CN102888185A - 一种仿石涂料及其制备方法 - Google Patents
一种仿石涂料及其制备方法 Download PDFInfo
- Publication number
- CN102888185A CN102888185A CN2012104226578A CN201210422657A CN102888185A CN 102888185 A CN102888185 A CN 102888185A CN 2012104226578 A CN2012104226578 A CN 2012104226578A CN 201210422657 A CN201210422657 A CN 201210422657A CN 102888185 A CN102888185 A CN 102888185A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- stone
- powder
- nano
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明具体涉及一种仿石涂料及其制备方法,属于化工生产领域。所述仿石涂料包括:金红石钛白粉、煅烧高岭土、重钙粉、纤维素、润湿剂、成膜助剂、防腐剂、多功能助剂、纳米锌粉、抗菌剂、固化剂、抗紫外线剂、弹性体改性环氧乙烯基酯、纳米二氧化硅、明矾、氢氧化铝粉末、纳米氧化铝粉、纳米硅防水剂、硅树脂、水。本发明研制的功能型仿石漆,为开发新产品来适应现代高质量、高品质生活的需要,其意义重大。得到产品的具有很好的弹性伸缩性、耐候、1m距离目视与天然石完全没有区别。抗紫外线,用于外墙不变色;防水。
Description
技术领域
本发明具体涉及一种仿石涂料及其制备方法,属于化工生产领域。
背景技术
仿石涂料 ( 也叫石头漆 ) , 顾名思义就是施工后具有天然石头效果的涂料,主要采用各种颜色的天然石粉配制而成,属于水性环保艺术涂料。仿石涂料有真石漆、碎石漆,还有仿大理石的,其装饰效果酷似大理石、花岗石。仿石涂料装修后的建筑物 ,具有天然真实的自然色泽,给人以高雅、和谐、庄重之美感,有一种令人回归自然的感觉。仿石涂料具有防火、防水、耐酸碱、耐污染、无毒、无味、粘接力强、永不褪色等特点,能有效地阻止外界恶劣环境对建筑物侵蚀 ,延长建筑物的寿命,由于仿石涂料具备良好的附着力和耐冻融性能,因此特别适合在寒冷地区使用。仿石涂料施工简便,易干省时,施工方便等优点,适合于各类建筑物的室内外装修,特别是在曲面建筑物上装饰,可达到生动逼真,回归自然的功效。
传统仿石漆产品中骨料多使用天然彩砂或人工彩色石英砂,致使产品因比重大等难以满足现代外墙面装饰的需求。在这种情况下研制功能型仿石漆,为开发新产品来适应现代高质量、高品质生活的需要,其意义重大。
发明内容
为了解决上述问题,本发明提供了一种仿石涂料及其制备方法。
本发明采取的技术方案如下:
本发明首先提供了一种所述仿石涂料,其原料配方按照重量份数包括以下组份:
金红石钛白粉2~8份
煅烧高岭土80~100份
重钙粉1~3份
纤维素1~3份
润湿剂1~3份
成膜助剂4~8份
防腐剂0.5~1份
多功能助剂0.5~1份
纳米锌粉0.1~0.5份
抗菌剂0.1~1份
固化剂0.1~0.5份
抗紫外线剂0.5~1份
弹性体改性环氧乙烯基酯1~3份
纳米二氧化硅0.5~1.5份
明矾0.05~0.3份
氢氧化铝粉末1~5份
纳米氧化铝粉0.5~1份
纳米硅防水剂0.1~1份
硅树脂80~100份
水100~120份。
