CN102877370A - 一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法 - Google Patents

一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法 Download PDF

Info

Publication number
CN102877370A
CN102877370A CN2012103512888A CN201210351288A CN102877370A CN 102877370 A CN102877370 A CN 102877370A CN 2012103512888 A CN2012103512888 A CN 2012103512888A CN 201210351288 A CN201210351288 A CN 201210351288A CN 102877370 A CN102877370 A CN 102877370A
Authority
CN
China
Prior art keywords
filter paper
parts
mixed
paper
filter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103512888A
Other languages
English (en)
Other versions
CN102877370B (zh
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PHOENIX FILTER CO., LTD.
Original Assignee
Bengbu Phoenix International Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Phoenix International Co Ltd filed Critical Bengbu Phoenix International Co Ltd
Priority to CN201210351288.8A priority Critical patent/CN102877370B/zh
Publication of CN102877370A publication Critical patent/CN102877370A/zh
Application granted granted Critical
Publication of CN102877370B publication Critical patent/CN102877370B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法，其由下列重量份的原料制成：阔叶木浆60-70、中空涤纶短纤20-30、石英玻璃纤维10-20、改性珍珠岩2-5、重质碳酸钙1-3、活性白土2-3、纳米二氧化硅1-2、硼酸锌0.5-0.8、改性水溶性环氧树脂乳液1-2、聚N-乙烯基吡啶1-2、脂肪醇聚氧乙烯醚0.5-1、乙烯基三(β-甲氧基乙氧基)硅烷0.5-1、月桂醇硫酸钠0.4-0.8、湿强剂PAE2-5。本发明制备出来的滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐破度强、耐高温等优点，过滤效率达到99.98％，在常温及高温工况下有稳定的性能指标，具有较好的耐温和过滤效果。

