CN102899970B - 一种苇浆滤纸的制备工艺 - Google Patents

一种苇浆滤纸的制备工艺 Download PDF

Info

Publication number
CN102899970B
CN102899970B CN201210360423.5A CN201210360423A CN102899970B CN 102899970 B CN102899970 B CN 102899970B CN 201210360423 A CN201210360423 A CN 201210360423A CN 102899970 B CN102899970 B CN 102899970B
Authority
CN
China
Prior art keywords
powder
filter paper
weight portion
reed pulp
weight
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210360423.5A
Other languages
English (en)
Other versions
CN102899970A (zh
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PHOENIX FILTER Co Ltd
Original Assignee
ANHUI PHOENIX FILTER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI PHOENIX FILTER Co Ltd filed Critical ANHUI PHOENIX FILTER Co Ltd
Priority to CN201210360423.5A priority Critical patent/CN102899970B/zh
Publication of CN102899970A publication Critical patent/CN102899970A/zh
Application granted granted Critical
Publication of CN102899970B publication Critical patent/CN102899970B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种苇浆滤纸的制备工艺，其滤纸是由下述重量份的原料制得：苇浆纤维80-85，大豆纤维10-15，聚四氟乙烯纤维10-12，改性纳米叶腊石粉1-2，改性矿物粉2-4，纯丙乳液1-2，滑石粉1-2，氢氧化镁0.2-0.4，硼酸锌0.3-0.5,滑石粉0.5-1，拉开粉BX-78？1-2，PAE湿强剂0.4-0.6。本发明所得滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐水性好等优点，在常温及高温工况下有稳定的性能指标，具有较好的耐温和过滤效果。

Description

一种苇浆滤纸的制备工艺
技术领域
本发明涉及滤纸领域，确切地说是一种苇浆滤纸的制备工艺。
背景技术
作为一种有效的过滤介质，过滤纸已被广泛地用于各个领域。根据组成滤纸的纤维种类不同，过滤纸的性能、用途也不一样，有用于一般场合的普通滤纸，用于高温下的的聚四氟乙烯纤维滤纸，也有超净用聚丙烯滤纸等。根据滤纸是否浸胶，可以分为两大类，即浸胶滤纸和非浸胶滤纸。浸胶滤纸又分为固化滤纸和非固化滤纸。
随着过滤要求的不断提高，任何由单种纤维组成的滤纸都越来越难以满足使用上的要求，所以由多种纤维组合而成的滤纸应运而生。滤纸生产中常用的纤维有木质纤维、化学纤维、聚四氟乙烯纤维等。
发明内容
本发明的目的在于提供一种最大孔径小、过滤精度高的苇浆滤纸的制备工艺。
上述目的通过以下方案实现：
一种苇浆滤纸的制备工艺，其特征在于：包括以下步骤：
（1）将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡6-8小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米叶腊石粉，备用；
（2）将2-4重量份蒙脱石、3-5重量份陶粒、1-2重量份迪开石混匀后，放入浓度为15-25%的氢氧化钠溶液中浸泡4-5小时后，取出水洗，再于450-550℃煅烧4-6小时，而后研磨成粉末，过100-200目筛后，即得改性矿物粉，备用；
（3）将80-85重量份苇浆纤维、10-15重量份大豆纤维、10-12重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解，得到固含量5-6%的浆料，再加入0.4-0.6重量份PAE湿强剂继续碎解，得混合浆料；
（4）将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到70-80℃；
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得：苇浆纤维80-85，大豆纤维10-15，聚四氟乙烯纤维10-12，改性纳米叶腊石粉1-2，改性矿物粉2-4，纯丙乳液1-2，滑石粉1-2，氢氧化镁0.2-0.4，硼酸锌0.3-0.5,滑石粉0.5-1，拉开粉BX-781-2，PAE湿强剂0.4-0.6；
（5）经疏解机疏解后，再磨浆，按照常规造纸工艺抄纸，成型压榨、干燥即得。
所述的一种苇浆滤纸的制备工艺，其特征在于：所述的纯丙乳液的固含量为40-45%。
所述的一种苇浆滤纸的制备工艺，其特征在于：所述的碳酸钠与高锰酸钾混合溶液由7-9g/L的碳酸钠溶液与0.9-1g/L的高锰酸钾溶液等体积混合而得。
所述的一种苇浆滤纸的制备工艺，其特征在于：磨浆后所得浆料经过加水调浆，至固含量2-3%后再进行抄纸工序。
本发明的有益效果为：本发明所得滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐水性好等优点，在常温及高温工况下有稳定的性能指标，具有较好的耐温和过滤效果，其成纸透气度在80-90L/m2.S之间，过滤精度＜10μm，杂质去除率＞99%。
具体实施方式
实施例1
一种苇浆滤纸的制备工艺，包括以下步骤：
（1）将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡6小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米叶腊石粉，备用；
（2）将2重量份蒙脱石、3重量份陶粒、1重量份迪开石混匀后，放入浓度为15%的氢氧化钠溶液中浸泡4小时后，取出水洗，再于450℃煅烧4小时，而后研磨成粉末，过100目筛后，即得改性矿物粉，备用；
（3）将80重量份苇浆纤维、10重量份大豆纤维、10重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解，得到固含量5%的浆料，再加入0.4重量份PAE湿强剂继续碎解，得混合浆料；
（4）将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到70-80℃；
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得：苇浆纤维80，大豆纤维10，聚四氟乙烯纤维10，改性纳米叶腊石粉2，改性矿物粉4，纯丙乳液2，滑石粉2，氢氧化镁0.2，硼酸锌0.3,滑石粉0.5，拉开粉BX-782，PAE湿强剂0.4；
（5）经疏解机疏解后，再磨浆，按照常规造纸工艺抄纸，成型压榨、干燥即得。
所述的纯丙乳液的固含量为45%。
所述的碳酸钠与高锰酸钾混合溶液由9g/L的碳酸钠溶液与1g/L的高锰酸钾溶液等体积混合而得。
本实施例最大孔径50-55μm，成纸透气度在85-90L/m2.S之间。
实施例2、
一种苇浆滤纸的制备工艺，包括以下步骤：
（1）将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡8小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米叶腊石粉，备用；
（2）将4重量份蒙脱石、3重量份陶粒、2重量份迪开石混匀后，放入浓度为20%的氢氧化钠溶液中浸泡4小时后，取出水洗，再于500℃煅烧6小时，而后研磨成粉末，过200目筛后，即得改性矿物粉，备用；
（3）将85重量份苇浆纤维、15重量份大豆纤维、12重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解8分钟，得到固含量6%的浆料，再加入0.6重量份PAE湿强剂继续碎解15分钟，得混合浆料；
（4）将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到80℃；
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得：苇浆纤维85，大豆纤维15，聚四氟乙烯纤维12，改性纳米叶腊石粉2，改性矿物粉4，纯丙乳液2，滑石粉2，氢氧化镁0.2，硼酸锌0.3,滑石粉0.5，拉开粉BX-782，PAE湿强剂0.6；
（5）经疏解机疏解后，再磨浆，磨浆后所得浆料经过加水调浆，至固含量3%后再按照常规造纸工艺抄纸，成型压榨、干燥即得。
所述的纯丙乳液的固含量为42%。
所述的碳酸钠与高锰酸钾混合溶液由8g/L的碳酸钠溶液与0.9g/L的高锰酸钾溶液等体积混合而得。
本实施例最大孔径53-55μm，成纸透气度在80-90L/m2.S之间。

