CN102898002A - 一种led用玻璃制备方法 - Google Patents

一种led用玻璃制备方法 Download PDF

Info

Publication number
CN102898002A
CN102898002A CN2012104047224A CN201210404722A CN102898002A CN 102898002 A CN102898002 A CN 102898002A CN 2012104047224 A CN2012104047224 A CN 2012104047224A CN 201210404722 A CN201210404722 A CN 201210404722A CN 102898002 A CN102898002 A CN 102898002A
Authority
CN
China
Prior art keywords
glass
glass melt
led
melt
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012104047224A
Other languages
English (en)
Inventor
许丽琴
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANTONG HUANGHAI MOTOR CO Ltd
Original Assignee
NANTONG HUANGHAI MOTOR CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANTONG HUANGHAI MOTOR CO Ltd filed Critical NANTONG HUANGHAI MOTOR CO Ltd
Priority to CN2012104047224A priority Critical patent/CN102898002A/zh
Publication of CN102898002A publication Critical patent/CN102898002A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种LED用玻璃制备方法，包括以下步骤：a、按重量份称取二氧化硅65-70份；氧化钙 5-15份；氧化镁4-8份；三氧化二铝5-10份；氧化钡1-5份；氧化钠2-7份；b、将原料混合后倒入石英坩埚内熔化，熔化温度为1500-2000℃，保温1-2小时，得玻璃熔体；c、将玻璃熔体倒入铸铁模具上，将模具放入退火炉中进行退火，进行热处理9-12小时，热处理温度150-200℃；d、将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置一段时间，得LED用玻璃。本发明的优点是：这种玻璃制备工艺简单，具有晶体基质优异的光谱激发特性，该玻璃的生产周期短、成本低，实现大尺寸、高惨杂的特点。

Description

一种LED用玻璃制备方法
技术领域
本发明还涉及一种LED用玻璃制备方法。
背景技术
现有的白光发光二极管，采用晶片取代萤光粉体，公开的白光LED用低熔点荧光玻璃制备方法，虽然能避免荧光粉的散热性差，实现白光LED荧光材料的耐久性等问题，但是存在制备周期长，工艺复杂，材料稳定性差的问题。因此，需要提供一种新的技术方案来解决上述问题。
发明内容
本发明的目的是提供一种制备周期短的LED用玻璃制备方法。
本发明采用的技术方案：
一种LED用玻璃制备方法，包括以下步骤：
a、按重量份称取二氧化硅 65-70份；氧化钙  5-15份；氧化镁       4-8份；三氧化二铝 5-10份；氧化钡1-5份；氧化钠 2-7份；
b、将原料混合后倒入石英坩埚内熔化，熔化温度为1500-2000℃，保温1-2小时，得玻璃熔体；
c、将玻璃熔体倒入铸铁模具上，将模具放入退火炉中进行退火，进行热处理9-12小时，热处理温度150-200℃；
d、将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置一段时间，得LED用玻璃。
所述c步骤中模具放入退火炉进行退火之前，先在退火炉中充入还原性气体。
所述还原性气体包括甲烷、一氧化碳或氢气。
所述d步骤中从冷柜内取出玻璃熔体，静置1-3小时。
本发明的优点是：这种玻璃制备工艺简单，具有晶体基质优异的光谱激发特性，该玻璃的生产周期短、成本低，实现大尺寸、高惨杂的特点。
具体实施方式
下述实施例仅用于说明本发明，但并不能限定本发明的保护范围。
实施例1
一种LED用玻璃制备方法，包括以下步骤：
a、称取二氧化硅 65-70㎏；氧化钙  5-15㎏；氧化镁  4-8㎏；三氧化二铝 5-10㎏；氧化钡1-5㎏；氧化钠 2-7㎏；
b、将原料混合后倒入石英坩埚内熔化，熔化温度为1500-2000℃，保温1-2小时，得玻璃熔体；
c、将玻璃熔体倒入铸铁模具上，在退火之前，先在退火炉中充入甲烷，将模具放入退火炉中进行退火，进行热处理9-12小时，热处理温度150-200℃；
d、将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置1-3小时，得LED用玻璃。
实施例2
一种LED用玻璃制备方法，包括以下步骤：
a、称取二氧化硅 65-70㎏；氧化钙  5-15㎏；氧化镁 4-8㎏；三氧化二铝 5-10㎏；氧化钡 1-5㎏；氧化钠 2-7㎏；
b、将原料混合后倒入石英坩埚内熔化，熔化温度为1500-2000℃，保温1-2小时，得玻璃熔体；
c、将玻璃熔体倒入铸铁模具上，在退火之前，先在退火炉中充入一氧化碳，将模具放入退火炉中进行退火，进行热处理9-12小时，热处理温度150-200℃；
d、将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置1-3小时，得LED用玻璃。
实施例3
一种LED用玻璃制备方法，包括以下步骤：
a、称取二氧化硅 65-70㎏；氧化钙  5-15㎏；氧化镁 4-8㎏；三氧化二铝 5-10㎏；氧化钡1-5㎏；氧化钠 2-7㎏；
b、将原料混合后倒入石英坩埚内熔化，熔化温度为1500-2000℃，保温1-2小时，得玻璃熔体；
c、将玻璃熔体倒入铸铁模具上，在退火之前，先在退火炉中充入氢气，将模具放入退火炉中进行退火，进行热处理9-12小时，热处理温度150-200℃；
d、将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置1-3小时，得LED用玻璃。
这种玻璃制备工艺简单，具有晶体基质优异的光谱激发特性，该玻璃的生产周期短、成本低，实现大尺寸、高惨杂的特点。

Claims (4)

1.一种LED用玻璃制备方法，其特征在于，包括以下步骤：
a、按重量份称取二氧化硅 65-70份；氧化钙  5-15份；氧化镁       4-8份；三氧化二铝 5-10份；氧化钡1-5份；氧化钠 2-7份；
b、将原料混合后倒入石英坩埚内熔化，熔化温度为1500-2000℃，保温1-2小时，得玻璃熔体；
c、将玻璃熔体倒入铸铁模具上，将模具放入退火炉中进行退火，进行热处理9-12小时，热处理温度150-200℃；
d、将热处理好的玻璃熔体放入冷柜内，急剧降温至35-40℃，从冷柜内取出玻璃熔体，静置一段时间，得LED用玻璃。
2.根据权利要求1所述的一种LED用玻璃制备方法，其特征在于：所述c步骤中模具放入退火炉进行退火之前，先在退火炉中充入还原性气体。
3.根据权利要求1所述的一种LED用玻璃制备方法，其特征在于：所述还原性气体包括甲烷、一氧化碳或氢气。
4.根据权利要求1所述的一种LED用玻璃制备方法，其特征在于：所述d步骤中从冷柜内取出玻璃熔体，静置1-3小时。
CN2012104047224A 2012-10-23 2012-10-23 一种led用玻璃制备方法 Pending CN102898002A (zh)