CN102621142A - 一种测定水泥制成品碱性的指示剂及其应用 - Google Patents
一种测定水泥制成品碱性的指示剂及其应用 Download PDFInfo
- Publication number
- CN102621142A CN102621142A CN201210078112XA CN201210078112A CN102621142A CN 102621142 A CN102621142 A CN 102621142A CN 201210078112X A CN201210078112X A CN 201210078112XA CN 201210078112 A CN201210078112 A CN 201210078112A CN 102621142 A CN102621142 A CN 102621142A
- Authority
- CN
- China
- Prior art keywords
- indicator
- ethanol
- dissolved
- volume ratio
- cement product
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于建筑工程领域,涉及一种测定水泥制成品碱性的指示剂,通过以下步骤制备完成:(1)将酚酞溶于60%的乙醇,质量体积比为1:1000;(2)将百里酚酞溶于90%的乙醇,质量体积比为1:100;(3)将茜素红溶于90%的乙醇,质量体积比为4:1000;(4)将达旦黄溶于90%的乙醇,质量体积比为3:1000;(5)将以上步骤所得溶液按照相同体积充分混匀,制得测定水泥制成品碱性的指示剂。本发明所提出的指示剂具有生产原料简单、成本极低且方便实用的优点。
Description
技术领域
本发明属于施工检测领域,具体地,涉及一种测定水泥制成品碱性的指示剂。
背景技术
目前,我国正处于经济腾飞的高速发展时代,各项建设都在紧张进行中,在建筑领域,水泥是最常用到的一种基本原料,起了至关重要的作用。在水泥的生产中,常常会加入碱性激发剂,用来改善原料的化学性质,而它的掺入又会影响水泥制成品的强度。
现有的水泥碱性测试技术,大多是将水泥成品粉碎后制成溶液,而后测试pH值,该种方法技术复杂,成本高且需将水泥制成品粉碎后检测,不便使用;同时,部分不能粉碎的水泥制成品,如大型重要建筑等不能进行破坏性检测,因此,传统的检测方法几乎无法实现。
发明内容
本发明要解决的技术问题是克服现有的缺陷,提供了一种方便实用、成本低的测定水泥制成品碱性的指示剂。
为了解决上述技术问题,本发明提供了如下的技术方案:
一种测定水泥制成品碱性的指示剂,通过以下步骤制备完成:
(1)将酚酞溶于60%的乙醇,质量体积比为1:1000;
(2)将百里酚酞溶于90%的乙醇,质量体积比为1:100;
(3)将茜素红溶于90%的乙醇,质量体积比为4:1000;
(4)将达旦黄溶于90%的乙醇,质量体积比为3:1000;
(5)将以上步骤所得溶液按照相同体积充分混匀,制得测定水泥制成品碱性的指示剂。
优选地,通过以下步骤制备完成:
(1)将0.1g酚酞溶于100mL60%的乙醇;
(2)将1g百里酚酞溶于100mL90%的乙醇;
(3)将0.4g茜素红溶于100mL90%的乙醇;
(4)将0.3g达旦黄溶于100mL90%的乙醇;
(5)将以上步骤所得溶液充分混匀,制得测定水泥制成品碱性的指示剂。
本发明提出的测定水泥制成品碱性的指示剂在测定水泥制成品碱性中的应用。
本发明所提出的测定水泥制成品碱性的指示剂具有以下有益效果:
本发明所提出的指示剂生产原料简单、易用,成本极低,且方便实用,只需根据比例配制后涂抹于水泥制成品表面,通过颜色变化即可直观读出其pH,与以往方法相比,极其简便,对建筑物没有任何损害。
具体实施方式
制备实施例:
测定水泥制成品碱性的指示剂,通过以下步骤制备完成:
(1)将0.1g酚酞溶于100mL60%的乙醇;
(2)将1g百里酚酞溶于100mL90%的乙醇;
(3)将0.4g茜素红溶于100mL90%的乙醇;
(4)将0.3g达旦黄溶于100mL90%的乙醇;
(5)将以上步骤所得溶液充分混匀,制得测定水泥制成品碱性的指示剂。
以上制备的指示剂,可以用来检测任何标号的凝固后的水泥成品,其显色范围为:
酚酞:pH 8.2~10.0
百里酚酞:pH 9.4~10.6
茜素红:pH 10.0~12.0
达旦黄:pH 12.0~13.0
因此,pH位于8.2-13.0的水泥制成品都可以进行检测。
应用实施例:
将以上实施例制备所得的指示剂用于水泥制成品检测:
待检建筑物:兰州市安宁区十里店桥:桥墩,建成时间1954年。
检测部位:(1)桥墩 (2)桥身水泥护栏
检测方法:将所得指示剂涂抹于检测部位的表面,5-10s时间内,与标准比色卡进行颜色比对,根据对比颜色,确定碱性大小。
标准比色卡:显色范围是pH:8.2-13.0,一般水泥制成品的碱性范围为9-12。
检测结果:部位(1)的pH为10.4,部位(2)的pH为10.1。
最后应说明的是:以上所述仅为本发明的优选实施例而已,并不用于限制本发明,尽管参照前述实施例对本发明进行了详细的说明,对于本领域的技术人员来说,其依然可以对前述各实施例所记载的技术方案进行修改,或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (3)
1.一种测定水泥制成品碱性的指示剂,其特征在于,通过以下步骤制备完成:
(1)将酚酞溶于60%的乙醇,质量体积比为1:1000;
(2)将百里酚酞溶于90%的乙醇,质量体积比为1:100;
(3)将茜素红溶于90%的乙醇,质量体积比为4:1000;
(4)将达旦黄溶于90%的乙醇,质量体积比为3:1000;
(5)将以上步骤所得溶液按照相同体积充分混匀,制得测定水泥制成品碱性的指示剂。
2.根据权利要求1所述的一种测定水泥制成品碱性的指示剂,其特征在于,通过以下步骤制备完成:
(1)将0.1g酚酞溶于100mL60%的乙醇;
(2)将1g百里酚酞溶于100mL90%的乙醇;
(3)将0.4g茜素红溶于100mL90%的乙醇;
(4)将0.3g达旦黄溶于100mL90%的乙醇;
(5)将以上步骤所得溶液充分混匀,制得测定水泥制成品碱性的指示剂。
3.权利要求1或2所述的测定水泥制成品碱性的指示剂在测定水泥制成品碱性中的应用。