CN102899970A - 一种苇浆滤纸的制备工艺 - Google Patents
一种苇浆滤纸的制备工艺 Download PDFInfo
- Publication number
- CN102899970A CN102899970A CN2012103604235A CN201210360423A CN102899970A CN 102899970 A CN102899970 A CN 102899970A CN 2012103604235 A CN2012103604235 A CN 2012103604235A CN 201210360423 A CN201210360423 A CN 201210360423A CN 102899970 A CN102899970 A CN 102899970A
- Authority
- CN
- China
- Prior art keywords
- filter paper
- parts
- powder
- weight portion
- reed pulp
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种苇浆滤纸的制备工艺,其滤纸是由下述重量份的原料制得:苇浆纤维80-85,大豆纤维10-15,聚四氟乙烯纤维10-12,改性纳米叶腊石粉1-2,改性矿物粉2-4,纯丙乳液1-2,滑石粉1-2,氢氧化镁0.2-0.4,硼酸锌0.3-0.5,滑石粉0.5-1,拉开粉BX-781-2,PAE湿强剂0.4-0.6。本发明所得滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐水性好等优点,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果。
Description
技术领域
本发明涉及滤纸领域,确切地说是一种苇浆滤纸的制备工艺。
背景技术
作为一种有效的过滤介质,过滤纸已被广泛地用于各个领域。根据组成滤纸的纤维种类不同,过滤纸的性能、用途也不一样,有用于一般场合的普通滤纸,用于高温下的的聚四氟乙烯纤维滤纸,也有超净用聚丙烯滤纸等。根据滤纸是否浸胶,可以分为两大类,即浸胶滤纸和非浸胶滤纸。浸胶滤纸又分为固化滤纸和非固化滤纸。
随着过滤要求的不断提高,任何由单种纤维组成的滤纸都越来越难以满足使用上的要求,所以由多种纤维组合而成的滤纸应运而生。滤纸生产中常用的纤维有木质纤维、化学纤维、聚四氟乙烯纤维等。
发明内容
本发明的目的在于提供一种最大孔径小、过滤精度高的苇浆滤纸的制备工艺。
上述目的通过以下方案实现:
一种苇浆滤纸的制备工艺,其特征在于:包括以下步骤:
(1)将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡6-8小时后,取出干燥,而后研磨成纳米粉末后即得改性纳米叶腊石粉,备用;
(2)将2-4重量份蒙脱石、3-5重量份陶粒、1-2重量份迪开石混匀后,放入浓度为15-25%的氢氧化钠溶液中浸泡4-5小时后,取出水洗,再于450-550℃煅烧4-6小时,而后研磨成粉末,过100-200目筛后,即得改性矿物粉,备用;
(3)将80-85重量份苇浆纤维、10-15重量份大豆纤维、10-12重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解,得到固含量5-6%的浆料,再加入0.4-0.6重量份PAE湿强剂继续碎解,得混合浆料;
(4)将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤(3)所得混合浆料中,加热到70-80℃;
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得:苇浆纤维80-85,大豆纤维10-15,聚四氟乙烯纤维10-12,改性纳米叶腊石粉1-2,改性矿物粉2-4,纯丙乳液1-2,滑石粉1-2,氢氧化镁0.2-0.4,硼酸锌0.3-0.5,滑石粉0.5-1,拉开粉BX-78 1-2,PAE湿强剂0.4-0.6;
(5)经疏解机疏解后,再磨浆,按照常规造纸工艺抄纸,成型压榨、干燥即得。
所述的一种苇浆滤纸的制备工艺,其特征在于:所述的纯丙乳液的固含量为40-45%。
所述的一种苇浆滤纸的制备工艺,其特征在于:所述的碳酸钠与高锰酸钾混合溶液由7-9g/L的碳酸钠溶液与0.9-1g/L的高锰酸钾溶液等体积混合而得。
所述的一种苇浆滤纸的制备工艺,其特征在于:磨浆后所得浆料经过加水调浆,至固含量2-3%后再进行抄纸工序。
本发明的有益效果为:本发明所得滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐水性好等优点,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果,其成纸透气度在80-90L/m2.S 之间,过滤精度< 10μm,杂质去除率> 99%。
具体实施方式
实施例1
一种苇浆滤纸的制备工艺,包括以下步骤:
(1)将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡6小时后,取出干燥,而后研磨成纳米粉末后即得改性纳米叶腊石粉,备用;
