CN102817141A - Production method of anion tweed fabric - Google Patents
Production method of anion tweed fabric Download PDFInfo
- Publication number
- CN102817141A CN102817141A CN2012102666732A CN201210266673A CN102817141A CN 102817141 A CN102817141 A CN 102817141A CN 2012102666732 A CN2012102666732 A CN 2012102666732A CN 201210266673 A CN201210266673 A CN 201210266673A CN 102817141 A CN102817141 A CN 102817141A
- Authority
- CN
- China
- Prior art keywords
- anion
- dyeing
- temperature
- producing method
- fancy suiting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention researches and develops a production method of an anion tweed fabric. The invention provides a tweed fabric which can release anions. The production method of the anion tweed fabric comprises the following steps of: 1) spinning; 2) weaving; 3) dyeing; 4) washing; 5) crabbing and 6) drying. On the one hand, the tweed garment fabric produced by the technology can release the anions, thus being comfortable to wear, dry and cool, fit, easy to wash, fast to dry, easy-care and beneficial to human health; and on the other hand, pollutant discharge can be reduced as an environment-friendly technology and a formula are adopted during the whole production process.
Description
Technical field
[0001] the present invention relates to the face weave field, particularly a kind of anion fancy suiting fabric plus material producing method.
Background technology
[0002] production method of lining generally comprises following steps: spin, weave, move back steps such as oar, base inspection, refining and bleaching, dyeing, fixation, arrangement and typing.The Along with people's living standard improves; To the also corresponding raising of the requirement of garment material; Add Market competition; Each lining production commercial city is strengthened new lining research and development and is dropped into, and constantly has new functional fabric to be applied in recent years, passes through warm lining etc. like nano-antibacterial lining, chitosan anti-bacteria lining, waterproof.Therefore the present invention carries out improvement in functionality to existing lining under this background, promotes product specification and added value, walks the differentiation road.
Through retrieval; The patent No. is that the wet anion lining that discharges of passing through of ZL201020112234.2 relates to a kind of wet anion lining that discharges; Warp thread adopts two kinds of yarns, and wherein first is through being the polyester filament of low twist, and second is through being the low twist compound silk that low-elasticity terylene fibre and viscose are formed; Weft yarn adopts two kinds of yarns; The first latitude is the terylene negative-ion fiber of low twist, and the second latitude is the low twist composite yarn that high moisture adsorption and releasing polyurethane fiber and artificial cotton are formed, and orthogonal the weaving of warp thread and weft yarn forms; The density of warp thread is 450/10cm, and the density of weft yarn is 310/10cm.
Summary of the invention
The present invention has researched and developed a kind of anion fancy suiting fabric plus material producing method, and purpose is: a kind of fancy suiting lining that can discharge anion is provided.
This technical scheme:
A kind of anion fancy suiting fabric plus material producing method comprises the steps:
1), spinning: 25 ℃ of temperature, under the relative humidity 75rh constant temperature and humidity condition 20% charing hair, 60% negative-ion fiber being become fineness with 20% sticking short fiber blending is 11 public yarns;
2), weave:, under the relative humidity 75 rh constant temperature and humidity conditions blended yarn is passed through the woven acquisition grey cloth of Rapier looms 25 ℃ of temperature;
3), dyeing: anion fancy suiting grey cloth adopts loose stock dyeing; Wool fibre is contaminated in REACTIVE DYES and acid mordant dye, and auxiliary agent is the low-temp dyeing accelerant of 1.5～2.5%o.w.f, and bath raio is 1:20; Dyeing temperature is 85～95 ℃, and dyeing time is 35～45 minutes;
4), braying: the grey cloth after will dyeing carries out braying to be handled, and 40 ℃ of temperature are washed in braying, and time 10min washes speed 280m/min, time 30min at a high speed;
5), crabbing: the grey cloth after will dyeing is washed crabbing and is handled; 80 ℃ of temperature, 40 minutes time, middle tension force, pressure 1.4Mpa adds acetate, and machine cools off outward, bath raio 1:8, interpolation 0.5% anti-staining agent;
6), oven dry: the grey cloth after the crabbing is dried processing, 130 ℃ of temperature, 40 meters/minute of the speed of a motor vehicle, overfeeding 101%.
