CN102877374B - 一种聚四氟乙烯纤维阻燃滤纸 - Google Patents
一种聚四氟乙烯纤维阻燃滤纸 Download PDFInfo
- Publication number
- CN102877374B CN102877374B CN201210360406.1A CN201210360406A CN102877374B CN 102877374 B CN102877374 B CN 102877374B CN 201210360406 A CN201210360406 A CN 201210360406A CN 102877374 B CN102877374 B CN 102877374B
- Authority
- CN
- China
- Prior art keywords
- filter paper
- weight
- parts
- nacrite
- polytetrafluoroethylene fibre
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种聚四氟乙烯纤维阻燃滤纸,其是由下述重量份的原料制得:竹浆纤维85-90,聚四氟乙烯纤维20-25,改性珍珠陶土2-4,改性纳米蒙脱石粉1-2,聚乙烯醇0.3-0.5,纳米二氧化钛1-2,氢氧化镁0.5-1,过硫酸钠0.3-0.4,氢氧化铝0.1-0.2,分散剂NNO1-2,PAE湿强剂0.2-0.4。本发明所得滤纸具有透水性好、过滤面积大、最大孔径小、过滤精度高、耐水性好等优点,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果。
Description
技术领域
本发明涉及滤纸领域,确切地说是一种聚四氟乙烯纤维阻燃滤纸。
背景技术
作为一种有效的过滤介质,过滤纸已被广泛地用于各个领域。根据组成滤纸的纤维种类不同,过滤纸的性能、用途也不一样,有用于一般场合的普通滤纸,用于高温下的的玻璃纤维滤纸,也有超净用聚丙烯滤纸等。根据滤纸是否浸胶,可以分为两大类,即浸胶滤纸和非浸胶滤纸。浸胶滤纸又分为固化滤纸和非固化滤纸。
随着过滤要求的不断提高,任何由单种纤维组成的滤纸都越来越难以满足使用上的要求,所以由多种纤维组合而成的滤纸应运而生。滤纸生产中常用的纤维有木质纤维、化学纤维、玻璃纤维等。
发明内容
本发明的目的在于提供一种阻燃性能好的聚四氟乙烯纤维阻燃滤纸。
上述目的通过以下方案实现:
一种聚四氟乙烯纤维阻燃滤纸,其特征在于:其是由下述重量份的原料制得:竹浆纤维85-90,聚四氟乙烯纤维20-25,改性珍珠陶土2-4,改性纳米蒙脱石粉1-2,聚乙烯醇0.3-0.5,纳米二氧化钛1-2,氢氧化镁0.5-1,过硫酸钠0.3-0.4,氢氧化铝0.1-0.2,分散剂NNO 1-2,PAE湿强剂0.2-0.4;
所述的改性珍珠陶土的制备方法为:将珍珠陶土放入碳酸钠与高锰酸钾混合溶液中浸泡5-6小时后,取出干燥,加入相当于珍珠陶土重量0.5-1.2%的硅烷偶联剂KH570、相当于珍珠陶土重量0.3-0.5%的脂肪醇聚氧乙烯醚、相当于珍珠陶土重量0.5-1%的氧化铝于1700-2000转/分下搅拌5-10分钟后研磨,过100-200目筛即得;
所述的改性纳米蒙脱石粉的制备方法为:将蒙脱石放入盐酸溶液中浸泡4-5小时后,取出水洗,再于600-700℃煅烧4-6小时,而后研磨成纳米粉末即得。
所述的一种聚四氟乙烯纤维阻燃滤纸,其特征在于:所述的碳酸钠与高锰酸钾混合溶液由7-9g/L的碳酸钠溶液与0.7-1.0g/L的高锰酸钾溶液等体积混合而得。
所述的一种聚四氟乙烯纤维阻燃滤纸,其特征在于:所述的盐酸溶液的浓度为15-30%。
所述的一种聚四氟乙烯纤维阻燃滤纸,其特征在于:制备方法为:
(1)将竹浆纤维、聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解,得到固含量为5-6%的浆料,再按照重量份加入PAE湿强剂继续碎解,得混合浆料;
(2)将其余原料按重量份加入步骤(1)所得混合浆料中,加热到70-80℃;
(3)经疏解机疏解后,再磨浆,按照常规造纸工艺抄纸,成型压榨、干燥即得。
所述的一种聚四氟乙烯纤维阻燃滤纸,其特征在于:磨浆后所得浆料经过加水调浆,至固含量2-3%后再进行抄纸工序。
本发明的有益效果为:本发明原料采用的改性珍珠陶土以及改性纳米蒙脱石粉增加了滤纸的吸附性能,氢氧化镁与氢氧化铝混配,为本发明提供了优良的阻燃性能,尤其适用于滤清器用。本发明所得滤纸具有最大孔径小、过滤精度高、耐水性好等优点,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果,本发明制得的滤纸的成纸透气度在70-90L/m2.S 之间,(△ P=127Pa)最大孔径50-55μm,平均孔径30-35μm,湿伸长率≤ 1%,湿耐破度≥ 350KPa,抗张强度/kN·m-1 2.26,过滤精度< 10μm,杂质去除率> 99%。
