固化成膜，是一种高性能、高效率的胶黏剂。通过合成预聚物，用活性稀释剂进行改性，并配合加入各种光引发剂的方法，制备了ZUV系列紫外光固化胶黏剂。该系列紫外光固化胶黏剂具有固化速度快、粘接强度高、抗震性好等优点。已广泛应用于金属、玻璃、水晶、石材等多种材料的粘接，具有较好的社会经济效益。但现有的胶黏剂也存在很多不足之处，例如抗冲击性差，光、热稳定性较低等。
发明内容
解决的技术问题： 本发明针对现有紫外光固化胶黏剂的缺陷，提供一种耐冲击、稳定性好的紫外光固化丙烯酸酯胶黏剂。
技术方案：紫外光固化丙烯酸酯胶黏剂，按质量份计由以下成份组成：甲基丙烯酸甲酯 40～50份，丙烯酸丁酯 50～60份，醋酸乙烯酯 5～10份，丙烯酸3～5份，邻苯二甲酸二辛酯5～20份，过氧化苯甲酰 0.2～1份，甲苯60～70份，四氢呋喃甲醇 5～10份，石英粉5～10份，过硫酸铵0.5～2份。
优选方案为：按质量份计由以下成份组成：甲基丙烯酸甲酯 45份，丙烯酸丁酯 55份，醋酸乙烯酯 8份，丙烯酸4份，邻苯二甲酸二辛酯10份，过氧化苯甲酰 0.5份，甲苯65份，四氢呋喃甲醇 8份，石英粉7份，过硫酸铵1份。
有益效果：本发明提供的紫外光固化丙烯酸酯胶黏剂，在双层玻璃检测中，40℃下，钢球227g从12m落下不穿透，背面剥落碎片重量小于20g，100℃水煮3小时不老化，剪切强度保持在6～7MPa。
具体实施方式
实施例1
紫外光固化丙烯酸酯胶黏剂，按质量份计由以下成份组成：甲基丙烯酸甲酯 45份，丙烯酸丁酯 55份，醋酸乙烯酯 8份，丙烯酸4份，邻苯二甲酸二辛酯10份，过氧化苯甲酰 0.5份，甲苯65份，四氢呋喃甲醇 8份，石英粉7份，过硫酸铵1份。
制备工艺为：现将单体在氮气保护下升温，至80℃聚合开始后，依次加入其它组分，反应2～3小时后，自然降温。
本发明提供的紫外光固化丙烯酸酯胶黏剂，在双层玻璃检测中，40℃下，钢球227g从12m落下不穿透，背面剥落碎片重量小于20g，100℃水煮3小时不老化，剪切强度保持在6～7MPa。
Claims (2)
1.紫外光固化丙烯酸酯胶黏剂，其特征在于按质量份计由以下成份组成：甲基丙烯酸甲酯 40～50份，丙烯酸丁酯 50～60份，醋酸乙烯酯 5～10份，丙烯酸3～5份，邻苯二甲酸二辛酯5～20份，过氧化苯甲酰 0.2～1份，甲苯60～70份，四氢呋喃甲醇 5～10份，石英粉5～10份，过硫酸铵0.5～2份。
2.根据权利要求1所述的紫外光固化丙烯酸酯胶黏剂，其特征在于按质量份计由以下成份组成：甲基丙烯酸甲酯 45份，丙烯酸丁酯 55份，醋酸乙烯酯 8份，丙烯酸4份，邻苯二甲酸二辛酯10份，过氧化苯甲酰 0.5份，甲苯65份，四氢呋喃甲醇 8份，石英粉7份，过硫酸铵1份。