CN102995495B - 一种含有改性凹凸棒土的滤清器滤纸及其制备方法 - Google Patents
一种含有改性凹凸棒土的滤清器滤纸及其制备方法 Download PDFInfo
- Publication number
- CN102995495B CN102995495B CN201210426518.2A CN201210426518A CN102995495B CN 102995495 B CN102995495 B CN 102995495B CN 201210426518 A CN201210426518 A CN 201210426518A CN 102995495 B CN102995495 B CN 102995495B
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- filter paper
- preparation
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种含有改性凹凸棒土的滤清器滤纸及其制备方法,其组成原料的重量份为:麻浆75-80、醋酸纤维28-32、中空纤维12-15、改性纳米粉2-4、交联剂TAC 1-2、偏苯三酸三辛酯1.3-1.8、氯化石蜡2.5-3.5、聚乙二醇4000 0.8-1.2、改性凹凸棒土7-9、抗氧剂DLTP 1-3、4,4′-二苯基甲烷二异氰酸酯 0.6-0.8、壳聚糖醋酸溶液0.8-1.5、硬脂酸锌1-2、六偏磷酸钠2.3-2.8、二氧化硅1.5-2.5和烷基酚聚氧乙烯醚 0.8-1.2。本发明采用麻浆、醋酸纤维和中空纤维同时作为主要材料,环保科学,原料配方合理,各组分间相容性好,强度、韧性、抗腐蚀性提高,表面光泽度好,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果,其最大孔径47-55μm,平均孔径29-34μm,成纸透气度在84-88L/m2.S 之间。
Description
技术领域
本发明涉及汽车滤清器领域,确切地说是一种含有改性凹凸棒土的滤清器滤纸及其制备方法。
背景技术
滤清器是发动机的重要零部件,其作用为滤除进入发动机的空气、柴油、机油中的尘埃和机械杂质等微粒,以减少发动机缸套活塞环、曲轴连杆运动副和高压油泵柱塞偶件的磨损,优化发动机的燃烧过程,降低一氧化碳等有机污染物的排放。
作为一种有效的过滤介质,过滤纸已被广泛地用于各个领域。根据组成滤纸的纤维种类不同,过滤纸的性能、用途也不一样,有用于一般场合的普通滤纸,用于高温下的的玻璃纤维滤纸,也有超净用聚丙烯滤纸等。根据滤纸是否浸胶,可以分为两大类,即浸胶滤纸和非浸胶滤纸。浸胶滤纸又分为固化滤纸和非固化滤纸。
随着过滤要求的不断提高,任何由单种纤维组成的滤纸都越来越难以满足使用上的要求,所以由多种纤维组合而成的滤纸应运而生,滤纸生产中常用的纤维有木质纤维、化学纤维、玻璃纤维等。
发明内容
本发明的目的在于提供一种含有改性凹凸棒土的滤清器滤纸及其制备方法,本发明采用麻浆、醋酸纤维和中空纤维同时作为主要材料,环保科学,原料配方合理,各组分间相容性好,强度、韧性、抗腐蚀性提高,表面光泽度好,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果,其最大孔径47-55μm,平均孔径29-34μm,成纸透气度在84-88L/m2.S 之间。
为了实现上述目的本发明采用如下技术方案:
含有改性凹凸棒土的滤清器滤纸,其组成原料的重量份为:麻浆75-80、醋酸纤维28-32、中空纤维12-15、改性纳米粉2-4、交联剂TAC 1-2、偏苯三酸三辛酯1.3-1.8、氯化石蜡2.5-3.5、聚乙二醇4000 0.8-1.2、改性凹凸棒土7-9、抗氧剂DLTP 1-3、4,4′-二苯基甲烷二异氰酸酯 0.6-0.8、壳聚糖醋酸溶液0.8-1.5、硬脂酸锌1-2、六偏磷酸钠2.3-2.8、二氧化硅1.5-2.5和烷基酚聚氧乙烯醚 0.8-1.2。
含有改性凹凸棒土的滤清器滤纸,其组成原料的重量份为:麻浆78、醋酸纤维30、中空纤维14、改性纳米粉3、交联剂TAC 1.5、偏苯三酸三辛酯1.5、氯化石蜡3、聚乙二醇4000 1、改性凹凸棒土8、抗氧剂DLTP 2、4,4′-二苯基甲烷二异氰酸酯 0.7、壳聚糖醋酸溶液1.2、硬脂酸锌1.5、六偏磷酸钠2.5、二氧化硅2和烷基酚聚氧乙烯醚 1。
含有改性凹凸棒土的滤清器滤纸的制备方法,包括以下步骤:
(1)按组成原料的重量份称取各原料,将麻浆、醋酸纤维和中空纤维混匀后放入碎浆机碎解,得到固含量为4-6%的浆料,得混合浆料;
