CN102701702A - 一种熔融石英空心球轻质浇注料的配方 - Google Patents
一种熔融石英空心球轻质浇注料的配方 Download PDFInfo
- Publication number
- CN102701702A CN102701702A CN2012100000638A CN201210000063A CN102701702A CN 102701702 A CN102701702 A CN 102701702A CN 2012100000638 A CN2012100000638 A CN 2012100000638A CN 201210000063 A CN201210000063 A CN 201210000063A CN 102701702 A CN102701702 A CN 102701702A
- Authority
- CN
- China
- Prior art keywords
- fused quartz
- fused silica
- prescription
- mould material
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开的熔融石英空心球轻质浇注料的配方，以熔融石英空心球作为骨料，配比如下（质量百分比）；熔融石英空心球、60~68%；熔融石英细粉、30~35%；二氧化硅微粉、2~5%；水泥、0~5%；外加占上述熔融石英空心球、熔融石英细粉、二氧化硅微粉及水泥四种料重量百分比例0~0.2%的三聚磷酸钠，重量百分比例8~12%的结合剂。本发明的熔融石英空心球轻质浇注料具有体积密度低、耐急冷急热性好、隔热性能好及化学性能稳定的优点。
Description
技术领域
本发明涉及轻质熔融石英制品技术领域，具体是涉及一种熔融石英空心球轻质浇注料的配方。
背景技术
与其它耐火隔热材料相比，熔融石英材料，如主要成分为SiO2的玻璃陶瓷具有两大显著特点：1）、热膨胀系数很低，其热膨胀系数仅为0.54×10-6/℃；2）、热传导率很低，其热传导率仅为2.1W/m·K。因此，熔融石英材料不仅具有非常优良的耐急冷急热性，而且具有非常优良的隔热性能。如果将熔融石英材料加工成轻质隔热制品，该轻质隔热制品的隔热效果是其它耐火轻质隔热制品无法比拟的。
熔融石英空心球轻质浇注料作为一种轻质隔热制品，采用熔融石英空心球制备，目前还未有专利和文件报道。
发明内容
本发明所要解决的技术问题是提供一种制备熔融石英空心球轻质浇注料的配方。
本发明的熔融石英空心球轻质浇注料的配方，以熔融石英空心球作为骨料，配比如下（质量百分比）；
熔融石英空心球 60~68%
熔融石英细粉 30~35%
二氧化硅微粉 2~5%
水泥 0~5%
占上述熔融石英空心球、熔融石英细粉、二氧化硅微粉及水泥四种料重量百分比例0~0.2%的三聚磷酸钠；
占上述熔融石英空心球、熔融石英细粉、二氧化硅微粉及水泥四种料重量百分比例8~12%的结合剂。
优选的，所述熔融石英空心球含SiO2含量为97.0~99.0wt%，球径为Φ2~5mm。
优选的，所述熔融石英细粉SiO2含量为97.0~99.0wt%，颗粒度为325~500目。
优选的，所述二氧化硅微粉的SiO2含量大于95wt%，颗粒度小于3000目。
优选的，所述水泥为高铝水泥或铝酸钙水泥。
优选的，所述三聚磷酸钠的颗粒度小于350目。
优选的，所述结合剂为水、水玻璃或硅溶胶中的一种。
本发明的熔融石英空心球轻质浇注料具有以下优点：
1）、体积密度低。本申请制备的熔融石英空心球轻质浇注料的体积密度为0.6~1.2g/cm3，因此，绝热效果非常好。
2）、耐急冷急热性好。本申请制备的熔融石英空心球轻质浇注料的热膨胀系数约为0.5×10-6/℃,具有很好的热震稳定性。
3）、隔热性能好。本申请制备的熔融石英空心球轻质浇注料的导热系数约为0.1 W/m·K，隔热效果非常好。
4）、化学性能稳定。SiO2属中性氧化物，除氢氟酸和热浓硫酸对其有侵蚀之外，与其它酸类物质和各种金属熔体几乎不发生作用，对各种玻璃熔渣也有非常好的耐侵蚀性。
由于熔融石英空心球轻质浇注料具有如上诸多优点，因此作为保温隔热材料具有很好的应用前景。
具体实施方式
一种熔融石英空心球浇注料的配比见表1，所制备的熔融石英空心球轻质浇注料的主要理化指标见表2。
表1 熔融石英空心球轻质浇注料的配比
表2 熔融石英空心球轻质浇注料的理化性能
Claims (7)
1.一种熔融石英空心球轻质浇注料的配方，其特征是：配比如下（质量百分比）；
熔融石英空心球 60~68%
熔融石英细粉 30~35%
二氧化硅微粉 2~5%
水泥 0~5%
占上述熔融石英空心球、熔融石英细粉、二氧化硅微粉及水泥四种料重量百分比例0~0.2%的三聚磷酸钠；
占上述熔融石英空心球、熔融石英细粉、二氧化硅微粉及水泥四种料重量百分比例8~12%的结合剂。
2.根据权利要求1所述的熔融石英空心球轻质浇注料的配方，其特征是：所述熔融石英空心球含SiO2含量为97.0~99.0wt%，球径为Φ2~5mm。
3.根据权利要求1所述的熔融石英空心球轻质浇注料的配方，其特征是：所述熔融石英细粉SiO2含量为97.0~99.0wt%，颗粒度为325~500目。
4.根据权利要求1所述的熔融石英空心球轻质浇注料的配方，其特征是：所述二氧化硅微粉的SiO2含量大于95wt%，颗粒度小于3000目。
5.根据权利要求1所述的熔融石英空心球轻质浇注料的配方，其特征是：所述水泥为高铝水泥或铝酸钙水泥。
6.根据权利要求1所述的熔融石英空心球轻质浇注料的配方，其特征是：所述三聚磷酸钠的颗粒度小于350目。
7.根据权利要求1所述的熔融石英空心球轻质浇注料的配方，其特征是：所述结合剂为水、水玻璃或硅溶胶中的一种。