CN102675609A - 一种快速结晶型纳米复合聚酯热熔胶及其制备工艺 - Google Patents
一种快速结晶型纳米复合聚酯热熔胶及其制备工艺 Download PDFInfo
- Publication number
- CN102675609A CN102675609A CN2012101864134A CN201210186413A CN102675609A CN 102675609 A CN102675609 A CN 102675609A CN 2012101864134 A CN2012101864134 A CN 2012101864134A CN 201210186413 A CN201210186413 A CN 201210186413A CN 102675609 A CN102675609 A CN 102675609A
- Authority
- CN
- China
- Prior art keywords
- dimethyl
- benzenedicarboxylate
- dmt
- melt adhesive
- polycondensation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
实施例号 | 2 | 3 | 4 | 5 | 6 |
有机蒙脱土 | 5.6 | 1.94 | 2.6 | 11.64 | 4.6 |
纳米二氧化硅 | 0.098 | 0.78 | 0.123 | 0.145 | 0.155 |
对苯二甲酸二甲酯 | 388.1 | 388.2 | 388.1 | 388.1 | 388.2 |
邻苯二甲酸二辛酯 | 156.3 | ||||
1,6-己二酸二丁酯 | 116.6 | ||||
1,10-癸二酸二丁酯 | 220.2 | ||||
1,6-己二酸二甲酯 | 104.8 | ||||
邻苯二甲酸二甲酯 | 97.5 | ||||
1,4-丁二醇 | 189.1 | 288.2 | 243.8 | 261.6 | 324.2 |
乙二醇 | 18.6 | 14.9 | 27.9 | ||
1,6-己二醇 | 59.2 | 59.6 | |||
2,2,4-甲基-1,3-戊二醇 | 90.5 | ||||
新戊二醇 | 31.2 | 46.8 | |||
1,3-丙二醇 | 18.2 | 30.4 | |||
纳米二氧化硅 | 0.078 | 0.118 | 0.120 | 0.155 | 0.116 |
稳定剂 | 0.12 | 0.122 | 0.155 | 0.14 | 0.09 |
三氧化二锑 | 0.038 | 0.032 | 0.078 | 0.052 | 0.064 |
酯化反应保温时间,min | 30 | 40 | 45 | 50 | 60 |
缩聚时间,min | 40 | 50 | 65 | 60 | 70 |
缩聚温度,℃ | 200-220 | 220-240 | 220-250 | 220-240 | 220-245 |
平均分子量 | 16240 | 20830 | 24050 | 26580 | 23870 |
熔点,℃ | 98~112 | 104~116 | 102-109 | 105-115 | 104-122 |
熔融指数,g/10min(160℃) | 95.7 | 88.3 | 84.7 | 83.2 | 81.9 |
Claims (4)