CN106634467A - 一种流变金属底色漆及其制备方法 - Google Patents

一种流变金属底色漆及其制备方法 Download PDF

Info

Publication number
CN106634467A
CN106634467A CN201610805730.8A CN201610805730A CN106634467A CN 106634467 A CN106634467 A CN 106634467A CN 201610805730 A CN201610805730 A CN 201610805730A CN 106634467 A CN106634467 A CN 106634467A
Authority
CN
China
Prior art keywords
parts
rheology
metal base
base coat
coating
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610805730.8A
Other languages
English (en)
Inventor
薛芳
薛路
陈玉龙
陈军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIANGSU ZUYI COATING CO Ltd
Original Assignee
JIANGSU ZUYI COATING CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIANGSU ZUYI COATING CO Ltd filed Critical JIANGSU ZUYI COATING CO Ltd
Priority to CN201610805730.8A priority Critical patent/CN106634467A/zh
Publication of CN106634467A publication Critical patent/CN106634467A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种流变金属底色漆及其制备方法,该流变金属底色漆由如下原材料配制而成:铝银浆4.5~10份,分散剂0.3~1份,合成聚脂树脂10~25份,丙烯酸树脂10~20份,醋酸丁酸纤维素5~7份,消泡剂0.3~1.5份,流平剂0.4~2.5份,防沉抗流挂助剂1.5~5份,防沉剂1.5~3.5份,稀释剂25~30份。本发明在原漆拉尺产生的流动漆膜,喷涂的湿膜、干膜中铝粉、珠光粉等效应颜料的定向排列均匀稳定、金属效应明显、颜色稳定;干湿膜颜色差异小、易调色、易施工,涂装效率高,同时,本发明的漆膜各项性能指标完全达到油性铝粉漆涂料的指标。