The said machine of weaving in the step is through close 160/10cm, 162/10cm of last machine filling density, and last gate width of cloth 176cm, warping coupe 80m, porter: 80, every reed penetrates several 2,2804 of total quantity of warps.
It is said that to weave Rapier looms model in the step be the two electric Picanol Rapier looms that Suzhou Picanol Textile Machinery Co., Ltd produces.
The orchid that REACTIVE DYES contain 2.1～3.1%o.w.f in the said staining procedure receives the orchid of plain red GE, 2.7～3.7%o.w.f and receives the orchid of plain red GN and 0.011%o.w.f and receive plain blue 3G.
Mordant dyes contain the media Huang of 0.44%o.w.f, the Mordant Black of 3～4%o.w.f, the medium red of 0.05～0.15%o.w.f in the said staining procedure.
Dolly is the N113A type rope-form washing dolly that the positive forever machinery plant of Wuxi City produces in the said braying step.
The invention has the beneficial effects as follows: the fancy suiting garment material through this explained hereafter can discharge anion on the one hand; Comfortable and easy to wear, dry and comfortable, very fit, be prone to wash, do soon, non-ironing; Be of value to health; Because whole process of production adopts environment-protective process and prescription, can reduce pollutant emission in addition.
The specific embodiment
Below in conjunction with embodiment the present invention is described further.
Embodiment one:
A kind of anion fancy suiting fabric plus material producing method comprises the steps:
1), spinning: 25 ℃ of temperature, under the relative humidity 75 rh constant temperature and humidity conditions 20% charing hair, 60% negative-ion fiber being become fineness with 20% sticking short fiber blending is 11 public yarns;
2), weave: 25 ℃ of temperature, with the two electric Picanol Rapier looms woven acquisition grey cloth of blended yarn through the production of Suzhou Picanol Textile Machinery Co., Ltd, machine is through close 160/10cm on the Rapier looms under the relative humidity 75 rh constant temperature and humidity conditions; 162/10cm of last machine filling density; Last gate width of cloth 176cm, warping coupe 80m, porter: 80; Every reed penetrates several 2,2804 of total quantity of warps;
3), dyeing: anion fancy suiting grey cloth adopts loose stock dyeing, and wool fibre is contaminated in REACTIVE DYES and acid mordant dye: the orchid that REACTIVE DYES contain 2.1%o.w.f receives the orchid of plain red GE, 2.7%o.w.f and receives the orchid of plain red GN and 0.011%o.w.f and receive plain blue 3G; Mordant dyes contain the media Huang of 0.44%o.w.f, the Mordant Black of 3%o.w.f, the medium red of 0.05%o.w.f; Auxiliary agent is the low-temp dyeing accelerant of 1.5%o.w.f, and bath raio is 1:20, and dyeing temperature is 85 ℃, and dyeing time is 35 minutes;
4), braying: the N113A type rope-form washing dolly that the grey cloth after will dyeing is produced with the positive forever machinery plant of Wuxi City carries out braying to be handled, and 40 ℃ of temperature are washed in braying, and time 10min washes speed 280m/min, time 30min at a high speed;
5), crabbing: the grey cloth after will dyeing is washed crabbing and is handled; 80 ℃ of temperature, 40 minutes time, middle tension force, pressure 1.4Mpa adds acetate, and machine cools off outward, bath raio 1:8, interpolation 0.5% anti-staining agent.
6), oven dry: the grey cloth after the crabbing is dried processing, 130 ℃ of temperature, 40 meters/minute of the speed of a motor vehicle, overfeeding 101%.
