CN102898823A - 高灼热丝起燃温度阻燃尼龙6制作工艺 - Google Patents
高灼热丝起燃温度阻燃尼龙6制作工艺 Download PDFInfo
- Publication number
- CN102898823A CN102898823A CN2012104385979A CN201210438597A CN102898823A CN 102898823 A CN102898823 A CN 102898823A CN 2012104385979 A CN2012104385979 A CN 2012104385979A CN 201210438597 A CN201210438597 A CN 201210438597A CN 102898823 A CN102898823 A CN 102898823A
- Authority
- CN
- China
- Prior art keywords
- nylon
- halogen
- retardant
- flame
- percent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种高灼热丝起燃温度阻燃尼龙6制作工艺，是由以下成分按重量比组成尼龙6：55-80％；无卤氮磷系阻燃剂：5-30％；无卤辅助阻燃剂1-6％；热稳定剂：1-5％；偶联剂：0.1-0.9％；抗氧剂：0.3-0.8％；其他助剂：0.1-5.5％，本发明的一种无卤高灼热丝起燃温度阻燃尼龙6及其制作工艺，环保无卤，且在综合机械性能保持良好与无卤防火阻燃的基础上增加了高灼热丝起燃温度的特征，生产采购方便，全部采用国产原辅料和添加剂以及生产设备，生产成本和原材料成本大大降低，这样有效的提高了产品的综合竞争能力。
Description
技术领域
本发明涉及一种有机高分子复合材料，更具体地说，是涉及一种高灼热丝起燃温度阻燃尼龙6制作工艺。
背景技术
尼龙6是目前应用最多的几种工程塑料之一，他的酰胺基团具有极性，在他的结构中具有结构牢固的氢键，使得尼龙6的熔点较高，具有很好的物理力学性能和耐磨性以及自润滑性，这些综合特点是其他塑料所不具备的。但是纯尼龙6存在阻燃性不够好的缺点，从而限制了尼龙6的应用，进而又缩小了下游行业设计工程师的选材余地。因此，展开了对尼龙6进行复合阻燃改性的研究。当前社会对安全性的重视不断提高，在电子电气领域，仅仅有较好的阻燃性已经不能满足用户对安全性的需求，有些用户需要这些产品在极高的温度情况下不仅很快可以熄灭，而且更进一步要求不能起燃，不产生明火以及较少烟雾。而目前欧洲/日本等等发达国家出于种种原因，掀起了对外国进口产品种种限制，设立了一系列的壁垒，其中对电子电器产品的材质环保无卤要求并且同时还要求必须满足上述性能，因此造成对我国较多出口企业严重困扰，更多的是无法做到环保与特殊性能的同时满足。本技术发明就为上述技术缺陷提供了更好的解决方案。
发明内容
本发明的目的在于克服现有技术的缺陷，提供一种在在综合机械性能保持良好与无卤防火阻燃的基础上增加了高灼热丝起燃温度的特征的无卤高灼热丝起燃温度阻燃尼龙6原料。
本发明提供的技术方案如下：本发明的一种无卤高灼热丝起燃温度阻燃尼龙6，是由以下成分按重量比组成，尼龙6：55-80％；无卤氮磷系阻燃剂：5-30％；无卤辅助阻燃剂1-6％；热稳定剂：1-5％；偶联剂：0.1-0.9％；抗氧剂：0.3-0.8％；其他助剂：0.1-5.5％。
本发明所述的无卤高灼热丝起燃温度阻燃尼龙6生产流程是：先将尼龙6按照90度烘干3-4小时，然后先将烘干后的尼龙6、热稳定剂、偶联剂、抗氧剂和其他助剂按照比例称量后在混料机中低速混合10分钟，再经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面按比例加入无卤氮磷阻燃剂和无卤辅助阻燃剂，低转速混炼挤出，水冷拉条切粒经过筛分脱水制得无卤高灼热丝起燃温度阻燃尼龙6材料。
本发明有效的克服了现有技术的缺陷，具有以下优点：
本发明的一种无卤高灼热丝起燃温度阻燃尼龙6及其制作工艺，环保无卤，且在综合机械性能保持良好与无卤防火阻燃的基础上增加了高灼热丝起燃温度的特征，生产采购方便，全部采用国产原辅料和添加剂以及生产设备，生产成本和原材料成本大大降低，这样有效的提高了产品的综合竞争能力。
具体实施方式
以下是本发明所述的无卤高灼热丝起燃温度阻燃尼龙6原料的最佳实施例，并不因此限定本发明的保护范围。
实施例一，提供一种无卤高灼热丝起燃温度阻燃尼龙6，由以下成分按重量比组成尼龙6：72.9％；无卤氮磷系阻燃剂：20％；无卤辅助阻燃剂：3％；热稳定剂：2.5％；偶联剂：0.3％；抗氧剂：0.6％；其他助剂：0.7％。
先将尼龙6烘干按照90度烘干3-4小时，然后先将烘干后的尼龙6、热稳定剂、偶联剂、抗氧剂和其他助剂按照比例称量后在混料机中低速混合10分钟，混料机采用低速混合，搅拌叶应与筒壁间隙小于0.5厘米，原辅料混合效果应目视各种粒子和粉末基本均匀，没有明显团块或集聚；再经36长径比双螺杆挤出机在中等强度剪切的螺杆组合情况下设置不高于200转/分钟的转速由侧面按比例加入无卤氮磷阻燃剂和无卤辅助阻燃剂，保持较高真空压力条件下低转速混炼挤出，水冷拉条切粒经过筛分脱水制得无卤高灼热丝起燃温度阻燃尼龙6材料。
Claims (2)
1.一种高灼热丝起燃温度阻燃尼龙6制作工艺，其特征在于是由以下成分按重量比组成，尼龙6：55-80％；无卤氮磷系阻燃剂：5-30％；无卤辅助阻燃剂1-6％；热稳定剂：1-5％；偶联剂：0.1-0.9％；抗氧剂：0.3-0.8％；其他助剂：0.1-5.5％。
2.一种高灼热丝起燃温度阻燃尼龙6制作工艺，其特征在于包括如下步骤：先将尼龙6按照90度烘干3-4小时，然后先将烘干后的尼龙6、热稳定剂、偶联剂、抗氧剂和其他助剂按照比例称量后在混料机中低速混合10分钟，再经双螺杆挤出机在中等强度剪切的螺杆组合情况下由侧面按比例加入无卤氮磷阻燃剂和无卤辅助阻燃剂，低转速混炼挤出，水冷拉条切粒经过筛分脱水制得无卤高灼热丝起燃温度阻燃尼龙6材料。