CN102850632B - 一种高弹性抗菌鞋底材料的制备方法 - Google Patents
一种高弹性抗菌鞋底材料的制备方法 Download PDFInfo
- Publication number
- CN102850632B CN102850632B CN201210355721.5A CN201210355721A CN102850632B CN 102850632 B CN102850632 B CN 102850632B CN 201210355721 A CN201210355721 A CN 201210355721A CN 102850632 B CN102850632 B CN 102850632B
- Authority
- CN
- China
- Prior art keywords
- mass
- parts
- mass parts
- mixing
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种高弹性抗菌鞋底材料的制备方法，该方法的步骤如下：（1）将60-70质量份EVA、68-75质量份LDPE、7-8质量份载铜磷酸锆、6质量份银离子抗菌剂、3.5-4质量份二乙醇苯胺与3质量份硬脂酸锌在密炼机混炼均匀；（2）将步骤（1）得到的混合材料混炼到70-75℃,混炼30-35分钟；（3）往步骤（2）得到的混合材料里面加入3质量份硫黄、1.5质量份偶氮二甲酰胺和2质量份氧化锌，在130℃的温度下混炼5分钟后排料；（4）将排出的材料通过抽粒机制成颗粒状组合物，即得到所述鞋底材料。该方法制得的鞋底材料具有杀菌除臭效果明显，持续时间长，安全卫生，制备工艺简单。
Description
技术领域
本发明涉及一种高弹性抗菌鞋底材料的制备方法。
技术背景
人们在行走时，脚上的汗腺会分泌出分泌物，这些分泌物在细菌、霉菌分解下会产生异味，而在剧烈运动后，大量的出汗后尤为明显，人们想到经常换鞋垫来改善，短期内效果还可以，但是长时间还是会复发，所以这只是治标不治本的办法。而市面上销售一些抗菌鞋，是在鞋内装上杀菌或抑菌的装置，虽然有效果，但是这类鞋都是非常笨重，让人穿了不舒适。
发明内容
本发明目的是为了克服现有技术的不足，提供一种高弹性抗菌鞋底材料的制备方法，该方法制得鞋底材料杀菌除臭效果明显，持续时间长。
为解决上述问题，本发明的一个技术方案是：一种高弹性抗菌鞋底材料的制备方法，该方法的步骤如下：（1）、将60-70质量份EVA、68-75质量份LDPE、7-8质量份载铜磷酸锆、6质量份银离子抗菌剂、3.5-4质量份二乙醇苯胺与3质量份硬脂酸锌在密炼机混炼均匀；（2）、将步骤（1）得到的混合材料混炼到70-75℃,混炼30-35分钟；（3）、往步骤（2）得到的混合材料里面加入3质量份硫黄、1.5质量份偶氮二甲酰胺和2质量份氧化锌，在130℃的温度下混炼5分钟后排料；（4）、将排出的材料通过抽粒机制成颗粒状组合物，即得到所述鞋底材料。
本发明的有益效果：该方法制得的鞋底材料具有杀菌除臭效果明显，持续时间长，安全卫生，制备工艺简单。
具体实施方式
实施例1
一种高弹性抗菌鞋底材料的制备方法，该方法的步骤如下：（1）、将60-70质量份EVA、68-75质量份LDPE、7-8质量份载铜磷酸锆、6质量份银离子抗菌剂、3.5-4质量份二乙醇苯胺与3质量份硬脂酸锌在密炼机混炼均匀；（2）、将步骤（1）得到的混合材料混炼到70-75℃,混炼30-35分钟；（3）、往步骤（2）得到的混合材料里面加入3质量份硫黄、1.5质量份偶氮二甲酰胺和2质量份氧化锌，在130℃的温度下混炼5分钟后排料；（4）、将排出的材料通过抽粒机制成颗粒状组合物，即得到所述鞋底材料。对该鞋底材料的性能检测效果如下：抗菌率99.6%，交联度85%，邵氏硬度（A）51，拉伸强度/MPa：20.1，断裂伸长率/%：148。
Claims (1)
1.一种高弹性抗菌鞋底材料的制备方法，其特征在于该方法的步骤如下：（1）、将60-70质量份EVA、68-75质量份LDPE、7-8质量份载铜磷酸锆、6质量份银离子抗菌剂、3.5-4质量份二乙醇苯胺与3质量份硬脂酸锌在密炼机混炼均匀；（2）、将步骤（1）得到的混合材料混炼到70-75℃,混炼30-35分钟；（3）、往步骤（2）得到的混合材料里面加入3质量份硫黄、1.5质量份偶氮二甲酰胺和2质量份氧化锌，在130℃的温度下混炼5分钟后排料；（4）、将排出的材料通过抽粒机制成颗粒状组合物，即得到所述鞋底材料。