更优选地,所述仿石涂料的原料配方按照重量份数包括以下组份:
金红石钛白粉6份
煅烧高岭土90份
重钙粉1.2份
纤维素2份
润湿剂1.2份
成膜助剂6份
防腐剂0.6份
多功能助剂0.6份
纳米锌粉0.2份
抗菌剂0.5份
固化剂0.1份
抗紫外线剂0.6份
弹性体改性环氧乙烯基酯1.5份
纳米二氧化硅1份
明矾0.1份
氢氧化铝粉末3份
纳米氧化铝粉0.7份
纳米硅防水剂0.3份
硅树脂90份
水100份。
所述多功能助剂为多功能助剂AMP-95。
本发明所采用的其它助剂均可以选用一般的仿真石涂漆的材料,即可实现。
本发明还提供了所述的仿石涂料的制备方法,包括以下步骤:
(1)首先将金红石钛白粉、煅烧高岭土、重钙粉、纤维素、润湿剂、成膜助剂、防腐剂、多功能助剂、纳米锌粉、抗菌剂、固化剂、抗紫外线剂、树脂、纳米二氧化硅、明矾、氢氧化铝粉末、纳米氧化铝粉先混合均匀,然后在50~55℃、相对湿度65%--75%以上、低嘈音的条件下密封恒温保存45~55小时;(2)在步骤(1)得到的混合物中加入纳米硅防水剂、硅树脂、水,搅拌均匀。
所述低嘈音为60分贝以下。
步骤(2)结束后加入调色剂调色。
另外提供了一种仿真装饰板,所述仿真装饰板包括基板,所述基板一侧面涂布有以上所述的仿石涂料。
本发明产品不仅作用于墙体,而且还可喷涂于各种基板上,所述基板可以是混凝土板、不锈钢板、木板、石膏板、冷轧钢板、泡沫板等。
本发明的仿石涂料采用喷涂方式施工,要求涂料制备后在6小时内施工完毕。
本发明产品的性能如下:
(1)1m距离目视与天然石完全没有区别;
(2)耐候、抗紫外线,用于外墙不变色;
(3)具有弹性(可伸缩),在墙面本身产生裂纹的情况下,本产品仍可保持完整。
(4)通用型强、无任何负重,施工后漆膜厚度在100um左右,大大减轻了建筑物体的承载负荷。
(5)防水。
具体实施方式
以下为本发明的几个具体实例,进一步描述本发明,但是本发明不仅限于此。
实施例1 最佳实施例
仿石涂料的原料配方按照重量份数如下:
金红石钛白粉6份
煅烧高岭土90份
重钙粉1.2份
纤维素2份
润湿剂1.2份
成膜助剂6份
防腐剂0.6份
多功能助剂AMP-95 0.6份
纳米锌粉0.2份
抗菌剂0.5份
固化剂0.1份
抗紫外线剂0.6份
弹性体改性环氧乙烯基酯MFE-9 1.5份
纳米二氧化硅1份
明矾0.1份
氢氧化铝粉末3份
纳米氧化铝粉0.7份
纳米硅防水剂0.3份
硅树脂90份
水100份。
制备方法如下:
(1)首先将金红石钛白粉、煅烧高岭土、重钙粉、纤维素、润湿剂、成膜助剂、防腐剂、多功能助剂AMP-95、纳米锌粉、抗菌剂、固化剂、抗紫外线剂、弹性体改性环氧乙烯基酯、纳米二氧化硅、明矾、氢氧化铝粉末、纳米氧化铝粉先混合均匀,然后在50℃、相对湿度70%、40分贝的条件下密封恒温保存50小时;(2)在步骤(1)得到的混合物中加入纳米硅防水剂、硅树脂、水,搅拌均匀。
得到产品的性能如下:
弹性伸缩性:墙体细龟裂3MM之内,本品仍可保持表面无裂痕。外部雨水、露水均不渗透到墙内。
耐候:使用寿命达10年以上,经人工老化试验600小时以上。
1m距离目视与天然石完全没有区别。
抗紫外线,用于外墙不变色;防水。
实施例2
仿石涂料的原料配方按照重量份数如下:
金红石钛白粉2份
煅烧高岭土80份
重钙粉1份
纤维素1份
润湿剂1份
成膜助剂4份
防腐剂0.5份
多功能助剂AMP-95 0.5份
纳米锌粉0.1份
抗菌剂0.1份
固化剂0.1份
抗紫外线剂0.5份
弹性体改性环氧乙烯基酯1份
纳米二氧化硅0.5份
明矾0.05份