Claims (1)

1.一种苇浆滤纸的制备工艺，其特征在于：包括以下步骤：
（1）将叶腊石放入碳酸钠与高锰酸钾混合溶液中浸泡6-8小时后，取出干燥，而后研磨成纳米粉末后即得改性纳米叶腊石粉，备用；
（2）将2-4重量份蒙脱石、3-5重量份陶粒、1-2重量份迪开石混匀后，放入浓度为15-25%的氢氧化钠溶液中浸泡4-5小时后，取出水洗，再于450-550℃煅烧4-6小时，而后研磨成粉末，过100-200目筛后，即得改性矿物粉，备用；
（3）将80-85重量份苇浆纤维、10-15重量份大豆纤维、10-12重量份聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解，得到固含量5-6%的浆料，再加入0.4-0.6重量份PAE湿强剂继续碎解，得混合浆料；
（4）将改性纳米叶腊石粉、改性矿物粉、以及其余原料按重量份加入步骤（3）所得混合浆料中，加热到70-80℃；
所述的含有聚四氟乙烯纤维的滤纸是由下述重量份的原料制得：苇浆纤维80-85，大豆纤维10-15，聚四氟乙烯纤维10-12，改性纳米叶腊石粉1-2，改性矿物粉2-4，纯丙乳液1-2，滑石粉1-2，氢氧化镁0.2-0.4，硼酸锌0.3-0.5,滑石粉0.5-1，拉开粉BX-781-2，PAE湿强剂0.4-0.6；
（5）经疏解机疏解后，再磨浆，按照常规造纸工艺抄纸，成型压榨、干燥即得；
所述的纯丙乳液的固含量为40-45%；所述的碳酸钠与高锰酸钾混合溶液由7-9g/L的碳酸钠溶液与0.9-1g/L的高锰酸钾溶液等体积混合而得；磨浆后所得浆料经过加水调浆，至固含量2-3%后再进行抄纸工序。
CN201210360423.5A 2012-09-25 2012-09-25 一种苇浆滤纸的制备工艺 Active CN102899970B (zh)