CN102875784A - 一种用于聚氨酯软泡的改性聚酯多元醇 - Google Patents

一种用于聚氨酯软泡的改性聚酯多元醇 Download PDF

Info

Publication number
CN102875784A
CN102875784A CN2012103891634A CN201210389163A CN102875784A CN 102875784 A CN102875784 A CN 102875784A CN 2012103891634 A CN2012103891634 A CN 2012103891634A CN 201210389163 A CN201210389163 A CN 201210389163A CN 102875784 A CN102875784 A CN 102875784A
Authority
CN
China
Prior art keywords
parts
foam
polyester polyol
modified polyester
polyurethane foam
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012103891634A
Other languages
English (en)
Other versions
CN102875784B (zh
Inventor
杨水清
罗伟
李海建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangsu Yingtian Environmental Protection Technology Co ltd
Original Assignee
JIANGSU YINGTIAN CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU YINGTIAN CHEMICAL CO Ltd filed Critical JIANGSU YINGTIAN CHEMICAL CO Ltd
Priority to CN201210389163.4A priority Critical patent/CN102875784B/zh
Publication of CN102875784A publication Critical patent/CN102875784A/zh
Application granted granted Critical
Publication of CN102875784B publication Critical patent/CN102875784B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由30-40的对苯二甲酸、5-10的苯酐、5-10的十四碳二酸、25-40的聚乙二醇、5-10的甘油、5-10的异戊四醇以及0.01-0.05的钛酸四丁酯组成；采用本发明提供的技术方案，其产品可提高软泡的承载能力、降低密度、提高开孔度、防止收缩大有帮助。同时可提高泡沫制品硬度、也增加初凝速度、降低催化剂用量并使泡沫的耐燃性能增加。

Description

一种用于聚氨酯软泡的改性聚酯多元醇
技术领域
本发明涉及一种用于聚氨酯软泡的改性聚酯多元醇。
背景技术
聚氨酯是使用最广泛的塑料之一，在现代社会众多领域中起着各种各样的作用。聚氨酯的化学反应通过选择制造工艺以及选用添加剂和催化剂予以控制，而添加发泡剂可使聚合物膨胀，生产各种不同用途及性能的聚氨酯泡沫。
软质聚氨酯泡沫塑料，简称聚氨酯软泡，是一种具有一定弹性的柔软性聚氨酯泡沫塑料，它是聚氨酯制品中用量最大的一种聚氨酯产品。主要用作家具垫材、床垫、交通工具座椅坐垫等垫材，工业和民用上也把软泡用作过滤材料、隔音材料、防震材料、装饰材料、包装材料及隔热材料等。按软硬程度，即耐负荷性能的不同，聚氨酯软泡可以分为普通软泡、超柔软泡、高承载软泡、高回弹软泡等。
发明内容
早期聚酯多元醇均指己二酸系聚酯多元醇，最大市场是微孔泡沫,应用于鞋底。近几年相继出现新品种，扩大了聚酯多元醇的应用面。
一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由以下组分组成：
Figure BDA00002251941900011
Figure BDA00002251941900021
优选的：一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由以下组分组成：
Figure BDA00002251941900022
优选的：一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由以下组分组成：
Figure BDA00002251941900023
本发明的技术方案中，以对苯二甲酸和苯酐为原料，合成聚酯多元醇，能使制品的早期强度提高，改善耐湿性及硬度等同时降低成本。采用长链二元酸可极大的改善聚酯的柔软性、抗张强度、低温性能，具有色泽光亮耐磨、冲击强度高的特点。
本发明的有益效果在于：可提高软泡的承载能力、降低密度、提高开孔度、防止收缩大有帮助。同时可提高泡沫制品硬度、也增加初凝速度、降低催化剂用量并使泡沫的耐燃性能增加。
具体实施例
实施例1
一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由以下组分组成：
将原料加入到反应釜中，通N2保护，升温，控制出水的速度和气相的温度(常压下在100-102℃之间)。再将温度缓慢升至250℃，当出水量达到理论出水量的70%-90%时，保温2h，取样测酸值，然后开始抽真空，逐渐提高真空度，当真空度＞0.09MPa约4h后，取样测酸值、羟值、水分，然后每隔1-2h测一次，直到各项指标合格后开始降温出料，产品外观为红色粘稠状液体。
实施例2
一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由以下组分组成：
Figure BDA00002251941900041
将原料加入到反应釜中，通N2保护，升温，控制出水的速度和气相的温度(常压下在100-102℃之间)。再将温度缓慢升至250℃，当出水量达到理论出水量的70%-90%时，保温2h，取样测酸值，然后开始抽真空，逐渐提高真空度，当真空度＞0.09MPa约4h后，取样测酸值、羟值、水分，然后每隔1-2h测一次，直到各项指标合格后开始降温出料，产品外观为红色粘稠状液体。
实施例3
一种用于聚氨酯软泡的改性聚酯多元醇，按照质量份数计，由以下组分组成：
Figure BDA00002251941900042
Figure BDA00002251941900051
将原料加入到反应釜中，通N2保护，升温，控制出水的速度和气相的温度(常压下在100-102℃之间)。再将温度缓慢升至250℃，当出水量达到理论出水量的70%-90%时，保温2h，取样测酸值，然后开始抽真空，逐渐提高真空度，当真空度＞0.09MPa约4h后，取样测酸值、羟值、水分，然后每隔1-2h测一次，直到各项指标合格后开始降温出料，产品外观为红色粘稠状液体。
表1为实施例中，产品的各项指标：
表1
Figure BDA00002251941900052

Claims (3)

1.一种用于聚氨酯软泡的改性聚酯多元醇，其特征在于，按照质量份数计，由以下组分组成：
Figure FDA00002251941800011
2.一种用于聚氨酯软泡的改性聚酯多元醇，其特征在于，按照质量份数计，由以下组分组成：
Figure FDA00002251941800012
3.一种用于聚氨酯软泡的改性聚酯多元醇，其特征在于，按照质量份数计，由以下组分组成：
Figure FDA00002251941800013
Figure FDA00002251941800021
CN201210389163.4A 2012-10-13 2012-10-13 一种用于聚氨酯软泡的改性聚酯多元醇 Active CN102875784B (zh)