CN102702854A - 超耐候性外用彩色水性油墨 - Google Patents
超耐候性外用彩色水性油墨 Download PDFInfo
- Publication number
- CN102702854A CN102702854A CN201210220431XA CN201210220431A CN102702854A CN 102702854 A CN102702854 A CN 102702854A CN 201210220431X A CN201210220431X A CN 201210220431XA CN 201210220431 A CN201210220431 A CN 201210220431A CN 102702854 A CN102702854 A CN 102702854A
- Authority
- CN
- China
- Prior art keywords
- water
- color
- super
- base material
- standard base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种超耐候性外用彩色水性油墨,该油墨由水性标准基础料和水性油墨色浆混合而成,所述水性标准基础料由下述组分组成:水、助溶剂、纯丙乳液树脂、金红石型钛白、800目重钙、1200目重钙、高岭土、分散剂、润湿剂、消泡剂、防霉剂、成膜助剂、增稠剂、氨水;所述水性色浆为占水性标准基础料重量的0.15%的吡咯红,其国际颜料索引号为PR254;还有占水性标准基础料重量的1.40%的喹啉黄,其国际颜料索引号为PY154。本发明可以最大限度保证所调水性油墨颜色的耐候性及准确性。
Description
技术领域
一种外用型彩色水性油墨,特别是超耐候性外用彩色水性油墨,由水性标准基础料和水性油墨色浆组成。
背景技术
随着我国数字印刷业的迅猛发展和人民生活水平的不断提高,人们对户外环境用色彩的性能有了新的要求,对户外用色彩要求也越来越高。作为一种新型的绿色环保型油墨,水性彩色油墨因具有健康、环保及色彩多样化等优点,而普遍得到人们的青睐,且广泛应用于户外应用的装饰,在最近几年还得到了很大的发展。但是,目前水性油墨特别是外用水性油墨在应用中还存在着许多不足之处,主要表现在褪色、变色、粉化等,出现这些弊病,一方面与当前我国水性油墨的生产技术水平以及所用原材料品质有关,另一方面也与颜色研究的滞后有关。
颜料作为水性彩色油墨的重要组成部分,主要起着遮盖、装饰和保护的作用,并对油墨漆膜的耐候、耐水、耐碱、耐洗刷及抗污染等有着重要的影响。随着水性油墨的发展和完善,单纯的单一油墨已经逐渐成为一种半成品,尤其是用于彩色装饰时,色彩丰富的水性油墨越来越受到人们的喜爱。高保色性不同的颜色搭配不仅可以满足人们个性化设计要求,实现环境对产品性能的要求,而且还能够实现生产厂家快速生产销售、提高效率品质的目的。
随着色彩设计的普及,人们对色彩的要求越来越高,颜色多样化,高保色性已经广泛应用于户外设计的工程中,由于其良好的色彩效果和环保的经济性普遍受到人们赞誉。但是,由于没有专业的水性油墨的标准色彩对应,导致调色的颜色准确性差,不能达到人们所期望的色彩效果,同时,不合理的选用色浆还有可能造成漆膜发生严重褪色、变色等问题。
发明内容
为了避免户外用彩色水性油墨出现变色、褪色、颜色差异等质量问题的产生,满足色彩保色性的要求,本发明所要解决的技术问题是提供一种超耐候性外用彩色水性油墨的配方,即通过在特定的水性标准基础料中按比例添加不同种类颜色的色浆,经过调色、搅拌均匀后,使制备的超耐候性外用彩色水性油墨的颜色与专用标准色彩的色卡相比,有效保障两者之间的色差,且所调颜色的耐候性和准确性也得到了一定的保证。
本发明解决所述技术问题的技术方案为:
一种超耐候性外用彩色水性油墨,由水性标准基础料和水性油墨色浆混合而成,所述水性标准基础料按质量百分比计由下述组分组成:15-24.2%的水、3-3.8%的助溶剂、34-40%的纯丙烯酸乳液树脂、12-15%的金红石型钛白、15-20%的800目重钙、 5-8%的1200目重钙、3-5%的高岭土、1.2-1.8%的分散剂、0.1-0.15%的润湿剂、0.2-0.3%的消泡剂、0.1-0.15%的防霉剂、1.6-2.0%的成膜助剂、0.50-0.60%的增稠剂、0.1-0.18%的氨水。
所述水性油墨色浆为占水性标准基础料重量的0.15%的吡咯红(国际颜料索引号为PR254)、1.0%的喹啉黄(国际颜料索引号PY154)。
进一步的,所述助溶剂是保湿剂;分散剂选自聚电介质疏水性分散剂;润湿剂选自改性聚氧乙烯醚类润湿剂;消泡剂选自脂肪烃类消泡剂;防霉剂选自含氮杂环化合物防霉剂,成膜助剂选自醇脂类成膜助剂;增稠剂选自羟乙基类增稠剂。
本发明所述的超耐候性外用彩色水性油墨,其中所采用的色浆PR254是吡咯红,其1/25耐候性为4~5级,颜料含量为33%;PY154是喹啉黄,其1/25耐候性为5级,颜料含量为38%。
本发明除了应用耐候性优良的颜料,还经过了大量的实验研究和数据分析,对其它各种助剂进行组合搭配,保证了产品的整体的耐候性。例如,本发明中使用了金红石型钛白、800目重钙 、1200目重钙、高岭土四种填充料,这四种填充料以合适的比例的搭配保证了产品的优异的悬浮性和稳定性。
