CN103483978A - 一种砂纹状粉末涂料 - Google Patents

一种砂纹状粉末涂料 Download PDF

Info

Publication number
CN103483978A
CN103483978A CN201310393219.8A CN201310393219A CN103483978A CN 103483978 A CN103483978 A CN 103483978A CN 201310393219 A CN201310393219 A CN 201310393219A CN 103483978 A CN103483978 A CN 103483978A
Authority
CN
China
Prior art keywords
parts
powder coating
mix
raw material
add
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310393219.8A
Other languages
English (en)
Inventor
吴杰芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Single-Minded Mechanical Means Co Ltd
Original Assignee
Anhui Single-Minded Mechanical Means Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Single-Minded Mechanical Means Co Ltd filed Critical Anhui Single-Minded Mechanical Means Co Ltd
Priority to CN201310393219.8A priority Critical patent/CN103483978A/zh
Publication of CN103483978A publication Critical patent/CN103483978A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种砂纹状粉末涂料，它是由下述重量份的原料组成的：E-12环氧树脂40-50、钛白粉1-2、有机膨润土6-10、乙撑双硬脂酰胺3.7-4.8,己二酸二辛酯2-3、酒石酸钾钠1-2、柠檬酸1-2、2-硫醇基苯骈咪唑1-2、氯化锌1-2、亚磷酸双酚A酯1-2、纹理剂0.1-1、复合填料10-20；本发明涂料静电喷涂固化后其表面有砂纸的纹理,手感好,具有立体感，其涂膜稳定，耐候性强，可以起到很好的保护作用。

Description

一种砂纹状粉末涂料
技术领域
    本发明主要涉及一种涂料，尤其涉及一种砂纹状粉末涂料。
背景技术
热固型粉末涂料是指以热固性树脂作为成膜物质，加入起交联反应的固化剂经加热后能形成不溶不熔的质地坚硬涂层。温度再高该涂层也不会像热塑性涂层那样软化，而只能发生分解。由于热固性粉末涂料所采用的树脂为聚合度较低的预聚物，分子量较低，所以涂层的流平性较好，具有较好的装饰性，而且低分子量的预聚物经固化后，能形成网状交联的大分子，因而涂层具有较好防腐性和机械性能。故热固性粉末涂料发展尤为迅速，而为了提高传统粉末的整体性能，通过加入新的复合填料等来改善其性能是很有必要的。
发明内容
本发明目的就是为了提供一种砂纹状粉末涂料。
本发明是通过以下技术方案实现的：
一种砂纹状粉末涂料，其特征在于它是由下述重量份的原料组成的：
E-12环氧树脂40-50、钛白粉1-2、有机膨润土6-10、乙撑双硬脂酰胺3.7-4.8,己二酸二辛酯2-3、酒石酸钾钠1-2、柠檬酸1-2、2-硫醇基苯骈咪唑1-2、氯化锌1-2、亚磷酸双酚A 酯1-2、纹理剂0.1-1、复合填料10-20；
所述的复合填料是由下述重量份的原料组成的：
红土50-60、骨粉4-6、铁矿渣粉10-13、硅灰石粉5-7、三聚磷酸钠1-2、十二烷基三甲基氯化铵2-3、桉树油1-2；
将上述红土、铁矿渣粉、硅灰石粉混合，在600-800℃下煅烧3-4小时，冷却出料，加入桉树油，混合均匀，得预混料，将三聚磷酸钠加入到15-20倍水中，搅拌均匀后加入十二烷基三甲基氯化铵，升高温度为60-80℃，与上述预混料混合研磨，烘干，过80-100目筛，即得所述复合填料。
一种砂纹状粉末涂料的制备方法，包括以下步骤：
将上述除了纹理剂以外的各原料混合，送入到挤出机中熔融挤出，挤出的片状料冷却后,投入到粉碎机内粉碎、研磨成100-150目的粉末中间体,然后加入浮花剂，充分混合，即得所述砂纹状粉末涂料。
本发明的优点是：
    本发明涂料静电喷涂固化后其表面有砂纸的纹理,手感好,具有立体感，其涂膜稳定，耐候性强，可以起到很好的保护作用。
具体实施方式
实施例1，
一种砂纹状粉末涂料，它是由下述重量份（公斤）的原料组成的：
E-12环氧树脂50、钛白粉1、有机膨润土10、乙撑双硬脂酰胺4.8,己二酸二辛酯2、酒石酸钾钠2、柠檬酸1、2-硫醇基苯骈咪唑1、氯化锌1-2、亚磷酸双酚A 酯1、纹理剂1、复合填料20；
所述的复合填料是由下述重量份的原料组成的：
红土60、骨粉6、铁矿渣粉13、硅灰石粉7、三聚磷酸钠2、十二烷基三甲基氯化铵2、桉树油1；
将上述红土、铁矿渣粉、硅灰石粉混合，在800℃下煅烧3小时，冷却出料，加入桉树油，混合均匀，得预混料，将三聚磷酸钠加入到20倍水中，搅拌均匀后加入十二烷基三甲基氯化铵，升高温度为80℃，与上述预混料混合研磨，烘干，过100目筛，即得所述复合填料。
一种砂纹状粉末涂料的制备方法，包括以下步骤：
将上述除了纹理剂以外的各原料混合，送入到挤出机中熔融挤出，挤出的片状料冷却后,投入到粉碎机内粉碎、研磨成150目的粉末中间体,然后加入浮花剂，充分混合，即得所述砂纹状粉末涂料。
性能测试：
抗冲击性：≥50kg/cm；
硬度：2H。

Claims (2)

1.一种砂纹状粉末涂料，其特征在于它是由下述重量份的原料组成的：
E-12环氧树脂40-50、钛白粉1-2、有机膨润土6-10、乙撑双硬脂酰胺3.7-4.8,己二酸二辛酯2-3、酒石酸钾钠1-2、柠檬酸1-2、2-硫醇基苯骈咪唑1-2、氯化锌1-2、亚磷酸双酚A 酯1-2、纹理剂0.1-1、复合填料10-20；
所述的复合填料是由下述重量份的原料组成的：
红土50-60、骨粉4-6、铁矿渣粉10-13、硅灰石粉5-7、三聚磷酸钠1-2、十二烷基三甲基氯化铵2-3、桉树油1-2；
将上述红土、铁矿渣粉、硅灰石粉混合，在600-800℃下煅烧3-4小时，冷却出料，加入桉树油，混合均匀，得预混料，将三聚磷酸钠加入到15-20倍水中，搅拌均匀后加入十二烷基三甲基氯化铵，升高温度为60-80℃，与上述预混料混合研磨，烘干，过80-100目筛，即得所述复合填料。
2.一种如权利要求1所述的砂纹状粉末涂料的制备方法，其特征在于包括以下步骤：
将上述除了纹理剂以外的各原料混合，送入到挤出机中熔融挤出，挤出的片状料冷却后,投入到粉碎机内粉碎、研磨成100-150目的粉末中间体,然后加入浮花剂，充分混合，即得所述砂纹状粉末涂料。
CN201310393219.8A 2013-09-03 2013-09-03 一种砂纹状粉末涂料 Pending CN103483978A (zh)