CN102660307A - Y值小于20mm的1/3焦煤参与的炼焦配煤方法 - Google Patents
Y值小于20mm的1/3焦煤参与的炼焦配煤方法 Download PDFInfo
- Publication number
- CN102660307A CN102660307A CN2012101612862A CN201210161286A CN102660307A CN 102660307 A CN102660307 A CN 102660307A CN 2012101612862 A CN2012101612862 A CN 2012101612862A CN 201210161286 A CN201210161286 A CN 201210161286A CN 102660307 A CN102660307 A CN 102660307A
- Authority
- CN
- China
- Prior art keywords
- coal
- coking
- cent
- coking coal
- blending
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种Y值小于20mm的1/3焦煤参与的炼焦配煤方法,该1/3焦煤的干燥无灰基挥发分>28.0%-32.0%,粘结指数G值≥85。本发明包括如下步骤:第一步,检测该1/3焦煤的胶质层指数;第二步,根据第一步检测结果确定配煤方案:当胶质层特征曲线为“平滑下降”型,作为气煤配用;当胶质层特征曲线为非“平滑下降”型,作为1/3焦煤配用。本发明采用胶质层特征曲线指标对Y值小于20mm的1/3焦煤进行合理区分后配煤炼焦,可以有效利用煤质资源,在未采用煤调湿、型煤技术及预粉碎工艺的条件下,焦炭质量得到稳定提高,且在6米以上焦炉所炼焦炭的CSR>63%。
Description
技术领域
本发明属于炼焦配煤技术领域,具体涉及Y值小于20mm的中挥发分1/3焦煤参与的炼焦配煤方法。
背景技术
近年来,随着钢铁企业的迅猛发展,对炼焦煤的需求量大增,尤其是对中变质程度强粘煤(肥煤、焦煤和1/3焦煤)需求更高。在配煤方案中,焦煤、肥煤和1/3焦煤的作用是完全不同的,焦煤是焦炭质量的主要支撑,肥煤在配煤炼焦中起调整配合煤的流变性和膨胀性,可配用一定量的弱粘性炼焦煤,同时提供一定的粒状结构支撑焦炭热性能,1/3焦煤主要是提供粒状结构支撑焦炭热性能。
根据中国煤炭分类标准(GB 5751-2009),1/3焦煤挥发分>28.0-37.0%,G值>65,Y值≤25.0。在我国,对该类炼焦煤的使用主要依赖于传统的煤质指标和煤岩指标的镜质组反射率及其分布,该两种指标及其组合指标均存在一定的缺陷,按照这些方法进行配煤炼焦,不能合理地配用1/3焦煤,进而影响炼得的焦炭质量。
发明内容
本发明所要解决的技术问题是提供一种炼焦配煤方法,以合理配用干燥无灰基挥发分>28.0%-32.0%,粘结指数G值≥85,胶质层最大厚度Y值<20.0mm的1/3焦煤。
为解决上述技术问题,本发明采用如下的技术方案:
检测其胶质层指数,单种煤成焦粗粒镶嵌结构百分比和单种煤成焦粒状镶嵌结构百分比,所述成焦粒状镶嵌结构百分比为粗粒镶嵌结构与细粒镶嵌结构百分比之和:
1)如果胶质层特征曲线为“平滑下降”型,作为气煤配用。
2)如果胶质层特征曲线非“平滑下降”型,作为1/3焦煤配用;其中:
a、单种煤成焦粗粒镶嵌结构百分比≥35%,作为优质1/3焦煤配用,即其占配煤总重量的百分比为15-30%;
b、单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比≥75%,作为一般煤质1/3焦煤配用, 即其占配煤总重量的百分比不高于15%;
c、单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比<75%,作为劣质1/3焦煤配用, 即其占配煤总重量的百分比不高于10%。
优选地,所述1/3焦煤的胶质层特征曲线为“平滑下降”型,该1/3焦煤记为1/3焦煤1#,各单种煤占配煤总重量的百分比为:1/3焦煤1#:3-5%;气肥煤:3-8%;肥煤:5-15%;不同于1/3焦煤1#的1/3焦煤:10-30%;焦煤:30-45%;瘦煤:7-15%。
优选地,所述1/3焦煤的胶质层特征曲线为非“平滑下降”型,且单种煤成焦粗粒镶嵌结构百分比≥35%,该1/3焦煤记为1/3焦煤2#,各单种煤占配煤总重量的百分比为:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;1/3焦煤2#:15-30%;粗粒镶嵌结构百分比<35%的1/3焦煤:0-15%;焦煤:30-45%;瘦煤:7-15%。