(2)将2重量份蒙脱石、3重量份陶粒、1重量份迪开石混匀后,放入浓度为15%的氢氧化钠溶液中浸泡4小时后,取出水洗,再于450℃煅烧4小时,而后研磨成粉末,过100目筛后,即得改性矿物粉,备用;
(3)将80重量份苇浆纤维、10重量份大豆纤维、10重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解,得到固含量5%的浆料,再加入0.4重量份PAE湿强剂继续碎解,得混合浆料;
(4)将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤(3)所得混合浆料中,加热到70-80℃;
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得:苇浆纤维80,大豆纤维10,聚四氟乙烯纤维10,改性纳米叶腊石粉2,改性矿物粉4,纯丙乳液2,滑石粉2,氢氧化镁0.2,硼酸锌0.3,滑石粉0.5,拉开粉BX-78 2,PAE湿强剂0.4;
(5)经疏解机疏解后,再磨浆,按照常规造纸工艺抄纸,成型压榨、干燥即得。
所述的纯丙乳液的固含量为45%。
所述的碳酸钠与高锰酸钾混合溶液由9g/L的碳酸钠溶液与1g/L的高锰酸钾溶液等体积混合而得。
本实施例最大孔径50-55μm,成纸透气度在85-90L/m2.S 之间。
实施例2、
一种苇浆滤纸的制备工艺,包括以下步骤:
(1)将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡8小时后,取出干燥,而后研磨成纳米粉末后即得改性纳米叶腊石粉,备用;
(2)将4重量份蒙脱石、3重量份陶粒、2重量份迪开石混匀后,放入浓度为20%的氢氧化钠溶液中浸泡4小时后,取出水洗,再于500℃煅烧6小时,而后研磨成粉末,过200目筛后,即得改性矿物粉,备用;
(3)将85重量份苇浆纤维、15重量份大豆纤维、12重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解8分钟,得到固含量6%的浆料,再加入0.6重量份PAE湿强剂继续碎解15分钟,得混合浆料;
(4)将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤(3)所得混合浆料中,加热到80℃;
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得:苇浆纤维85,大豆纤维15,聚四氟乙烯纤维12,改性纳米叶腊石粉2,改性矿物粉4,纯丙乳液2,滑石粉2,氢氧化镁0.2,硼酸锌0.3,滑石粉0.5,拉开粉BX-78 2,PAE湿强剂0.6;
(5)经疏解机疏解后,再磨浆,磨浆后所得浆料经过加水调浆,至固含量3%后再按照常规造纸工艺抄纸,成型压榨、干燥即得。
所述的纯丙乳液的固含量为42%。
所述的碳酸钠与高锰酸钾混合溶液由8g/L的碳酸钠溶液与0.9g/L的高锰酸钾溶液等体积混合而得。
本实施例最大孔径53-55μm,成纸透气度在80-90L/m2.S 之间。
Claims (4)
1.一种苇浆滤纸的制备工艺,其特征在于:包括以下步骤:
(1)将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡6-8小时后,取出干燥,而后研磨成纳米粉末后即得改性纳米叶腊石粉,备用;
(2)将2-4重量份蒙脱石、3-5重量份陶粒、1-2重量份迪开石混匀后,放入浓度为15-25%的氢氧化钠溶液中浸泡4-5小时后,取出水洗,再于450-550℃煅烧4-6小时,而后研磨成粉末,过100-200目筛后,即得改性矿物粉,备用;
(3)将80-85重量份苇浆纤维、10-15重量份大豆纤维、10-12重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解,得到固含量5-6%的浆料,再加入0.4-0.6重量份PAE湿强剂继续碎解,得混合浆料;
(4)将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤(3)所得混合浆料中,加热到70-80℃;
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得:苇浆纤维80-85,大豆纤维10-15,聚四氟乙烯纤维10-12,改性纳米叶腊石粉1-2,改性矿物粉2-4,纯丙乳液1-2,滑石粉1-2,氢氧化镁0.2-0.4,硼酸锌0.3-0.5,滑石粉0.5-1,拉开粉BX-78 1-2,PAE湿强剂0.4-0.6;
(5)经疏解机疏解后,再磨浆,按照常规造纸工艺抄纸,成型压榨、干燥即得。
2.根据权利要求1所述的一种苇浆滤纸的制备工艺,其特征在于:所述的纯丙乳液的固含量为40-45%。
3.根据权利要求1所述的一种苇浆滤纸的制备工艺,其特征在于:所述的碳酸钠与高锰酸钾混合溶液由7-9g/L的碳酸钠溶液与0.9-1g/L的高锰酸钾溶液等体积混合而得。
4.根据权利要求1所述的一种苇浆滤纸的制备工艺,其特征在于:磨浆后所得浆料经过加水调浆,至固含量2-3%后再进行抄纸工序。