CN104030700A - 一种锆莫来石匣钵 - Google Patents

一种锆莫来石匣钵 Download PDF

Info

Publication number
CN104030700A
CN104030700A CN201410229659.4A CN201410229659A CN104030700A CN 104030700 A CN104030700 A CN 104030700A CN 201410229659 A CN201410229659 A CN 201410229659A CN 104030700 A CN104030700 A CN 104030700A
Authority
CN
China
Prior art keywords
saggar
zirconium mullite
mullite saggar
sio
zro
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201410229659.4A
Other languages
English (en)
Inventor
高寿林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Zhejiang Li Xin High-Temperature Refractory Co Ltd
Original Assignee
Zhejiang Li Xin High-Temperature Refractory Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Li Xin High-Temperature Refractory Co Ltd filed Critical Zhejiang Li Xin High-Temperature Refractory Co Ltd
Priority to CN201410229659.4A priority Critical patent/CN104030700A/zh
Publication of CN104030700A publication Critical patent/CN104030700A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种锆莫来石匣钵，属于耐火材料领域，有效阻止锂溶液对匣钵的酸性侵蚀和碱性侵蚀。为了解决上述技术问题，本发明通过下述技术方案得以解决：一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO和MgO,所述锆莫来石匣钵中各组分的重量百分比为Al2O368％-79％、SiO210.65％-18.5％、ZrO210％-12.7％、Fe2O30.2％-0.5％、CaO0.05％-0.1％和MgO0.1％-0.2％。

Description

一种锆莫来石匣钵
技术领域
本发明涉及一种锆莫来石匣钵，属于耐火材料领域。
背景技术
锂通常需要熔化成液态锂，提纯后，在模具中冷却为锂棒。锂可以与氧气反应生成氧化锂，锂也可以与水反应生成氢氧化锂，所以，熔化锂的匣钵既要能够抗酸性，又要能够抗碱性。现有的匣钵是由刚玉砖黏合而成，刚玉砖的成分及其重量百分比为Ai2O395％、ZrO24.5％、Fe2O30.3％、SiO20.2％。然而，刚玉砖黏合的匣钵，不能很好的抵抗锂溶液的酸性侵蚀和碱性侵蚀，因此使用寿命较短。
发明内容
本发明需要解决的问题是提供了一种锆莫来石匣钵，有效阻止锂溶液对匣钵的酸性侵蚀和碱性侵蚀。
为了解决上述技术问题，本发明通过下述技术方案得以解决：一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO和MgO,所述锆莫来石匣钵中各组分的重量百分比为Al2O368％-79％、SiO210.65％-18.5％、ZrO210％-12.7％、Fe2O30.2％-0.5％、CaO0.05％-0.1％和MgO0.1％-0.2％。
进一步的，所述锆莫来石匣钵中，各组分的重量百分比为Al2O368％、SiO218.5％、ZrO212.7％、Fe2O30.5％、CaO0.1％和MgO0.2％。
进一步的，所述锆莫来石匣钵中，各组分的重量百分比为Al2O379％、SiO210.65％、ZrO210％、Fe2O30.2％、CaO0.05％和MgO0.1％。
进一步的，所述锆莫来石匣钵中，各组分的重量百分比为Al2O374％、SiO214％、ZrO211.5％、Fe2O30.3％、CaO0.08％和MgO0.12％。
进一步的，还包括Li2CO3，所述锆莫来石匣钵中Li2CO3的重量百分比为1％-2％。
本发明的有益效果：
SiO2可与Al2O3反应可生成莫来石，莫来石是一种优质的耐火材料，有效提高锆莫来石匣钵的耐火温度。SiO2除了可以与Al2O3反应外，还能够用于填充熔化状态下的玻璃在冷却为非结晶固体过程中产生的气泡。MgO也可以与Al2O3反应生成晶体，晶体夹在在莫来石中，增加了锆莫来石匣钵的抗酸性和抗碱性。MgO在锆莫来石匣钵中含量过多时，锆莫来石匣钵会被软化。
锆莫来石匣钵中各组分的重量百分比为Al2O368％-79％、SiO210.65％-18.5％、ZrO210％-12.7％、Fe2O30.2％-0.5％、CaO0.05％-0.1％和MgO0.1％-0.2％时，锆莫来石匣钵的耐压强度为85MPa以上，荷重软化温度1580℃以上，体积密度2.75g/cm3以上。
ZrO2可以增强锆莫来石匣钵的韧性和增强锆莫来石匣钵的抗酸碱性。锆莫来石匣钵中通过加入Fe2O3与SiO2、CaO二者发生化学反应，不仅能够使锆莫来石匣钵内产生低融物，避免液态锂侵润锆莫来石匣钵。Fe2O3还能够提高锆莫来石匣钵的荷软温度，加入Fe2O3后的锆莫来石匣钵荷软温度为1650℃。
Li2CO3可以增加锆莫来石匣钵抵抗液态锂的侵蚀，同时，也阻止了锆莫来石匣钵冷却液态锂时产生的热震现象。
具体实施方式
实施例1
一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO和MgO,所述锆莫来石匣钵中各组分的重量百分比为Al2O368％、SiO218.5％、ZrO212.7％、Fe2O30.5％、CaO0.1％和MgO0.2％。
实施例2
一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO和MgO,所述锆莫来石匣钵中各组分的重量百分比为Al2O379％、SiO210.65％、ZrO210％、Fe2O30.2％、CaO0.05％和MgO0.1％。
实施例3
一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO和MgO,所述锆莫来石匣钵中各组分的重量百分比为Al2O374％、SiO214％、ZrO211.5％、Fe2O30.3％、CaO0.08％和MgO0.12％。
实施例4
一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO、MgO和Li2CO3,所述锆莫来石匣钵中各组分的重量百分比为Al2O368％、SiO217.5％、ZrO212.7％、Fe2O30.5％、CaO0.1％、MgO0.2％、Li2CO31％。
实施例5
一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO、MgO和Li2CO3,所述锆莫来石匣钵中各组分的重量百分比为Al2O378％、SiO214.65％、ZrO211％、Fe2O30.2％、CaO0.05％、MgO0.1％、Li2CO32％。
实施例6
一种锆莫来石匣钵，所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO、MgO和Li2CO3,所述锆莫来石匣钵中各组分的重量百分比为Al2O373.5％、SiO213％、ZrO211.5％、Fe2O30.3％、CaO0.08％、MgO0.12％、Li2CO31.5％
以上均为本发明的有限实施方案，Al2O3、SiO2、ZrO2、Fe2O3、CaO、MgO和Li2CO3七种组分的重量百分比可以根据实际需要，在其重量百分比的范围内做出适当调节。