(2)在步骤(1)的混合浆料中按组成原料的重量份加入剩余其他原料,加热到65-75℃;经疏解机疏解后,再磨浆,磨浆后所得浆料经过加水调浆,至固含量3-5%后按照常规造纸工艺抄纸,成型压榨、干燥即得。
所述的改性纳米粉制备方法为由碳酸钙、天青石粉、钾长石粉按比例1:1:1在600-700℃温度下烧损4-5小时,后研磨成纳米粉末,拌入相当于粉体重量3-5%的双(二辛氧基焦磷酸酯基)乙撑钛酸酯拌搅均匀,烘干,粉碎成粉末。
所述的改性凹凸棒土的制备方法为:先用15-20%盐酸浸泡凹凸棒土1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,粉碎成粉末。
本发明的有益效果:
本发明采用麻浆、醋酸纤维和中空纤维同时作为主要材料,环保科学,原料配方合理,各组分间相容性好,强度、韧性、抗腐蚀性提高,表面光泽度好,在常温及高温工况下有稳定的性能指标,具有较好的耐温和过滤效果,其最大孔径47-55μm,平均孔径29-34μm,成纸透气度在84-88L/m2.S 之间。
具体实施方式
实施例1:含有改性凹凸棒土的滤清器滤纸,其组成原料的重量份为:麻浆78、醋酸纤维30、中空纤维14、改性纳米粉3、交联剂TAC 1.5、偏苯三酸三辛酯1.5、氯化石蜡3、聚乙二醇4000 1、改性凹凸棒土8、抗氧剂DLTP 2、4,4′-二苯基甲烷二异氰酸酯 0.7、壳聚糖醋酸溶液1.2、硬脂酸锌1.5、六偏磷酸钠2.5、二氧化硅2和烷基酚聚氧乙烯醚 1。
含有改性凹凸棒土的滤清器滤纸的制备方法,包括以下步骤:
(1)按组成原料的重量份称取各原料,将麻浆、醋酸纤维和中空纤维混匀后放入碎浆机碎解,得到固含量为4-6%的浆料,得混合浆料;
(2)在步骤(1)的混合浆料中按组成原料的重量份加入剩余其他原料,加热到65-75℃;经疏解机疏解后,再磨浆,磨浆后所得浆料经过加水调浆,至固含量3-5%后按照常规造纸工艺抄纸,成型压榨、干燥即得。
所述的改性纳米粉制备方法为由碳酸钙、天青石粉、钾长石粉按比例1:1:1在600-700℃温度下烧损4-5小时,后研磨成纳米粉末,拌入相当于粉体重量3-5%的双(二辛氧基焦磷酸酯基)乙撑钛酸酯拌搅均匀,烘干,粉碎成粉末。
所述的改性凹凸棒土的制备方法为:先用15-20%盐酸浸泡凹凸棒土1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,粉碎成粉末。
用上述的方法制得的含有改性凹凸棒土的滤清器滤纸的性能检测数据如下:
克重:119g/cm2;耐破度:303Kpa;透气度:512ml/10cm2 min;其最大孔径47-55μm,平均孔径29-34μm,成纸透气度在84-88L/m2.S之间。
Claims (3)
1.一种含有改性凹凸棒土的滤清器滤纸,其特征在于其组成原料的重量份为:麻浆75-80、醋酸纤维28-32、中空纤维12-15、改性纳米粉2-4、交联剂TAC 1-2、偏苯三酸三辛酯1.3-1.8、氯化石蜡2.5-3.5、聚乙二醇4000 0.8-1.2、改性凹凸棒土7-9、抗氧剂DLTP 1-3、4,4′-二苯基甲烷二异氰酸酯 0.6-0.8、壳聚糖醋酸溶液0.8-1.5、硬脂酸锌1-2、六偏磷酸钠2.3-2.8、二氧化硅1.5-2.5和烷基酚聚氧乙烯醚 0.8-1.2;
所述的改性纳米粉制备方法为由碳酸钙、天青石粉、钾长石粉按比例1:1:1在600-700℃温度下烧损4-5小时,后研磨成纳米粉末,拌入相当于粉体重量3-5%的双(二辛氧基焦磷酸酯基)乙撑钛酸酯拌搅均匀,烘干,粉碎成粉末;
所述的改性凹凸棒土的制备方法为:先用15-20%盐酸浸泡凹凸棒土1-2小时,静置,澄清,离心,固体用水洗至中性,烘干后,加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀,烘干,粉碎成粉末。
2.根据权利要求1所述的含有改性凹凸棒土的滤清器滤纸,其特征在于其组成原料的重量份为:麻浆78、醋酸纤维30、中空纤维14、改性纳米粉3、交联剂TAC 1.5、偏苯三酸三辛酯1.5、氯化石蜡3、聚乙二醇4000 1、改性凹凸棒土8、抗氧剂DLTP 2、4,4′-二苯基甲烷二异氰酸酯 0.7、壳聚糖醋酸溶液1.2、硬脂酸锌1.5、六偏磷酸钠2.5、二氧化硅2和烷基酚聚氧乙烯醚 1。
3.一种如权利要求1所述的含有改性凹凸棒土的滤清器滤纸的制备方法,其特征在于包括以下步骤:
(1)按组成原料的重量份称取各原料,将麻浆、醋酸纤维和中空纤维混匀后放入碎浆机碎解,得到固含量为4-6%的浆料,得混合浆料;
(2)在步骤(1)的混合浆料中按组成原料的重量份加入剩余其他原料,加热到65-75℃;经疏解机疏解后,再磨浆,磨浆后所得浆料经过加水调浆,至固含量3-5%后按照常规造纸工艺抄纸,成型压榨、干燥即得。