CN102702870A - Water-based marking paint and preparation method thereof - Google Patents
Water-based marking paint and preparation method thereof Download PDFInfo
- Publication number
- CN102702870A CN102702870A CN2012101526087A CN201210152608A CN102702870A CN 102702870 A CN102702870 A CN 102702870A CN 2012101526087 A CN2012101526087 A CN 2012101526087A CN 201210152608 A CN201210152608 A CN 201210152608A CN 102702870 A CN102702870 A CN 102702870A
- Authority
- CN
- China
- Prior art keywords
- water
- parts
- marking paint
- based marking
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a water-based marking paint which comprises the following components in parts by weight: 300-500 parts of water-based emulsion, 15-25 parts of industrial alcohol, 5-15 parts of titanium white, 200-350 parts of coarse whiting, 5-15 parts of glass bead, 5-15 parts of film-forming assistant, 1-2 parts of defoaming agent, 0.5-1.5 parts of wetting agent, 1.0-2.5 parts of dispersant, 0.5-1.0 part of pH regulator, 0.5-1.5 parts of thickening agent and 10-20 parts of water. The water-based marking paint disclosed by the invention uses water as the dispersion medium, thus, is safe and environment-friendly, and does not need heating in the construction process; and the water-based marking paint has the characteristics of favorable wear resistance, weather resistance, rain water resistance, acid resistance, alkali resistance and the like.
Description
Technical field
The present invention relates to a kind of marking paint, relate to a kind of reflection type water-based marking paint and preparation method thereof specifically.
Background technology
At present; Domestic marking paint is mainly thermoplastic solvent-borne type marking paint, and construction process needs special heating installation, the big potential safety hazard that exists of difficulty of construction; And solvent type marking paint is a large amount of VOC objectionable impurities of meeting volatilization in drying process, and surrounding environment is caused very big pollution.
Summary of the invention
Technical problem to be solved by this invention just provides a kind of constructing operation is simple and safe and VOC content is the extremely low water-based marking paint and the preparation method of this water-based marking paint.
The present invention adopts following technical scheme:
A kind of water-based marking paint comprises the composition of following weight content: water-based emulsion 300-500 part, industrial alcohol 15-25 part, white titanium pigment 5-15 part; Coarse whiting 200-350 part, granulated glass sphere 5-15 part, film coalescence aid 5-15 part; Skimmer 1-2 part, wetting agent 0.5-1.5 part, dispersion agent 1.0-2.5 part; PH regulator 0.5-1.0 part, thickening material 0.5-1.5 part, water 10-20 part; Promptly being base-material with the water-based emulsion, is main stuffing with white titanium pigment, granulated glass sphere, coarse whiting, adds an amount of aqueous paint additive and water and processes.
Further, described water-based emulsion is one or more in phenylpropionic acid emulsion, pure-acrylic emulsion, the polyaminoester emulsion, and its solid content is 50%-60%.
Further, the granularity of described white titanium pigment is 800 orders-2500 orders.
Further, the granularity of described coarse whiting is 800 orders-2000 orders.
Further, the granularity of described granulated glass sphere is the 20-80 order.
A kind of preparation method of above-mentioned water-based marking paint comprises the steps:
(1) successively with water-based emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.
The invention has the beneficial effects as follows:
The disclosed water-based marking paint of the present invention is dispersion medium with water, and safety and environmental protection, construction process need not heating; Have characteristics such as good wear-resisting, weather-proof, anti-rainwater, acid and alkali-resistance.
Be used for highway pavement to the disclosed water-based marking paint of the present invention and execute when drawing the vehicle lines, can directly spray or the roller coating moulding, easy construction, rapidly dry, surface drying 15 minutes was done solid work 30 minutes; Paint film is good to pitch and concrete road surface sticking power, and shock resistance is difficult for phenomenons such as producing variable color, chap and peel off.
Embodiment
In order to make the object of the invention, technical scheme and advantage clearer,, the present invention is further elaborated below in conjunction with embodiment.Should be appreciated that specific embodiment described herein only in order to explanation the present invention, and be not used in qualification the present invention.
Embodiment 1, and present embodiment discloses a kind of water-based marking paint, comprises the composition of following weight content: 300 parts of pure-acrylic emulsions, 15 parts of industrial alcohols; 5 parts of 2000 order white titanium pigments, 350 parts of 800 order coarse whitings, 10 parts of 20 order granulated glass spherees, 5 parts of film coalescence aid; 1 part of skimmer, 0.5 part of wetting agent, 1.5 parts of dispersion agents; 0.5 part of PH regulator, 1.5 parts of thickening materials, 10 parts in water.
Present embodiment also discloses the method for preparing above-mentioned water-based marking paint, may further comprise the steps:
(1) successively with pure-acrylic emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.