优选地,所述1/3焦煤的胶质层特征曲线为非“平滑下降”型,且单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比≥75%,该1/3焦煤记为1/3焦煤3#,各单种煤占配煤总重量的百分比为:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%; 粗粒镶嵌结构百分比≥35%的1/3焦煤:15-30%;1/3焦煤3#:5-15%;焦煤:30-45%;瘦煤:7-15%。
优选地,所述1/3焦煤的胶质层特征曲线为非“平滑下降”型,且单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比<75%,该1/3焦煤记为1/3焦煤4#,各单种煤占配煤总重量的百分比为:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;粗粒镶嵌结构百分比≥35%的1/3焦煤:15-30%;1/3焦煤4#:0-10%;焦煤:30-45%;瘦煤:7-15%。
本发明采用胶质层特征曲线,单种煤成焦粗粒镶嵌结构百分比、单种煤成焦粒状镶嵌结构百分比等指标,对干燥无灰基挥发分>28.0-32.0%,粘结指数G值≥85,胶质层最大厚度Y值<20.0mm的1/3焦煤进行合理区分后配煤炼焦,可以合理利用煤质资源,在未采用煤调湿、型煤技术及预粉碎工艺的条件下,在6米以上焦炉所炼焦炭的CSR>63%。
具体实施方式
下面结合具体实施方式对本发明作进一步详细的说明。
本发明的Y值<20.0mm的1/3焦煤,其干燥无灰基挥发分>28.0-32.0%,粘结指数G值≥85,该1/3焦煤参与的炼焦配煤方法如下:
检测其胶质层指数,单种煤成焦粗粒镶嵌百分比和单种煤成焦粒状镶嵌百分比:
1)如果胶质层特征曲线为“平滑下降”型,作为气煤配用,记为1/3焦煤1#。
2)如果胶质层特征曲线非“平滑下降”型,配用量<5%:
a、单种煤成焦粗粒镶嵌结构百分比≥35%,作为优质1/3焦煤配用,配用量为15-30%,记为1/3焦煤2#;
b、单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比≥75%,作为一般煤质1/3焦煤配用,配用量不高于15%,记为1/3焦煤3#,;
c、单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比<75%,作为劣质1/3焦煤配用,配用量低于10%,记为1/3焦煤4#。
各单种煤煤质分析结果见表1。
表1 单种煤煤质分析结果
对于上表的1#煤样,由于其胶质层特征曲线为平滑下降型,作为气煤配用;例如,按以下重量百分比进行配煤:1#煤样:3-5%;气肥煤:3-8%;肥煤:5-15%;不同于1/3焦煤1#的1/3焦煤:10-30%;焦煤:30-45%;瘦煤:7-15%。更优选地,1#煤样:5%;气肥煤:5%;肥煤:10%;不同于1/3焦煤1#的1/3焦煤:25%;焦煤:45%;瘦煤:10%。按以上方法进行配煤,在未采用煤调湿、型煤技术及预粉碎工艺的条件下,在6米以上焦炉所炼焦炭的CSR为65.2%。
对于上表的2#煤样,由于其胶质层特征曲线为 “之”型,单种煤成焦粗粒镶嵌结构百分比≥35%,作为优质1/3焦煤配用,配用量可高于15%;例如,按以下重量百分比进行配煤:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;2#煤样:15-30%;粗粒镶嵌结构百分比<35%的1/3焦煤:0-15%;焦煤:30-45%;瘦煤:7-15%。更优选地,气煤:4%;气肥煤:6%;肥煤:14%;2#煤样:21%;不同于1/3焦煤2#的1/3焦煤:10%;焦煤:37%;瘦煤:8%。按以上方法进行配煤,在未采用煤调湿、型煤技术及预粉碎工艺的条件下,在6米以上焦炉所炼焦炭的CSR为63.9%。
对于上表的3#煤样,由于其胶质层特征曲线为 “之”型,单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比≥75%,作为一般煤质1/3焦煤配用,配用量不高于15%;例如,按以下重量百分比进行配煤:
气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;粗粒镶嵌结构百分比≥35%的1/3焦煤:15-30%;3#煤样:5-15%;焦煤:30-45%;瘦煤:7-15%。更优选地,气煤:3%;气肥煤:5%;肥煤:13%;粗粒镶嵌结构百分比≥35%的1/3焦煤:20%;3#煤样:11%;焦煤:38%;瘦煤:10%。按以上方法进行配煤,在未采用煤调湿、型煤技术及预粉碎工艺的条件下,在6米以上焦炉所炼焦炭的CSR为64.2%。
对于上表的4#煤样,由于其胶质层特征曲线为微波型,单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比<75%,作为劣质1/3焦煤配用。例如,按以下重量百分比进行配煤:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;粗粒镶嵌结构百分比≥35%的1/3焦煤:15-30%;4#煤样:0-10%;焦煤:30-45%;瘦煤:7-15%。更优选地,气煤:2%;气肥煤:6%;肥煤:13%;粗粒镶嵌结构百分比≥35%的1/3焦煤:25%;4#煤样:8%;焦煤:38%;瘦煤:8%。按以上方法进行配煤,在未采用煤调湿、型煤技术及预粉碎工艺的条件下,在6米以上焦炉所炼焦炭的CSR为64.5%。
Claims (8)
1.一种Y值小于20mm的1/3焦煤参与的炼焦配煤方法,该1/3焦煤的挥发分为>28.0-32.0%,粘结指数G值≥85,其特征在于,包括如下步骤:
第一步,检测该1/3焦煤的胶质层指数;
第二步,根据第一步检测结果确定配煤方案:
当胶质层特征曲线为“平滑下降”型,作为气煤配用;
当胶质层特征曲线为非“平滑下降”型,作为1/3焦煤配用。
2.根据权利要求1所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:
所述1/3焦煤的胶质层特征曲线为非“平滑下降”型,且单种煤成焦粗粒镶嵌结构百分比≥35%,作为优质1/3焦煤配用。
3.根据权利要求1所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:
所述1/3焦煤的胶质层特征曲线为非“平滑下降”型,且单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比≥75%,作为一般煤质1/3焦煤配用。
4.根据权利要求1所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:
所述1/3焦煤的胶质层特征曲线为非“平滑下降”型,且单种煤成焦粗粒镶嵌结构百分比<35%,单种煤成焦粒状镶嵌结构百分比<75%,作为劣质1/3焦煤配用。
5.根据权利要求1所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:
所述1/3焦煤的胶质层特征曲线为“平滑下降”型,作为气煤配用,记为1/3焦煤1#,各单种煤占配煤总重量的百分比为:1/3焦煤1#:3-5%;气肥煤:3-8%;肥煤:5-15%;不同于1/3焦煤1#的1/3焦煤:10-30%;焦煤:30-45%;瘦煤:7-15%。
6.根据权利要求2所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:所述1/3焦煤记为1/3焦煤2#,各单种煤占配煤总重量的百分比为:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;1/3焦煤2#:15-30%;粗粒镶嵌结构百分比<35%的1/3焦煤:0-15%;焦煤:30-45%;瘦煤:7-15%。
7.根据权利要求3所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:所述1/3焦煤记为1/3焦煤3#,各单种煤占配煤总重量的百分比为:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%; 粗粒镶嵌结构百分比≥35%1/3焦煤:15-30%;1/3焦煤3#:5-15%;焦煤:30-45%;瘦煤:7-15%。
8.根据权利要求4所述的Y值小于20mm的1/3焦煤参与的炼焦配煤方法,其特征在于:所述1/3焦煤记为1/3焦煤4#,各单种煤占配煤总重量的百分比为:气煤:0-5%;气肥煤:3-10%;肥煤:5-15%;粗粒镶嵌结构百分比≥35%1/3焦煤:15-30%;1/3焦煤4#:0-10%;焦煤:30-45%;瘦煤:7-15%。