Claims (5)

1.一种锆莫来石匣钵，其特征在于：所述锆莫来石匣钵的组分包括Al2O3、SiO2、ZrO2、Fe2O3、CaO和MgO,所述锆莫来石匣钵中各组分的重量百分比为Al2O368％-79％、SiO210.65％-18.5％、ZrO210％-12.7％、Fe2O30.2％-0.5％、CaO0.05％-0.1％和MgO0.1％-0.2％。
2.根据权利要求1所述的一种锆莫来石匣钵，其特征在于：所述锆莫来石匣钵中，各组分的重量百分比为Al2O368％、SiO218.5％、ZrO212.7％、Fe2O30.5％、CaO0.1％和MgO0.2％。
3.根据权利要求1所述的一种锆莫来石匣钵，其特征在于：所述锆莫来石匣钵中，各组分的重量百分比为Al2O379％、SiO210.65％、ZrO210％、Fe2O30.2％、CaO0.05％和MgO0.1％。
4.根据权利要求1所述的一种锆莫来石匣钵，其特征在于：所述锆莫来石匣钵中，各组分的重量百分比为Al2O374％、SiO214％、ZrO211.5％、Fe2O30.3％、CaO0.08％和MgO0.12％。
5.根据权利要求1所述的一种锆莫来石匣钵，其特征在于：还包括Li2CO3，所述锆莫来石匣钵中Li2CO3的重量百分比为1％-2％。
CN201410229659.4A 2014-05-26 2014-05-26 一种锆莫来石匣钵 Pending CN104030700A (zh)