Embodiment 2, and present embodiment discloses a kind of water-based marking paint, comprise the composition of following weight content: 200 parts of phenylpropionic acid emulsions, 300 parts of polyaminoester emulsions, 20 parts of industrial alcohols; 15 parts of 800 order white titanium pigments, 200 parts of 2000 order coarse whitings, 15 parts of 40 order granulated glass spherees, 15 parts of film coalescence aid; 2 parts of skimmers, 1.5 parts of wetting agents, 2.5 parts of dispersion agents; 1.0 parts of PH regulators, 0.5 part of thickening material, 20 parts in water.
Present embodiment also discloses the method for preparing above-mentioned water-based marking paint, may further comprise the steps:
(1) successively with phenylpropionic acid emulsion, polyaminoester emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.
Embodiment 3, and present embodiment discloses a kind of water-based marking paint, comprise the composition of following weight content: 200 parts of pure-acrylic emulsions, 200 parts of phenylpropionic acid emulsions; 25 parts of industrial alcohols, 10 parts of 2500 order white titanium pigments, 200 parts of 1250 order coarse whitings, 5 parts of 80 order granulated glass spherees; 8 parts of film coalescence aid, 1 part of skimmer, 1 part of wetting agent, 2.5 parts of dispersion agents; 0.5 part of PH regulator, 0.5 part of thickening material, 16 parts in water.
Present embodiment also discloses the method for preparing above-mentioned water-based marking paint, may further comprise the steps:
(1) successively with pure-acrylic emulsion, phenylpropionic acid emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.
Embodiment 4, and present embodiment discloses a kind of water-based marking paint, comprise the composition of following weight content: 200 parts of pure-acrylic emulsions, 100 parts of phenylpropionic acid emulsions; 200 parts of polyaminoester emulsions, 20 parts of industrial alcohols, 5 parts of 1250 order white titanium pigments, 350 parts of 2000 order coarse whitings; 10 parts of 60 order granulated glass spherees, 5 parts of film coalescence aid, 1.5 parts of skimmers, 0.5 part of wetting agent; 2 parts of dispersion agents, 0.5 part of PH regulator, 1.0 parts of thickening materials, 10 parts in water.
Present embodiment also discloses the method for preparing above-mentioned water-based marking paint, may further comprise the steps:
(1) successively with pure-acrylic emulsion, phenylpropionic acid emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.
Embodiment 5, and present embodiment discloses a kind of water-based marking paint, comprise the composition of following weight content: 400 parts of polyaminoester emulsions, 15 parts of industrial alcohols; 15 parts of 1250 order white titanium pigments, 200 parts of 2000 order coarse whitings, 15 parts of 20 order granulated glass spherees, 8 parts of film coalescence aid; 1.0 parts of skimmers, 0.5 part of wetting agent, 2.5 parts of dispersion agents; 1.0 parts of PH regulators, 0.5 part of thickening material, 20 parts in water.
Present embodiment also discloses the method for preparing above-mentioned water-based marking paint, may further comprise the steps:
(1) successively with polyaminoester emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.
Claims (6)
1. a water-based marking paint is characterized in that, comprises the composition of following weight content: water-based emulsion 300-500 part, industrial alcohol 15-25 part; White titanium pigment 5-15 part, coarse whiting 200-350 part, granulated glass sphere 5-15 part, film coalescence aid 5-15 part; Skimmer 1-2 part, wetting agent 0.5-1.5 part, dispersion agent 1.0-2.5 part; PH regulator 0.5-1.0 part, thickening material 0.5-1.5 part, water 10-20 part.
2. water-based marking paint according to claim 1 is characterized in that: described water-based emulsion is one or more in phenylpropionic acid emulsion, pure-acrylic emulsion, the polyaminoester emulsion, and its solid content is 50%-60%.
3. water-based marking paint according to claim 1 is characterized in that: the granularity of described white titanium pigment is 800 orders-2500 orders.
4. water-based marking paint according to claim 1 is characterized in that: the granularity of described coarse whiting is 800 orders-2000 orders.
5. water-based marking paint according to claim 1 is characterized in that: the granularity of described granulated glass sphere is the 20-80 order.
6. the preparation method of the described water-based marking paint of claim 1 is characterized in that, comprises the steps:
(1) successively with water-based emulsion, wetting agent, dispersion agent, dispersed with stirring was even in the middle of 1/2 skimmer, 1/2 water joined scuffing of cylinder bore;
(2) white titanium pigment, coarse whiting are joined in the mixed solution that makes in the above-mentioned steps (1), dispersion grinding is even;
(3) 1/2 skimmer, 1/2 water, industrial alcohol, PH regulator, granulated glass sphere are joined in the slurry that step (2) makes, add film coalescence aid again, add thickening material at last and regulate viscosity.