制备本发明所述的这种超耐候性外用彩色水性油墨时,首先制备相应的水性标准基础料,然后再将色浆按比例添加到基础料中,充分搅拌均匀即可。
具体步骤可分为以下三个步骤:
(1)制造浆料:将各种溶剂,粉料及润湿分散等助剂加入,通过高速分散及砂磨,控制使基础漆的细度小于10um;
(2)生产水性标准基础料:加入乳液树脂、成膜助剂及增稠剂调整涂料的粘度,控制涂料的粘度,流动性;
(3)调配颜色:将色浆按照比例加入到水性基础料中,搅拌10~15min。
与现有技术相比,本发明所述的这种超耐候性外用彩色水性油墨,可以最大限度保证该颜色的耐候性及准确性,通过值化的颜色三属性值定义水性油墨颜色,使最终颜色兼具保色性通用性与准确性。
具体实施方式
下面结合实施例对本发明进行详细的说明,实施例仅是本发明的优选实施方式,不是对本发明的限定。
实施例1:制备超耐候性外用彩色水性油墨:
本实施例的水性标准基础料,以总重量100克计,各组份及其重量为:
组份 含量(g) 产地
水 18.8
丙二醇 3.8
分散剂PE-2774 1.2 CLARIANT
润湿剂PM-407 0.1 CLARIANT
防霉剂D-LFM 0.15 COGNIS
增稠剂HS--100000 0.5 CLARIANT
金红石型钛白996 12.0 LONGMANG
重钙(800目) 15.0 JINGFU
重钙(1200目) 8.0 JINGFU
高岭土(800目) 4.0 JINGFU
成膜助剂TEXANOL 1.6 EASEMENT
丙烯酸树脂A-200 34.4 BDF
消泡剂SN-NXZ 0.3 NOPCO
氨水 0.15 。
上述水性标准基础料的制备方法为,将各种溶剂,粉料及润湿分散等助剂加入,通过高速分散及砂磨,控制使基料的细度小于10um;然后加入丙烯酸乳液、成膜助剂和增稠剂调整油墨的粘度。
然后在制备的水性标准基础料中加入水性色浆(惠州市君道实业有限公司生产的)PR254:0.15克 、PY154:1.40克,搅拌10min,使其充分混匀。
将调制的颜色使用漆膜厚度为50um的湿膜制备器涂刷板面,让水性油墨漆膜自然干燥,使用分光光度仪检测,先测出标准色样的LAB值,再测出色块的LAB,计算得色差=0.28,可充分真实再现颜色80252。通过采用ISO105-B04耐候性测试方法,使用氙灯耐老化仪为XEXOTEST BATE LM,用GB250-1995灰色变色卡标准评定得出80252,气候牢度1000小时测定结果为4级。
实施例2:
本实施例的水性标准基础料,以总重量100克计,各组份及其重量为:
组份 含量(g) 产地
水 17.65
丙二醇 3.5
分散剂PE-2774 1.8 CLARIANT
润湿剂PM-407 0.15 CLARIANT
防霉剂D-LFM 0.15 COGNIS
增稠剂HS--100000 0.5 CLARIANT
金红石型钛白996 12.5 LONGMANG
重钙(800目) 15.0 JINGFU
重钙(1200目) 7.0 JINGFU
高岭土(800目) 3.0 JINGFU
成膜助剂TEXANOL 1.8 EASEMENT
丙烯酸树脂A-200 36.5 BDF
消泡剂SN-NXZ 0.3 NOPCO
氨水 0.15
上述水性标准基础料的制备方法为,将各种溶剂,粉料及润湿分散等助剂加入,通过高速分散及砂磨,控制使基料的细度小于10um;然后加入丙烯酸乳液、成膜助剂和增稠剂调整油墨的粘度。
然后在制备的水性标准基础料中加入水性色浆(惠州市君道实业有限公司生产的)PR254:0.15克 、PY154:1.40克,搅拌10min,使其充分混匀。
将调制的颜色使用漆膜厚度为50um的湿膜制备器涂刷板面,让水性油墨漆膜自然干燥,使用分光光度仪检测,先测出标准色样的LAB值,再测出色块的LAB,计算得色差=0.38,可充分真实再现颜色80252。通过采用ISO105-B04耐候性测试方法,使用氙灯耐老化仪为XEXOTEST BATE LM,用GB250-1995灰色变色卡标准评定得出80252,气候牢度1000小时测定结果为4级。
Claims (6)
1.一种超耐候性外用彩色水性油墨,其特征在于:由水性标准基础料和水性油墨色浆混合而成,
所述水性标准基础料按质量百分比计由下述组分组成: 15-24.2%的水;3.0-3.8%的助溶剂;34-40%的纯丙烯酸乳液树脂;12-15%的金红石型钛白;15-20%的800目重钙; 5-8%的1200目重钙;3-5%的高岭土;1.2-1.8%的分散剂;0.1-0.15%的润湿剂;0.2-0.3%的消泡剂;0.1-0.15%的防霉剂;1.6-2.0%的成膜助剂;0.50-0.6%的增稠剂;0.1-0.18%的氨水;
所述水性油墨色浆为占水性标准基础料重量的0.15%的吡咯红,其国际颜料索引号为PR254;还有占水性标准基础料重量的1.40%的喹啉黄,其国际颜料索引号为PY154。
2.根据权利要求1所述的超耐候性外用彩色水性油墨,其特征在于,所述防霉剂是含氮杂环类防霉剂。
3.根据权利要求1或2所述的超耐候性外用彩色水性油墨,其特征在于,所述的润湿剂是改性聚氧乙烯醚类润湿剂。
4.根据权利要求1或2所述的超耐候性外用彩色水性油墨,其特征在于,所述的增稠剂是羟乙基类增稠剂。
5.根据权利要求1或2所述的超耐候性外用彩色水性油墨,其特征在于,所述消泡剂是脂肪烃类消泡剂。
6.根据权利要求1或2所述的超耐候性外用彩色水性油墨,其特征在于,所述成膜助剂是醇酯类成膜助剂。