CN102716900A - 一种酸洗钢带报废闪光焊机电极的回收利用方法 - Google Patents
一种酸洗钢带报废闪光焊机电极的回收利用方法 Download PDFInfo
- Publication number
- CN102716900A CN102716900A CN2012102263055A CN201210226305A CN102716900A CN 102716900 A CN102716900 A CN 102716900A CN 2012102263055 A CN2012102263055 A CN 2012102263055A CN 201210226305 A CN201210226305 A CN 201210226305A CN 102716900 A CN102716900 A CN 102716900A
- Authority
- CN
- China
- Prior art keywords
- electrode
- flash welder
- flash
- gaskets
- welder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种酸洗钢带报废闪光焊机电极的回收利用方法，技术方案是：包含如下步骤：A用金属切割机将报废的闪光焊机电极加工成若干个垫片（2），垫片的截面平行于闪光焊机电极的焊接面；B将垫片（2）进行磨削抛光；C在磨削抛光后的垫片（2）上钻成螺栓孔（3），位置与闪光焊机电极（1）的螺栓相对应；D将垫片（2）放在闪光焊机电极的非焊接面上，垫片的厚度与闪光焊机电极的磨损相适应，使用螺栓将闪光焊机电极与垫片固定，然后一起固定在闪光焊机上；E将闪光焊机电极压住待焊接的钢带（4）进行焊接。本发明的积极效果是：回收利用了已经报废的闪光焊机电极，节约了采购新电极的费用，降低了生产成本，同时提高了焊接质量。
Description
技术领域
本发明专利涉及一种酸洗钢带报废焊机电极的回收利用方法，特别适用于冷轧酸洗钢带闪光焊机电极的回收利用方法。
背景技术
在冷轧连续式酸洗线有一个重要的设备就是焊机，尤其是闪光焊机，它的主要作用就是把展开以后的热轧卷进行头尾焊接成为一条不间断的钢带，进而保证连续式酸洗和轧机的连续式生产。闪光焊机电极是焊机上一个重要的零部件，它在焊接过程中起到压紧带钢进行对中以及导电焊接的作用。在实际的使用过程中，由于电极的材质是铜，因此与带钢接触摩擦的过程中磨损较快，会给焊接和生产造成一连串的问题：1、闪光焊机电极磨损快，焊接时电极压不紧带钢给对中和焊接带来困难。2、磨损严重后的电极由于接触面积不光滑易造成焊接电流不稳影响焊缝质量。3、磨损严重的电极会出现焊接位降低，严重影响焊接质量。鉴于上面三点，根据闪光焊机电极的磨损程度，一部分进行报废处理，另一部分磨削抛光后继续使用。
发明内容
本发明专利的目的是提供一种酸洗钢带报废闪光焊机电极的回收利用方法，将报废的闪光焊机电极加工后作为垫片使用，解决背景技术中存在的上述问题。
本发明的技术方案为：
一种酸洗钢带报废闪光焊机电极的回收利用方法，包含如下步骤：
A用金属切割机将报废的闪光焊机电极加工成若干个垫片，垫片的截面平行于闪光焊机电极的焊接面；
B将垫片进行磨削抛光；
C在磨削抛光后的垫片上钻螺栓孔，位置与闪光焊机电极的螺栓相对应；
D将垫片放在闪光焊机电极的非焊接面上，垫片的厚度与闪光焊机电极的磨损相适应，使用螺栓将闪光焊机电极与垫片固定，然后一起固定在闪光焊机上；
E将闪光焊机电极压住待焊接的钢带进行焊接。
本发明的积极效果是：回收利用了已经报废的闪光焊机电极，节约了采购新电极的费用，降低了生产成本，同时提高了焊接质量，避免了由于焊缝质量差在焊缝过轧机时出现断带的问题。
附图说明
附图1为本发明专利实施例的结构示意图；
图中：1.闪光焊机电极、2.垫片、3.螺栓孔、4.带焊焊接的钢带。
具体实施方式
下面通过实施例对本发明做进一步说明。
以下结合附图，通过实施例对本发明专利作进一步说明。
一种酸洗钢带报废闪光焊机电极的回收利用方法，包含如下步骤：
A用金属切割机将报废的闪光焊机电极加工成若干个垫片（2），垫片的截面平行于闪光焊机电极的焊接面；
B将垫片（2）进行磨削抛光；
C在磨削抛光后的垫片（2）上钻两个螺栓孔（3），位置与闪光焊机电极的螺栓相对应；
D将垫片放在闪光焊机电极的非焊接面上，垫片的厚度与闪光焊机电极的磨损相适应，使用螺栓将闪光焊机电极与垫片固定，然后一起固定在闪光焊机上；
E将闪光焊机电极压住待焊接的钢带（4）进行焊接。
Claims (1)
1.一种酸洗钢带报废闪光焊机电极的回收利用方法，其特征在于包含如下步骤：
A用金属切割机将报废的闪光焊机电极加工成若干个垫片（2），垫片的截面平行于闪光焊机电极的焊接面；
B将垫片（2）进行磨削抛光；
C在磨削抛光后的垫片（2）上钻成螺栓孔（3），位置与闪光焊机电极（1）的螺栓相对应；
D将垫片（2）放在闪光焊机电极的非焊接面上，垫片的厚度与闪光焊机电极的磨损相适应，使用螺栓将闪光焊机电极与垫片固定，然后一起固定在闪光焊机上；
E将闪光焊机电极压住待焊接的钢带（4）进行焊接。