CN102863633A - 一种橡胶制品的生产方法 - Google Patents
一种橡胶制品的生产方法 Download PDFInfo
- Publication number
- CN102863633A CN102863633A CN2012104047525A CN201210404752A CN102863633A CN 102863633 A CN102863633 A CN 102863633A CN 2012104047525 A CN2012104047525 A CN 2012104047525A CN 201210404752 A CN201210404752 A CN 201210404752A CN 102863633 A CN102863633 A CN 102863633A
- Authority
- CN
- China
- Prior art keywords
- superoxide
- weight
- parts
- weight part
- rubber item
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种橡胶制品的生产方法，包括以下步骤：a、将40-50重量份的硫粉末、1-3重量份的粘土、1-3重量份的增强剂、1-3重量份的助剂和40-50重量份的水一起球磨碾磨，成悬浮液；b、将上述悬浮液通过连续涂布机喷涂到过氧化物上，将得到的含过氧化物的橡胶制品，在热空气管式炉中加热到160-200℃，并通过足够量的氧气，以强制空气循环固化5-10分钟。本发明的优点是：用过氧化物交联具有更好的耐热性、压缩变定、电绝缘性，交联时通入足量的氧气，并以强制空气循环固化，防止橡胶表面交联进行的不够充分。
Description
技术领域
本发明还涉及一种橡胶制品的生产方法。
背景技术
通常使用过氧化物或硫作为交联剂来交换橡胶，用过氧化物交联具有更好的耐热性、压缩变定、电绝缘性以及与有色物质混合时，着色稳定，但过氧化物交联受到氧气阻碍，因此，交联在空气中进行时，不能使橡胶表面进行的足够程度，导致过度的粘性，降低了强度，硬度不够。因此，需要提供一种新的技术方案来解决上述问题。
发明内容
本发明的目的是提供一种橡胶制品的生产方法。
本发明采用的技术方案：
一种橡胶制品的生产方法，包括以下步骤：
a、将40-50重量份的硫粉末、1-3重量份的粘土、1-3重量份的增强剂、1-3重量份的助剂和40-50重量份的水一起球磨碾磨，成悬浮液；
b、将上述悬浮液通过连续涂布机喷涂到过氧化物上，将得到的含过氧化物的橡胶制品，在热空气管式炉中加热到160-200℃，并通过足够量的氧气，以强制空气循环固化5-10分钟；
所述过氧化物为过缩酮、过酸酯或过氧化二叔丁基；
所述增强剂为炭黑；
所述助剂为氧化锌。
所述悬浮液中存在的90%硫颗粒直径低于80-100μm。
所述a步骤中的粘土为膨润土。
本发明的优点是：用过氧化物交联具有更好的耐热性、压缩变定、电绝缘性，交联时通入足量的氧气，并以强制空气循环固化，防止橡胶表面交联进行的不够充分。
具体实施方式
下述实施例仅用于说明本发明，但并不能限定本发明的保护范围。
实施例1
一种橡胶制品的生产方法，包括以下步骤：
a、将40㎏的硫粉末、1㎏的膨润土、1㎏的炭黑、1㎏的氧化锌和40㎏的水一起球磨碾磨，成悬浮液，悬浮液中存在的90%硫颗粒直径低于80μm；
b、将上述悬浮液通过连续涂布机喷涂到过缩酮上，将得到的含过氧化物的橡胶制品，在热空气管式炉中加热到160℃，并通过足够量的氧气，以强制空气循环固化5分钟。
实施例2
一种橡胶制品的生产方法，包括以下步骤：
a、将45㎏的硫粉末、2㎏的膨润土、2㎏的炭黑、2㎏的氧化锌和45㎏的水一起球磨碾磨，成悬浮液，悬浮液中存在的90%硫颗粒直径低于90μm；
b、将上述悬浮液通过连续涂布机喷涂到过酸酯上，将得到的含过氧化物的橡胶制品，在热空气管式炉中加热到180℃，并通过足够量的氧气，以强制空气循环固化7分钟。
实施例3
一种橡胶制品的生产方法，包括以下步骤：
a、将50㎏的硫粉末、3㎏的膨润土、3㎏的炭黑、3㎏的氧化锌和50㎏的水一起球磨碾磨，成悬浮液，悬浮液中存在的90%硫颗粒直径低于100μm；
b、将上述悬浮液通过连续涂布机喷涂到过氧化二叔丁基上，将得到的含过氧化物的橡胶制品，在热空气管式炉中加热到200℃，并通过足够量的氧气，以强制空气循环固化10分钟。
用过氧化物交联具有更好的耐热性、压缩变定、电绝缘性，交联时通入足量的氧气，并以强制空气循环固化，防止橡胶表面交联进行的不够充分。
Claims (3)
1.一种橡胶制品的生产方法，其特征在于，包括以下步骤：
a、将40-50重量份的硫粉末、1-3重量份的粘土、1-3重量份的增强剂、1-3重量份的助剂和40-50重量份的水一起球磨碾磨，成悬浮液；
b、将上述悬浮液通过连续涂布机喷涂到过氧化物上，将得到的含过氧化物的橡胶制品，在热空气管式炉中加热到160-200℃，并通过足够量的氧气，以强制空气循环固化5-10分钟；
所述过氧化物为过缩酮、过酸酯或过氧化二叔丁基；
所述增强剂为炭黑；
所述助剂为氧化锌。
2.根据权利要求1所述的一种橡胶制品的生产方法，其特征在于：所述悬浮液中存在的90%硫颗粒直径低于80-100μm。
3.根据权利要求1所述的一种橡胶制品的生产方法，其特征在于：所述a步骤中的粘土为膨润土。