Description

一种流变金属底色漆及其制备方法
技术领域
[0001] 本发明涉及一种汽车用涂料,尤其涉及一种流变金属底色漆及其制备方法。
背景技术
[0002] 随着我国国力及人民生活水平不断提高,居民汽车保有量不断上升,汽车涂料产 量在迅速增长。据国家统计局公布的统计数据显示,中国涂料总产量达1648.188万吨以上, 其中汽车漆所占比例较大的。
[0003] 高科技的机器人在汽车喷涂上的广泛运用、汽车修补市场调色、喷涂熟练工的短 缺,迫切需要一种较原有汽车漆更易喷涂易调色的技术,我公司顺应市场的要求开发控制 流变金属底色漆的制备方法。
[0004] 流变控制金属底色漆比原有的这类型涂料施工性能更好,同时降低了对喷涂技能 的要求。无论机械还是人工喷涂,漆膜平整光滑、铝粉排列均匀,合格率高。容易调色,原漆 拉尺时产生的漆膜铝粉颗粒清晰、稳定性强不易变色,可操作性强,干湿膜颜色差异小,提 高了调色工作效率。这一发明深受市场欢迎,前景是非常广阔的。
发明内容
[0005] 本发明的目的是根据市场的需求,提供控制流变金属底色漆的制备方法,其铝粉 珠光粉等效应颜料具有在流平、防沉等多种助剂控制作用下,在干湿膜中处于稳定的定向 的状态,颜色差异小,可调色及施工性能突出,优异的装饰性、良好的耐候性,适用于汽车和 工程机械原厂及修补等的涂装。
[0006] 本发明的目的可以通过以下措施达到:
[0007] -种控制流变金属底色漆的制备方法,主要由下述重量份的组分配制而成:
[0008] ⑴分散剂0.3~1份;
[0009] (2)铝银浆4.5~10份;
[0010] ⑶合成聚脂树脂1〇~25份;
[0011] ⑷丙烯酸树脂10-20
[0012] (5)消泡剂0 · 3~1 · 5份;
[0013] ⑶流平剂0.4~2.5份;
[0014] (7)醋酸丁酸纤维素7~12份;
[0015] ⑶防沉剂1.5~3.5份;
[0016] (9)稀稀剂35~45份。
[0017] 本发明中的分散剂采用BYK P-104S。
[0018] 本发明中的铝银浆采用的是星铂联的SSP 695-AP。
[0019] 本发明中的合成聚脂树脂采用纽佩斯的173。
[0020] 本发明中的丙烯酸树脂采用长兴的ETERAC7131-TK-50。
[0021] 本发明中的醋酸丁酸纤维素采用帝斯曼的CAB381-0.5。
[0022] 本发明中的消泡剂为含有机硅的消泡剂AFC0NA3280。
[0023] 本发明中的流平剂为聚醚改性有机硅BYK331。
[0024] 本发明中的增稠剂为楠本的6900-20X。
[0025] 本发明中的防沉剂为BYK的聚乙烯蜡CERAFAK103。
[0026] 流变控制金属底色漆的制备方法如下:
[0027] 单组分铝粉漆由如下方法配制而成:
[0028] (1)将分散剂、稀释剂和铝银浆混合搅拌均匀,浸泡60分钟以上,检验分散均匀无 颗粒后备用;
[0029] (2)合成聚酯树脂、丙烯酸树脂、消泡剂、流平剂、抗流挂树脂、防沉剂和稀释剂混 合均匀,在先低后高剪切力下搅拌均匀;
[0030] ⑶将⑵在低速搅拌下,边搅拌边加入⑴,搅拌均匀;
[0031] ⑷用稀释剂将单组分铝粉漆的粘度调整在65-120之间即可。
[0032] 施工时首先将以上的单组份漆搅拌均匀,用50-100%的稀释剂兑稀,然后根据施 工要求,将施工粘度调整到12-25秒/室温,均匀喷涂于待涂工件上。
[0033] 本发明流变控制金属底色漆具有以下特点:
[0034] (1)本发明的涂料采用合成聚脂树脂、丙烯酸树脂及醋酸丁酸纤维素,能赋予漆膜 优异的装饰性和成膜性;
[0035] ⑵本发明的涂料具备良好的柔韧性,能防止漆膜开裂,脱落;
[0036] (3)本发明的涂料具有突出的特点,对施工人员技能的要求不高;
[0037] ⑷本发明的涂料具有良好的易施工性;
[0038] (5)本发明的涂料提高了工作效率;
[0039] ⑶本发明的涂料降低了对大气污染;
[0040] ⑵本发明的涂料仅采用低毒性有机溶剂,改善了作业环境条件;
[0041] 本发明流变金属底色漆的制备方法,提高了油漆开罐效果,降低了干湿漆膜的差 异,提尚调色速度,提尚施工可靠性能,大大的提尚了工作效率。
具体实施方式
[0042] 以下结合实施例对本发明做进一步的描述。
[0043] 实施例1
[0044] 本实施例单组分铝粉漆重量组份:分散剂0.4份,稀释剂5份,铝银浆8.5份,Sn822 合成聚脂17份,ETERAC7131-TK-50丙烯酸树脂13份,CAB381-0.5醋酸丁酸纤维素5份,消泡 剂0.7份,流平剂0.4份,抗流挂助剂6.8份,防沉剂4.5份,稀释剂38.1份。
[0045] (1)将分散剂0.4份、稀释剂5份和铝银浆4.5份加入容器,混合搅拌均匀,浸泡60分 钟检验分散均匀无颗粒后备用;
[0046] (2)Sn822 合成聚脂 30 份、ETERAC7131-TK-50 丙烯酸树脂 13 份,CAB381-0.5 醋酸丁 酸纤维素5份,消泡剂0.7份、流平剂0.4份、抗流挂助剂6.8份,防沉剂4.5份,稀释剂33.1份 加入容器,在先低后高剪切力下搅拌均匀;
[0047] ⑶将(2)在低速搅拌下,边搅边加入(1),用5份稀释剂冲刷⑴的容器倒入(2)中, 低速搅拌15-20分钟;
[0048] ⑷用稀释剂将单组分铝粉漆的粘度调整在65-120之间即可。
[0049] 使用时,漆组份与稀释剂100 : 50~100的配比(重量)混合均匀,喷涂在马口铁板 上,对比干湿膜及原漆拉尺差异;80°C烘30分钟,测得各项技术指标见表1。
[0050] 实施例2
[0051] 本实施例铝粉漆重量组份:分散剂0.6份,稀释剂5份,铝银浆8.5份,Sn聚脂树脂17 份,ETERAC7131-TK-50丙烯酸树脂13份,CAB381-0.5醋酸丁酸纤维素6份,消泡剂1份,流平 剂1份,抗流挂助剂8.5份,防沉剂4.5份,稀释剂35.9份。
[0052] (1)将分散剂0.6份、稀释剂5份和铝银浆8.5份加入容器,浸泡60分钟检验分散均 匀无颗粒后备用
[0053] (2) Sn822合成聚脂树脂、ETERAC7131-TK-50丙烯酸树脂 13份,CAB381-0.5醋酸丁 酸纤维素6份、消泡剂1份、流平剂1份、抗流挂助剂8.5份、防沉剂4.5份,稀释剂29.9份加入 容器,在低剪切力下搅拌均;
[0054] ⑶将⑵在低速搅拌下,边搅边加入(1),用5份稀释剂冲刷⑴的容器倒入⑵中, 浸泡60分钟检验分散均匀无颗粒后备用;
[0055] ⑷用稀释剂将单组分铝粉漆的粘度调整在65-120之间即可。
[0056] 使用时,漆组份与稀释剂100 : 50~100的配比(重量)混合均匀,喷涂在马口铁板 上,对比干湿膜及原漆拉尺差异;80°C烘30分钟,测得各项技术指标见表1。
[0057] 实施例3
[0058] 本实施例水性铝粉漆重量组份:分散剂0.6份,稀释剂5份,铝银浆8.5份,Sn822合 成聚脂树脂17份,ETERAC7131-TK-50丙烯酸树脂13份,CAB381-0.5醋酸丁酸纤维素7份,消 泡剂1.5份,流平剂1.5份,抗流挂助剂10份,防沉剂4.5份,稀释剂31.4份。
[0059] (1)将分散剂0.6份、稀释剂5份和铝银浆8.5份加入容器,混合搅拌均匀,浸泡60分 钟检验分散均匀无颗粒后备用
[0060] (2)Sn822 合成聚脂树脂 17 份,ETERAC7131-TK-50 丙烯酸树脂 13 份,CAB381-0.5 醋 酸丁酸纤维素7份、消泡剂1.5份、流平剂1.5份、抗流挂助剂10份、防沉降蜡4.5份,稀释剂 26 · 4加入容器,在低剪切力下搅拌均匀;
[0061] (3)将(2)在低速搅拌下,边搅边加入(1),用5份稀释剂冲刷⑴的容器倒入(2)中, 低速搅拌15-20分钟;
[0062] ⑷用稀释剂将单组分铝粉漆的粘度调整在65-120之间即可。
[0063] 使用时,漆组份与稀释剂100 : 50~100的配比(重量)混合均匀,喷涂在马口铁板 上,对比干湿膜及原漆拉尺差异;80°C烘30分钟,测得各项技术指标见表1。
[0064] 参照有关国家或行业标准,对以上具体实施例进行性能检测,结果如表1。
[0065] 表 1
Figure CN106634467AD00071