具体实施方式
实施例1
一种聚四氟乙烯纤维阻燃滤纸,其是由下述重量份(kg)的原料制得:竹浆纤维85,聚四氟乙烯纤维20,改性珍珠陶土4,改性纳米蒙脱石粉2,聚乙烯醇0.3,纳米二氧化钛2,氢氧化镁1,过硫酸钠0.4,氢氧化铝0.2,分散剂NNO 2,PAE湿强剂0.4;
所述的改性珍珠陶土的制备方法为:将珍珠陶土放入碳酸钠与高锰酸钾混合溶液中浸泡5小时后,取出干燥,加入相当于珍珠陶土重量1 %的硅烷偶联剂KH570、相当于珍珠陶土重量0.3%的脂肪醇聚氧乙烯醚、相当于珍珠陶土重量1%的氧化铝于1700转/分下搅拌10分钟后研磨,过100目筛即得;
所述的改性纳米蒙脱石粉的制备方法为:将蒙脱石放入盐酸溶液中浸泡4小时后,取出水洗,再于650℃煅烧6小时,而后研磨成纳米粉末即得。
所述的碳酸钠与高锰酸钾混合溶液由8g/L的碳酸钠溶液与1.0g/L的高锰酸钾溶液等体积混合而得。
所述的盐酸溶液的浓度为15%。
所述的一种聚四氟乙烯纤维阻燃滤纸,制备方法为:
(1)将竹浆纤维、聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解,得到固含量为5%的浆料,再按照重量份加入PAE湿强剂继续碎解,得混合浆料;
(2)将其余原料按重量份加入步骤(1)所得混合浆料中,加热到80℃;
(3)经疏解机疏解后,再磨浆,按照常规造纸工艺抄纸,成型压榨、干燥即得。
本实施例最大孔径50-55μm,平均孔径33-35μm,成纸透气度在80-90L/m2.S 之间。
实施例2、
一种聚四氟乙烯纤维阻燃滤纸,其是由下述重量份(kg)的原料制得:竹浆纤维90,聚四氟乙烯纤维25,改性珍珠陶土2,改性纳米蒙脱石粉1,聚乙烯醇0.5,纳米二氧化钛1,氢氧化镁0.5,过硫酸钠0.3,氢氧化铝0.1,分散剂NNO 1,PAE湿强剂0.2;
所述的改性珍珠陶土的制备方法为:将珍珠陶土放入碳酸钠与高锰酸钾混合溶液中浸泡6小时后,取出干燥,加入0.5%的硅烷偶联剂KH570、0.3%的脂肪醇聚氧乙烯醚、1%的氧化铝于2000转/分下搅拌5分钟后研磨,过200目筛即得;
所述的改性纳米蒙脱石粉的制备方法为:将蒙脱石放入盐酸溶液中浸泡4小时后,取出水洗,再于700℃煅烧4小时,而后研磨成纳米粉末即得。
所述的碳酸钠与高锰酸钾混合溶液由7g/L的碳酸钠溶液与0.7g/L的高锰酸钾溶液等体积混合而得。
所述的盐酸溶液的浓度为23%。
所述的一种聚四氟乙烯纤维阻燃滤纸,制备方法为:
(1)将竹浆纤维、聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解25分钟,得到固含量为6%的浆料,再按照重量份加入PAE湿强剂继续碎解,得混合浆料;
(2)将其余原料按重量份加入步骤(1)所得混合浆料中,加热到70℃;
(3)经疏解机疏解后,再磨浆,磨浆后所得浆料经过加水调浆,至固含量3%后再按照常规造纸工艺抄纸,成型压榨、干燥即得。
本实施例最大孔径53-55μm,平均孔径30-35μm,成纸透气度在80-90L/m2.S 之间。
Claims (1)
1.一种聚四氟乙烯纤维阻燃滤纸,其特征在于:其是由下述重量份的原料制得:竹浆纤维85-90,聚四氟乙烯纤维20-25,改性珍珠陶土2-4,改性纳米蒙脱石粉1-2,聚乙烯醇0.3-0.5,纳米二氧化钛1-2,氢氧化镁0.5-1,过硫酸钠0.3-0.4,氢氧化铝0.1-0.2,分散剂NNO 1-2,PAE湿强剂0.2-0.4;
所述的改性珍珠陶土的制备方法为:将珍珠陶土放入碳酸钠与高锰酸钾混合溶液中浸泡5-6小时后,取出干燥,加入相当于珍珠陶土重量0.5-1.2%的硅烷偶联剂KH570、相当于珍珠陶土重量0.3-0.5%的脂肪醇聚氧乙烯醚、相当于珍珠陶土重量0.5-1%的氧化铝于1700-2000转/分下搅拌5-10分钟后研磨,过100-200目筛即得;
所述的改性纳米蒙脱石粉的制备方法为:将蒙脱石放入盐酸溶液中浸泡4-5小时后,取出水洗,再于600-700℃煅烧4-6小时,而后研磨成纳米粉末即得;
所述的碳酸钠与高锰酸钾混合溶液由7-9g/L的碳酸钠溶液与0.7-1.0g/L的高锰酸钾溶液等体积混合而得;
所述的盐酸溶液的浓度为15-30%;
所述的一种聚四氟乙烯纤维阻燃滤纸制备方法为:
(1)将竹浆纤维、聚四氟乙烯纤维按重量份混匀后放入碎浆机碎解,得到固含量为5-6%的浆料,再按照重量份加入PAE湿强剂继续碎解,得混合浆料;
(2)将其余原料按重量份加入步骤(1)所得混合浆料中,加热到70-80℃;
(3)经疏解机疏解后,再磨浆,按照常规造纸工艺抄纸,成型压榨、干燥即得;
磨浆后所得浆料经过加水调浆,至固含量2-3%后再进行抄纸工序。