CN102850669A - 一种改性三元乙丙橡胶及其制备方法 - Google Patents

一种改性三元乙丙橡胶及其制备方法 Download PDF

Info

Publication number
CN102850669A
CN102850669A CN2012103848263A CN201210384826A CN102850669A CN 102850669 A CN102850669 A CN 102850669A CN 2012103848263 A CN2012103848263 A CN 2012103848263A CN 201210384826 A CN201210384826 A CN 201210384826A CN 102850669 A CN102850669 A CN 102850669A
Authority
CN
China
Prior art keywords
parts
epdm
minutes
poe
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012103848263A
Other languages
English (en)
Inventor
于金花
白丽英
陆洲
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI MINGZHU CABLE CO Ltd
Original Assignee
WUXI MINGZHU CABLE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI MINGZHU CABLE CO Ltd filed Critical WUXI MINGZHU CABLE CO Ltd
Priority to CN2012103848263A priority Critical patent/CN102850669A/zh
Publication of CN102850669A publication Critical patent/CN102850669A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种具有较高机械性能的改性三元乙丙橡胶及其制备方法，该橡胶包括三元乙丙橡胶100份；POE20～24份；白油10～12份；白炭黑40～45份；硫化促进剂2.0～2.2份；促进剂1.8～2.0份；DCP0.4～0.5份；交联剂2.0～2.8份；抗氧化剂0.4～0.6份。制备方法为：先将上述重量份数的三元乙丙橡胶、POE、白油在密炼机中密炼5～6分钟，再加入白炭黑密炼8～10分钟，最后加入DM、CE、DCP、TAIC、抗氧化剂密炼2分钟后在开炼机上压片、出片，即得成品。

Description

一种改性三元乙丙橡胶及其制备方法
 
技术领域
    本发明涉及新型橡胶的合成技术领域，具体是一种改性三元乙丙橡胶及其制备方法，三元乙丙橡胶主要用于生产橡皮绝缘电线电缆的绝缘层。
背景技术
三元乙丙橡胶(EPDM)是乙烯、丙烯、第三单体共聚而成的合成橡胶，具有耐热、耐老化、耐腐蚀、体积电阻高的特性。在电线电缆行业大量应用于特种电缆的绝缘层。但现有的三元乙丙橡胶由于分子中结晶度低，因而机械强度较低，特别是应用于生产橡皮绝缘电线电缆的绝缘层时，较低的机械强度降低了电线电缆的整体性能，影响了电线电缆的使用寿命。
发明内容
   本发明所要解决的技术问题是提供一种改性三元乙丙橡胶及其制备方法，使用该方法制备的三元乙丙橡胶具有较高的机械性能。
一种改性三元乙丙橡胶，其特征在于该橡胶包括以下组份及重量份数：
三元乙丙橡胶 100份；POE（Polyolefin elastomer，聚烯烃弹性体） 20～24份；白油 10～12份；白炭黑 40～45份；硫化促进剂 2.0～2.2份；促进剂 1.8～2.0份；DCP（邻苯二甲酸二仲辛酯） 0.4～0.5份；交联剂 2.0～2.8份；抗氧化剂 0.4～0.6份。
作为改进，所述硫化促进剂优选为DM（二硫化二苯并噻唑），促进剂优选为CPE（复合型噻二唑硫化剂），交联剂优选为TAIC（三烯丙基异氰脲酸酯）。
上述改性三元乙丙橡胶的制备方法，其包括以下步骤：
先将上述重量份数的三元乙丙橡胶、POE、白油在密炼机中密炼5～6分钟，再加入白炭黑密炼8～10分钟，最后加入DM、CPE、DCP、TAIC、抗氧化剂密炼2分钟后在开炼机上压片、出片，即得成品。
本发明使用POE改性EPDM，并采用CPE（复合型噻二唑硫化剂），使POE、EPDM共同硫化，POE、乙烯、辛烯共聚物（8150）与EPDM的相容性极好，提高了EPDM的机械强度，并改善了加工性能。
表1是测试本发明的性能参数：
检测项目 检测方法 检测结果
拉伸强度MPa 拉力机 14.5
断裂伸长率% 拉力机 380
具体实施方式
   以下结合具体实施例对本发明作进一步说明。  
   实施例1：
   原料及配比（重量份数）：
三元乙丙橡胶 100份；POE(8150) 20份；白油 12份；白炭黑 40份；DM 2.2份；CPE 1.8份；DCP 0.5份；TAIC 2.0份；抗氧化剂 0.6份。其中POE(8150)拉伸强度≥15MPa，断裂伸长率≥800%。
实施工艺：
先将三元乙丙橡胶、POE、白油在密炼机中密炼5～6分钟，再加入白炭黑密炼8～10分钟，最后加入DM、CPE、DCP、TAIC、抗氧化剂密炼2分钟后在开炼机上压片、出片，即得成品。
 
实施例2：
   原料及配比（重量份数）：
三元乙丙橡胶 100份；POE(8150 )24份；白油 10份；白炭黑 45份；DM 2.0份；CPE2.0份；DCP 0.4份；TAIC 2.8份；抗氧化剂 0.4份。其中POE(8150)拉伸强度≥15MPa，断裂伸长率≥800%。
实施工艺：
先将三元乙丙橡胶、POE、白油在密炼机中密炼5～6分钟，再加入白炭黑密炼8～10分钟，最后加入DM、CPE、DCP、TAIC、抗氧化剂密炼2分钟后在开炼机上压片、出片，即得成品。
 
实施例3：
   原料及配比（重量份数）：
三元乙丙橡胶 100份；POE (8150) 22份；白油 11份；白炭黑 42份；DM 2.1份；CPE 1.9份；DCP 0.4份；TAIC 2.5份；抗氧化剂 0.5份。其中POE(8150)拉伸强度≥15MPa，断裂伸长率≥800%。
实施工艺：
先将三元乙丙橡胶、POE、白油在密炼机中密炼5～6分钟，再加入白炭黑密炼8～10分钟，最后加入DM、CPE、DCP、TAIC、抗氧化剂密炼2分钟后在开炼机上压片、出片，即得成品。
    本发明具体应用途径很多，以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明原理的前提下，还可以作出若干改进，这些改进也应视为本发明的保护范围。

Claims (5)

1.一种改性三元乙丙橡胶，其特征在于该橡胶包括以下组份及重量份数：
三元乙丙橡胶 100份；POE 20～24份；白油 10～12份；白炭黑 40～45份；硫化促进剂 2.0～2.2份；促进剂 1.8～2.0份；DCP 0.4～0.5份；交联剂 2.0～2.8份；抗氧化剂 0.4～0.6份。
2.根据权利要求1所述的改性三元乙丙橡胶，其特征在于，所述硫化促进剂为DM。
3.根据权利要求1所述的改性三元乙丙橡胶，其特征在于，所述促进剂为CPE。
4.根据权利要求1所述的改性三元乙丙橡胶，其特征在于，所述交联剂为TAIC。
5.一种权利要求1所述改性三元乙丙橡胶的制备方法，其特征在于包括以下步骤：
先将上述重量份数的三元乙丙橡胶、POE、白油在密炼机中密炼5～6分钟，再加入白炭黑密炼8～10分钟，最后加入DM、CE、DCP、TAIC、抗氧化剂密炼2分钟后在开炼机上压片、出片，即得成品。
CN2012103848263A 2012-10-12 2012-10-12 一种改性三元乙丙橡胶及其制备方法 Pending CN102850669A (zh)