Claims (10)

1. 一种流变金属底色漆,其特征在于:所述涂料部分由以下重量份的原材料组分配制 而成:
Figure CN106634467AC00021
2. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的分散剂, 包括改性聚丙烯酸酯高聚物、不饱和聚酰胺酸均聚体和有机硅、高分子量不饱和羧酸和高 相容性有机改性聚硅氧烷的混和物、脂肪酸改性聚酯中的一种或几种以任意比例的混合。
3. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的铝银浆是 非浮型铝银浆,其铝银粉粒径范围在5-80微米。
4. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的丙烯酸树 月旨,包括热塑性丙烯酸树脂、羟基丙烯酸树脂中的一种或几种以任意比例的混合。
5. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的合成聚酯 树脂,包括改性聚酯树脂、饱和聚酯树脂中的一种或几种以任意比例的混合。
6. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的消泡剂, 包括含有机硅改性消泡剂、有机改性的聚二甲基硅氧烷、氟炭改性有机硅、乙烯基聚合物中 的一种或几种以任意比例的混合。
7. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的流平剂, 包括聚醚改性有机硅、特殊有机改性的聚硅氧烷、改性聚硅氧烷、氟碳改性聚丙烯酸酯、丙 烯酸-有机硅共聚物中的一种或几种以任意比例的混合。
8. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的防沉抗流 挂助剂,包括聚乙烯蜡、乙烯-醋酸乙烯共聚物蜡分散液、环保型混和蜡中的一种或几种以 任意比例的混合。
9. 根据权利要求1所述的一种流变金属底色漆,其特征在于:配制涂料所用的防沉剂, 包括聚酰胺防沉腊、气相二氧化硅、膨润土中的一种或几种以任意比例的混合。
10. 根据权利要求1-9任一所述的一种流变金属底色漆,其特征在于:所述的流变控制 金属底色漆的制备方法如下: (1) 将分散剂、稀释剂和铝银浆混合搅拌均匀,浸泡60分钟以上,待分散均匀无颗粒后 备用; (2) 将合成聚酯树脂、丙烯酸树脂、消泡剂、流平剂、防沉抗流挂助剂、防沉剂和稀释剂 混合均匀,在先低后高剪切力下搅拌均匀; ⑶将⑵在低速搅拌下,边搅拌边加入(I),搅拌均匀; ⑷用稀释剂将单组分铝粉漆的粘度调整在65-120之间即可。
CN201610805730.8A 2016-09-07 2016-09-07 一种流变金属底色漆及其制备方法 Pending CN106634467A (zh)