氢氧化铝粉末1份
纳米氧化铝粉0.5份
纳米硅防水剂0.1份
硅树脂80份
水100份。
制备方法如下:
(1)首先将金红石钛白粉、煅烧高岭土、重钙粉、纤维素、润湿剂、成膜助剂、防腐剂、多功能助剂、纳米锌粉、抗菌剂、固化剂、抗紫外线剂、弹性体改性环氧乙烯基酯、纳米二氧化硅、明矾、氢氧化铝粉末、纳米氧化铝粉先混合均匀,然后在55℃、相对湿度85%、50分贝的条件下密封恒温保存55小时;(2)在步骤(1)得到的混合物中加入纳米硅防水剂、硅树脂、水,搅拌均匀。
实施例3
实施例2
仿石涂料的原料配方按照重量份数如下:
金红石钛白粉8份
煅烧高岭土100份
重钙粉3份
纤维素3份
润湿剂3份
成膜助剂8份
防腐剂1份
多功能助剂AMP-95 1份
纳米锌粉0.5份
抗菌剂1份
固化剂0.5份
抗紫外线剂1份
弹性体改性环氧乙烯基酯3份
纳米二氧化硅1.5份
明矾0.3份
氢氧化铝粉末5份
纳米氧化铝粉1份
纳米硅防水剂1份
硅树脂100份
水120份。
制备方法如下:
(1)首先将金红石钛白粉、煅烧高岭土、重钙粉、纤维素、润湿剂、成膜助剂、防腐剂、多功能助剂、纳米锌粉、抗菌剂、固化剂、抗紫外线剂、弹性体改性环氧乙烯基酯、纳米二氧化硅、明矾、氢氧化铝粉末、纳米氧化铝粉先混合均匀,然后在53℃、相对湿度65%、60分贝的条件下密封恒温保存50小时;(2)在步骤(1)得到的混合物中加入纳米硅防水剂、硅树脂、水,搅拌均匀。
Claims (7)
1.一种仿石涂料,其特征在于:所述仿石涂料的原料配方按照重量份数包括以下组份:
金红石钛白粉2~8份
煅烧高岭土80~100份
重钙粉1~3份
纤维素1~3份
润湿剂1~3份
成膜助剂4~8份
防腐剂0.5~1份
多功能助剂0.5~1份
纳米锌粉0.1~0.5份
抗菌剂0.1~1份
固化剂0.1~0.5份
抗紫外线剂0.5~1份
弹性体改性环氧乙烯基酯1~3份
纳米二氧化硅0.5~1.5份
明矾0.05~0.3份
氢氧化铝粉末1~5份
纳米氧化铝粉0.5~1份
纳米硅防水剂0.1~1份
硅树脂80~100份
水100~120份。
2.根据权利要求1所述的仿石涂料,其特征在于:所述仿石涂料的原料配方按照重量份数包括以下组份:
金红石钛白粉6份
煅烧高岭土90份
重钙粉1.2份
纤维素2份
润湿剂1.2份
成膜助剂6份
防腐剂0.6份
多功能助剂0.6份
纳米锌粉0.2份
抗菌剂0.5份
固化剂0.1份
抗紫外线剂0.6份
弹性体改性环氧乙烯基酯1.5份
纳米二氧化硅1份
明矾0.1份
氢氧化铝粉末3份
纳米氧化铝粉0.7份
纳米硅防水剂0.3份
硅树脂90份
水100份。
3.根据权利要求1所述的仿石涂料,其特征在于:所述多功能助剂为多功能助剂AMP-95。
4.一种如权利要求1、2或3所述的仿石涂料的制备方法,其特征在于:所述制备方法包括以下步骤:(1)首先将金红石钛白粉、煅烧高岭土、重钙粉、纤维素、润湿剂、成膜助剂、防腐剂、多功能助剂、纳米锌粉、抗菌剂、固化剂、抗紫外线剂、树脂、纳米二氧化硅、明矾、氢氧化铝粉末、纳米氧化铝粉先混合均匀,然后在50~55℃、相对湿度65%-85%、低嘈音的条件下密封恒温保存45~55小时;(2)在步骤(1)得到的混合物中加入纳米硅防水剂、硅树脂、水,搅拌均匀。
5.根据权利要求4所述的仿石涂料的制备方法,其特征在于:所述低嘈音为60分贝以下。
6.根据权利要求4所述的仿石涂料的制备方法,其特征在于:步骤(2)结束后加入调色剂调色。
7.一种仿真装饰板,其特征在于:所述仿真装饰板包括基板,所述基板一侧面涂布有权利要求1或2所述的仿石涂料。