Embodiment two:
A kind of anion fancy suiting fabric plus material producing method comprises the steps:
1), spinning: 25 ℃ of temperature, under the relative humidity 75 rh constant temperature and humidity conditions 20% charing hair, 60% negative-ion fiber being become fineness with 20% sticking short fiber blending is 11 public yarns;
2), weave: 25 ℃ of temperature, with the two electric Picanol Rapier looms woven acquisition grey cloth of blended yarn through the production of Suzhou Picanol Textile Machinery Co., Ltd, machine is through close 160/10cm on the Rapier looms under the relative humidity 75 rh constant temperature and humidity conditions; 162/10cm of last machine filling density; Last gate width of cloth 176cm, warping coupe 80m, porter: 80; Every reed penetrates several 2,2804 of total quantity of warps;
3), dyeing: anion fancy suiting grey cloth adopts loose stock dyeing, and wool fibre is contaminated in REACTIVE DYES and acid mordant dye: the orchid that REACTIVE DYES contain 3.1%o.w.f receives the orchid of plain red GE, 3.7%o.w.f and receives the orchid of plain red GN and 0.011%o.w.f and receive plain blue 3G; Mordant dyes contain the media Huang of 0.44%o.w.f, the Mordant Black of 4%o.w.f, the medium red of 0.15%o.w.f; Auxiliary agent is the low-temp dyeing accelerant of 2.5%o.w.f, and bath raio is 1:20, and dyeing temperature is 95 ℃, and dyeing time is 45 minutes;
4), braying: the N113A type rope-form washing dolly that the grey cloth after will dyeing is produced with the positive forever machinery plant of Wuxi City carries out braying to be handled, and 40 ℃ of temperature are washed in braying, and time 10min washes speed 280m/min, time 30min at a high speed;
5), crabbing: the grey cloth after will dyeing is washed crabbing and is handled; 80 ℃ of temperature, 40 minutes time, middle tension force, pressure 1.4Mpa adds acetate, and machine cools off outward, bath raio 1:8, interpolation 0.5% anti-staining agent;
6), oven dry: the grey cloth after the crabbing is dried processing, 130 ℃ of temperature, 40 meters/minute of the speed of a motor vehicle, overfeeding 101%.
Claims (6)
1. an anion fancy suiting fabric plus material producing method comprises the steps:
1), spinning: 25 ℃ of temperature, under the relative humidity 75rh constant temperature and humidity condition 20% charing hair, 60% negative-ion fiber being become fineness with 20% sticking short fiber blending is 11 public yarns;
2), weave:, under the relative humidity 75 rh constant temperature and humidity conditions blended yarn is passed through the woven acquisition grey cloth of Rapier looms 25 ℃ of temperature;
3), dyeing: anion fancy suiting grey cloth adopts loose stock dyeing; Wool fibre is contaminated in REACTIVE DYES and acid mordant dye, and auxiliary agent is the low-temp dyeing accelerant of 1.5～2.5%o.w.f, and bath raio is 1:20; Dyeing temperature is 85～95 ℃, and dyeing time is 35～45 minutes;
4), braying: the grey cloth after will dyeing carries out braying to be handled, and 40 ℃ of temperature are washed in braying, and time 10min washes speed 280m/min, time 30min at a high speed;
5), crabbing: the grey cloth after will dyeing is washed crabbing and is handled; 80 ℃ of temperature, 40 minutes time, middle tension force, pressure 1.4Mpa adds acetate, and machine cools off outward, bath raio 1:8, interpolation 0.5% anti-staining agent;
6), oven dry: the grey cloth after the crabbing is dried processing, 130 ℃ of temperature, 40 meters/minute of the speed of a motor vehicle, overfeeding 101%.
2. a kind of anion fancy suiting fabric plus material producing method according to claim 1 is characterized in that: the said machine of weaving in the step is through close 160/10cm, 162/10cm of last machine filling density; Last gate width of cloth 176cm, warping coupe 80m, porter: 80; Every reed penetrates several 2,2804 of total quantity of warps.
3. a kind of anion fancy suiting fabric plus material producing method according to claim 1 is characterized in that: said to weave Rapier looms model in the step be the two electric Picanol Rapier looms that Suzhou Picanol Textile Machinery Co., Ltd produces.
4. a kind of anion fancy suiting fabric plus material producing method according to claim 1 is characterized in that: the orchid that REACTIVE DYES contain 2.1～3.1%o.w.f in the said staining procedure receives the orchid of plain red GE, 2.7～3.7%o.w.f and receives the orchid of plain red GN and 0.011%o.w.f and receive plain blue 3G.
5. a kind of anion fancy suiting fabric plus material producing method according to claim 1 is characterized in that: mordant dyes contain the media Huang of 0.44%o.w.f, the Mordant Black of 3～4%o.w.f, the medium red of 0.05～0.15%o.w.f in the said staining procedure.
6. a kind of anion fancy suiting fabric plus material producing method according to claim 1 is characterized in that: dolly is the N113A type rope-form washing dolly that the positive forever machinery plant of Wuxi City produces in the said braying step.