CN102747198B - 金属冲压模具表面硬化加工工艺 - Google Patents

金属冲压模具表面硬化加工工艺 Download PDF

Info

Publication number
CN102747198B
CN102747198B CN201210271078.8A CN201210271078A CN102747198B CN 102747198 B CN102747198 B CN 102747198B CN 201210271078 A CN201210271078 A CN 201210271078A CN 102747198 B CN102747198 B CN 102747198B
Authority
CN
China
Prior art keywords
stamping die
metal stamping
hardening process
absorbing coating
surface hardening
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201210271078.8A
Other languages
English (en)
Other versions
CN102747198A (zh
Inventor
陈振丰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chongqing Chuanglong Industry Co Ltd
Original Assignee
Chongqing Chuanglong Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chongqing Chuanglong Industry Co Ltd filed Critical Chongqing Chuanglong Industry Co Ltd
Priority to CN201210271078.8A priority Critical patent/CN102747198B/zh
Publication of CN102747198A publication Critical patent/CN102747198A/zh
Application granted granted Critical
Publication of CN102747198B publication Critical patent/CN102747198B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种模具成型工艺，具体涉及一种金属冲压模具的表面硬化加工工艺；包括有如下步骤：1）对金属冲压模具表面进行抛光；2）去除金属冲压模具表面油污；3）将二氧化硅吸光涂料均匀地涂在金属冲压模具表面，控制厚度在0.04～0.08mm，二氧化硅吸光涂料中添加有质量配比为5%的镍基合金粉、1%的WC和1%的TiC混合物；4）干燥步骤3）得到的金属冲压模具；5）采用二氧化碳激光束快速扫描步骤4）中得到的金属冲压模具的表面，保持激光功率P=2800～4000W，光斑直径8～15mm，扫描速度V=4～6m/min；经测试表明，采用本发明的硬化加工工艺，可以提高金属冲压模具表面的耐磨性和硬度，降低修磨时间和次数，进而降低使用成本。

Description

金属冲压模具表面硬化加工工艺
技术领域
本发明涉及一种模具成型工艺，具体涉及一种金属冲压模具的表面硬化加工工艺。  
背景技术
汽车大型覆盖件通常通过冲压形成，冲压模具是汽车生产的关键性工艺装备，由于其结构尺寸大，模具型面形状复杂，尺寸精度和表面质量要求高，因此模具制造周期长，成本高。汽车覆盖件冲压模具在使用过程中，要承受强烈的摩擦、径向应力及压缩应力，因此非常容易发生尺寸磨损和表面产生沟槽的报废状况，可见汽车覆盖件冲压模具对硬度和耐磨性要求较高。
发明内容
本发明要解决的技术问题是提供一种可以提高金属冲压模具的耐磨性和硬度的硬化加工工艺。
为了实现上述目的，本发明提供一种金属冲压模具表面硬化加工工艺，包括有如下步骤：
1）采用金相砂纸和绒布对金属冲压模具表面进行抛光；
2）采用清洗剂去除金属冲压模具表面的油污；
3）将二氧化硅吸光涂料均匀地涂在金属冲压模具表面，控制厚度在0.04～0.08mm，二氧化硅吸光涂料中添加有质量配比为5%的镍基合金粉、1%的WC和 1%的TiC混合物；
4）干燥步骤3）得到的金属冲压模具；
5）采用二氧化碳激光束快速扫描步骤4）中得到的金属冲压模具的表面，保持激光功率P=2800～4000W，光斑直径8～15mm，扫描速度V=4～6m/min。
作为优选方案，经多次实验发现在步骤5）中，保持激光功率P=3200W，光斑直径12mm，扫描速度V=5m/min时，金属冲压模具表面硬化效果最好。
经实验验证，采用本发明技术方案的高强度板材热冲压保护涂料具有如下优点：金属冲压模具表面涂抹的0.04～0.08mm厚添加有质量配比为5%的镍基合金粉、1%的WC和 1%的TiC混合物的二氧化硅吸光涂料，经激光扫描后，表面硬度达到HV0.31000左右；激光扫描硬化后的金属冲压模具表面耐磨性、光洁度和尺寸精度都有所提高，大大降低修磨时间和次数，降低使用成本。
具体实施方式   
本发明实施例提供一种金属冲压模具表面硬化加工工艺，包括有如下步骤：
1）采用金相砂纸和绒布先后对金属冲压模具表面进行抛光；
2）采用清洗剂去除金属冲压模具表面的粉末和油污；
3）将二氧化硅吸光涂料均匀地涂在金属冲压模具表面，控制涂抹厚度在0.06mm左右，二氧化硅吸光涂料中添加有质量配比为5%的镍基合金粉、1%的WC和 1%的TiC混合物；
4）阴凉风干步骤3）得到的金属冲压模具，使二氧化硅吸光涂料形成均匀的薄膜；
5）采用二氧化碳激光束快速扫描步骤4）中得到的金属冲压模具的表面，保持激光功率P=3200W，光斑直径12mm，扫描速度V=5m/min时，金属冲压模具表面硬化效果最好。
经实验验证，采用本发明技术方案的高强度板材热冲压保护涂料具有如下优点：金属冲压模具表面涂抹的0.06mm厚添加有质量配比为5%的镍基合金粉、1%的WC和 1%的TiC混合物的二氧化硅吸光涂料，经激光扫描后，表面硬度达到HV0.31000以上；激光扫描硬化后的金属冲压模具表面耐磨性、光洁度和尺寸精度都有所提高，大大降低修磨时间和次数，降低使用成本。
以上所述的仅是本发明的部分优选实施方式，应当指出，对于本领域的技术人员来说，在不脱离本发明组分及配比的前提下，还可以作出若干改进，这些也应该视为本发明的保护范围。

Claims (2)

1.金属冲压模具表面硬化加工工艺，其特征在于包括有如下步骤：
1）采用金相砂纸和绒布对金属冲压模具表面进行抛光；
2）采用清洗剂去除金属冲压模具表面的油污；
3）将二氧化硅吸光涂料均匀地涂在金属冲压模具表面，控制厚度在0.04～0.08mm，二氧化硅吸光涂料中添加有质量配比为5%的镍基合金粉、1%的WC和 1%的TiC混合物；
4）干燥步骤3）得到的金属冲压模具；
5）采用二氧化碳激光束快速扫描步骤4）中得到的金属冲压模具的表面，保持激光功率P=2800～4000W，光斑直径8～15mm，扫描速度V=4～6m/min。
2.根据权利要求1所述的金属冲压模具表面硬化加工工艺，其特征在于:步骤5）中，保持激光功率P=3200W，光斑直径12mm，扫描速度V=5m/min。
CN201210271078.8A 2012-07-31 2012-07-31 金属冲压模具表面硬化加工工艺 Active CN102747198B (zh)