Description

一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法
技术领域
本发明涉及一种滤清器滤纸，具体涉及一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法。
背景技术
柴油滤清器是燃油滤清器中一类，是一种用于滤除柴油中混入的其他固体杂质的装置，其中滤芯起到过滤柴油的作用，柴油滤清器的滤芯多采用滤纸制做，所以滤纸的质量直接影响滤芯过滤柴油的效率，现有的滤纸吸附性较差，滤清效率低，只能滤除机油中60%的杂质，对大于或小于其纸滤芯微孔的杂质都起不到永久的过滤作用，只能对那些相等于纸滤芯微孔并镶嵌到纸滤芯微孔中的杂质起到永久的滤除作用；另外现有的滤纸还具有耐高温性差，耐水性差，抗张强度低等缺点，限制了滤纸的使用寿命。
发明内容
本发明的目的在于针对现有技术的不足，提供一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法，增加滤纸的吸附性能及耐高温等性能，从而提高滤纸的滤清效率和延长滤纸的使用寿命。
为达到上述目的，本发明采用的技术方案如下：  
一种掺有中空涤纶短纤柴油滤清器用滤纸，由下列重量份的原料制成：阔叶木浆60-70、中空涤纶短纤20-30、石英玻璃纤维10-20、改性珍珠岩2-5、重质碳酸钙1-3、活性白土2-3、纳米二氧化硅1-2、硼酸锌0.5-0.8、改性水溶性环氧树脂乳液1-2、聚N-乙烯基吡啶1-2、脂肪醇聚氧乙烯醚0.5-1、乙烯基三(β-甲氧基乙氧基)硅烷 0.5-1、月桂醇硫酸钠 0.4-0.8、湿强剂PAE 2-5。
    所述的改性珍珠岩由以下方法制得：先将珍珠岩磨细后过200-300目筛，然后将其加热膨胀，之后逐渐冷却至常温，再加适量氨水预处理，向预处理后的珍珠岩中加入2-3%的硅烷偶联剂KH550和3-5%的无水乙醇，在100-110℃下加热搅拌20-30min，烘干、粉碎即得改性珍珠岩。
    所述的改性水溶性环氧树脂乳液由以下方法制得：取下列重量份的原料：3-4份水溶性酚醛树脂、1-2份羧甲基纤维素、3-4份偏苯三酸三辛酯、2-3份纳米氧化铝、0.5-1份木质素磺酸盐混合均匀后加热至70-80℃，30-40分钟后冷却至常温即可。
    所述的掺有中空涤纶短纤柴油滤清器用滤纸的制备方法，其特征在于包括以下步骤：
    （1）先将改性珍珠岩、重质碳酸钙、活性白土、纳米二氧化硅搅拌混合均匀，再加入乙烯基三(β-甲氧基乙氧基)硅烷，充分搅拌10-20min后，静置5-8min，然后在100-120℃下烘干，得到粉体材料；
    （2）将阔叶木浆、中空涤纶短纤、石英玻璃纤维分别按配比称重，放入碎浆机中，加入适量的硫酸水碎解至固含量为5-6%的浆料，加入湿强剂PAE继续碎解1-2h，制成混合浆料；
（3）将步骤（1）制好的粉体材料加入混合浆料中，加入硼酸锌、脂肪醇聚氧乙烯醚、月桂醇硫酸钠，加热至70-80℃，搅拌均匀，经疏解机疏解后，再磨浆，加适量的水调浆至固含量为2-3%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
    （4）将改性水溶性环氧树脂乳液和聚N-乙烯基吡啶混合均匀后稀释至固含量为5-8%，用涂布器使脱水后的纸均匀浸渍乳液，然后将浸渍好的纸电热鼓风干燥箱内烘干2-5min，最后在上光机上干燥5-10min，取出后即得本发明掺有中空涤纶短纤柴油滤清器用滤纸。
本发明与现有技术具有以下有益效果：
本发明通过对珍珠岩进行改性，提高了滤纸的吸附性能，改性水溶性环氧树脂乳液可以提高滤纸的抗张强度和耐破度。本发明制备出来的滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐破度强、耐高温等优点，过滤效率达到99.98％，在常温及高温工况下有稳定的性能指标，具有较好的耐温和过滤效果。
具体实施方式
下面结合具体实施例对本发明作进一步的说明。
实施例
一种掺有中空涤纶短纤柴油滤清器用滤纸，由下列重量份的原料制成：阔叶木浆70、中空涤纶短纤30、石英玻璃纤维20、改性珍珠岩5、重质碳酸钙3、活性白土3、纳米二氧化硅2、硼酸锌0.8、改性水溶性环氧树脂乳液2、聚N-乙烯基吡啶2、脂肪醇聚氧乙烯醚1、乙烯基三(β-甲氧基乙氧基)硅烷 1、月桂醇硫酸钠 0.8、湿强剂PAE 5。
    所述的改性珍珠岩由以下方法制得：先将珍珠岩磨细后过200目筛，然后将其加热膨胀，之后逐渐冷却至常温，再加适量氨水预处理，向预处理后的珍珠岩中加入3%的硅烷偶联剂KH550和5%的无水乙醇，在100℃下加热搅拌30min，烘干、粉碎即得改性珍珠岩。
    所述的改性水溶性环氧树脂乳液由以下方法制得：取下列重量份的原料：4份水溶性酚醛树脂、2份羧甲基纤维素、4份偏苯三酸三辛酯、3份纳米氧化铝、1份木质素磺酸盐混合均匀后加热至80℃，40分钟后冷却至常温即可。
    所述的掺有中空涤纶短纤柴油滤清器用滤纸的制备方法，其特征在于包括以下步骤：
    （1）先将改性珍珠岩、重质碳酸钙、活性白土、纳米二氧化硅搅拌混合均匀，再加入乙烯基三(β-甲氧基乙氧基)硅烷，充分搅拌20min后，静置8min，然后在120℃下烘干，得到粉体材料；
    （2）将阔叶木浆、中空涤纶短纤、石英玻璃纤维分别按配比称重，放入碎浆机中，加入适量的硫酸水碎解至固含量为6%的浆料，加入湿强剂PAE继续碎解2h，制成混合浆料；
（4）将步骤（1）制好的粉体材料加入混合浆料中，加入硼酸锌、脂肪醇聚氧乙烯醚、月桂醇硫酸钠，加热至80℃，搅拌均匀，经疏解机疏解后，再磨浆，加适量的水调浆至固含量为3%，调好的浆料经成型网成型后，在0.05Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
    （4）将改性水溶性环氧树脂乳液和聚N-乙烯基吡啶混合均匀后稀释至固含量为6%，用涂布器使脱水后的纸均匀浸渍乳液，然后将浸渍好的纸电热鼓风干燥箱内烘干3min，最后在上光机上干燥6min，取出后即得本发明掺有中空涤纶短纤柴油滤清器用滤纸。
经检测，本发明制得的滤纸的成纸透气度在91 L/m2·s ，最大孔径为49μm，平均孔径为30μm，湿伸长率为0.5%，湿耐破度为 367KPa，抗张强度为13.24kN·m，过滤精度为6μm，杂质去除率为99.98%。

Claims (4)

1.一种掺有中空涤纶短纤柴油滤清器用滤纸，其特征在于，由下列重量份的原料制成：
阔叶木浆60-70、中空涤纶短纤20-30、石英玻璃纤维10-20、改性珍珠岩2-5、重质碳酸钙1-3、活性白土2-3、纳米二氧化硅1-2、硼酸锌0.5-0.8、改性水溶性环氧树脂乳液1-2、聚N-乙烯基吡啶1-2、脂肪醇聚氧乙烯醚0.5-1、乙烯基三(β-甲氧基乙氧基)硅烷 0.5-1、月桂醇硫酸钠 0.4-0.8、湿强剂PAE 2-5。
2.根据权利要求书1所述的掺有中空涤纶短纤柴油滤清器用滤纸，其特征在于，所述的改性珍珠岩由以下方法制得：先将珍珠岩磨细后过200-300目筛，然后将其加热膨胀，之后逐渐冷却至常温，再加适量氨水预处理，向预处理后的珍珠岩中加入2-3%的硅烷偶联剂KH550和3-5%的无水乙醇，在100-110℃下加热搅拌20-30min，烘干、粉碎即得改性珍珠岩。
3.根据权利要求书1所述的掺有中空涤纶短纤柴油滤清器用滤纸，其特征在于，所述的改性水溶性环氧树脂乳液由以下方法制得：取下列重量份的原料：3-4份水溶性酚醛树脂、1-2份羧甲基纤维素、3-4份偏苯三酸三辛酯、2-3份纳米氧化铝、0.5-1份木质素磺酸盐混合均匀后加热至70-80℃，30-40分钟后冷却至常温即可。
4.一种如权利要求1所述的掺有中空涤纶短纤柴油滤清器用滤纸的制备方法，其特征在于包括以下步骤：
（1）先将改性珍珠岩、重质碳酸钙、活性白土、纳米二氧化硅搅拌混合均匀，再加入乙烯基三(β-甲氧基乙氧基)硅烷，充分搅拌10-20min后，静置5-8min，然后在100-120℃下烘干，得到粉体材料；
（2）将阔叶木浆、中空涤纶短纤、石英玻璃纤维分别按配比称重，放入碎浆机中，加入适量的硫酸水碎解至固含量为5-6%的浆料，加入湿强剂PAE继续碎解1-2h，制成混合浆料；
（3）将步骤（1）制好的粉体材料加入混合浆料中，加入硼酸锌、脂肪醇聚氧乙烯醚、月桂醇硫酸钠，加热至70-80℃，搅拌均匀，经疏解机疏解后，再磨浆，加适量的水调浆至固含量为2-3%，调好的浆料经成型网成型后，在0.05-0.08Mpa的真空条件下对成型后的湿纸进行抽吸脱水；
（4）将改性水溶性环氧树脂乳液和聚N-乙烯基吡啶混合均匀后稀释至固含量为5-8%，用涂布器使脱水后的纸均匀浸渍乳液，然后将浸渍好的纸电热鼓风干燥箱内烘干2-5min，最后在上光机上干燥5-10min，取出后即得本发明掺有中空涤纶短纤柴油滤清器用滤纸。
CN201210351288.8A 2012-09-20 2012-09-20 一种掺有中空涤纶短纤柴油滤清器用滤纸及其制备方法 Active CN102877370B (zh)